Article
The Removal of Zinc from Aqueous Solutions Using Malvaparviflora
إزالة الزنك من المحاليل المائية باستخدام نبات الخباز

Authors: Ahlam Mohammed Farhan احلام محمد فرحان --- Rasha Abed Jassim رشا عبد جاسم --- Nafeesa J. Kadhim نفيسه جبار كاظم
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2016 Volume: 13 Issue: 3 Pages: 482-488
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, the adsorption of Zn (NO3)2 is carried out by using surfaces of malvaparviflora. The validity of the adsorption is evaluated by using atomic absorption Spectrophotometry through determination the amount of adsorbed Zn (NO3)2. Various parameters such as PH, adsorbent weight and contact time are studied in terms of their effect on the reaction progress. Furthermore, Lagergren’s equation is used to determine adsorption kinetics. It is observed that high removal of Zn (NO3)2 is obtained at PH=2. High removal of Zn (NO3)2 is at the time equivalent of 60 min and reaches equilibrium,where 0.25gm is the best weight of adsorbant . For kinetics the reaction onto malvaparviflora follows pseudo first order Lagergren’s equation.

تم في هذا البحث دراسة امتزاز Zn (NO3)2 على سطح نبات الخباز و قياس سرعة الامتزاز باستخدام جهاز قياس المطيافية الذرية من خلال تحديد كمية Zn (NO3)2الممتزة .كما تم دراسة العديد من العوامل المؤثرة في سرعة التفاعل ومنها : الدالة الحامضية ,وزن السطح الماز وزمن التلامس بالإضافة الى ذلك تم استخدام معادلة Lagergren لتحديد حركيات الامتزاز.حيث لوحظ انه اعلى ازالة Zn (NO3)2) كانت عند pH=2 و زمن التماس للوصول الى التوازن عند (60 دقيقة) وافضل وزن (0,25غرام ).اما بالنسبة لحركيات الامتزاز فان التفاعل كان من الرتبة الاولى الكاذبة معادلة Lagergren على سطح نبات الخباز.


Article
Anticorrosion Behavior of Deposited Magnetite on Galvanized Steel in Saline Water Using RF-Magnetron Sputtering
السلوك المضاد للتآكل من ترسيب المغنتايت على الحديد المغلون في المياه المالحه بأستخدام الموجات الراديويه-الترذيذ الماكتروني الفعال

Authors: Nafeesa J. Kadhim نفيسه جبار كاظم --- Ahlam M. Farhan احلام محمد فرحان --- Harith I. Jaafer حارث ابراهيم جعفر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2018 Volume: 15 Issue: 4 Pages: 406-414
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Thin films of Magnetite have been deposited on Galvanized Steel (G-S) alloy using RF-reactive magnetron sputtering technique and protection efficiency of the corrosion of G-S. A Three-Electrodes Cell was used in saline water (3.5 % NaCl) solution at different temperatures (298, 308, 318 & 328K) using potentiostatic techniques with. Electrochemical Impedance Spectroscopy (EIS) and fitting impedance data via Frequency Response Analysis (FRA) were applied to G-S alloy with Fe3O4 and tested in 3.5 % NaCl solution at 298K.Results taken from Nyquist and Bode plots were analyzed using software provided with the instrument. The results obtained show that the rate of corrosion of G.S alloy increased with increasing the temperatures from 298 to 323K; and showed that deposition of Fe3O4 caused protection efficiency to reach 79.76% for G-S in 318K. In addition the enthalpy & entropy of activation were evaluated. Apparent energies of activation have been calculated for the corrosion process of uncoated and coated G.S alloy by sputtering technique in saline water (3.5 % NaCl). The morphological analysis was carried out using Scanning Electron Microscopy (SEM) technique.

تم في هذا البحث ترسيب غشاء رقيق من المغنتايت على سبيكة الحديد المغلون بأستخدام الموجات الراديويه – تقنية الترذيذ الماكتروني الفعال كطلاء حمايه,و درست كفاءة حماية التآكل للحديد المغلون في المياه المالحه (3.5% كلوريد الصوديوم)بأستخدام جهاز مقياس الجهد الساكن مع ثلاثة اقطاب, وبأستعمال جهاز قياس الممانعه الكهروكيميائيه الطيفي تم تحليل النتائج. أظهرت النتائج أن معدل سرعة التآكل للحديد المغلون بدون طلاء زاد بزيادة درجة الحراره (298-328) كلفن, و اظهرت النتائج أن ترسيب المغنتايت الناجم عن كفاءة حمايه بلغ 79.76% في درجة حراره 318 كلفن ,تم حساب قيم التغير في الانثالبي وطاقة التنشيط,حيث قدرت قيم الطاقات الظاهريه من التنشيط لعملية التآكل لسبيكة الحديد المغلون المطليه وغير المطليه في المياه المالحه (3.5% كلوريد الصوديوم), تم أجراء التحليل المورفولوجي بأستخدام تقنية المجهر الضوئي الالكتروني.