EFFECT OF SHOT PEENING TIME ON MECHANICAL PROPERTIES OF ALUMINUM ALLOY AA2024 –T4
تأثير زمن القصف بالكرات الفولاذية على الخواص الميكانيكية لسبيكة الالمنيوم AA2024-T4

Loading...
Loading...
Abstract

This research is devoted to study the effect of shot peening time with steel balls on mechanical properties of AA2024-T4 alloy. The test carried out using standard tensile specimens under various peening times (5, 10 , 15 , 20 and 30 minutes). Results showed an increase in yield and tensile strength values with increasing peening time up to 15 minutes where they were 355 & 505 MPa respectively. Also the strain hardening factor (n =0.26) and strength factor (k = 910 MPa) were maximum at this period of peening .On the other hand the maximum percentage of elongation was 22.7% obtained at 30 minute peening time .

تم في هذا البحث دراسة تأثير زمن القصف بكرات فولاذية على الخواص الميكانيكية لسبيكة الالمنيوم . AA2024 –T4 أجري فحص الشد على العينات المقصوفة بازمان مختلفة (5 , 10 ,15 ,20 , 30 ) دقيقة ، بينت النتائج زيادة قيم مقاومة الخضوع ومقاومة الشد لتسجل اعلى زيادة عند زمن قصف قدره ( 15 ) دقيقة حيث كانت مقاومة الخضوع والشد هي 355 &505 MPa على التوالي. كذلك لوحظ ان أعلى قيمة لمعامل الاصلاد الانفعالي (n = 0.26 ) ومعامل المتانة (k = 910 MPa ) سجلت عند تلك الفترة الزمنية ، في حين كانت أعلى نسبة أستطالة (22.7 % ) عند زمن قصف (30) دقيقة .


Article
USING FRICTION STIR PROCESS (FSP) TO IMPROVE THE PROPERTIES OF AA7020 ALUMINUM ALLOY WELDMENTS WELDED BY TUNGSTEN INERT GAS (TIG).
استخدام عملية الخلط الاحتكاكي (FSP ) لتحسين خواص ملحومات الالومنيوم (AA720 ) الملحومة بطريقة لحام القوس الكهربائي المحمي بالغاز الخامل (TIG)

Authors: Nashwa Abdul Hammied Saad --- Fadhel Abass Hashim --- Athraa Hussien Hashim
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2015 Volume: 13 Issue: 3 Pages: 50-60
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

One technique that may be used for repair of defects arising from process upsets is simply re-welding using the nominal process parameters. In such a case, it is important to know whether or not using a different welding process is capable of repairing defects in the already welded material (which will presumably have somewhat different properties as compared to the base metal). To examine this issue , three TIG weld passes were performed in aluminum AA7020 strips(6 piers of strips with 25 *200 *9.5 mm dimension ) by used (Al Mg 5 Cr ) filler metal according to AWS (A- 5.10) standard .Then friction stir weld pass were performed in exiting TIG welds (for only 3 piers of welded strips) with a tool rotation speed of (1000 rpm) and moved straight speed (welding speed ) of (14 m /min). Microstructure and Vickers hardness testes were done for weldments in three regions (base metal , TIG and FSP weld metals) to comparison . Results indicate that for this material and these conditions weld control parameters its possible to use another welding process to reduce defects in upsets process. Weld metallurgy is only slightly changed in the interface between TIG and FSP structures due to refining in exiting TIG welds structures. While there is no change in metallurgy of other TIG passes and base metal. Hardness in the weld metal after FSP pass increased by about 120% of the base metal.

أحد تقنيات معالجة العيوب التي تظهر في عملية التطبيق هي أعادة اللحام بأستخدام احد الطرق المعروفة ،في هذه الحالة يكون من الضروري معرفة فيما اذا كانت طرق اللحام المختلفة قادرة على معالجة العيوب في منطقة ملحومة ( والتي تكون لها خواص نوع ما مختلفة عن معدن الاساس ). ولفحص هذا الهدف ،تم اجراء ثلاث تمريرات لحام القوس الكهربائي المحمي بالغاز الخامل TIGعلى اشرطة من الالمنيوم AA7020 ( ستة ازواج من الاشرطة بأبعاد 9.5*20*25 ملم) وباسنخدام معدن الحشو نوع (Al Mg 5 Cr ) وتم اللحام حسب المواصفة الامريكية القياسية AWS (A – 5.10)، ثم تم اجراء تمريرة لحام احتكاكي (FSP) على ثلاث ازواج من الاشرطة الملحومه مسبقا بأستخدام اداة تدور بسرعة (1000 دورة / دقيقة )وتتحرك بسرعة خطية (سرعة اللحام) تساوي ( 14 متر/ دقيقة ) . ولغرض المقارنة بين الاشرطة الملحومة تم اجراء الفحص المجهري ,الصلادة فيكرز في المناطق الثلاثة (معدن الاساس ، ومعدن اللحام TIG ، ومعدن اللحام الاحتكاكي FSP) . بينت النتائج لهذا المعدن وضمن نفس هذه الظروف امكانية استخدام طريقة اللحام اخرى لتقليل من عيوب اللحام اثناء التطبيق. كذلك اشارت النتائج بوجود تنعيم بالبنية المجهرية للطبقة العليا للحام TIG عند اجراء اللحام الاحتكاكي عليها مع الاحتفاظ بنفس البنية المجهرية للطبقات البعيدة من لحام TIG ومعدن الاساس .اما بالنسبة للصلادة لمعدن اللحام بعد اجراء اللحام الاحتكاكي FSP فقد زادت حوالي 120% من قيمة الصلادة لمعدن الاساس .