Investigation of fatigue life of 6061-T6 aluminum alloys welded by metal inert gas welding
دراسة عمر الكلال لسبيكة الالمنيوم (6061-T6) الملحومة بطريقة الغاز الخامل (MIG)

Author: Nawres Jabar Nasser نورس جبار ناصر
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2015 Volume: 19 Issue: 3 Pages: 1-15
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The present research aims to investigate the effects of Metal Inert Gas (MIG) welding process on the mechanical properties and fatigue life of AA 6061 T6. A series of experimental techniques has been conducted to evaluate the mechanical and fatigue life. metal inert gas (MIG) have been carried out on Rolled sheet of 12mm thickness to obtain many butt welding joints with dimensions of (200 *100* 12) mm and with geometry of single and double V at (70⁰) and square using ER- 5356 as a filler metal and argon as shielding gas. The welded pieces were tested by X-ray radiography and Faulty pieces were excluded Welding joints were subjected to heat treatment including heating the joints in furnace to (150 °C) for one hour then air cooling to relief heating stress.All specimens subjected to Vickers hardness, tensile test and microstructure examination. The examinations were carried out to show the effect of MIG weld method on the joint microstructure. The fatigue test of the welds and base alloy were examined to obtain the S-N curve.Results showed a general decay of mechanical properties of MIG weld joint that is due to heat input during the welding process and low cooling rate.

يهدف البحث الى بيان تاثير لحام القوس الكهربائي المحمي بالغازMIG على الخواص الميكانيكية ومقاومة الكلال لسبيكة المنيوم 6061 T6. تم استخدام صفيحتين من المعدن في لحام عدة وصلات تناكبية بالابعاد mm (200*100*12) بعد عمل زاوية لحام تحضيرية من جهة واحدة ومن جهتين مقدارها (70) درجة على شكل حرف (V) وبدون زاوية باستخدام سلك لحام 5356 والاركون كغار حماية .بعد عملية اللحام والتاكد من خلو الوصلة من العيوب من خلال فحصها بواسطة جهاز X-ray radiographyاجريت معاملة حرارية تضمنت تسخين الوصلة في فرن كهربائي عند درجة حرارة (°C 150) لمدة ساعة ثم التبريد بالهواء بهدف ازالة اجهادات اللحام اجري اختبار صلادة عيانية ومكروية بطريقة فيكرز واختبار شد وفحص البنية المجهرية لبيان تأثير اللحام على الخواص الميكانيكية وطبق اختبار الكلال للحصول على منحني العمر.أظهرت النتائج تدنيا في الخواص الميكانيكية للعينات الملحومة مقارنة بالمعدن الاساس للخواص الميكانيكية بسبب كمية الحرارة الداخلة والتبريد البطئ.


Article
Mechanical Properties of MIG Joints for Dissimilar Aluminum Alloys (2024-T351 and 6061-T651)
الخواص الميكانيكية لوصلات لحام القوس الكهربائي (MIG) من سبائك الالمنيوم غير المتشابهة (2024 T351, 6061-T651)

Author: Nawres Jabar Nasser نورس جبار ناصر
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 3 Pages: 121-128
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The research aims to investigate the effects of GMAW or MIG welding process on the mechanical properties of dissimilar aluminum alloys 2024-T351 and AA 6061- T651. A series of experimental techniques have been conducted to evaluate mechanical properties of the alloys, by carrying out hardness, tensile and bending tests for welded and un-welded specimens.Metal inert gas (MIG) has been carried out on sheet metal using ER- 4043(AlSi5) as a filler metal and argon as shielded gas. The welded joints were tested by X-ray radiography and Faulty pieces were excluded. Welding joints without defects are subjected to heat treatment including heating the joints in furnace to 170 °C for half an hour then air cooling to relief welding stress.Tensile test was implemented for all specimens which prepared in the dimensions according to ASTM 17500 by using Testing machine smart series with preload value 100 kN. Vickers hardness test and microstructure examination were made, the last test was bending test which implemented on the welded and un welded specimens which machined into standard test specimen dimensions. Results of mechanical properties Using MIG welding process appear a general decay compared with un welded and in the dissimilar joint comparing with parent metal that is due to the microstructure change during the welding process. The location of the failure for welded specimens after all mechanical test was found predominantly along the heat affected zone ( HAZ ).but Unwedded specimens were failed near the center line of the specimen.

يهدف البحث الى بيان تاثير طريقة لحام القوس الكهربائي المحمي بالغاز على الخواص الميكانيكية لسبائك غير متماثلة من سبائك الالمنيوم عالية المتانة هما -T32024 , 6061-T6 حيث تضمن البحث اجراء سلسلة من التجارب التقنية لتقييم الخواص الميكانيكية للسبائك الملحومة وغير الملحومة وهي خصائص الشد و الصلادة, والحني والبنية المجهرية .انجز اللحام على صفيحتين من السبائك اعلاه للحصول على وصلات تناكبية بالابعاد 200)*100*8) ملم بعد عمل زاوية تحضيرية من جهة واحدة مقدارها 70 درجة حرف(V) ووصلة اخرى بنفس الابعاد بدون زاوية باستخدام سلك لحام 4043 ER والاركون كغار حماية بعد عملية اللحام والتاكد من خلو الوصلة من العيوب من خلال فحصها بواسطة جهاز X-ray radiographyاجريت معاملة حرارية تضمنت تسخين الوصلة في فرن كهربائي عند درجة حرارة 170 درجة مئوية لمدة نصف ساعة ثم التبريد بالهواء بهدف ازالة اجهادات اللحام .تم تحضير عينات اختبار الشد من وصلات اللحام والمعدن الاساس وفق المواصفة القياسية ASTM17500 وكذلك عينات اختبارالحني وفق المواصفةASTM (E 190-92) ثم اجراء عمليات تحضير من تنعيم وصقل لغرض فحص البنية المجهرية لمناطق اللحام والمعدن الاساس واجري اختبار صلادة عيانية, وصلادة دقيقة لبيان تأثير اللحام على الخواص الميكانيكية .اظهرت النتائج انخفاض في الخواص الميكانيكية للعينات الملحومة مقارنة بالمعدن الاساس وللسبائك غير متماثلة مع السبيكه الاساس وان موقع الفشل في منطقة الوسط للعينات اما العينات الملحومة فقد ظهر الفشل في المنطقة المتاثرة بالحرارة.