Silicon Carbide Particle Reinforced Aluminum Matrix Composite Prepared by Stir-Casting.

Authors: Ali Hubi Haleem --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 2 Pages: 442-449
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The developed aluminum matrix composite (AMCs) is considered to be a promising material for low and high temperature applications. Particles reinforced AMCs materials have high specific strength and modulus of elasticity, together with excellent heat resistance. Silicon carbide particles reinforced aluminum matrix composite (AMCs) for hardness, impact strength, and material toughness improvement were prepared. Stir-casting processing was optimized. The hardness, impact strength, and material toughness were evaluated. Under stir-casting, the silicon carbide particles were uniformly distributed in the aluminum and well bonded with aluminum matrix. The hardness and material toughness were increased 1.84 and 2.16 times respectively at particles weight fraction (10% ) that of the of the unreinforced aluminum based on the high hardness and deformation resistance of the silicon carbide particles.

تعتبر المواد المركبة المتقدمة ذات الأساس المكون من معدن الألمنيوم (AMCs) من المواد المهمة في التطبيقات ذات درجات الحرارة المرتفعة والمنخفضة. تمتاز هذه المواد (AMCs) بامتلاكها مقاومة نوعية ومعامل مرونة نوعي عالي مقترنة بمقاومة جيدة لدرجات الحرارة المرتفعة.تم تحضير مادة مركبة ذات أساس ألمنيوم مدعم بدقائق كاربيد السليكون بهدف تحسين الصلادة ومتانة المادة المركبة. اعتمدت طريقة السباكة بالخلط في اسلوب التحضير, حيث توزعت دقائق كاربيد السليكون بانتظام في مادة الأساس (الألمنيوم). إذ ارتبطت الدقائق بشكل جيد مع مادة الأساس. ازدادت الصلادة ومتانة المادة بمقدار( 1.84 , (2.16 مرة على التوالي وبنسبة تقوية وزنية ((10% بالمقارنة مع معدن الألمنيوم غير المقوى. وهذا يعود إلى الصلادة العالية ومقاومة التشوه الجيدة التي تمتاز بها دقائق كاربيد السليكون.


Article
Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.


Article
Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.


Article
Study of Some Mechanical Properties for Aluminum Reinforced by Alumina Fibers

Authors: Shaker Jahel Eddres --- Ali Hubi Haleem --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 607-615
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this research was to study the ability of improving the impact resistance and Vickers microhardness of composite material based on aluminum metal reinforced by 5, 10, and 15wt.% of chopped alumina fibers. Stirring casting method has been used to make composite material by using vortex technique which is used to pull the chopped alumina fibers to inside the melted aluminum and distributed them homogeneously.Regarding the impact test, results shown that the impact resistance of the composite material are more than that in the aluminum metal and these values are increased with increasing of the amount add fibers and they reached maximum values at (10 wt. %). Then they are decreased at (15 wt. %) but these values remain at higher values than that in the aluminum metal. While the Vickers microhardness reached maximum values at (15 wt. %).

يهدف البحث الحالي إلى دراسة تحسين مقاومة الصدمة و صلادة فيكرز المايكروية لمادة مركبة ذات أساس من معدن الألمنيوم مقوى بألياف الألومينا المقطعة وبنسب وزنية (5%, 10%, 15%). وتم استخدام طريقة السباكة بالمزج في تصنيع المادة المتراكبة باستخدام تقنية الدوامة والتي تعمل على سحب ألياف الألومينا ألمقطعه إلى داخل منصهر معدن الألمنيوم وتوزيعها خلاله بشكل متجانس.أظهرت نتائج اختبار الصدم إن مقاومة الصدمة للمادة المركبة أعلى مما هي عليه لمعدن الألمنيوم وتزداد هذه القيم مع زيادة النسب الوزنية لألياف الألومينا والى حد (10%) ثم تسلك سلوكا مغايرا لكنها تبقى محافظة على قيم أعلى مما هي عليه لمعدن الألمنيوم . في حين تصل صلادة فيكرز المايكروية أعلى قيمها عند التقوية بألياف الألومينا المقطعة وبكسر وزني ((15%.