Preparation and Characterization of Nickel Oxide Thin Films by Electrostatic Spray Technique
تحضير ودراسة خصائص الاغشية الرقيقة لاوكسيد النيكل المحضرة بتقانه الرش الكهربائي المستقر

Loading...
Loading...
Abstract

A simple, inexpensive, and home–built electrostatic spray deposition (ESD) system with stable cone-jet mode was used to obtain nickel oxide (NiO) thin films on glass substrates kept at temperature of 400°C. The primary precursor solution of 0.1 M concentration hydrated nickel chloride dissolved in isopropyl alcohol. The structural, optical and electrical parameters were studied. The optical absorbance spectra for the studied samples showed its maximum around 280 nm. On the other hand, thickness interferometry measurements on the tested samples showed that film thickness was around 400 nm. The optical energy gap of the prepared NiO samples was determined to be 3.75 eV and the maximum value of refractive index was determined to be 2.1 at 350 nm.

تم استخدام طريقة ترسيب الرش الكهربائي المستقر البسيطة وغير المكلفة والمتجانسة للحصول على اغشية رقيقة لاوكسيد النيكل المرسبة على قواعد زجاجية بدرجة حرارية 400 سيليزي. المحلول الاولي كان كلورايد النيكل المهدرج المذاب في ايسوبروبيل الكحول بتركيز 0.1 مولاري.ثم دراسة الخصائص التركيبية والكهربائية والبصرية ولذلك طيف الامتصاص البصري للاغشية المحضرة اظهرت اعلى قيمة لها عند الطول الموجي 280 نانو متر. وكذلك ،تم قياس السمك بطريقة التداخل البصري حيث ان سمك الاغشية كان حوالي 400 نانومتر. فجوة الطاقة البصرية للاغشية والعينات المحضرة حددت ب 3.75 الكترون فولت واقصى قيمة لمعامل الانكسار كان بحدود 2.1 عند 350 نانومتر.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2016 (1)