Hollow fiber ultrafiltration (UF) membranes were prepared using Polyethersulfone(PES), alcohol (n-Propanol) as additive and N, N-dimethylacetamide (DMAc) as asolvent. Asymmetric hollow fiber UF membranes were spun by wet phaseinversion method from 17 wt% solids of PES/additive/NMP solutions. The alcoholadditive was n-Propanol while the external coagulant was water. Effects of n-Propanol concentrations in the dope solution on morphology and separationperformance of PES hollow fiber UF membranes were investigated. UFmembranes were characterized in terms of scanning electron microscope (SEM)while UF experiments were conducted using polyethylene glycol (PEG20,000MW)and poly (vinyl pyrrolidone) (PVP 40,000MW), as a solute. It was found that the PESUF membrane morphology changed from long two finger-like structure through ashort two finger-like structure to the two void-like structure as n-propanolconcentration in the dope solution increased from 5 to 20 wt % using water as abore fluid; pure water permeation fluxes (PWP) increased from 47 to 201L/m2.h.bar while rejections of PEG MW20,000 and PVP MW40,000 for wet-spunPES hollow fiber membranes were decreased with increased of n-propanolconcentration up to 20%. Using above method, PES hollow fiber UF membranewith high pure water permeation flux could be prepared while the molecularweight cut-off of PES hollow fiber membranes is approximately 20,000.

وآحول البروبانول آمضاف (PES) اعشية بولمرية مجوفة حضرت من مادة بولي ايثر سيلفون(wet phase آمذيب للبولمر .تحضر الاغشية تم باستخدام طريقة تغير الطور (DMAC) ومادة. (PES/additive /NMP) الصلبة من محاليل (PES) من (% 17 )من مادة inversion method)المادة المضافة آانت البروبانول بينما الماء استخدم آمخثر خارجي للاغشية .تاثير ترآيزعلى البنية الداخلية والخارجية للاغشية واداءها (PES) البروبانول في محلولتم التحقق منها في هذه الدراسة .بينما التجارب التي تمت باستخدام بولي (SEM) للاغشية وصفت بدلالة (ultra filtration)آمذيبات . (PVP) (40000MW) وبولي فينل بروليدون (PEG) (20000 MW) اثيلين آلايكولمن النتائج تم ايجاد تغيير في ترآيب الاغشية من طبقتين طويلتين نوع الاصبع الى طبقتينآلما زاد ترآيز البروبانول في محلول (Void) قصيرتين نوع الاصبع ومن ثم الى طبقتين نوع( زاد من- 47 (PWP) 5) باستخدام الماء آمخفف داخلي وان معدل جريان النافذ - البوليمر من (% 20201 باستخدام الطريقة اعلاه يمكن الحصول على معدل تدفق عالي للماء النقي ) (L/m2.hr.bar).( ويمكن استخدام هذه الاغشية لفصل آافة المواد المذابة التي تمتلك وزن جزيئي اآثر من( 20000

Ultrafiltration membrane --- hollow fiber --- phase inversion method --- polyethersulfone --- alcohol additive

Two different polyvinyl alcohol/polyvinyl chloride (PVA/PVC) hollow fiber composite nanofiltration membranes were prepared after PVC hollow fiber membranes were coated using dip-coating method with PVA aqueous solution, which was composed of PVA, fatty alcohol polyoxyethylene ether (AEO9), and water [PVA/AEO9/water (4:0.5:95.5) wt%]. Effect of two different PVC hollow fiber immersion times in coating solution were studied. Cross-section, internal and external surfaces of the PVC hollow fibers and PVA/PVC composite nanofiltration membranes structures were characterized by scanning electron microscopy (SEM), pure water permeation flux and solutes rejection. It was found that, the coating layer thickness on the outer surface of the 19 wt% PVC hollow fiber was thin and about (6µm), while the coating solution penetrates through the outer edge of the PVC hollow fiber and it looks like sponge-like structure with increase of the dip-coating time from 20 to 30 sec. Besides, the pure water permeation flux decreases and solutes rejection increases with an increase of the coating time from 20 to 30 sec for the two PVA/PVC composite nanofiltration membranes.Molecular weight cut-off (MWCO) of the PVA/PVC composite nanofiltration membranes were in the range of NF (i.e. 200-3000 Mw).

تم تحضير نوعين من اغشية الالياف المجوفة والنانوية المكونة من PVA/PVC بواسطة طريقة الاكساء بالتغطيس في محلول PVA المائي المكون من بولي فنيل الكحول PVA, الماء و(AEO9) Fatty Alcohol Polyoxyethylene Ether وبنسب وزنية مئوية(0.5, 95.5, 4) على التوالي.تم دراسة تاثير وقتين مختلفين لزمن اكساء اغشية الالياف المجوفة على التركيب الداخلي والخارجي لاغشية الياف PVA/PVC المركبة والنانوية باستخدام جهاز المجهر الالكتروني الماسح (SEM) وايضا على اداء الاغشية في فصل المذابات وانتاج الماء النقي. وجد ان سمك طبقة الاكساء للالياف المحضرة من19% PVC كان رقيقا وبسمك µm6بينما يدخل محلول الاكساء خلال السطح الخارجي ويسد التراكيب الاصبعية الشكل عندما يزداد زمن الاكساء من 20-30 ثانية. بالاضافة الى ذلك, تقل نفاذية الماء النقي ويزداد فصل المذابات بزيادة زمن الاكساء من 20-30 ثانية لكلا نوعي الالياف المجوفة النانوية. ان الوزن الجزيئي للمذابات المفصولة(MWCO) لاغشية اليافPVA/PVC المجوفة النانوية كان ضمن مدى اغشية الفصل النانوية (200- 3000Da ).

Hollow fiber composite membrane --- Nanofiltration --- Polyvinyl Chloride --- Polyvinyl Alcohol --- Morphology --- Separation performance.