Early and delayed effect of 2% chlorhexidine on the shear bond strength of composite restorative material to dentin using a total etch adhesive

Authors: Rabeia J. Khalil --- Abdulla M.W. Al-Shamma عبد الله محمد وجيه الشماع
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2015 Volume: 27 Issue: 2 Pages: 24-31
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the mostimportant problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2%chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours andthree months of water storage.Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which wereacid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth eachaccording to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application forgroups I and III which were tested after twenty-four hours and three months respectively, while the distal water wasapplied for 60 seconds before the application of adhesive for group II and IV which were tested after twenty-fourhours and three months respectively.The Prime and Bond® NT™ adhesive (Dentsply) was applied and cured,Composite (Ceram X mono, Dentisply) was applied through special mold with 2 mm thickness and light cured, Thenall specimens were stored in distilled water 37oC until the time of testing of each group.Shear bond strength test wasperformed at the end of the storage period (24 hours or 3 months).Results:T-test results showed high statistically significant reduction in shear bond strength (SBS) in non CHX group IV(tested after 3 months) compared to non CHX group II (tested after 24 hours)(P< 0.01). In CHX groups I (tested after24 hours) and III (tested after 3 months), results showed no statistically significant differences in shear bondstrength(p> 0.05).On the other hand result showed statistically no significant differences between groups I and II in 24hours shear bond strength (P> 0.05). After 3 months water storage, there was statistically high significant differencesbetween the groups III and IV (P< 0.01).Conclusion: the use of 2 % CHX glocounate solution after acid etching and before bonding of dentin have noadverse effect on immediate bond strength (24 hours storage), and was effective in reducing degradation of resindentinbond interface after three months of water storage

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2015 (1)