Mechanical And Physical Properties oF a Hybrid Composite With Basis oF Aluminum
الخواص الميكانيكية والفيزيائية لمتراكب هجين ذي اساس من الالمنيوم

Author: Raed N. Razooqi رائد نجيب رزوقي
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2017 Volume: 22 Issue: 5 Pages: 148-155
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research inculdes using a powder metallurgy technique (PM) to manufacture composites with a basis of (99.7%) purity of Aluminum, and by adopting a volumetric ratios via adding both copper with purity and Graphite with (99.8%) purity as reinforced materials. The Copper is added in a constant ratio and with different ratios (0, 3, 6, 9, 12) and (15%). The pressing process was in one way with a pressure of (700-MPa).for forming. This research studied effect of the reinforcing on the physical and mechanical properties of composites after sintering them with a temperature of (600◦C) for two hours by an oven with a heat rate of (4◦C/min).The results show that the Graphite content is inversely proportional with the volumetric and apparent density and the thermal conductivity when the composite F (Al+4%Cu) got high properties. Furthermore , both composites F and A had the same behavior for mechanical properties such as hardness and radial compression strength .In addition , the total porosity and the ability of water absorption was increase with Graphite ratio in composites, as example the ability of water absorption increased by (0.61%) for composite B (Al+4%Cu+3%Gr) Compared with composite F.

تضمن البحث استخدام تقانة المساحيق (PM) في تصنيع المتراكبات ذات اساس من الالمنيوم بنقاوة 99.7%)) مع اعتماد النسب الحجمية في اضافة كل من النحاس بنقاوة 99.7%)) والكرافيت بنقاوة (99.8%) كمواد تدعيم مشترك , اضيف النحاس بنسبة ثابتة وهي 4%)), اما الكرافيت فقد اضيف بنسب مختلفة وهي 0, 3, 6, 9, 12, 15)%) وتم الكبس باتجاه واحد وبضغط كبس مقداره ((700-Mp لغرض التشكيل.تم دراسة تأثير التدعيم المشترك على الخواص الفيزيائية والميكانيكية للمتراكبات بعد تلبيدها بدرجة حرارة (600◦C) لمدة ساعتين باستخدام فرن كهربائي وبمعدل تسخين (4◦C/min).اظهرت النتائج ان علاقة محتوى الكرافيت بالكثافة الحجمية والظاهرية والتوصيلية الحرارية علاقة عكسية فالمتراكب (F) (Al+4%Cu+15%Gr) الاكثر انخفاضا عند زيادة النسبة مقارنة بالمتراكب ((A (Al + 4%Cu) الذي امتلك خواص اعلى وهي ذات السلوك بالنسبة للخواص الميكانيكية الصلادة ومقاومة الانضغاط القطرية. تزداد نسبة المسامية الكلية والظاهرية وقابلية امتصاص الماء بزيادة نسبة الكرافيت في المتراكبات اذ ازدادت قابلية امتصاص الماء للمتراكب (B) (Al + 4%Cu + 3%Gr) بمقدار (0.61%) مقارنة بالمتراكب F)).


Article
Effect of Aluminium Content on Some Physical and Mechanical Properties of The compounds With Base of Ceramic
تأثير تغير محتوى الألمنيوم على بعض الخواص الفيزياوية والميكانيكية لمتراكبات ذات اساس سيراميكي

Loading...
Loading...
Abstract

This research includes the study of the effect of the Aluminium (Al) addition as reinforcement material at a different weight percentages (4,8,12,16,20) % to ceramic matrix material formed from ( Silicon Dioxide , Oxide Chromium (III) , Titanium Dioxide ) with fixed ratios of elements (Co , Ni) for each of them , by using powder metallurgy technique with pressure of (5) tons were used for forming. We have studied the effect of the Aluminium addition on some physical and mechanical properties of prepared sample after sintered it at (1000 Cº) for (2hr) .The results shown that the Aluminium addition have been enhanced the physical and mechanical properties of the Composites samples , When increasing the proportion of aluminum from (% 4) to (% 20) we note that Apparent density , specific gravity and hardness of the composite (C): [ Cr2O3 + Al + Co + Ni ] for example, had improved by (% 3.2) , (% 4.8) and (% 13) respectively, as for Composites (B): [ TiO2+ Al+ Co+ Ni ] and (A): [SiO2 + Al + Co + Ni ] are similar behavior with composite (C) but at low rates according to form of the composite .It is also found that relation between the Aluminium addition with the porosity and water absorption for all compound is an inverse relation , while their relations with the apparent density , specific gravity and other mechanical is a direct relation exact . And the Composite (C) which is containing (Cr2O3) showed the best properties with for all additional rates as a comparing with the other Composites.

يتضمن هذا البحث دراسة تأثير إضافة الألمنيوم ( Al ) كمادة تدعيم وبنسب وزنية مختلفة (4,8,12,16,20)% الى مواد ذات أساس سيراميكي متكونة من ( ثاني اوكسيد السليكون , ثاني اوكسيد التيتانيوم , اوكسيد الكروم الثلاثي ) مع نسبة ثابتة من عنصري ( Ni ,Co ) لكل منهم. باستخدام تقانة ميتالورجيا المساحيق وبضغط كبس (5 ton) لغرض التشكيل .تم دراسة تأثير نسب الإضافة على الخواص الفيزياوية والميكانيكية بعد تلبيدها بدرجة حرارة (1000°C) لمدة ( 2 hr) . وقد تم التوصل إلى أن زيادة نسبة الألمنيوم تعمل على تحسين الخواص الفيزيائية والميكانيكية للنماذج فعند زيادة نسبة الألمنيوم من (%4) إلى (%20) نلاحظ إن الكثافة الظاهرية والوزن النوعي والصلادة للمتراكب (C):[ Cr2O3+Al+Co+Ni]على سبيل المثال قد تحسنت بالنسب (%3.2) و (%4.8) و (%13) على التوالي أما المتراكبان (B):[TiO2+Al+Co+Ni] و SiO2+Al+Co+Ni] [:(A) فيتشابهان بالسلوك مع المتراكب C ولكن بنسب خواص أقل تبعاً لنوع المتراكب . وان علاقة نسبة إضافة الألمنيوم بالمسامية الظاهرية وقابلية امتصاص الماء للمتراكبات كافة هي علاقة عكسية , بينما تكون علاقتها طردية بالكثافة الظاهرية والوزن النوعي والخواص الميكانيكية الأخرى وان المتراكب (C)الذي يحتوي على اوكسيد الكروم الثلاثي (Cr2O3) أظهر أفضل الخواص ولجميع نسب الألمنيوم مقارنة بالمتراكبات الأخرى .