The Influence of Immersion in Different Chemical Solutions on the Mechanical and Physical properties of (Epoxy/Styrene-Butadiene Rubber) Blend Reinforced with Nano Copper Oxide

Author: Rana M. Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (B) Engineering Pages: 104-109
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this work was to evaluate some mechanical and physicalproperties of a composite material which consists of (epoxy/styrene-butadienerubber) blend as a matrix, reinforced with copper oxide (CuO) with a weightfraction 3%, and the composite material was manufactured by hand lay-up.The optimum mixing ratio was (75:25) % of epoxy and (SBR) was chosen toaccomplish the work due to its highest impact strength (2.1KJ/m2). The teststhat were performed on the material were: tensile test, impact test, thermalconductivity test, and the absorption test, in addition to the microscopicimaging using scanning electron microscope (SEM), to determine the surfacemorphology of the specimens. Sodium hydroxide (NaOH) and hydrochloricacid (HCl), both (0.1) normal concentration solutions, were used for theimmersion. The results showed that CuO nanofiller improved tensile andimpact properties of the blend, besides increasing resistance to diffusion ofchemicals into the material. The results showed that the immersion in HClsolution increased the impact strength of the composite from (2.27KJ/m2) to(3.38KJ/m2), and also increased the tensile strength from (9.2MPa) to (9.8MPa), while immersion in NaOH solution decreased the tensile strength to(7.3MPa), but increased the impact strength to (2.42KJ/m2). Thermalconductivity was (0.21W/m.°C) before immersion in solutions, but changed to(0.27W/m.°C) and (0.24W/m.°C) after immersion in HCl and NaOHrespectively. The weight gain after immersion in NaOH was higher than weightgain after immersion in HCl.


Article
Effect of water absorption on some mechanical and physical properties of epoxy/polyurethane blend reinforced with nano silica powder
تأثير امتصاصية الماء على بعض الخصائص الميكانيكية والفيزيائية على خليط الأيبوكسي / بولي يوريثان المدعم بدقائق السيليكا النانوية

Author: Rana M. Salih رنا مهدي صالح
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2017 Volume: 15 Issue: 32 Pages: 92-98
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of this work is to evaluate some mechanical and physical properties (i.e. the impact strength, hardness, flexural strength, thermal conductivity and diffusion coefficient) of (epoxy/polyurethane) blend reinforced with nano silica powder (2% wt.). Hand lay-up technique was used to manufacture the composite and a magnetic stirrer for blending the components. Results showed that water had affectedthe bending flexural strength and hardness, while impact strength increased and thermal conductivity decreased. In addition to the above mentioned tests, the diffusion coefficient was calculated using Fick’s 2nd law.

يهدف البحث الى دراسة بعض الخصائص الفيزيائية والميكانيكية(الصدمة،الصلادة،متانة الانحناء، معامل التوصيل الحراري) وكذلك معامل الأنتشار للماء في مادة متراكبة اساسها خليط من الأيبوكسي والبولي يوريثان مدعمة بدقائق السيليكا النانوية وبكسر وزني 2%. استخدمت تقنية القولبة اليدوية لتصنيع النماذج مع استخدام الهزاز المغناطيسي لخلط المكونات. اوضحت النتائج ان متانة الصدمة تزداد بعد الغمر بالماء بينما تقل متانة الانحناء والصلادة والتوصيل الحراري. تم حساب معامل الأنتشار للنماذج استنادا الى قانون فك الثاني في الأنتشارية.


Article
Preparation and Study of some Physical Properties of (Polystyrene/Ethel vinyl acetate) Blend Nanofibers

Authors: Hanaa J. Khadhim --- Rana M. Salih
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 4 Pages: 1267-1274
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This search aims to fabricate immiscible nanofibers (Polystyrene/Ethyl phenyl acetate) blends with different average porous for different applications by electrospinning technique. PS and EVA were mixed by (50/50) to prepare 0.1 (w/v) con.%, each polymer dissolved in (Tetra hydro furan ). Resulting nanofibers morphology was studied by Atomic force microscopy (AFM) and high optical resolution microscope (HORM) , Contact angle between the water and the surface of nanofibers by contact angle analyzer also studied for (hydrophilic or hydrophopic behavior ). FTIR test for checking the emergence or not of new bonds in the nanofibers blend was performed. AFM Results show that the prepared blends of (PS+EVA) have homogenous needle structures (nanofibers) at three dimensions , while the results of (HORM) shows the nonwoven structures contain intermediates pours structure , Contact angle results show that decrease of the contact angle after adding the EVA polymer to PS, and this refers to the (EVA/PS) nanofibers blends have hydrophilic behavior.

يهدف هذا البحث الى تحضير انسجة نانوية من خلائط غير متجانسة من الياف (بولي ستايرين / اثيل فاينيل استيت) النانوية ومعدلات مختلفة المسامسية لتطبيقات مختلفة باستخدام تقنية الغزل الكهربائي . تم خلط اثيل فاينيل استيت مع البولي ستايرين بنسبة (50/50) لتحضير تركيز (0.1 w/v) ، حيث اذيب كل بوليمير في مذيب التتراهيدروفيوران . خواص المورفولوجية للنسيج المحضر درست باستخدام مجهر القوة الذرية AFM ومجهر ضوئي عالي الوضوح . كما استخدم محلل زاوية التماس لقياس زاوية التماس وتحديد سلوك النسيج المحضر من ناحية الماء . كما استخدم مطياف الاشعة تحت الحمراء لمعرفة ظهور او عدم ظهور اواصر جديدة في النسيج النانوي المحضر. اثبتت نتائج مجهر القوة الذرية ان النسيج المحضر يحتوي تراكيب ابرية متجانسة والتي هي عبارة عن الالياف النانوية بتوزيع منتظم في ثلاثة ابعاد . كما اثبتت نتائج المجهر الضوئي ان النسيج المحضر يحتوي ضمن تركيبه على بعض التراكيب المسامية . اما محلل زاوية التماس فقد اثبت ان سلوك النسيج المحضر يتحول من كاره للماء لالياف البولي ستايرين النانوية الى محب للماء بعد اضافة اثيل فاينيل استيت.


Article
Preparation and Study of some Physical Properties of (Polystyrene/Ethel vinyl acetate) Blend Nanofibers

Authors: Hanaa J. Khadhim --- Rana M. Salih
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 4 Pages: 1267-1274
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This search aims to fabricate immiscible nanofibers (Polystyrene/Ethyl phenyl acetate) blends with different average porous for different applications by electrospinning technique. PS and EVA were mixed by (50/50) to prepare 0.1 (w/v) con.%, each polymer dissolved in (Tetra hydro furan ). Resulting nanofibers morphology was studied by Atomic force microscopy (AFM) and high optical resolution microscope (HORM) , Contact angle between the water and the surface of nanofibers by contact angle analyzer also studied for (hydrophilic or hydrophopic behavior ). FTIR test for checking the emergence or not of new bonds in the nanofibers blend was performed. AFM Results show that the prepared blends of (PS+EVA) have homogenous needle structures (nanofibers) at three dimensions , while the results of (HORM) shows the nonwoven structures contain intermediates pours structure , Contact angle results show that decrease of the contact angle after adding the EVA polymer to PS, and this refers to the (EVA/PS) nanofibers blends have hydrophilic behavior.

يهدف هذا البحث الى تحضير انسجة نانوية من خلائط غير متجانسة من الياف (بولي ستايرين / اثيل فاينيل استيت) النانوية ومعدلات مختلفة المسامسية لتطبيقات مختلفة باستخدام تقنية الغزل الكهربائي . تم خلط اثيل فاينيل استيت مع البولي ستايرين بنسبة (50/50) لتحضير تركيز (0.1 w/v) ، حيث اذيب كل بوليمير في مذيب التتراهيدروفيوران . خواص المورفولوجية للنسيج المحضر درست باستخدام مجهر القوة الذرية AFM ومجهر ضوئي عالي الوضوح . كما استخدم محلل زاوية التماس لقياس زاوية التماس وتحديد سلوك النسيج المحضر من ناحية الماء . كما استخدم مطياف الاشعة تحت الحمراء لمعرفة ظهور او عدم ظهور اواصر جديدة في النسيج النانوي المحضر. اثبتت نتائج مجهر القوة الذرية ان النسيج المحضر يحتوي تراكيب ابرية متجانسة والتي هي عبارة عن الالياف النانوية بتوزيع منتظم في ثلاثة ابعاد . كما اثبتت نتائج المجهر الضوئي ان النسيج المحضر يحتوي ضمن تركيبه على بعض التراكيب المسامية . اما محلل زاوية التماس فقد اثبت ان سلوك النسيج المحضر يتحول من كاره للماء لالياف البولي ستايرين النانوية الى محب للماء بعد اضافة اثيل فاينيل استيت.