Effect of industrial powder on mechanical properties of glass fiber reinforced epoxy composite
تأثير المساحيق الصناعية على الخواص الميكانيكية للمواد المركبة المدعمة بألياف الزجاج

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding and investigated. The composites constituents were epoxy resin as the matrix, 6% volume fractions of Glass Fibers (G.F) as reinforcement and 3%, 6% of industrial powder (Calcium Carbonate CaCO3, Potassium Carbonate K2CO3 and Sodium Carbonate Na2CO3) as filler. Density, water absorption, hardness test, flexural strength, shear stress measurements and tests were conducted to reveal their values for each type of composite material. The results showed that the non – reinforced epoxy have lower properties than composites material. Measured density results had show an incremental increase with volume fraction increase and water absorption, hardness, flexural strength and shear stress results had show an incremental increase with volume fraction increase and with smaller particle size.

تم في هذا البحث تحضير مواد متراكبه بواسطة طريقة القولبة اليدوية ودراسة خصائصها. تتكون المواد المتراكبة من راتنج الايبوكسي كماده اساس وبألياف الزجاج بكسر حجمي6% وكذلك 3%و 6% مساحيق صناعية تدعيم من (كاربونات الكاليسوم CaCO3, كاربونات البوتاسيوم K2CO3, كاربونات الصوديوم Na2CO3). تم اجراء فحوصات الكثافة وامتصاصية الماء، فحص الصلادة, مقاومة الانحناء و اجهاد القص للكشف عن قيمها لكل نوع من المواد المتراكبة. اظهرت النتائج ان الايبوكسي غير المقوى يمتلك خواص اقل من المواد المتراكبة. عند اجراء اختبارات الكثافة فان النتائج اظهرت بان الكثافة تزاد مع زياد الكسر الحجمي وامتصاصية الماء والصلادة ومقاومة الانحناء واقصى اجهاد قص بانها تزداد مع زيادة الكسر الحجمي مع اصغر حجم حبيبي.


Article
Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin
تأثير الطلاء لبعض المواد المتراكبة التي اساسها مواد طبيعية على سلوك بلى التعرية لراتنج الايبوكسي المدعم بالالياف الزجاجية

Loading...
Loading...
Abstract

In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than natural based material composites and the specimen (Epoxy+6%glass fiber+6%RHA) has higher resistance erosion than composites reinforced with carrot powder and sawdust at 30cm , angle 60°, grin size of sand 425µm , temperature 30Ċ , 300 gm salt content in 2liter of water and 15 hour. Coating specimen with mixed epoxy resin -RHA with particles size in the range (1.4-4.2) µm improves erosion wear resistance characteristics of the coated specimen, coating thickness was (16 ± 1) μm and after erosion at (15 hour) the thickness was (10) μm .

تم في هذا البحث تحضير المواد المتراكبة بوساطة طريقة القولبة اليدوية . تتكون المواد المتراكبة من راتنج الايبوكسي ماده اساس والياف الزجاج مادة تقوية بكسر حجمي 6% و مساحيق طبيعية محضرة ( رماد قشور الرز و مسحوق الجزر و بودرة الخشب ) بكسر حجمي (3% , 6% ) . دراسة سلوك بلى التعرية والطلاء بوساطة النفايات الطبيعية (رماد قشور الرز) مع راتنج الايبوكسي بعد التعرية . النتائج اظهرت بان الايبوكسي غير المقوى يمتلك مقاومة للتعرية قليلة من المواد المتراكبة التي اساسها مواد طبيعة والعينة (الايبوكسي + 6%الالياف زجاج + 6% رماد قشور الرز) تملك مقاومة للتعرية من المواد المتراكبة المدعمة بمسحوق الجزر وبودرة الخشب عند25 سم ، زاوية 30º، حجم دقائق تعرية 850 مايكرون , ودرجة حرارة 25Ċ ,200 غم ملح في 3 لتر من ماء 15 ساعة . طلاء العينات براتنج الايبوكسي مع رماد قشور الرز مع حجم حبيبي ضمن المدى (1.4-2.4) مايكرون لتحسين خواص مقاومة التعرية للعينات التي تم طلائها , وسمك الطلاء كان (16 ± 1) مايكرون وبعد التعرية عند 15 ساعة اصبح سمك الطلاء (10) مايكرون .