Study the effect of annealing on the Structural and Optical properties of Copper oxide films prepared by Sol-Gel Spin Coating
دراسة تأثير التلدين على الخواص التركيبية والبصرية لأوكسيد النحاس المحضر بطريقة الطلاء الدوراني (SOL-GEL)

Authors: Thuraya yarb ثريا يعرب صبري --- Riyadh sami رياض سامي عنتر --- Ali saleh علي اسماعيل صالح
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 5 Pages: 148-153
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research is to study the effect of annealing on the structural and optical properties on the thin films copper oxide(CuO,Cu2O) was deposited on glass substrate by using technique Spin-Coating (Sol-Gel) with speed (3000 RPM) during the time of the deposition (30 sec). Was the preparation of the solution using a material of copper acetate (Cu(C2H3O2)2.H2O) as a basis and Diethanolamine (DEA) (C4H11NO2) as installed and Ethanol (C2H6O) as a solvent, the solution prepard at a concentration of 0.2M. The annealing at temperatures (250,350, 450,550)°C for one hour. We have investigated the Structural characteristics using (XRD and AFM) analyses ,from of (XRD) analyses show that the thin films are polycrystalline and annealing the films at 350 °C completely converts these films to tenorite structure with composition of CuO. And from (AFM) analyses show that the grian size increases with increasing annealing temperature. Either optical characteristics by spectroscopy UV in the range of wavelength (300-1100) nm. It is observed that the transmittance and allowed direct optical band gap of the films decreases with the increase of annealing temperature from 4.0 eV to 3.92 eV.

في هذا البحث تمت دراسة تأثير التلدين على الخواص التركيبية والبصرية لأغشية اوكسيد النحاس CuO,Cu2O)) المرسبة على قواعد من الزجاج باستخدام تقنية الطلاء الدوراني Sol-Gel)) وبسرعة (3000 RPM) خلال زمن ترسيب (30sec). حضر المحلول بأستخدام مادة خلات النحاس المائية (Cu(C2H3O2)2.H2O) كمادة اساس ومادة Diethanolamine (DEA) (C4H11NO2) كمادة مثبتة وكحول الايثانول (C2H6O) كمادة مذيبة وحضر المحلول بمولارية 0.2M . تم تلدين الاغشية بدرجات حرارة (250,350,450,550)°C لمدة ساعة واحدة. تم دراسة الخصائص التركيبية من خلال فحوصات XRD,AFM)), وخلال فحص(XRD) تبين ان الاغشية ذات تركيب متعدد التبلور وعند تلدين الغشاء بدرجة حرارة 350°C يتحول كليا الى تركيبCuO)) , ومن خلال فحص (AFM) تبين أن معدل الحجم الحبيبي يزداد بزيادة درجة حرارة التلدين, اما الخصائص البصرية تم فحصها بواسطة مطيافية الاشعة المرئية وفوق البنفسجية ضمن مدى الطول الموجي 300-1100)nm). ويلاحظ ان النفاذية وفجوة الطاقة البصرية للاغشية تقل بزيادة درجة حرارة التلدين من 4.0 eV الى 3.92 eV. .


Article
Study The Molarity Influence on the structural properties of titanium oxide (TiO2) Prepared with (Sol_Gel)
دراسة التأثير المولاري على الخصائص التركيبية لأوكسيد التيتانيوم TiO2 المحضر بطريقة Sol _ Gel

Authors: Riyadh sami رياض سامي عنتر --- Rafea A. Munef رافع عبد الله منيف --- Fares Saleh Atallah فارس صالح عطاالله
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 2 Pages: 162-170
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This report was conducted to study the molar effect on structural characteristics of Titanium dioxide TiO2 ,the deposition of films on glass substrates was done by using sol gel solution with Spin-Coting method (speed =3000 rpm) during 30 sec of the deposition where the solution have been prepared using Titanium hydroxyl Material Ti[O(CH2)3(CH3)]4 and C4H11NO2 as Fixative and Ethanol as a solvent. we have prepared different concentrations of solution (0.05, 0.10 , 0.15, 0.20, 0.30) M ,the films have been annealing with temperature (500 °C), we have investigated the Structural characteristics using (XRD,AFM and SEM) analyses. The (XRD) results have shown that the Anatase phase is the prevalent phase when the concentrations (0.05 and 0.10)M and after increase the concentration start changes gradually from Anatase phase to Rutile phase when the concentration (0.2)M. The SEM analyses have approved that the film has good topography. The granules had a rhombus form then its shape became cluster with the increasing of concentration . The (AFM) have shown that the membranes had nano- thickness,and they are soft with good coating

تم في هذا البحث دراسة التأثير المولاري على الخصائص التركيبية لثنائي أوكسيد التيتانيوم TiO2 حيث رسبت الاغشية على ارضيات من الزجاج باستخدام محلول (Sol_Gel) وبتقنية Spin_Coting وبسرعة RPM 3000 خلال زمن ترسيب قدره 30sec وتم تحضير المحلول باستخدام مادة اوكسيد التيتانيوم المائي Ti[O(CH2)3CH3]4 و [C4H11NO2] كمثبت والايثانول كمذيب (C3H8O2) وحضر المحلول بمولاريات مختلفة منM (0.05,0.1,0.15,0.2,0.3) ويتم تلدين الأغشية بدرجة حرارة 500℃ ,وتم دراسة الخصائص التركيبة من خلال فحوصات (XRD & AFM,SEM). حيث تبين من النتائج XRD)) ان طور الانتاس هو الطور السائد عند التركيزM 0.05)& (0.1 وبعد زيادة التركيز يبدا التحول التدريجي بالطور حيث يتحول من الانتاس الى الروتايل عند تركيز 0.2M, وبينت فحوصات SEM)) ان الغشاء ذو طبوغرافية جيدة ,وان شكل الحبيبات يكون معيني ثم يتحول بزيادة التركيز الى عناقيد زهرية الشكل, ومن خلال فحوصات(AFM) تبين ان الاغشية ذات سمك نانوي وناعمة وذات اكساء جيد .