Mechanical Properties for Polymer Hybrid Composites Reinforced by Fibers and Particles
الخواص الميكانيكية لمتراكبات بوليمرية هجينة مقواةبالالياف والدقائق

Author: Ruaa Haitham Abdel-Rahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 3 Part (A) Engineering Pages: 635-643
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The Mechanical properties of hybrid composites based on epoxy resin (ER) filled with metal powders (Al) and Glass fibers (GF) are studied. The specimens are prepared using hand lay-up techniques according to ASTM standard for different volume fractions of fiber, particles& matrix material. Glass fibers (GF) are one of the most useful filler materials in composites, its major use being the manufacture of components in the aerospace, automotive, and leisure industries. The epoxy was reinforced with GF:( metal powders)in the ratio 10%:40%, 20%:30%, 30%:20%, and 40%:10%. It was observed that in the ratio 40%:10% has the maximum(UTS), fracture strength, flexural strength, fracture toughness and hardness increase with the increase of volume fraction of fibers when compared to unfilled epoxy.

تم في هذا البحث دراسة الخواص الميكانيكية من متراكبات هجينة ذات اساس راتنج الايبوكسي مقواة بدقائق معدنية من الالمنيوم والياف الزجاج.العينات حضرت بطريقة الصب اليدوي وفقا لمعيار ASTM لكسورحجميةمختلفة منالألياف والدقائقوالمادة الاساس.الألياف الزجاجية(GF) هي واحدة منموادحشوالأكثر فائدةفي المواد المتراكبة، وتدخل في كثير من الصناعات منهاصناعة الطائرات والسيارات، والصناعاتالترفيهية. الايبوكسي كانت تقويته مع GF: MPفي نسبة10٪: 40٪، 20٪: 30٪، 30٪: 20٪، و 40٪: 10٪. لوحظأنه نسبة 40%:10% تمتلك اقصى اجهاد شد, مقاومة كسر,مقاومة انحناء,متانة كسر وصلادة ونلاحظ تزداد مع زيادة الكسر الحجمي للالياف مقارنة مع الايبوكسي الغير مدعم .


Article
Effect of Filler Type on some Physical and Mechanical Proparties of Carbon Fibers / Polyester Composites
تأثیر نوع الاضافه على بعض الخواص الفیزیائیه والمیكانیكیه من الیاف كاربون ومتراكبات البولي استر

Authors: Osama Sultan Muhammed --- Abbas Khammas Hussein --- Ruaa Haitham Abdel-Rahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 15 Part (A) Engineering Pages: 2905-2924
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present study, traditional and hybrid composites were prepared by Hand lay-upmolding and investigated. The composites constituents were unsaturated polyester resinas the matrix, 3% and 6% volume fractions of carbon fibers as reinforcement and 3% ofAl2O3, Al, Cement and local Gypsum (calcium sulfate anhydrate CaSO4) as fillerparticles. The investigated physical properties were density, porosity while themechanical properties were tensile properties, bending modulus of elasticity. Theexperimental results showed that increased volume fraction of carbon fibers to (6%) ledto increase in physical properties (density, porosity. As for the mechanical properties,carbon fiber composites and (3% carbon fibers/Al2O3)-contained hybrid composites gavethe higher tensile and fracture strength, carbon fiber then gypsum composites gave thehigher bending modulus.


Article
MECHANICAL PROPERTIES OF EPOXY BASED HYBRID COMPOSITES REINFORCED BY GLASS FIBERS AND SiC PARTICLES.
الخواص الميكانيكية لمتراكبات هجينة اساس ايبوكسي مقواة بواسطةالياف الزجاج ودقائق السليكون كاربيد

Loading...
Loading...
Abstract

In the present study mechanical properties of pure epoxy and hybrid composites were studied. Pure epoxy and hybrid composites were prepared by Hand lay-up molding and investigated. The composites constituents were epoxy resin as the matrix, 4% and 8% volume fractions of glass fibers as reinforcement and 4% and 8% of silicon carbide as filler particles. The investigated mechanical properties were hardness, tensile properties (ultimate tensile strength (UTS), fracture strength), and impact properties (impact strength, fracture toughness). The experimental results showed that the mechanical properties, Hybrid composite with (Epoxy +8%GF+8% SiC) has the maximum hardness of (82) shore D, Hybrid composites with (Epoxy +8%GF+4% SiC) has the maximum (UTS), fracture strength, impact strength (Gc) & fracture toughness (Kc) of (107) MPa, (108) MPa, (9900) J/m2, (27. 487) MPa.m-1/2 respectively

تم في هذا البحث دراسة الخواص الميكانيكية لمتراكبات هجينة ذات اساس من الايبوكسي. تم تحضير المتراكبات الهجينة وراتنج الايبوكسي بواسطة المقالبة اليدوية وتم فحصها. مكونات المواد المتراكبة كانت راتنج الايبوكسي كماده اساس و(4%، 8%) كسر حجمي من الياف الزجاج كمادة تقوية و (4%، 8%) من كاربيد السليكون كدقائق تقوية.الخواص الميكانيكيه التي تم فحصها كانت ( الصلادة , الشد (اقصى مقاومة شد , مقاومة الكسر ) والصدمة ( مقاومة الصدمة ومتانة الكسر). أظهرت النتائج التجريبية بالنسبه للخواص الميكانيكية فأن المتراكبات الهجينة الحاوية على ( ايبوكسي/8%الياف زجاج %8%سليكون كاربيد ) اعطت اعلى صلادة شور مقدارها (82) شور D , والمتراكبات الهجينة مع (ايبوكسي /8%الياف زجاج/ 4%سليكون كاربيد) كانت لها اعلى مقاومة شد , مقاومة كسر, مقاومة الصدمة , متانة كسر من (107 MPa) , (108MP)و (9900 J/m2) , (27. 487 MPa. m-0.5) على التوالي .