Article
Influence of Laser Irradiation Times on Properties of Porous Silicon
تأثير أزمنة تشعيع الليزر على خواص السليكون المسامي

Authors: Oday A. Abass عدي أركان عباس --- Alwan M. Alwan علوان محمد علوان --- Sabah M. Ali صباح محمد علي
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2007 Volume: 4 Issue: 4 Pages: 640-646
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Porous silicon (P-Si) has been produced in this work by photoelectrochemical (PEC) etching process. The irradiation has been achieved using diode laser of (2 W) power and 810 nm wavelength. The influence of various irradiation times on the properties of P-Si material such as P-Si layer thickness, surface aspect, pore diameter and the thickness of walls between pores as well as porosity and etching rate was investigated by depending on the scanning electron micrograph (SEM) technique and gravimetric measurements.

تم تحضيرالسليكون المسامي باستخدام عملية القشط الضوئي-الكهروكيميائي. التشعيع اجري باستخدام ليزر شبة موصل بقدرة (2 W) وطول موجي 810 nm. تم تحري ودراسة تأثير أزمنة التشعيع المختلفة على خواص مادة السليكون المسامي مثل سمك طبقة السليكون المسامي, طبيعة السطح, قطر المسام و سمك الجدارن بين المسامات بالاضافة الى المسامية ومعدل القشط بالاعتماد على تقنية المجهر الكتروني الماسح ) (SEM و القياسات الوزنية.


Article
Effect of Zn Substitution on thestructural Properties of Cobalt Ferrite Nano Particles Prepared Via Sol-Gel Route
تأثير تعويض الزنك على الخواص التركيبية لفرايت الكوبلت ذو الدقائق النانوية والمحضر بالطريقه (sol-gel ).

Authors: Tahseen H. mubarak تحسین حسین مبارك --- Sabah M Ali صباح محمد علي --- Laith S Mahmood ليث شاكر محمود
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2013 Volume: 9 Issue: 1 Pages: 56-62
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Zinc substituted cobalt ferrite nanoparticles (CoxZn1-xFe2O4, with x = 0.0, 0.1, 0.2, 0.3, 0.4, and 0.5) were prepared via sol-gel route and the effect of zinc concentration on Lattice constant and particle size and powder‎ densitywere investigated. X-ray diffraction analysis confirms the formation of ferrites in nano phase. The Results showed that the particle size decreasing from (22) to (16) nm with increasing the concentration of ‎zinc to the (x= 0.5). The lattice constant increased from (8.36682) to )8.40943)A0 with increasing the concentration of zinc to (x = 0.5), while the theoretical powder‎ density decreased from (5.3225) to (5.2237) g/cm3 by ‎increasing zinc ion concentration to value at (x=0.5).‎

تم في هذا البحث تحضير فيرايت الكوبالت المعوضة بايونات الزنك ذات السلسلة الفيراتية Co1-xZnxFe2O4), حيث تأخذ xقيم من الصفرالى (0.5 بالطريقة الكيميائية الحديثة(sol-gel auto combustion) المحضرة وأظهرت النتائج بأن حجم دقائق المسحوق يقل حجم من 22 الى 16 نانومتر مع زيادة تركيز ايونات الزنك . إن ثابت الشبيكة يزداد من 8.367 إلى 8.40943 انكستروم بزيادة تركيز ايونات الزنك إلى القيمة (x=0.5 ) .إما بالنسبة لكثافة المسحوق فإنها تقل من (5.3225) غم/سم3 بزيادة تركيز ايونات الزنك وصولا إلى القيمة5.2237 غم/سم3 عند x= 0.5)).