Article
Failure Characteristics Of Boiler Pipes In Al-Emsaeb Electric Power Plants

Author: Sami Ibrahim Jafar
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 101-104
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Boilers are a main part of electric power plants , which mostly suffer from different types of failures. Overheating & corrosion are considered to be the most important causes of failures in boiler pipes in power plants. These Failures can be categorized as long- term & short term overheating . Failures also caused by collection of corrosion products, deposits or other foreign material on the inner surfaces of tubes boiler. Several failed samples from different locations in the boilers was tested. The microscopic examination of failure areas of the pipes, showed different types of distortion and clear appearance of corroded area in the microstructures of the pipe metal. The micro structural analysis of failure and the causes of the failure have been determined and the mechanism of corrosion in one of Iraqi electric power plant has been discussed in this work.

المرجل هو الجزء الرئيسي في وحدات الطاقة الكهربائيةو الذي غالبا ماتعاني انابيبه من انواع مختلفة من الفشل. يعتبر الافراط بالتسخين والتاكل من اسباب الفشل . يتمثل الفشل بفترات الافراط بالتسخين الطويلة والقصيرة. يحدث الفشل احيانا بسبب تجمعات من الرواسب الناتجة من التاكل او المواد الغريبة على السطوح الداخلية للانابيب. اختيرت في هذا البحث عينات فاشلة من مواقع مختلفة من انابيب مراجل وحدات الطاقة الكهربائية العاملة في المسيب وتم تحليل الفشل ودراسة انواع التاكل ومحاولة التعرف على اسبابه .


Article
Failure Characteristics Of Boiler Pipes In Al-Emsaeb Electric Power Plants

Author: Sami Ibrahim Jafar
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 87-100
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Boilers are a main part of electric power plants , which mostly suffer from different types of failures. Overheating & corrosion are considered to be the most important causes of failures in boiler pipes in power plants. These Failures can be categorized as long- term & short term overheating . Failures also caused by collection of corrosion products, deposits or other foreign material on the inner surfaces of tubes boiler. Several failed samples from different locations in the boilers was tested. The microscopic examination of failure areas of the pipes, showed different types of distortion and clear appearance of corroded area in the microstructures of the pipe metal. The micro structural analysis of failure and the causes of the failure have been determined and the mechanism of corrosion in one of Iraqi electric power plant has been discussed in this work.

المرجل هو الجزء الرئيسي في وحدات الطاقة الكهربائيةو الذي غالبا ماتعاني انابيبه من انواع مختلفة من الفشل. يعتبر الافراط بالتسخين والتاكل من اسباب الفشل . يتمثل الفشل بفترات الافراط بالتسخين الطويلة والقصيرة. يحدث الفشل احيانا بسبب تجمعات من الرواسب الناتجة من التاكل او المواد الغريبة على السطوح الداخلية للانابيب. اختيرت في هذا البحث عينات فاشلة من مواقع مختلفة من انابيب مراجل وحدات الطاقة الكهربائية العاملة في المسيب وتم تحليل الفشل ودراسة انواع التاكل ومحاولة التعرف على اسبابه .


Article
Effect of Applied of Pre-Stresses on Corrosion Behavior of 304 Stainless Steel in 1N H2SO4
تأثير تسليط الأجهادات المسبقة على سلوك تأكل الفولاذ المقاوم للصدأ نوع 304 في محلول N H2SO41

Authors: Sami Ibrahim Jafar --- Israa Abud Alkadir --- Samah Abdul Kareem Khashin
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 3 Part (A) Engineering Pages: 600-612
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research is devoted to study the effect of applying different pre-tensile stresses (255,305,355,405,455,505 555 and 605) MPa on the microstructure, hardness and corrosion behavior of 304 stainless steel in 1N H2SO4. The stress-strain curve was drawn for standard (304) stainless steel in laboratory environment. The curve was divided into three zones. At zone one the values of elastic pre-stresses vary between (σ0 - σpro.) MPa. The results showed; that the corrosion rate was very little increased compared with that of as received (304) stainless steel. The microstructure presented undeformed austenitic grains and the hardness value was (157.433) Hv. At zone two the value of plastic pre-stress varies between (σpro.- σ U.T.S) MPa. The corrosion rate increases after applying pre-stress between (σ255 - σ 455) MPa. The microstructure showed that the austenitic grains begin to deform in the direction of applied pre-stresses. The maximum hardness at this region was (229.2) Hv, but at higher pre-stress (σ455 – σ 605) MPa, the corrosion rate decreases. The microstructure inspection shows the deformed austenitic grain and ά-martensitic phase needle are appeared inside austenitic grains and the hardness reached the maximum value (332.433) Hv. At zone three the values of pre-stresses are between (σ605 - σf) MPa. The results showed that the corrosion rate increases. The investigation of microstructure showed that there are distortion in austenitic grains and ά- martensite phase observed inside austenitic grains. The hardness reached the maximum value at (354.3) Hv. The necking of gauge length of specimens occurs in specimens and this leads to deterioration in original properties

يهدف البحث الحالي الى دراسة تأثير التشوه على البارد من خلال تسليط اجهادات شدية مسبقة مختلفة القيم (255,305,355,405,455,505 555,605) ميكاباسكال على البنية المجهرية والصلادة المجهرية وسلوك التاكل للفولاذ المقاوم للصدأ نوع 304 في محلول1N H2SO4.. تم قياس معدل التأكل قبل وبعد تسليط الاجهادات المسبقة . تم رسم منحنى الاجهاد- الانفعال لعينة قياسية من 304 فولاذ مقاوم للصدا في جو المختبر.قسم المنحني الى ثلاثة مناطق: المنطقة الاولى : تكون قيم الاجهادات المرن بين (σ0 – σpro) ميكا باسكال , حيث أظهرت النتائج حدوث زيادة طفيفة في معدل التأكل مقارنة مع عينات غير مجهدة من الفولاذ المقاوم للصدأ 304 . وعند اجراء الفحص المجهري تبين ان البنية الدقيقة هي عبارة عن حبيبات اوستنايتية غير مشوهة ومن نتائج فحص الصلادة كانت صلادة الفولاذ المقاومة للصدأ غير المجهد هي .(157.433Hv) وعندالمنطقة الثانية: تتغير قيم الاجهاد اللدن المسبق بين (σpro. – σ U.T.S) ميكا باسكال, حيث أظهرت نتائج قياس معدل التأكل أن معدل التاكل قد أزداد بعد تسليط اجهاد المسبق بين (σ255 – σ 405 ) ميكا باسكال . ومن نتائج فحص البنية المجهرية تبين ان البنية المجهرية هي عبارة حبيبات اوستنايتية مشوهة بأتجاه الاجهاد المسلط وتبين من نتائج فحص الصلادة ان أعلى قيمة للصلادة في تلك المنطقة هي 229.2 Hv)).لكن عند قيم الاجهادات المسبقة العالية بين ( (σ455 –σ 605 ميكا باسكال , انخفض معدل التأكل بشكل كبير. كما تبين من فحص البنية المجهرية انها عبارة عن حبيبات اوستنايتية مشوهة مع ظهورطور ά-martensitic أبري الشكل داخل حبيبات الاوستنايت, مما أدى ذلك الى أزدياد قيمة الصلادة حيث بلغت أعلى قيمة مقدارها (332.433 Hv).أما في المنطقة الثالثة : تتغير فيها قيم الاجهادات المسبقة المسلطة بين ( (σ605 –σf ميكا باسكال , حيث أظهرت النتائج حدوث زيادة في معدل التأكل . ومن نتائج الفحص المجهري تبين حدوث تشويه كبير لحبيبات الاوستنايت مقارنة بالاجهادات المسبقة المسلطة أعلاه أضافة الى وجود طور ά-martensitic أبري الشكل داخل حبيبات الاوستنايت ونسبته عالية ,حيث بلغت أفضل قيمة للصلادة (354.3 Hv)لكن التخصر الحاصل في العينات أدى الى حدوث تدهور الخواص الاصلي الاصلية.