Article
Effect of Corrosion Time on Critical Buckling Load of AISI 304 Columns

Authors: Hussain J. Al-alkawi --- Samih K. Al-najjar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 7 Part (A) Engineering Pages: 742-747
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work Corrosion buckling interaction behavior of AISI 304 stainless steel circular columns was investigated. Long and intermediate columns diameter of (6 mm) are tested in as received and corroded condition. Corroded columns are tested after embedded it in soil for different times. Rotating buckling machine test was used to evaluate the critical buckling load (pcr) under dynamic compression loads. By using Perry Robertson formula, experimental work results are compared. The results showed that increasing in corrosion time (embedding time), the reduction in critical buckling load increases also. Maximum reduction of buckling load value are (2.28%, 1.37%) for long and intermediate column respectively as compared with as received condition.


Article
Effect of Degassing Process of Squeeze Casting Aluminum Alloy on Tensile Strength Under Different Pressures
تأثير عملية إزالة الغازات لطريقة السباكة بالعصر على مقاومة الشد لسبيكة المنيوم تحت ضغوط مختلفة

Authors: Hussain J. Al-alkawi --- Dhafir S. Al-Fattal --- Samih K. Al-najjar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 2 Part (A) Engineering Pages: 320-330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Degassing technique currently applied to cast aluminum alloys due to its technological and economic advantages. The present work aimed to study the effect of degassing technique of cast aluminum alloy (LM2) under different pressures using squeeze casting process. Inert argon gas was pumped into the molten aluminum with flow rate (2,5-5-7)l/min. at constant pumped duration (5min.). Different applied pressures were used(17, 35, 52) MPa. The test was performed at room temperature. The physical and mechanical properties of degassed samples were measured and compared with non-degassing (ND) samples. The results showed that the best condition of degassing is found at 2.5 l/min flow rate and 35 MPa applied pressure. It was found that a slight difference is observed for the density and the lowest value of porosity was obtained at 2.5 l/min flow rate and 52 MPa applied pressure.

تقنية أزالة الغازات تطبق في الوقت الحالي لصب سبائك الألمنيوم بسبب مزاياها التكنولوجية والاقتصادية . يهدف البحث الحالي إلى دراسة تأثير عملية إزالة الغازاتالناتجة من السباكة لسبيكة الالمنيوم (LM2)تحت ضغوط مختلفة باستخدام طريقة السباكة بالعصر. تم ضخ غاز الاركون الخامل إلى منصهر الالمنيوم بمعدلات تدفق ( 2.5- 5 - 7) لتر/دقيقة وبزمن ضخ ثابت (5) دقائق. تم تسليط ضغوط مختلفة (17 – 35 – 52 ميكاباسكال) . اجري الاختبار في درجة حرارة الغرفة. تم حساب الخواص الميكانيكية والفيزيائية لنماذج المصبوبات المزالة الغاز عنها وقورنت النتائج مع النماذج الغير مزالة الغازات عنها.أظهرت النتائج أن معدل ضخ 2.5 لتر/دقيقة وبضغط 35 ميكاباسكال حقق افضل النتائج. وجد أن هنالك اختلاف طفيف في قيم الكثافة, وحصول على اقل قيمة للمسامية عند معدل ضخ 2.5لتر/دقيقة وبضغط 52 ميكاباسكال.