Study on coloring of aluminum alloys by Microplasma oxidation (MPO) technique

Author: Samir H. Awad
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 293-300
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Over the past years, great scientific and industrial achievements have been made in the domain of existing many coloring technologies of aluminum alloys for different applications ,mostly, coloring after anodizing for decoration and physical applications. However, the coloring after anodizing process strongly depends on thickness and color of Al2O3 thin film , and on its porosity and their distribution which can affect the hardness of alumina layer. Also, this technology requires sequenced processes and controlled conditions to get the desired color. The MPO technology has recently been studied as a novel and effective means to provide improved properties such as thick and hard ceramic coating with excellent load-bearing and wear resistance properties on aluminum alloys. In the present study, the MPO technique was used for deposition of ceramic layers colored with different colors and hardness better than those produced by anodizing . This study is expected to promote the research in coloring of aluminum alloys so as to meet the increased demands for colored aluminum alloys for hard environmental applications ,where, such know-how can not be gained easily from the literature and the internet.

ظهرت خلال السنوات الأخيرة تطورات بحثية وصناعية في مجال تلوين سبائك الألمنيوم بطرق مختلفة ولأغراض مختلفة , أشهرها التلوين بعد الانودة لأغراض الديكور والتطبيقات الفيزيائية .على كل حال, التلوين بعد الانودة يعتمد على عدة عوامل أهمها سمك ولون غشاء الالومينا Al2O3 المتكون قبل التلوين وكثافة المسامات وتوزيعها فيه وهي المؤثرة في صلادة الغشاء , وكذلك التلوين بعد الانودة يتميز نسبيا بالتعقيد الناتج من سلسة الخطوات والظروف الواجب توفرها للحصول على اللون المطلوب.حديثا, أثبتت تكنولوجيا الأكسدة بالبلازما المايكروية MPO الحديثة تفوقها الاقتصادي والفني على باقي التقنيات في الترسيب السريع لطبقات سيراميكية سميكة ، صلدة جداً ،مقاومة للتآكل وملائمة لظروف التحميل الترايبولوجية الشديدة. في هذا البحث, تم استخدام هذه التكنولوجيا في تلوين سبائك الألمنيوم بألوان مختلفة ذات صلادة أعلى من صلادة الطبقات الملونة بعد الانودة , كخطوة قد تسهم في تطوير البحث في هذا المجال في ظل تزايد الطلب على الألمنيوم الملون ملائم للظروف الجوية الشديدة خصوصا وان الشركات والبحوث المتوفرة لاتعطي تفاصيل دقيقة عن أسرار عملها في هذا المجال.


Article
Study on coloring of aluminum alloys by Microplasma oxidation (MPO) technique

Author: Samir H. Awad
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 293-300
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Over the past years, great scientific and industrial achievements have been made in the domain of existing many coloring technologies of aluminum alloys for different applications ,mostly, coloring after anodizing for decoration and physical applications. However, the coloring after anodizing process strongly depends on thickness and color of Al2O3 thin film , and on its porosity and their distribution which can affect the hardness of alumina layer. Also, this technology requires sequenced processes and controlled conditions to get the desired color. The MPO technology has recently been studied as a novel and effective means to provide improved properties such as thick and hard ceramic coating with excellent load-bearing and wear resistance properties on aluminum alloys. In the present study, the MPO technique was used for deposition of ceramic layers colored with different colors and hardness better than those produced by anodizing . This study is expected to promote the research in coloring of aluminum alloys so as to meet the increased demands for colored aluminum alloys for hard environmental applications ,where, such know-how can not be gained easily from the literature and the internet.

ظهرت خلال السنوات الأخيرة تطورات بحثية وصناعية في مجال تلوين سبائك الألمنيوم بطرق مختلفة ولأغراض مختلفة , أشهرها التلوين بعد الانودة لأغراض الديكور والتطبيقات الفيزيائية .على كل حال, التلوين بعد الانودة يعتمد على عدة عوامل أهمها سمك ولون غشاء الالومينا Al2O3 المتكون قبل التلوين وكثافة المسامات وتوزيعها فيه وهي المؤثرة في صلادة الغشاء , وكذلك التلوين بعد الانودة يتميز نسبيا بالتعقيد الناتج من سلسة الخطوات والظروف الواجب توفرها للحصول على اللون المطلوب.حديثا, أثبتت تكنولوجيا الأكسدة بالبلازما المايكروية MPO الحديثة تفوقها الاقتصادي والفني على باقي التقنيات في الترسيب السريع لطبقات سيراميكية سميكة ، صلدة جداً ،مقاومة للتآكل وملائمة لظروف التحميل الترايبولوجية الشديدة. في هذا البحث, تم استخدام هذه التكنولوجيا في تلوين سبائك الألمنيوم بألوان مختلفة ذات صلادة أعلى من صلادة الطبقات الملونة بعد الانودة , كخطوة قد تسهم في تطوير البحث في هذا المجال في ظل تزايد الطلب على الألمنيوم الملون ملائم للظروف الجوية الشديدة خصوصا وان الشركات والبحوث المتوفرة لاتعطي تفاصيل دقيقة عن أسرار عملها في هذا المجال.

Keywords


Article
Glazing and Coloring of Cellular Concrete Blocks

Authors: Samir H. Awad --- Elham Abd Al-Majeed --- Mohammed Al-Issawi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 3 Pages: 678-688
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Thermostone is one of the important materials which have been spraying glazed using different glass mixtures based on alkaline (A5), lead glasses (A4) and their composition at different glass/water (G/W) ratios using a special holder have been designed to keep the glazing on top of thermostone and thereby, protect the other surfaces from damage. Physical and mechanical properties, color, roughness and other properties have been investigated with the aid of microscopic analysis. Duplex layers of A5-glazed layer on pre-coated A4-layer (total thickness of 1.4mm) proved their superiority among A4-glazed layer (0.2mm) and unglazed surfaces, especially those glazed at G/W ratio of 30/70 where the standard thickness (1.5mm) for glazing of pours bodies due to the action of composition of A5- glaze mixture and its effects in sealing the pores and thereby, improving all the properties. The glazing process in this study introduced a glazed thermostone with improved properties using spray technique by means of compressive strength ,porosity, hardness , water absorption and bulk density aspects.

ان الكتل الخرسانية الخلوية او ما يسمى بالثرمستون اصبح له استخدامات كثيرة في السنوات الاخيرة في عمليات البناء والانشاءات والتقطيع في الدور و العمارات نظرا لتميزه بمواصفات مثل العزل الحراري الخاص للاستخدام في البنايات من الداخل والخارج , خفة وزنه و كبر حجم المقاطع المستخدمة.ان مقاومة الانضغاط لهذه المادة والمسامية العالية تحد من استخدام الثرمستون لبعض التطبيقات علاوة على ان سطوح الثرمستون بعد البناء تحتاج عمليات تشطيب وانهاء باستخدام السمنت او السيراميك والمواد الاخرى لحماية السطوح ولغرض الحصول على الديكور والمنظر المناسب. تم في هذا البحث تزجيج سطوح عينات من الثرمستون المجهز من قبل معمل ثرمستون كربلاء بطريقة الرش وباستخدام خلطات زجاجية مختلفة ,قلوية (خلطة A5 بدرجة 920C°) , وزجاج الرصاص (خلطة A4 بدرجة 550C°) وخلطات اخرى مركبة من مزيجهما عند نسب زجاج/ماء (G/W) مختلفة وباستخدام حواضن خاصة لغرض تزجيج السطح العلوي فقط وحماية بقية السطوح من التلف.المواصفات الفيزيائية والميكانيكية ,اللون ,خشونة السطح وفحوصات بصرية تم دراستها بمساعدة الفحص المجهري باستخدام المجهر الضوئي لتقيم الطبقات الناتجة بعد التزجيج. النتائج اظهرت امكانية استخدام عملية التزجيج الثنائي الطبقة (طبقة من زجاج A4 ثم طبقة من زجاج A5 بسمك اجمالي 1.4ملم) في خلق طبقة زجاجية ملتصقة بالسطح الاساس وبسمك ضمن السمك القياسي للتزجيج (1.5ملم) وتحسين مواصفات الثرمستون وتحقيق الديكور والجمالية والتلوين المطلوبة. البحث في هذا الموضوع يحتاج الكثير من الدراسات المستقبلية لدعم هذه المحاولة.هذه الطبقة الثنائية وبالخصوص عند نسبة G/W مساوية 30/70 حققت مواصفات افضل من كل الخلطات ومن مواصفات الثرمستون بدون تزجيج نفسه بسبب خاصية مكونات الطبقة A5 القلوية في غمر المسامات وتحسين الصفات بوجود الطبقة الزجاجية. النتائج اوضحت ان مقاومة الانضغاط و الصلادة قد تحسنت بعد التزجيج. كذلك المسامية ,امتصاصية الماء ,الكثافة و خشونة السطح قد تحسنت بعد التزجيج ايضا بالوان جذابة اختلفت باختلاف تركيب الزجاج. نتائج الفحص المجهري اثبتت تأثير التزجيج في الحصول على اجسام قليلة المسامية خصوصا تلك المزججة عند نسبة G/W مساوية الى 30/70 .


Article
STUDY THE OPTICAL PROPERTIES OF COPPER OXIDE THIN FILM DEPOSITED BY COLD SPRAY
دراسة الخواص البصرية لأغشية أوكسيد النحاس الرقيقة المرسبة بالرش البارد

Authors: Samir H. Awad سمير حامد عواد --- Riyam I. Jadaan ريام عماد جدعان
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 4 Pages: 439-454
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Copper oxide (CuO) thin films were prepared by cold spray process using inert atmosphere (helium gas) without employing any catalyst. CuO dry powder was sprayed onto microscope glass slide by heating carrier gas at 100, 200, 300, and 400 °C ,with 30 bar gas pressure onto substrates of 300 ± 5°C at different angles 0°, 30°, 45°, then study the effect of these parameter on the structural, and optical properties of the resulted thin film. The X-ray diffraction (XRD) studies showed that the as-deposited CuO has the monoclinic structure with low strain. SEM images show that the thin film has no porosity or agglomeration and deposit on the entire region. The CuO thin film exhibited a high transmittance of about (96%)

تم ترسيب أغشية أوكسيد النحاس باستخدام طريقه الرش البارد عن طريق استخدام غاز خامل (غاز الهليوم) بدون استخدام أي مواد مساعدة. حيث تم رش مسحوق أوكسيد النحاس الجاف على أرضيات زجاجية المسخنة بدرجه حرارة 300درجه مئوية بواسطة تسخين الغاز بدرجات (100,200,300,400) درجة مئوية بضغط 30 بار بزوايا ترسيب مختلفة ( 0, 30, 45) .بعدها تم دراسة تأثير هذه المتغيرات على الخواص التركيبية والبصرية للأغشية الناتجة .حيث اظهرت نتائج حيود الاشعه السينيه أن الاغشيه المترسبه تمتلك تركيب أحادي الميل .أما صوره المجهرالالكتروني الماسح فاظهرت بان الغشاء لا يحوي على اي مسامات او تكتلات وان المسحوق مترسب على كل الارضيه .و الغشاء يمتلك شفافيه عاليه تصل الى (96%).

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2015 (1)

2013 (1)

2012 (2)