Characterization of (SnO2)1-x(TiO2:CuO)x films as NH3 gas sensor
خواص اغشيه (SnO2)1-x (TiO2: CuO)x كمتحسس لغاز NH3

Authors: Sara S. Mahmood ساره صادق محمود --- Bushra A. Hasan بشرى عباس حسن
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 39 Pages: 71-80
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Tin dioxide (SnO2) were mixed with (TiO2 and CuO) with concentration ratio (50, 60, 70, 80 and 90) wt% films deposited on single crystal Si and glass substrates at (523 K) by spray pyrolysis technique from aqueous solutions containing tin (II) dichloride Dihydrate (SnCl2, 2H2O), dehydrate copper chloride (CuCl2.2H2O) and Titanium(III) chloride (TiCl3) with molarities (0.2 M). The results of electrical properties and analysis of gas sensing properties of films are presented in this report. Hall measurement showed that films were n-type converted to p- type as titanium and copper oxide added at (50) % ratio. The D.C conductivity measurements referred that there are two mechanisms responsible about the conductivity, hence it possess two activation energies. Maximum sensitivity 16 % obtained for sample (SnO2)40(TiO2: CuO) 60 toward (NH3) gas at the operating temperature (473 K), whereas faster response time and recovery time were 20 (s) for (SnO2) and (SnO2)20(TiO2:CuO)80 respectively.

تم تحضير الاغشية الرقيقة من (SnO2)1-x (TiO2: CuO)x وذلك بخلط اوكسيد القصدير مع اوكسيد التيتانيوم و اوكسيد النحاس بنسب وزنية (50, 60, 70, 80 and 90) wt% على قواعد مختلفة مثل الزجاج والسيليكون احادي التبلورباستخدام تقنية الرش الحراري الكيميائي عند درجة حرارة 250 ºCوذلك بمزج كل من كلوريدي القصدير و النحاس المائي الثنائي وكلوريد التيتانيوم الثلاثي بمولارية (0.2 M). في هذا البحث تم عرض نتائج الخواص الكهربائية وتحليل نتائج التحسس الغازي. اظهرت قياسات تاثير هول ان اغشية اوكسيد القصديركانت نوع سالب التوصيل تتحول الى النوع موجب التوصيل مع مزجها مع كل من اوكسيد التيتانيوم والنحاس عند النسبه (%50). اشارت دراسة التوصيلية المستمرة ان الاغشية لها ميكانيكتا توصيل والذي يعني ان هناك طاقتا تنشيط. اعلى قيمة للتحسسية لغاز (NH3) كانت 16 % تم الحصول عليها من الغشاء (SnO2)40(TiO2:CuO)60 عند درجة تشغيل 473 K فيما كان اسرع زمن استجابة وهبوط 20 and 32 (s) لاغشيةSnO2 و (SnO2)70(TiO2:CuO)30على التوالي.


Article
Effect of Dopant Concentration on the Structural, Optical and Sensing Properties of (SnO2)1-x(TiO2:CuO)x Sprayed Films
تأثير تركيز التشويب على الخواص التركيبية والبصرية والتحسسيه للأغشية SnO2) 1-x (TiO2: CuO) x) الرقيقه

Authors: Sara S. Mahmood ساره صادق محمود --- Bushra A. Hasan بشرى عباس حسن
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2019 Volume: 16 Issue: 2 Pages: 361-369
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Spray pyrolysis technique was subjected to synthesized (SnO2)1-x (TiO2: CuO) x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO2 while no peaks of (CuO , TiO2 ) phase appear in the X-ray profiles by increasing of the content of (TiO2 , CuO) in the sprayed films. Mixing concentration (TiO2 , CuO) influences on the size of the crystallites of the SnO2 films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO2 , CuO) amount. The effect of mixing concentration on the optical properties of the films was also investigated. The reflectance and transmittance spectra in the wavelength range (300-1100) nm were employed to determine the optical properties such as energy band gap (Eg) and refractive index (n), extinction coefficient (k) , real and imaginary parts of dielectric constants (ε1, ε2) for (SnO2)1-x(TiO2:CuO)x films. The energy band gap omit of which showed reduction from (3.65 to 2.2) eV by reducing of SnO2 amount from (100 to 70) % .The reduction of energy band gap was ascribed to the new tail states introduced in the band gap of tin oxide. The sensitivity of the prepared sensor film was determined resistance difference of the films when exposed to oxidizing gas. The data declared that the mixed SnO2 films have better sensitivity in comparison with unmixed films.

تم تصنيع اغشية رقيقة من (SnO2) 1-x (TiO2: CuO) x )على ركائز مختلفة مثل الزجاج والسيليكون احادي التبلور باستخدام تقنية االرش الكيميائي الحراري. تم فحص تركيب الاغشيه المرسبه باستخدام حيود الأشعة السينية. في مخطط السينية تظهر قمم حيود SnO2 اكثر وضوحا في حين لا تظهر قمم CuO و TiO2 ويتحسن التركيب عند زيادة محتوى TiO2: CuO في اغشيه الرش. تركيز التشويب لاغشيه TiO2: CuO يؤثر على حجم تبلور اغشيه SnO2 حيث يتغير حجم تبلور اغشيه الرش الحراري بصوره منتظمة بزيادة كمية TiO2: CuO. كما تم دراسة تأثيرتركيز التشويب على الخواص البصرية للأغشية. تم استخدام طيف الانعكاس والنفاذيه لاغشيه SnO2) 1-x (TiO2: CuO) x) في مدى الطول الموجي nm (300-1100) لتحديد الخواص البصرية مثل فجوة حزمه الطاقة (Eg) ومعامل الانكسار (n) ومعامل الخمود (k) والقيم الحقيقية والتخيلية لثوابت العزل الكهربائي ε1، ε2. لوحظ ان فجوة حزمه الطاقة تقل من 3.8 فولت إلى 2.65 فولت من خلال تقليل كمية TiO2: CuO. ويعزى انخفاض فجوة نطاق الطاقة وبالتالي زيادة طاقة أورباخ إلى الحالات الذيليه للشوائب على حزمه التوصيل أو حزمه التكافؤ لاوكسيد القصدير. يمكن حساب قيمة تحسسيه الغشاء عند تغيير مقاومة الغشاء عند التعرض لغاز اوكسيد النيتروجين. تظهر النتائج أن اغشيه SnO2 المشوبه لديها حساسية أفضل عند مقارنتها بالأغشية غير المشوبه.