Article
A Comparative Study on the Electrical Characteristics of Generating Plasma by Using Different Target Sources
دراسة مقارنه للخصائص الكهربائية للبلازما المتولدة من أهداف مختلفة

Authors: Sarah K. Taha سارة خضير طه --- Sabah N. Mazhir صباح نوري مزهر --- Mohammed K. Khalaf محمد خماس خلف
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2018 Volume: 15 Issue: 4 Pages: 436-440
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, the electrical characteristics of glow discharge plasma were studied. Glow discharge plasma generated in a home-made DC magnetron sputtering system, and a DC-power supply of high voltage as input to the discharge electrodes were both utilized. The distance between two electrodes is 4cm. The gas used to produce plasma is argon gas which flows inside the chamber at a rate of 40 sccm. The influence of work function for different target materials (gold, copper, and silver), - 5cm in diameter and around 1mm thickness - different working pressures, and different applied voltages on electrical characteristics (discharge current, discharge potential, and Paschen’s curve) were studied. The results showed that the discharge current and potential increase by increasing the applied voltage ranging between 300-700 V. Discharge current increased as working pressure increased in the beginning, and then semi-stabilized (slight increase) starting from 1×100 mbar, while discharge potential decreased at the beginning as working pressure increased and then semi-stabilized at the same point at which discharge current stabilized. The Paschen’s curves were compared with each other. It was concluded that the lower breakdown voltage was associated with lower work function of the (Au, Cu, and Ag) cathode material. Breakdown voltages were (395, 398, and 420) for Ag, Cu and Au respectively.

تم في هذا البحث دراسة الخصائص الكهربائية لبلازما التفريغ التوهجي باستخدام منظومة الترذيذ الماكنتروني ذات التيار المستمر المحلية الصنع لتوليد بلازما التفريغ. كذلك أستخدم غاز الاركون لانتاج البلازما بمعدل تدفقSccm 40 وبمسافة فاصلة بين الاقطاب بمقدار cm4 وباستخدام مجهز قدرة عالي الفولتية. تم دراسة تأثير كل من دالة الشغل لاهداف مختلفة (ذهب، فضة ، نحاس) - بقطر 5 سم وسمك 1 ملم- على الفولتية المسلطة وضغط التشغيل على الخصائص الكهربائية (تيار التفريغ، جهد الكاثود ومنحنى باشن). أظهرت النتائج ان كلا من تيار التفريغ وجهد الكاثود يزداد بزيادة الفولتية المسلطة والذي يتراوح بين 300-700. ان تيار التفريغ يزداد مع زيادة الضغط المسلط في البداية ثم يستقر نسبياَ عند ضغط (زيادة ضئيلة ) ابتدأ من mbar1. بينما يقل جهد الكاثود مع زيادة الضغط المسلط ثم يستقر في نفس النقطة التي استقر فيها تيار التفريغ.لقد قورنت منحنيات باشن مع بعضها بالاعتماد على نوع مادة الهدف. وتم الاستنتاج ان جهد الانهيار يرتبط بدالة الشغل لكل من الذهب والفضة والنحاس.


Article
Antibacterial activity and mechanism of the silver nanoparticle in gram positive and negative bacteria
النشاط المضاد للبكتيريا وآلية الجسيمات النانوية للفضة في البكتيريا الموجبة والسالبة لصبغة غرام

Loading...
Loading...
Abstract

Biomedical alloy 316L stainless steel enhancing to replace biological tissue or to help stabilize a biological structure, such as bone tissue, enhancing were coated with deposition a thin layer of silver nanoparticles as anti-bacterial materials by using DC- magnetron sputtering device. The morphology surface of The growth nanostructure under the influence of different working pressure were studied by atomic force microscope. The average grain size decrease but roughness of the silver thin layer was increased with” “increasing the working pressure. The thickness of silver thin layer was increased from 107 nm at 0.08 mbar to 126 nm at 1.1 mbar. Antimicrobial activity of silver thin layers at different working pressure were studied. The results showed that the increasing in working pressure, lead to increase in activity of silver thin coating layer against the bacteria as a result of increasing in thickness and” roughness of thin coating layer. This work has been extended to study the anti-bacterial activity were fount the diameters of inhibition zone of gram positive bacteria between 16.5±1.5 and 19±0.5 while the diameters of inhibition zone of gram positive bacteria between 17±1 and 26±1. Finally the measurements of the 316L alloy coated by silver nanocoating layer after immersing the in simulated body fluid (SBF) solution for one month is the XRD pattern for the sample showed obviously that the Hydroxyapatite layer was appeared at (2= 31.8).

تم في هذا العمل، تحسين سبائك الفولاذ المقاوم للصدا الطبية نوعL 316 لتحل محل الانسجه البيولوجية أو للمساعدة في تثبيت البنية البيولوجية، مثل الانسجه العظمية للمساعدة في عمليه الاستشفاء. وقد تمت عمليات التدعيم عن طريق طلاء بمادة الفضة باستخدام منظومة الترذيذ الماكنتروني ذات التيارات المستمرة .درست طبوغرافية السطح للتركيب النانوي المتكونة تحت تاثير ضغوط تشغيلية مختلفة. نلاحظ ان قطر الحبيبة يقل مع زيادة الضغط، في حين ان معدل الخشونة يزداد مع زيادة الضغط المستخدم.بالاضافة الى ذلك نلاحظ زيادة سمك طبقه الطلاء من 107nm عند ضغط 0.08 mbar الى126 nm عند ضغط 1.1 mbar. كما درست الفعالية المضادة لنوعين من البكتريا لطبقات طلاء الفضة المحضرة في ضغوط تشغيلية مختلفة. وأظهرت النتائج ان الزيادة في ضغط التشغيل يؤدي إلى زيادة في الفعالية ضد البكتيريا نتيجة لزيادة في سمك وخشونة طبقه طلاء الفضة الرقيقه. حيث تراوحت اقطار التثبيط بين 1.5±16.5 و0.5±19 للبكتريا الموجبة لصبغة غرام في حين تراوحت اقطار التثبيط بين 1±17 و 1±26 للبكتريا السلبية لصبغة غرام. وأخيرًا، قياسات سبائك 316L المغلفة بطبقة من الفضة النانوية بعد غمرها في محلول مذيب (SBF) في الجسم لمدة شهر واحد هو نموذج XRD للعينة أظهر بوضوح أن طبقة الهيدروكسيباتيت عند الزاوية (2 = 31.8).