Annealing Effect on Structure and Optical Properties of ZnO Thin Films Prepared by Spray Pyrolysis
تأثير التلدين على الخصائص الكهربائية والبصرية للأغشية الرقيقة ZnO المرسبة بطريقة الرش الكيميائي الحراري

Author: Selma M.H. Al-Jawad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (B) Scientific Pages: 160-171
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polycrystalline films ZnO has been grown onto glass substrates by chemical spray pyrolysis (CSP) method. They were given heat treatment at different temperatures and constant time and for different times with constant temperature in air. The change in structural and optical properties was studied by means of X-ray diffraction (XRD), SEM, and optical absorption measurements. Structural analysis by X-ray diffraction pattern showed annealed ZnO film has high-orientation along c - direction (0 0 2), which remained the same with different heat treatment. The lattice constants of ZnO thin films were also obtained from XRD data. It is found that, with the increase of different heat treatments, the lattice constant a increases from 3.208 Å to 3.254 Å, and c increases from 5.125 Å to 5.219 Å. Where at higher annealing temperature and time the lattice constant c and a approach from bulk value. Other orientations corresponding to (1 0 0) and (1 0 1) are presented with very low relative intensities as compared to that of (0 0 2) plane. The transparency is increasing with increasing annealing temperature and time due to decreasing in films thickness with increasing annealing temperature and time. Change in bandgap energy from 3.2 to 3.01 eV was observed for different heat treatments.

رسبت اغشية متعددة التبلور من ZnO على قواعد زجاجية بطريقة الرش الكيميائي الحراري (CSP). وتم اجراء معاملة حرارية للاغشية لدرجات حرارة مختلفة وزمن ثابت وكذلك لازمان تلدين مختلفة وعند درجة حرارة ثابتة في الهواء. درست الخصائص التركيبية والبصرية للاغشية بأستخدام جهاز حيود الاشعة السينية(XRD) ,SEM,وقياسات الامتصاص البصري. ظهر من خلال فحص حيود الاشعة السينية ان الاغشية الملدنة تمتلك تمحور عالي عند الاتجاه (002) للمحور c, ويبقى التمحور نفسه لمختلف المعاملات الحرارية. وتم حساب معاملات الشبيكة لاغشية ZnO من خلال بيانات حيود الاشعة السينية. حيث وجد انه بزيادة درجات حرارة التلدين او ازمان التلدين يزداد ثابت الشبيكة a من3.208 Å الى 3.254 Å, ويزداد ثابت الشبيكة c من 5.125 Åالى 5.219 Å. حيث عند درجات حرارة التلدين العالية وازمان التلدين العالية يصبح ثابت الشبيكة a و c قريب من قيم ثابت الشبيكة الكتلوي لاغشية ZnO. وظهرت كذلك قمم حيود عند ال (100) و(101) ولكن بشدة واطئة بالمقارنة مع المستوي (002). تزداد النفاذية بزيادة درجة حرارة التلدين وزمن التلدين نتيجة نقصان سمك الاغشية بزيادة درجة حرارة التلدين وزمن التلدين.وحصل تغيرفي فجوة الطاقة من 3.2 الى 3.01 eV نتيجة المعاملة الحرارية.


Article
Studies on solution – growth thin films of CdS : Zn for photovoltaic application
دراسة أغشية CdS:Zn المرسبة بطريقة النمو بالمحلول المستخدم في تطبيقات الفوتولتائية

Author: Selma M. H. Al- Jawad سلمى محمد حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2009 Volume: 6 Issue: 1 Pages: 135-140
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Structural, optical, and electrical properties of thin films of CdS : Zn prepared by the solution – growth technique are reported as a function of zinc concentration. CdS are window layers influencing the photovoltaic response of CIS solar cells. The zinc doping concentration was varied from 0.05 to 0.5 wt %, zinc doping apparently increase the band gap and lowers the resistivity. All beneficial optical properties of chemically deposited CdS thin films for application as window material in heterojunction optoelectronic devices are retained. Heat treatment in air at 400 °C for 1h modify crystalline structure, optical, and electrical properties of solution growth deposited CdS : Zn films.

درست الخصائص التركيبية والبصرية والكهربائية للاغشية الرقيقة CdS : Zn المحضرة بتقنية النمو بالمحلول كدالة لتركيز شوائب الزنك. اذ توثر اغشية ال CdS المستخدمة كنافذة للخلايا الشمسية CIS على الاستجابية الفوتوفولتائية. حيث غيرت تراكيز شوائب الزنك من 0.05 الى 0.5% , اذ عملت شوائب الزنك على زيادة فجوة الطاقة مع تقليل المقاومية الكهربائية, مع الحفاظ على نفاذية عالية للاغشية الرقيقة المرسبة بتقنية النمو بالمحلول اللازمة لاستخدام غشاء CdS كنافذة للتركيب الهجيني المستخدم في النبائط الالكترونية – البصرية. كذلك اجري تلدين للاغشية الرقيقة بدرجة حرارة 400 درجة مئوية ولمدة ساعة ، الذي ادى الى تغير التركيب البلوري والخصائص البصرية والكهربائية لاغشية CdS:Zn .


Article
Analysis of Linearity Response and Spectral Responsivity in CdS Photoconductive Detector
تحلیل الاستجابة الخطیة والاستجابة الطیفیة لكاشف التوصیلیة الضوئیة CdS

Authors: Ali M. Mousa --- Selma M. H. Al- Jawad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 3 Pages: 584-591
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thin films of cadmium sulfide have been deposited by chemical bath deposition.The effect of temperature and time deposition on spectral responsivity for CdSphotoconductive investigation. The effect of temperature bath and time depositionwhere study. Linearity response of photoconductive detector were carry on analyzingthe light current with incident power curves. The results show that high spectral nonsaturated responsivity was achieved, further the detector were manufacture with lowcost.

حضرت أغشية كبريتيد الكادميوم بطريقة الترس يب بالحمام الكيميائي . إذ درس تأثير درجة حرارةوكذلك درس تأ ثير .CdS الحمام وزمن الترسيب على الاستجابة الطيفية لكاشف التوصيلية الضوئيةدرجة حرارة الحمام وزمن الترسيب على الاستجابة الخطية لكاشف التوصيلية الضوئية بتحليل منحنياتالتيار الضوئي مع القدرة الساقطة . حيث أبدى الكاشف المصنع بأقل كلفة استجابة عالية واستجابة خطيةدون حصول أي استقرارية للتيار الضوئي مع القدرة الساقطة.


Article
Determined the parameters effected on sensitivity and lower limit detection of XRF–WDS for different metals particles suspended in engine oil.
تحديد المعلمات المؤثرة على الحساسية والحد الادنى للتحسس لمطيافية تألق الاشعة السينية لمختلف الجسيمات المعدنية العالقة في زيت المحرك

Author: Selma M. H. Al-Jawad سلمى محمد حسين
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك - الدراسات العلمية ISSN: 19920849 / 26166801 Year: 2009 Volume: 4 Issue: 1 Pages: 12-19
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

In this work Different weight of pure Copper,Nickel,Cobalt and Iron fine powders were blended carefully with engine Oil.X-ray fluorescence system was operated at 30KV and 17mA,the XRF intensities of Kα lines for all samples were measured at the peak and at background.The Lower Limit detection (LLD) and Sensitivity (m) of XRF Spectrometer were determined for different metal particles with different Concentrations (Wt%).The results of LLD and sensitivity of all suspended samples were plotted as a function of concentration , and the average values of LLD and m were calculated and plotted as a function of atomic number of metal particles suspended in engine oil.

اخذت أوزان مختلفة من المساحيق النقية لمعادن النحاس والنيكل والكوبلت والحديد خلطت بعناية مع زيت المحرك.اذ تم استخدام منظومة تألق الأشعة السينية وتم تشغيلها بظروف تشغيلية30KV,17mA.تم قياس الشدة للخط kαللقمة وللأستطارة الخلفية ولجميع النماذج الحد الأدنى للتحسس والحساسية لمطياف تألق الأشعة السينية وجد لمختلف الجسيمات المعدنية وبمختلف التراكيز.نتائج الحد الأدنى للتحسس والحساسية للنماذج العالقة رسم كدالة للتركيز وتم إيجاد معدل قيمة الحد الأدنى للتحسس والحساسية ورسمت كدالة للعدد الذري للجسيمات المعدنية العالقة في زيت المحرك.


Article
Kinetics of Growth and Structural Characterization of Cd1-Xznxs Thin Films Synthesized By Cbd Method
حركية النمو و خصائص التركيبية لاغشية Cd1-xZnxS المحضرة بطريقة الترسيب بالحمام الكيمياوي ((CBD

Authors: Selma M.H. Al-Jawad --- Fadheela H.Alioy
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 4 Part (B) Scientific Pages: 505-519
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this paper, we reported the study of Cd1-xZnxS thin film which have been deposited on glass substrates by Chemical Bath Deposition (CBD ) technique by using Cadmium sulphate, Zinc sulphate, thiourea, Ammonia and EDTA. The thickness of Cd0.5Zn0.5S thin films with different deposition times, pH, and temperature are also study and show increase with increasing times pH, and temperature. The optimum condition to prepared Cd0.5Zn0.5S thin films were obtained in times 3h, temperature 80 ºC, and pH 10. Structure and surface morphology of Cd1-xZnxS thin films were characterized by X-ray diffraction (XRD), Atomic Force microscope (AFM), and Scanning Electron Microscopy (SEM) Measurements. The XRD indicates that all the grown films show only one diffraction peak located at (2θ= 26.7°) with hexagonal structure in predominant (002). The average grain size changes from 9.3nm to 4.48nm with the increase in zinc content (x = 0 to 0.65). It was found that as the zinc content increases, the peak intensity decreases and for (x ≥ 0.7) the films have amorphous character. The values of lattice constant ‘a’ and ‘ c’ have been observed to vary with composition from 5.75 nm to 4.68 nm and 6.66 nm to 6.62 nm, respectively, with the increase in zinc content (x = 0 - 0.65). The AFM studies showed that the smooth surface texture was observed in the deposited Cd1-xZnxS films with x= 0.3, the surface roughness of the Cd1-xZnxS thin films is about 2.66nm to 9.47nm and the root mean square (RMS) is about 3.41nm to 11.9nm with increase in zinc content x = 0.3 to 0.6. The SEM exhibits that grains in the film are distributed to cover the surface of the substrate completely, the grains become small in diameters with increasing Zn-contents.

في هذا البحث تم دراسة الأغشية الرقيقة Cd1-xZnxS المرسبة على قواعد زجاجية بأستخدام تقنية الترسيب بالحمام الكيميائي ((CBD من خلال أستخدم كبريتات الكادميوم و كبريتات الخارصين والثايوريا والامونيا والعامل الكلابيEDTA . وجد السمك للاغشية الرقيقة Cd0.5Zn0.5S المرسبة عند ازمان مختلفة وقيم مختلفة لدرجة الحامضية pH وعند درجات حرارة مختلفة يزداد بزيادة زمن الترسيب و دالة الحامضية و درجة الحرارة. الظروف المثلى لتحضير الاغشية الرقيقة Cd0.5Zn0.5S تم الحصول عليها عندما يكون الزمن 3 ساعات و درجة حــرارة 80ºC ودرجة الحامضية [pH=10] . شخصت الخصائص التركيبية وهيئة السطح لاغشية الرقيقة Cd1-xZnxS بواسطة فحص حيود الاشعة السينية و مجهر القوة الذرية والمجهر الالكتروني الماسح . حيث تشير فحوصات الاشعة السينية الى ان جميع الأغشية تمتلك قمة واحدة عند الزاوية ( 2θ = 26. 7° ) مع تركيب سداسي يكون فيها المستوي (002) هو المستوي السائد على بقية المستويات , يتغير معدل الحجم الحبيبي من 9.3nmالى4.48nm عند زيادة محتوى الخارصين ( x = 0 - 0.65) كما وجد ان زيادة محتوى الخارصين يقلل من شدة القمة وعند (x ≥ 0.7 ) يصبح الغشاء عشوائي التركيب كذلك لوحظ ان قيم ثابت الشبيكة ‘a’ و ‘c’تتفاوت بين 5.75nm الى4.68nm و nm 6.66 الى 6.62 nm , على التوالي وذلك يحدث عند زيادة محتوى الخارصين( x = 0 - 0.65) . اظهرت دراسات مجهر القوة الذرية هيئة السطح ناعمة لاغشية Cd1-xZnxS عند قيمة ( x = 0.3 ) ومعدل الخشونة للاغشية يتراوح بين 2.66nm الى 9.47nm ومربع متوسط الجذر يكون حوالي 3.41nm الى11.9nm وذلك يحدث عند زيادة محتوى الخارصين (x = 0.3 - 0.6) . كما اظهرت قياسات المجهر الالكتروني الماسح ان الغشاء يمتلك حبيبات تنتشر على جميع اجزاء السطح ويصبح قطر هذه الحبيبات اصغر عند زيادة محتوى الخارصين .


Article
Effect of Hydrothermal Reaction Temperatures on Structural and Optical Properties of ZnS Nanoparticles

Authors: Selma M .H. Al-Jawad --- Mukhlis M .Ismail --- Sora Emad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 6 Part (B) Scientific Pages: 808-819
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A ZnS nanoparticle was prepared using hydrothermal interaction of zinc acetate with Thiourea in different reaction temperatures (170oC, 180oC, 185oC, 190oC). The structural characterization of synthesized nanoparticle was determined by X-ray diffraction (XRD) which showed a hexagonal structural of ZnS. Scanning electron microscopy (SEM) and energy dispersive spectrum (EDS) analysis were confirmed that the morphology and elemental analysis was formed ZnS nanoparticle. Absorption study has been carried out using UV-VIS spectrophotometer to determine the band gap of ZnS nanoparticle. The optical energy band gap was changed at values equal to (4.16, 4.46, 4.1 and 4.35eV) with different hydrothermal temperatures at (170oC, 180oC, 185oC and 190oC) respectively. However, these values of energy gaps for ZnS nanoparticles are blue shift and larger than that bulk value due to quantum confinement. Fourier Transform Infrared Spectra (FTIR) is recorded in an FTIR spectrometer to verify the presence of ZnS powder. The particle size of ZnS calculated was ranged between 3.5 to 3.9 nm according to Sherrer's equation and the results were compatible when using Effective Mass Approximation (EMA).


Article
Physical Properties of Indium Tin Oxide (ITO) Nanopartical Thin Films Used as Gas Sensor
الخصائص الفيزياوية لاوكسيد الانديوم المشوب ذات الجسيمات النانوية واستخدامه كمتحسس غازي

Authors: Saryia D.M AL-Algawi --- Selma M.H Al-Jawad --- Noor M. Saadoon
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (B) Scientific Pages: 141-151
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

ITO/ Si gas sensor was fabricated by an efficient and size – controlled by using DC-Sputtering technique suitable for large deposition area and high quality thin films. Structural, optical and electrical properties of ITO thin films were investigated and analyzed extensively under different doping concentration. Structure and surface morphology of ITO thin films were characterized by X-ray diffraction, Atomic Force Microscope. XRD technique that showed these films is polycrystalline structure with a preferred orientation of (222),( 440),(400) the best orientation plain is (222) It was found that crystalline size decreases with increasing doping concentration. The optical properties of ITO thin films were studied such as transmissions, energy gap The transmittance was measured in the wavelength range from(300nm to 900 nm) for all the films it was highly transparent (greater than 85%). The optical energy band gap was increased with doping concentration in range from (3.9 to 4.15) eV. The electrical properties for ITO thin films include D.C electrical conductivity and Hall effect which shows that the type of films is (n- type), and the film has two activation energies in the rang (305-355)K, and the resistivity increases with doping concentration at 8wt%. The sensitivity toward NH3, NO2 gas has been measured.In2O3 doped with (Sn) has higher sensitivity to NH3, The sensitivity toward, NO2 gas has been measured, where In2O3 doped with (Sn) has higher sensitivity to NO2than to NH3.

في هذا المشروع تم تصنيع متحسس غازي بطريقة تمتاز بكفاءتها وإمكانية السيطرة على الحجم الحبيبي للغشاء المحضر بطريقة الترذيذ بالتيار المستمر والتي تعتبر طريقة غير مكلفة ومناسبة لترسيب اغشية ذات كفاءة ونقاوة عاليـة وتجانس تام للغشاء المرسب. , تبين من خلال دراسة حيود الاشعة السينية بان الاغشية ذات طبيعة متعددة التبلور وباتجاهية سائده (222,440,400) واتجاهية مفضلة (222), لوحظ تناقص بالحجم الحبيبي بازدياد نسبة التشويب.اظهرت دراسة الخصائص البصرية للأغشية بوساطة قياس طيف النفاذية وفجوة الطاقة ان النفاذية قيست عند طول موجي يتراوح من ( 300 nmالى 900 nm) لجميع الاغشية وان جميع الاغشية الرقيقة هي شفافة للغاية بنسبة اكثر من (85%) . بينما تدرجت فجوة الطاقة بزيادة تركيز الاشابة في مدى منeV ( 3.9 الى (4.15. الخصائص الكهربائية لأغشية اوكسيد الانديوم المشوب تضمنت التوصيلية المستمرة وتأثير هول حيث ان النتائج بينت ان الغشاء من نوع,(n-type) يمتلك طاقتي تنشيط ضمن المدى الحراري(305-335)K , زيادة في المقاومية عند نسبة تشويب 8wt% تم حساب تحسسيه الاغشية المشوبة لغاز NH3وغاز NO2 , امتلكت الاغشية تحسسيه عالية لغاز NO2 من تلك التي تحسست غاز الامونيا.

Keywords

D.C Sputtering --- ITO --- Gas sensor


Article
Preparation and Characterization of Tin Oxide Thin Films by Using Spray Pyrolysis Technique
تحضير وخصائص أغشية ثنائي اوكسيد القصدير الرقيقة بواسطة استخدام تقنية الرش الحراري

Authors: Selma M. H. Al-Jawad --- Fadheela H. Oleiwe --- Jabbar .H. Khulaef
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 3 Part (B) Scientific Pages: 528-538
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, tin oxide thin films have been prepared by Spray pyrolysis technique, using tin chloride over soda – lime glass. Structural and optical properties were studied under different conditions like substrate temperatures of 300, 350 and 400°C, and annealing in air at temperature 300°C for 1 hr. The films were characterized by XRD, SEM, AFM, and UV-VIS analysis. The optical spectra of the films were measured in the wavelength range of 300 –900 nm by UV-VIS Spectrometer device. The X-ray diffraction studies confirmed the films have the orthogonal structure at low substrate temperature change to a tetragonal structure at high substrate temperature. Films prepared with different substrate temperatures were correspond to preferential orientation along the plane (132) and (110) planes for structural orthogonal, tetragonal respectively. The grain size founded( 25.2-9.77nm) for different substrate temperatures range ( 300- 400°C) after annealing , from the (SEM) images the grain size values of the SnO2 thin films are found to be in the range of (32.3-24.2 nm) corresponding to the substrate temperature (350 and 400°C) after annealing and from the AFM the root mean square (RMS) values for the thin film at substrate temperature 350C was found to be 10.4 nm, the surface roughness 8.86 nm. The maximum value of transmittance was found to be 78 % around the wavelength of 900nm at substrate temperatures 300°C also have energy gap (2.9-3.4eV) at substrate temperatures range ( 300- 400°C) after annealing in air at temperature 300°C for 1 hr.

في هذا العمل حضر ثنائي أوكسيد القصدير بطريقة الرش الحراري , باستخدام كلوريد القصدير على قاعدة زجاجية , درست الخصائص التركيبية والبصرية تحت شروط مختلفة مثل درجة حرارة القاعدة (400,350,300) درجة سيلزية ولدنت في الهواء عند درجة حرارة (300) درجة سيلزية ولمدة ساعة . شخصت خصائص الاغشية بواسطة فحص حيود الأشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذرية وقياسات الأطياف للأشعة المرئية وفوق البنفسجية , الأطياف البصرية للأغشية حسبت عند الطول الموجي (من 300الى900) نانومتر . أكدت دراسة حيود الأشعة السينية ان الاغشية تمتلك تركيب متعامد عند درجات الحرارة الواطئة للقاعدة وتتغير الى تركيب رباعي الزاوية عند درجات الحرارة العالية للقاعدة , وجدت قيمة الحجم الحبيبي تتغير (من 9.77 الى25.2 ) نانومتر عندما تتغير درجة حرارة القاعدة بين ( 300 الى 400) درجة سيلزية بعد التلدين , كذلك وجدت من صور المجهر الالكتروني الماسح قيمة الحجم الحبيبي لأغشية اوكسيد القصدير تساوي (24.2- 32.3) نانومتر الذي يقابل درجة حرارة القاعدة ( 350 و 400) درجة سيلزية بعد التلدين , اظهرت نتائج مجهر القوة الذرية ان قيمة مربع متوسط الجذر تساوي (10.4) نانومتر ومعدل الخشونة يساوي 8.86 نانومتر عندما تكون درجة حرارة القاعدة 350 درجة سيلزية . بالاضافة الى ذلك وجد ان أعلى قيمة للنفاذية تساوي 78% عند الطول الموجي ( 900) نانومتر عند درجة حراة القاعدة 350 درجة سلزية , وتمتلك فجوة طاقة (2.9-3.4) الكترون فولت لاغشية اوكسيد القصدير عندما درجة الحرارة تتغير بين (300- 400) درجة سليزية بعد التلدين لمدة ساعة.


Article
The Effect of Annealing Temperature on Structural & Optical Properties of Nanocrystalline SnO2 Thin Films Prepared by Sol-Gel Technique

Authors: Selma M.H. AL-Jawad --- Abdulhussain K. Elttayf --- Amel S. Sabr
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 4 Part (B) Scientific Pages: 490-498
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, studying the structural and optical Nano crystalline SnO2 thin films grown on cleaned glass substrates by using sol- gel (dip coating) technique. It is worthy to say that the thickness of the deposited film was of the order of (300-400)nm . The films are annealed in air at , 300◦C, 400◦C and 500◦C temperatures for 60 minutes. The films that are analyses by X-ray diffraction (XRD), Scanning electron microscopy (SEM) , atomic force microscopy and optical absorption spectroscopy technique. The size of crystalline was observed, as well as, so as to increase with increasing annealing temperature . XRD analysis reveals that the whole films are polycrystalline with tetragonal structure with preferred orientation of (110),(101),(200) and (211) . The increase of annealing temperature leads to raise the diffraction peaks and decrease of FWHM. The atomic force microscopy (AFM) and Scanning electron microscopy (SEM) results showed that the average grain size was increase with the increase in annealing temperature. Spectra of transmittance and absorbance was recorded at wavelengths range (300-1000)nm .The optical properties showed high transmission at visible regions. The optical band gap energy was found to be (3.5 , 3.75 , 3,87) eV at annealing temperature (300,400,500 )°C respectively.


Article
Immersion Time and Annealing Temperature Effect on TiO2 Thin Films Deposited by Hydrothermal Method

Authors: Selma M. H. Al-Jawad --- Mohammad R. Mohammad --- Natheer Jamal Imran
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2017 Volume: 20 Issue: 3 Pages: 67-76
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work, TiO2 nanofibers thin films were prepared by using different immersion times for hydrothermal method. Annealing in air at different temperatures of (400,500, and 600)°C at constant time (1 hour) were achieved for all films. Many analysis and measurement had been done (XRD, SEM, EDX, and AFM), and optical (UV-Visible spectroscopy, PL spectroscopy, and Spectral Response). The properties of nanofibers TiO2 films were investigated and analyzed for films. The SEM analysis of TiO2 films showed nanofibers shapes with diameter of about 21 nm. The absorption edges are located at UV-region, and the Eg has higher values compared with Eg for bulk TiO2 film. Spectral response measurements show photocurrent peaks for TiO2 nanotube films centered at UV-region (350 nm).

Listing 1 - 10 of 14 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (14)


Language

English (13)

Arabic (1)


Year
From To Submit

2019 (1)

2017 (2)

2016 (3)

2015 (3)

2013 (1)

More...