Article
Acoustic and Mechanical Properties of Polymer Composites Reinforced by Pre-Deformed Palm Fiber
الخواص الصوتية والميكانيكية لمتراكبات بوليمرية مقواة بألياف النخيل المشوه مسبقا

Author: Sihama I.Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 3 Part (A) Engineering Pages: 484-499
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research was carried out to study the mechanical properties and thermal and acoustic insulation properties of prepared polymer composite. Petiole date palm fibers with the length (2-3mm) and with different volume fraction ratio (10, 20, 30 and 40%) were used as filler in preparation of polymer composite.The research imply study effect of pre- deformation for petiole date palm fiber by chosen compression loads (0, 2, 4 and 6 MPa) on the mechanical properties as well as on the thermal and acoustic insulation properties of prepared composites. It was concluded that the pre-deformation to the fibers improves the thermal and acoustic insulation properties of prepared composite, as well as an increase in the tensile strength and hardness values with increasing compression load on the fibers. The highest values of the tensile strength and hardness reach to (133MPa) and (106) respectively for the polymer composite filled with 40% volume fraction of petiole date palm fibers which pre-deformed under compression load equal to 6 MPa.

البحث الحالي يدرس الخواص الميكانيكية والعزل الحراري والصوتي لمادة متراكبة بوليمرية محضره. استخدمت الياف ساق شجرة النخيل بطول (mm 3-2) وبكسور حجميه مختلفه (40% and 30, 20, 10) كحشوات في تحضير المتراكبات البوليمرية. وتناول البحث دراسة تأثير التشوية المسبق لالياف ساق النخيل تحت ضغوط مختارة (6 MPa and 4, 2, 0) على الخواص الميكانيكية علاوة على خواص العزل الحراري والصوتي للمتراكبات المحضره. وقد استنتج ان التشويه المسبق للالياف يحسن خواص العزل الحراري والصوتي. فضلاً عن حصول زيادة ملحوظة في قيم الصلادة ومقاومة الشد مع زيادة الحمل الأنضغاطي المسلط مسبقا على الالياف. وبلغت اعلى قيم لمقاومة الشد وصلادة (133MPa)و (106)على الترتيب للعينات المحضرة من الياف ساق شجرة النخيل بنسبة كسر حجمي مقداره 40%)) والمشوه مسبقا تحت حمل انضغاطي مقداره (6 MPa ).


Article
Effect of Sb2O3 and/or CdO nanoparticle substitution on the properties of high-TC superconducting Bi1.6-x SbxPb0.4Sr2Ca2-yCdyCu3OZ material
تأثير الأستبدال الجيزيئى بألدقائق النانوية Cd2O3 و/ أو Sb2O3 على خواص المادة الفائقة التوصيلية Bi1.6-x SbxPb0.4Sr2Ca2-yCdyCu3OZ

Author: Sihama I. Salih سهامه عيسى صالح
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 36 Pages: 73-84
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2) and Cd with ratio (y=0.01), has the maximum value of zero resistance temperature, where was the TC(onset) and TC(0) values for this sample are (140 K) and (123 K) respectively, and XRD results reveal that this sample has the highest percentage of Bi- 2223 phase, as well as the analysis of XRD patterns of the prepared materials showed polycrystalline structure and signalize that all samples had an orthorhombic crystalline structure. It was concluded that Sb2O3 nanoparticles it may be acts as a flux agent in the matrix to lower the partial melting temperature of the samples and that leads to the promotion of the high-TC phase.

تم تحضير مواد فائقة التوصيل ذو تركيباتBi1.6-xSbxPbo.4Ca2-yCdyCu3OZ حيث ان (X = 0.0, 0.1, 0.2, 0.3) وان (y = 0.0, 0.01, 0.02) بواسطة طريقة تفاعل الحالة الصلبة. وتمت دراسة أختبار تأثير نسب الأستبدال الجزيئي لكل من Bi و Ca ب Sb وCd على التوالي على خصائص التوصيلية الفائقة, تم تلبيد جميع العينات عند نفس درجة الحرارة (850 درجة مئوية) و خلال فترة زمنية (195h ). تم إجراء التحليل البنيوي للعينات المحضرة باستخدام المجهر الإلكتروني الماسح (SEM) ودراسة حيود الأشعة السينية (XRD) والتي أجريت في درجة حرارة الغرفة كما تم اختبار المقاومة الكهربائية كدالة لدرجة الحرارة. وقد بينت النتائج أن العينة المحضرة ذات نسب استعاضة جزئية بكل من Sb (x=0.2) وCd (y = 0.01) تمتلك القيمة المثلى لدرجة حرارة التحول الى التوصيلة الفائقة، حيث كانت قيم (TC(onset)) و(TC (0)) لهذه العينة هي (140 K) و (123 K) على التوالي. و أظهرت أنماط الحيود للأ شعة السينية ( (XRDان هذه العينة تمتلك أعلى نسبة مئوية من الطورالفائق التوصيل Bi-2223)), فضلا عن ذالك بينت أنماط حيود الأشعة السينية للعينات المحضرة بأن البنية الناتجة هي متعدَد البلورات وأن جميع العينات لها بنية بلورية ذات طور معيني قائم (Orthorhombic). وانه يمكن استنتاج الى أن التعويض بالدقائق النانوية Sb2O3 بنسب تعويضية محددة قد تكون بمثابة عامل مساعد لصهر مادة الاساس جزئيا مما تودي الى خفض درجة حرارة الانصهار الجزئي للعينات والتي تؤدي إلى تعزيز الطور العالية.


Article
Mechanical and Morphological Properties of HDPE: PP and LDPE: PP Polymer Blend Composites Reinforced with TiO2 particles
الخواصالمیكانیكیة و المجھریة لمتراكبات الخلائط البولیمریة HDPE: PP و LDPE: PP المقواة بدقائق اوكسید التیتانیوم

Authors: Sihama I. Salih --- Abdullkhaliq F.hamood --- Alyaa H. Abdalsalam
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 12 Part (A) Engineering Pages: 2211-2227
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research two groups of polymer blends have been prepared First group included (High density polyethylene (HDPE): Polypropylene (PP))While the Second group(included Low density polyethylene (LDPE): Polypropylene (PP)) both groups prepared withpolypropylene of (20% and 80%). From the results of tensile test for the prepared blends it has been showed that the optimum blending ratio was (20%LDPE:80%PP and 20%HDPE:80%PP) which thenreinforced with (2, 5 and 8wt%) oftitanium dioxide (TiO2), particle size (0.421μm). Titaniaparticles weremechanically mixed with the polymers prior tomelt mixing for better dispersion.Polymerblend composites were obtained by using single screw extruder. Results showed that mechanical properties increased as titania content increased except elongation.Furthermore the result recorded highest values ofimpact strength and fracture toughness at2%wt TiO2which is 312 Mpa and 572.8Mparespectively,for the polymer blend (20%HDPE: 80%PP) composite and for the polymer blend (20%LDPE: 80%PP) composites the impact strength and fracture toughness are 262.5Mpa and 468 Mpa respectively.The mechanical properties values of 20%HDPE: 80%PP is higher than 20%LDPE: 80%PP polymer blendcomposites. Scanningelectron microscopy (SEM) imagesshowed that there isbonding developed between TiO2 and polymer blends in some regions.

Keywords

Polymer blend --- TiO2 --- HDPE --- PP --- composite --- Mechanical properties


Article
Numerically and Theoretically Studying of the Upper Composite Complete Prosthetic Denture
دراسة تحليلية ونظرية لطقم الاسنان الاصطناعي الكامل المتراكب العلوي

Authors: Sihama I. Salih --- Jawad K. Oleiwi --- Qahtan A. Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (A) Engineering Pages: 1023-1037
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study focused on the manufacturing and development properties of upper prosthesis complete denture from composite materials with the basis cold cured resin of poly methyl methacrylate as new fluid resin and reinforced materials by two different types of particles (nano-hydroxyapatite (nHA), micro zirconia (ZrO2)), that added with different volume fractions of (1%, 2% and 3%), and the different types of woven fibers (Glass fiber, Kevlar fiber), it were added with a fixed volume fraction of (5%) to PMMA composites.Specimens’ consist of a six groups where prepared by using (Hand Lay-Up) method from the composites materials and hybrid laminated composites materials. This research includes theoretical and numerical studies by using finite element method to confirming the experimental results of the effect of selected volume fractions of theseparticles and fibers on the (total deformation distribution, equivalent elastic strain and equivalent Von Mises stress) of the composite prosthetic dentures.The theoretical part included calculations the values of theoretical safety factor and Poisson's ratio. While the numerical part based on finite element method (F.E.M), which was performed by using program (ANSYS-15) to analyze the prepared of denture composite materials and evaluate its characteristics which represent total deformation distribution, equivalent stress and equivalent elastic strain. This was performed by obtaining twenty one models for the PMMA composite dental prostheses which were treated as three dimension structure. The numerical results of the F.E.A showed coincided with some of the experimental results.

في هذا البحث تم التركيز على تصنيعوتطوير مواصفات طقم أسنان أصطناعي كامل علوي من مواد متراكبة. وقد حضرت هذه المواد المتراكبة من راتنج البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية تم اضافتهما بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج والياف الكفلر والتي تمت اضافتها الى المواد المتراكبةبكسر حجمي ثابت هو (%5)الى المواد المتراكبة. تتكون العينات من ستة مجاميع تم تحضيرها باستخدام طريقة الصب اليدوي تمثل مواد متراكبة ومواد متراكبة طبائقية هجينية. تضمن البحث دراسة نظرية وتحليلية باستخدام طريقة العناصر المحددة للتاكد من النتائج العمليةلتأثير الكسور الحجمية المختارة لهذه الألياف والدقائق على (توزيع التشوه الكلي، الانفعال المرن المكافيء والاجهاد المكافيء) لأطقام الاسنان الأصطناعية المتراكبة.تضمنتنتائج الجانب النظري حساب قيم معامل الامان النظريونسبة بويزن. أما الجانب التحليلي فيتضمن أستخدام أستخدام طريقة العناصر المحددة والتي أنجزت بأستخدام برنامج(ANSYS-15) لغرض تحليل المواد المتراكبة المحضرة لطقم الأسنان وحساب خصائصه والتي تمثل (توزيع التشوه الكلي، الاجهاد المكافيء والانفعال المرن المكافيء)، وقد تم انجاز ذلك عن طريق الحصول على واحد وعشرون موديل لطقم الاسنان الأصطناعي باعتبارها أطقام أسنان متراكبة مكونة من راتنج البولي مثيل ميثا اكريليت ذات هيكل ثلاثي الابعاد، وقد أظهرت النتائج التحليلية لطريقة العناصر المحددة تطابق مع بعض النتائج العملية.


Article
Preparation and Investigation of Flexural Strength and Impact Strength for Nano Hybrid Composite Materials of the Tri- Polymeric Blend used in Structural Applications

Authors: Sihama I. Salih --- Wleed B. Salih --- Mustafa S. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 1 Part (B) Scientific Pages: 12-24
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Current work is aimed to preparation the nanocomposites laminatesof low density and good durability to use in structural applications. So, in thispaper, the preparation and compare of some mechanical properties of twogroups of tri-polymer blends composites consisting of ((93% unsaturatedpolyester resin (UP)+(5%PMMA) (Poly methyl methacrylate)+2%NR(Natural Rubber)) as the matrix materials. Added the reinforce materials(silica (SiO2) and zirconia (ZrO2) nanoparticles) individually, with differentvolume fraction of (0, 0.5, 1, 1.5%) to the ternary polymer blends accordingto the following formula:- [((100-X) (93%UP)+2%NR+5%PMMA): (X%SiO2or X% ZrO2)] The first group is composed of matrix material reinforced withzirconia (ZrO2) nanoparticles with average diameter of nanoparticles(56.88nm) and the second group is composed of matrix material reinforcedwith silica (SiO2) nanoparticles with average diameter of nanoparticles(24.59nm). Then used as a matrix material for the preparation of hybridlaminar composites materials, reinforcement with one and two layers ofwoven carbon fibers The research included the study of the influence ofvolume fraction of nanoparticles on some of mechanical and physicalproperties like flexural strength, flexural modulus impact strength, and impactfracture toughness, in addition to test infrared spectroscopy (FTIR) and all ofthese tests were carried out at laboratory temperature. Search results haveshown that the values of (flexural modulus and impact strength and fracturetoughness) increases with the increase of the nanoparticles ratios in polymerblend nano composite of prepared samples. While flexural strength valuedecreases with the increase in the volume fraction of nanoparticles in polymerblend nano composite. The fracture energy of the of hybrid laminarcomposites is higher than those containing only the nanoparticles powders.Morphology test by scanning electron microscope indicates that a goodadhesion or interfacial interactions between the Nano powders particles,carbon fibers and components of ternary polymer blend. Which results inhigher the carbon fibers efficiency factor, and hence higher mechanicalstrength. So, the hybrid laminar nano composites, which appear high flexuralmodulus and impact strength and fracture toughness, can be foreseen toprovide valuable contribution to high performance structural applications.


Article
Study Compression and Impact Properties of PMMA Reinforced by Natural Fibers Used in Denture

Authors: Jawad K. Oleiwi --- Sihama I. Salih --- Hwazen S. Fadhil
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 6 Part (A) Engineering Pages: 652-655
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The fracture in dentures prepared from acrylic resin occurs frequently during the accidental damage or service through heavy occlusal force [1]. Impact failures usually occur out of the mouth as a result of accidental dropping due to cleaning, coughing or sneezing or a sudden blow to the denture [2]. This paper is focused on the effect of natural fibers on the mechanical properties of PMMA by changing two parameters (content of fibers and length of fibers). Fibers were treated with alkaline solution to improve the interfacial adhesion. Composite specimens were prepared by using hand lay-up method. The results were showed that the increasing the weight fraction of both fibers lead to increase compression strength and decrease impact strength of composite specimens. While, increasing fiber length of both fibers lead to decrease compression strength and increase impact strength of the composite specimens. The largest value obtained for bamboo specimens at (2mm) fiber length and (9wt. %) and reach (530 MPa.). The main goal of this research is studying the impact and compression properties of PMMA reinforced by natural fibers (siwak and bamboo) by varying length and concentration of both kinds of fibers.


Article
Study Some Mechanical Properties of Binary Polymer Blends Fabricated by Friction Stir Processing

Authors: Jawad Kadhim Oleiwi1 --- Sihama I. Salih --- SajidAbd Alkhidhir
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 5 Pages: 362-370
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Friction stir processing (FSP) is a promising technique to improve the mechanical properties of the polymer blends surface with retainment of bulk properties, in this workan attempt was done to adddifferent ratios of polypropylene (PP), styrene acrylonitrile (SAN) and polyvinyl chloride (PVC) as a second material to the matrix plate high density polyethylene(HDPE). Mechanical properties were estimated for hardness and tensile tests were carried out to assess the performance of friction stir processedto prepared the binary polymers blends (HDPE: PP), (HDPE: SAN) and (HDPE: PVC)at depth 3 mm from the surface of (HDPE) plate.The results of the tests showed that the best values of the tensile strength, young modulus and hardness, it was obtained when adding the ratio of (15%) of the (PVC) to matrix (HDPE). The friction stir processing technique was successfully used to improve the mechanical properties of polymer surface. In view of the foregoing, it can be concluded that the friction stir processing technique, can be utilizing to repair the cracks and imperfections that are formed in polymeric materials.

تعتبرطريقةالاحتكاكوالخلط تقنيةواعدةلتحسينالخواصالميكانيكيةلسطحالخلائطالبوليميريةمعالاحتفاظبخواصباقيالجسم،فيهذاالعملجرتمحاولةلإضافةنسبمختلفةمنالبوليبروبلين،ستيرينأكريلونيتريل والبوليفينيلكلوريد كمادةثانيةإلىالبولياثيلينعاليالكثافة (كمادةاساس). تمأجراءالاختباراتالميكانيكية(الصلادةوالشد) لتقييمأداءعمليةالاحتكاكوالخلط لتحضيرالخلائطالبوليميريةالثنائية: (البولياثيلينعاليالكثافة: بوليفينيلكلوريد)، (البولياثيلينعاليالكثافة: ستيرينأكريلونيتريل) و (البولياثيلينعاليالكثافة: بوليبروبلين) علىعمق 3 مممنسطح (البولياثيلينعاليالكثافة).أظهرتنتائجالاختباراتأنأفضلقيمللصلادةومقاومة الشدتمالحصولعليهاعندإضافةنسبة (15٪) من (البوليفينيلكلوريد) إلىالمادةالاساس (البولياثيلينعاليالكثافة). فيضوءماسبق،يمكنالاستنتاجأنتقنيةالاحتكاكوالخلط،يمكنأنتستخدملإصلاحالتشققاتوالعيوبالتيتتكونعلىسطحالموادالبوليميرية.


Article
Effects of Irradiation by UV- Acceleration on Mechanical Properties of Polymer Blends (Polyester: Starch)

Authors: Sihama I. Salih --- Qahtan A. Hamad --- Safaa N. Abdul Jabbar --- Najat H. Sabit
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2018 Volume: 21 Issue: 1 Pages: 147-152
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This work covers mixing of unsaturated polyester (un- polyester) with starch powders as polymer blends and study the effects of irradiation by UV-acceleration on mechanical properties of its. The unsaturated polyester was mixing by starch powders at particle size less than (45 μm) at selected weight fraction of (0, 0.5, 1, 1.5, 2, 2.5 and 3%). These properties involve ultimate tensile strength, modulus of elasticity, elongation percentage, flexural modulus, flexural strength, fracture toughness, impact strength and hardness. The results illustrate decrease in the ultimate tensile strength at and elongation percentage, while increasing modulus of elasticity, with increasing the weight ratio of starch powder to 3 % weight fraction, whereas the maximum value of hardness and flexural, impact properties happened at 1 % weight fraction for types of polymer blends.


Article
COMPARATIVE STUDY THE FLEXURAL PROPERTIES AND IMPACT STRENGTH FOR PMMA REINFORCED BY PARTICLES AND FIBERS FOR PROSTHETIC COMPLETE DENTURE BASE
دراسة مقارنة حول خصائص الانحناء ومقاومة الصدمة للبولي مثيل ميثا اكريليت المقوى بالدقائق والألياف لمادة قاعدة طقم أسنان أصطناعي كامل

Loading...
Loading...
Abstract

In the present search, attempts are made to develop the properties of PMMA resin that used for upper and lower prosthesis complete denture, by addition two different types of particles, which included: nano-hydroxyapatite (nHA) particles and micro-zirconia (ZrO2) particles that added with different volume fractions of (1%, 2% and 3%) to poly methyl methacrylate (PMMA) cold cured resin as new fluid resin matrix. Also woven glass fiber kind (E-glass) and woven Kevlar fiber kind (49), it were added with a fixed volume fraction of (5%) to PMMA composites. In this work the composite prosthetic dentures specimens preparation was done by using (Hand Lay-Up) method as six groups which includes: the first group consists of PMMA resin reinforced by nHA particles, the second group consists of PMMA resin reinforced by ZrO2 particles, the third group consists of (PMMA-nHA) and glass fiber layer as laminated composite , the fourth group consists of (PMMA-ZrO2) and glass fiber layer, the fifth group consists of (PMMA-nHA) and Kevlar fiber layer and the sixth group consists of (PMMA-ZrO2) and Kevlar fiber layer.The experimental part of this study included performing many mechanical tests which, includes (Flexural, Maximum Shear Stress and Impact) tests. The result of this study showed the values of most properties increased with increasing of the volume fraction of (nHA and ZrO2) particles in polymer composite materials. While, the impact strength decreased. The ZrO2 particle and woven mat Kevlar fiber had shown greater values for the most composite materials properties for all groups’ specimens except the flexural strain.Also the results showed the maximum values for hybrid laminated composite properties (flexural modulus and impact strength) were obtained in hybrid laminated composite materials for sixth group specimens. While, the maximum value for properties (flexural strength and max shear stress) were obtained in hybrid laminated composite materials for fourth group specimens.

تم في هذا البحث أجراء عدة محاولات لغرض تطوير مواصفات راتنج البولي مثيل ميثا اكريليت المستخدم كطقم أسنان أصطناعي كامل علوي أو سفلي. وقد حضرت هذه المواد المتراكبة من البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية اضيفت بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج نوع (E-GLASS) والياف الكفلر نوع (49) وقد اضيفت الى المواد المتراكبة بكسر حجمي ثابت هو (%5). في هذا البحث حضرت عينات من أطقام الاسنان الأصطناعية المتراكبة بطريقة (الصب اليدوي) على شكل ستة مجاميع هي: المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت ودقائق الهيدروكسي اباتايت النانوية، المجموعة الثانية تضم راتنج البولي مثيل ميثا اكريليت ودقائق الزركونيا، المجموعة الثالثة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الهيدروكسي اباتايت النانوية، المجموعة الرابعة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الزركونيا، المجموعة الخامسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الهيدروكسي اباتايت النانوية، المجموعة السادسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الزركونيا.يتضمن الجزء العملي من هذا البحث اجراء العديد من الاختبارات الميكانيكية والتي شملت فحوصات (الانحناء، اجهاد القص الأعظم والصدمة(. وقد بينت النتائج بان قيم اغلب الخواص ازدادت مع زيادة الكسر الحجمي لدقائق الهيدروكسي أباتايت النانوية ودقائق الزركونيا، بينما قلت مقاومة الصدمة. وان دقائق الزركونيا والياف الكفلر الحصيرية تعطي قيم أعلى لاغلب خواص المواد المتراكبة ولكافة مجاميع العينات ماعدا الانفعال الأنحنائي. كذلك أظهرت النتائج بان اعلى قيم لخصائص (معامل الانحناء ومقاومة الصدمة) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة السادسة. بينما اعلى قيم لخصائص (مقاومة الانحناء واجهاد القص الأقصى) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة الرابعة.


Article
Investigation of Mechanical and Thermal Properties of the ternary Polymeric Blend prepared from Different materials (Thermosets, Thermoplastic and Elastomer) for Structural Applications
استقصاء الخواص الميكانيكية والحرارية لخليط بوليمري ثلاثي محضر من مواد مختلفة (متصلدة حرارياً، ملدنة حرارياً وإلاستومر) للتطبيقات الهيكلية

Loading...
Loading...
Abstract

In this paper, prepare a set of ternary polymer blend , consisting of thermosets material which is (unsaturated polyester resin (UP)) and thermoplastic material (poly methyl methacrylate(PMMA)) and elastomers material which is natural rubber material (Natural Rubber (NR)) by hand lay-out technique. the basis material was prepared from the blend of binary polymeric materials (polyester (UP) 98% with natural rubber (NR)% 2)) then the material of (poly methyl methacrylate( PMMA)) was added by weight % (0,5,10,15) to binary polymer blend and according to the following formula: [ (100-X) % UP: X% PMMA) + 2% NR]. The research study included the effect of addition of weight percentages of poly (methyl methacrylate) PMMA) on the blends properties ternary polymer blend, and test the mechanical & physical properties like (the tensile strength and modulus tensile elasticity and compressive strength, and flexural strength , impact and fracture toughness and hardness and thermo- physical properties like thermal conductivity and thermal diffusivity beside specific heat) , all of these tests were conducted under laboratory temperature, the results showed that the values (tensile strength and modulus tensile elasticity, flexural modulus and impact strength and fracture toughness and hardness and thermal properties thermal conductivity and specific heat) increases with the weight ratios of the (poly methyl methacrylate) in tri- polymer blend. While values the compressive strength, flexural strength and thermal diffusivity decreases with the increase in the weight ratios of the (poly methyl methacrylate(PMMA)) in the the polymeric blends.

يتناول البحث الحالي تحضير مجموعة من الخلائط البوليمرية الثلاثية, تتكون من مادة متصلدة حرارياً هي (راتنج البولي استر غير المشبع (UP unsaturated polyester resin) ومادة مطاوعة للحرارة من (راتنج بولي مثيل ميثا اكرليت poly (methyl methacrylate) PMMA) ومادة المطاط الطبيعي( Natural Rubber(NR) بطريقة الصب اليدوي وقد حضرت المادة الاساس من الخليط البوليمري الثنائي ( البولي استر بنسبة %98 والمطاط الطبيعي %2 ) ((98%UP +2%NR, وتم اضافة راتنج البولي مثيل ميثا اكرليت بنسب وزنية مختارة (0, 5، 10، 15)% الى الخلائط البوليمرية الثنائية وحسب الصيغة التالية ( ((98-X )%UP: X%PMMA +2%NR. وتضمن البحث دراسة تأثير النسب الوزنية المختارة لراتنج البولي مثيل ميثا اكرليت على خصائص الخلائط البوليمرية الثلاثية المحضرة وعليه أجريت مجموعة من الإختبارات الميكانيكية المتمثلة ( مقاومة الشد ومعامل مرونة الشد والانضغاطية ومقاومة الانحناء ومقاومة الصدمة والصلادة والتوصيلية الحرارية والإنتشارية الحرارية والحرارة النوعية) وجميع هذه الإختبارات تم إجراؤها عند درجة حرارة المختبر ، أظهرت نتائج البحث إن قيم (مقاومة الشد و معامل مرونة الشد ومعامل مرونة الانحناء ومقاومة الصدمة ومتانة الكسر والصلادة والتوصيلية الحرارية والحرارة النوعية ) تزداد مع زيادة النسب الوزنية لراتنج البولي مثيل ميثا اكرليت في الخلائط البوليمرية الثلاثية. بينما قيم (الانضغاطية ومقاومة الانحناء والانتشارية الحرارية ( تنخفض مع زيادة النسب الوزنية لراتنج البولي مثيل ميثا اكرليت في الخليط الثلاثي.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (10)

Arabic (1)


Year
From To Submit

2018 (6)

2017 (1)

2016 (1)

2015 (2)

2013 (2)