Article
The modification of some properties of Al-2%Mg alloy by Ti &Li alloying elements

Author: Talib Abdulameer Jasim
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 239-246
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Aluminium-Magnisium alloys are light, high strength with resistance to corrosion and good weldability. When the content of magnesium exceeds 3% there is a tendency to stress corrosion .This work is an attempt is to prepare low density alloy with up to approximately 2.54 g / cm3 by adding different contents of Ti, and lithium to aluminum-2%Magnisium alloy. The lithium is added in two aspects, lithium chloride and pure metal. The casting performed using conventional casting method. Moreover, solution heat treatment (SHT) at 520 ºC for 4 hrs, quenching in cold water, and aging at 50ºC for 4 days were done to get better mechanical properties of all samples. Microstructure was inspected by light optical microscope before and after SHT. Alloy3 which contains 1.5%Ti was tested by SEM and EDS spectrometer to exhibit the shape and micro chemical analysis of Al3Ti phase. Hardness, ultimate tensile strength, and modulus of elasticity were tested for all alloys. The results indicated that Al3Ti phase precipitates in alloys contain 0.5%T, 1%Ti, And 1.5%Ti. The phases Al3Li as well as Al3Ti were precipitated in alloy4 which contains 2%Ti, and 2.24%Li. Mechanical properties test results also showed that the alloy4 has achieved good results, the modulus of elasticity chanced from 310.65GPa before SHT to 521.672GPa, after SHT and aging, the ultimate tensile strength was changed from 365MPa before SHT to 469MPa, after SHT and aging, and hardness was increased from 128 to 220HV.

تعتبر سبائك الالمنيوم-مغنيسيوم من السبائك الخفيفة. تجمع هذه السبائك بين المتانة العالية ، مقاومة التاكل الكيمياوى، والقابلية للحام. عندما تتعدى نسبة المغنيسيوم في هذه السبائك عن 3% فاها تصبح عرضة للتاكل الاجهادي.يتم في هذا البحث تحضير سبيكة ذات كثافة قليلة تصل الى (2.54غمسم2) باضافة الليثيوم ونسب مختلفة من التيتانيوم الى سبيكة ( Al-2%Mg) . تم اضافة الليثيوم على شكل معدن نقي وعلى شكل مركب كلوريد الليثيوم. اجريت السباكة بالطريقة التقليدية واجريت لها عملية المعاملة المحلولية بدرجة حرارة (520) درجة سليزية لمدة (5) ساعات ثم التقسية بالماء البارد بعدها اجريت لها عملية التعتيق بدرجة حرارة (50) دلرجة سليزية لمدة (4) ايام. تم اختبار البنية المجهرية بواسطة المجهر الضوئي قبل وبعد المعاملة المحلولية لمعرفة تاثير هذه المعاملة على البنية المجهرية والخواص الميكانيكية، تم فحص البنية الماكروية باستخدام المجهر الالكتروني الماسح(SEM) و (EDS) للعينة التي تحتوي 1.5%Ti. كذلك تم فحص خواص الصلادة، مقاومة الشد، ومعامل المرونة. اظهرت النتائج تكون طور (AL3Ti) في السبائك 1-3 التي تحتوي( 0.5%Ti، 1%Ti، 1.5%Ti) على التوالي. اما في السبيكة 4 التي تحتوي على (2%Ti, 2.24%Li) فان كلا الطورين (Al3Ti و Al3Li) قد تكونا. وقد اظهرت نتائج فحص الخواص الميكانيكية ان السبيكة 4 ذات خواص عالية بعد المعاملة المحلولية افضل من السباك الاخرى، حيث ان معمل المرونة تغيرمن 310.65 قبل المعاملة المحلولية والتعتيق الى 521.672GPa بعد المعاملة المحلولية والتعتيق) ، كذلك مقاومة الشد القصوى من 365 الى469Mpa بعد المعاملة المحلولية والتعتيق)، و الصلادة قد ازدادت من 128HV الى220HV).


Article
Review on the Mechanisms ofModification Al-Si alloys

Author: Talib abdulameer Jasim
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 1 Pages: 338-343
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The present paper investigates some mechanisms of modification the eutectic of aluminum-Silicon (Al-Si) alloys.These alloys have been many applications in general industries especially in military, aerospace and automobiles. These alloys in some cases need to modify their properties In particular the wear resistance. This can be overcome by modification the morphology of Si-eutectic. Many mechanisms were suggested in this field. The most common mechanisms are chemical modification and quenching modification. The chemical modification achieved by adding some rare earth elements like sodium (Na), strontium (Sr), and antimony (Sb). Also can be refined the structure of these alloys by using master alloys such as Al-Ti, Al-Ti-B and Al-B. According to restricted growth theory, the impurity induced twinning which reduce the growth. According to the restricted nucleation, the twin plane re-entrant edge (TPRE) Poisoning, which stopped the twin plane. The addition of sodium (Na) in the range of 0.005 to 0.01% modifies the eutectic Si but it has high vapourity and it is difficult to determine its resulting level. Strontium is added in a range of 0.02 to 0.04% but it is ability to oxidation is high as contact with atmosphere.

تبحثهذهالمقالةفيبعضآلياتتعديلااليوتكتكمنسبائكالألومنيوم-السيليكون. لقداستخدمت سبائكAl-Siفي العديدمنالتطبيقاتفيمعظم الصناعاتوخاصةفيالمجالاتالعسكريةوالفضائيةوالسيارات. تحتاجهذهالسبائكفيبعضالحالاتإلىتعديلخصائصهاعلىوجهالخصوصمقاومةالتآكل. ويمكنالتغلبعلىهذاعنطريقتعديلمورفولوجيةSi-eutectic. تماقتراحالعديدمنالآلياتفيهذاالمجال، وأكثرالآلياتشيوعًاهيالتعديلالكيميائيوتعديلبالتصقيع (معدلات التبريد). التعديلالكيميائيالذيتمتحقيقهبإضافةبعضالعناصرالأرضيةالنادرة (Rare earth) مثلالصوديوم (Na) والسترونتيوم (Sr) والأنتيمون (Sb). كمايمكنتحسينالتركيب المجهريلهذهالسبائكباستخدامالسبائكالرئيسية (Master alloys)مثلAl-Ti،Al-Ti-BوAl-B. وفقالنظريةعرقلة النمو،فان الشوائب تسببفي تكوين توائم (Twins)ممايقللالنمو. ووفقًالنظرية عرقلة التخليق،فإنتشويب ال (re-entrant edge) للمستوي التوأمسوف يوقف نموذلك المستوي. إنإضافةالصوديوم (Na) فيالمدىمن 0.005 إلى 0.01٪ يعدلاليوتكتك لكن للصوديوم قابلية عالية للتبخر لذا من الصعب تحديد النسبة المؤثرة فعلا. كذلك يستخدمالسترونتيومSrفيمدىيتراوحبين 0.02 و 0.04٪،إلاأنقابليته على الأكسدةمرتفعةعندتلامسهمع الجو.


Article
Influence of Titanium & Carbon Additions on the Phosphorous Modification Efficiency in Near Eutectic Al–14Si alloy

Authors: Talib Abdulameer Jasim --- Lamyaa Mahde Asaad
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 3 Pages: 919-926
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The influence of Titanium (Ti) & Carbon (C), as gray cast iron master alloy, additions on the structure modification efficiency of the phosphorous (P) in near eutectic Al–14Si alloy and the nucleating mechanism was studied in this work. The results show that the phosphorous modification efficiency can be significantly affected by this addition and the sizes of the primary Si particles can be obviously refined after the addition of trace Ti&C. Micro probe Analyzer (MPA) shows there is a coupling of aluminium phosphides (AlP) and Al4C3 particles in the center of primary Si. Moreover, the nucleation mechanism of primary Si by like-peritectic coupling of AlP and Al4C3 was presented. The formation mechanism of like-peritectic coupling of these particles was also discussed.

في هذا البحث تمت دراسة تاثير اضافة التيتانيوم والكربون،على شكل حديد الزهر الرمادي كسبيكة اشابة، على كفائة الفوسفور في تعديل البنية البلورية لسبيكة الالمنيوم- %14سليكون، كما تم ايضا دراسة سلوك التنوية لهذه السبيكة. لقد اظهرت النتائج بان كفائة تعديل الفوسفور للبنية البلورية تتاثر كثيرا بهذه الاضافة وان الحجم الحبيبي لدقائق السليكون الاولي تاثر هو الاخر بشكل ملحوظ باضافة التيتانيوم والكربون. ويظهرمجس التحليل المايكروي (MPA) ان هناك ارتباط بين دقائق فوسفيد الالمنيوم ودقائق كربيد الالمنيوم في مركز حبيبة السليكون الاولي. علاوة على ذلك فقد تم عرض الية تخليق دقائق السليكون الاولي بواسطة مزدوج شبه بيرتكتك لفوسفيد وكربيد الالمنيوم (AlP and Al4C3. تم ايضا مناقشة الية تكوين مزدوج شبيه البيرتكتك لتلك الدقائق.