Article
The Effect of PVP Addition on the Mechanical Properties Of [84%LLDPE: 15 %(( 100- X) %PP: X%PVP):1%Basalt Particle] Polymer Blend Composites.
دراسة تأثير أضافة (PVP) على الخواص الميكانيكيه للخليط البوليمري المتراكب: [84%LLDPE:15%((100-X)%PP:X%PVP):1%basalt particle]

Authors: Teeb A. Mohammed --- Akram R. Jabur --- Sihama E. salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 573-585
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polymer blends composites were prepared according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all theprepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests). The results are as following:- results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8% wt. which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively.While the highest values of fracture toughness and hardness recorded at 12% wt. (1.4696Pa√m), and at 4% wt. (56.5) respectively.

حضرت المتراكبات ذات أساس الخليط البوليمري الثلاثي, وفق الصيغة [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] وبنسب وزنية مختارة لقيم x 16,12 ,8 ,4 ,0) %). وقد تم تحضيرها بشكل شرائط حضرت بعملية البثق بواسطة باثقة ثنائية اللولب واستخدمت عملية كبس الاشرطة لتحضير العينات وفق المواصفة القياسية (ASTM) , درست الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاط والصدمة والصلادة والزحف) أظهرت النتائج زيادة في الخصائص الميكانيكية مع زيادة نسبة PVP باستثناء المطيلية وعلاوة على ذلك سجلت النتائج أعلى قيم لمقاومة الشد, معامل الرونة, مقاومة الانضغاط ومقاوة الانحناء واعلى أجهاد قص ومعامل مرونة الانحناء ومعامل الزحف عند نسبة (8% wt) PVPوهي على الترتيب (31.32MPa , 0.14GPa , 0.6MPa , 27.4MPa , ( 0.558GPa , 1.08Gpaفي حين سجلت أعلى قيم لمتانة الصدمة وقيم الصلادة عند نسبةPVP 12% wt.)) (1.696 Pa√m) و 4%wt ((56.5 على الترتيب .


Article
Comparative Study of the Mechanical Properties of Two Groups Ternary Polymer Blends Composites
دراسة مقارنة للخواص الميكانيكيه لمجموعتين من الخلائط البوليمرية الثلاثية المتراكبة الخلاصة

Authors: Sihama E. salih --- Akram R. Jabur --- Teeb A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 7 Part (A) Engineering Pages: 1870-1886
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermoplastic polymer blends composites were prepared as strips by double screw extruder. The prepared composites consists of two groups, the first group was prepared as ternary polymer blend according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with X values (0,4,8,12,16%).The second group was prepared with replacing the weight ratios for each of the LLDPE and PP according to formula [84%PP:15%((100-X)%LLDPE:X%PVP):1%B.P] with same X values. Mechanical properties for all prepared samples (tensile, flexural, compression, impact toughness, hardness and creep tests) were studied. The results of this research showed that the fracture strength, young modulus, compressive strength, flexural modulus and creep modulus for the two groups increase with increasing in PVP percentage and the highest values were at 8%PVP, while elongation decreases with addition PVP to the composites. Moreover flexural strength, shear stress and hardness values increase slightly with increasing in PVP percentage for both groups. In addition to that, the impact strength and fracture toughness for the second group samples were high and reach the maximum values (0.45 kJ/m²) at 4%PVP and (4.58 Pa√m) at 8%PVP respectively, as well as all results show that the second groups samples have better mechanical properties.

الخلائط البوليمرية اللدائنية المتراكبة تم تحضيرها بشكل شرائط بواسطة باثقة ثنائية اللولب .المتراكبات المحضرة تتكون من مجموعتين,المجموعة الاولى حضرتكمزيج بوليمري لدائني ثلاثيوطبقا الى الصيغة التالية [84% LLDPE: 15% ((100-X) %PP: X%PVP): 1%B.P]وعندقيم X (16,12,8,4,0). والمجموعة الثانية حضرت باستبدال النسب الوزنية لكل من LLDPE وPP فيما بينهما وحسب الصيغة التالية [84%PP:15((100-X)%LLDPE:X%PVP):1%B.P] وبنفس قيم X . تم دراسة الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاطومتانة الصدمة والصلادة والزحف)وبينت النتائج البحث ان كل من مقاومة الكسر ومعامل المرونة ومقاومة الانضغاط ومعامل مرونة الانحناء ومعامل الزحف لكلا المجموعتين تزداد بزيادة نسبة PVP في الخليط وسجلت أعلى قيم عند النسبة PVP(8%) بينما تناقصت قيم الاستطالة لكلا المجموعتين عند أضافة PVP للمتراكبات المحضرة ,أما قيم مقاومة الانحناء واجهاد القص والصلادةازدادت قليلاً مع زيادةنسبة PVP في المجموعتين الاولى والثانية.ومن خلال فحص مقاومة الصدمة لوحظ ان عينات المجموعة الثانية تمتلك اعلى قيم لمقاومة الصدمة ومتانة الكسر والبالغة (0.45 kJ/m²)عند نسبة %PVP 4و4.58 Pa√m)) عند نسبة 8%PVP على الترتيب. كما وبينت النتائج أن عينات المجموعة الثانية تمتلك خواص ميكانيكية افضل مما تمتلكها عينات المجموعة الأولى.

Keywords

polymer composites --- PVP --- PP --- LLDPE