Surface Modification of Ti-6Al-4V Alloy by Glow Discharge-Plasma Nitriding
تحسين سطوح سبيكة Ti-6Al-4V باستخدام النترتة لبلازما التفريغ التوهج

Loading...
Loading...
Abstract

Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε –Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti,N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion resistance was observed rather than for untreated specimens.

في هذا البحث تمت معاملة عينات من سبيكة Ti-6Al-4V ببلازما النايتروجين بضغوط (3,1.3) ملي بار بمبدأ التفريغ التوهجي للتيار المستمر . اجريت المعاملة للعينات بزمن ( 15,10,5) ساعة وبدرجة حرارة تقريبا 800 درجة مئوية. التركيب البلوري لطبقات النترته فحصت وشخصت بأستخدام حيود الاشعة السينية والمجهر البصري . الاطوار المتشكلة هي , - Ti3N3-X ,-Ti2N  - Ti3N2-Xبالاضافة الى طور الصلب للنايتروجين في التيتانيوم (TiN) . فحوصات الصلادة المايكروية اظهرت زيادة في المقدار لسبائك التيتانيوم المعاملة ببلازما ( لمدة 15,10 ساعة بدرجة 800 درجة مئوية ). قياسات التأكل حصلت باستخدام محلول (Ringer) للعينات المعاملة بالبلازما واظهرت وجود تحسس واضح في مقاومة التأكل للعينات المعاملة بالبلازما مقارنة مع العينات غير المعاملة.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2011 (1)