Article
Effect of Biopolymer Alginate on some properties of concrete
تأثير البايوبوليمر الجينات على بعض خواص الخرسانة

Authors: Waleed A. Abbas وليد عبد الرزاق عباس --- Hawraa M. Mohsen حوراء محمد محسن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2020 Volume: 26 Issue: 6 Pages: 121-131
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Alginate from Large brown seaweeds act as natural polymer has been investigated as polymer and has been added to concrete in different percentages ( 0% , 0.5% , 1% and 1.5% ) by the cement weight and the study show the effect of using alginate biopolymer admixtures on some of the fresh properties of the concrete (slump & the density fresh) also in the hardened state ( Compressive strength , Splitting tensile strength and Flexural strength ) at 28 days. The mix proportion was (1:2.26:2.26) (cement: sand: gravel) respectively and at constant w/c equal to 0.47. The results indicate that the use of alginate as a percent of the cement weight possess a positive effect on fresh properties of concrete at 28 days. In other words, increasing the percentages of alginate addition has enhanced the slump and fresh density of concrete at 28 days, so the 1.5% alginate addition as percent of the cement weight showed the higher percentage of increasing where it was 2.5% for fresh density and 41%for slump of concrete at 28days compared with the reference mix without any addition, also the hardened properties (compression ,splitting tensile and flexural strength) at 28 days showed an increasing when using alginate at a percentage from the cement weight, so the highest increase was at 0.5% and 1.5% of alginate addition where it was about 40%.

الالجينات من أعشاب بحرية بنية كبيرة تم دراستها كبوليمر طبيعي وأضيفت إلى الخرسانة بنسب مئوية مختلفة (0,0.5,1,1.5) من وزن الأسمنت وأظهرت الدراسة تأثير استخدام البوليمر الحيوي الالجينات كمواد مضافة على بعض خواص الخرسانة الطرية (الهطول والكثافة الطرية) وعلى خواص الخرسانة المتصلبة (مقاومة الانضغاط، مقاومة الشد ومقاومة الانثناء) في 28 يومًا. كانت نسبة الخلط (1: 2.26: 2.26) (الأسمنت: الرمل: الحصى) على التوالي ينسبة ماءِ سمنت ثابتة مساوية الى 0.47. اظهرت النتائج إلى أن استخدام الالجينات كنسبة مئوية من وزن الأسمنت له تأثير إيجابي على بعض الخواص الخرسانة الطرية. بمعنى آخر ، فإن زيادة النسب المئوية لإضافات الالجينات قد حسنت الهطول والكثافة الطرية للخرسانة في 28 يومًا ،حيث ان اضافة الالجينات بنسبة 1.5٪ كنسبة مئوية من وزن الأسمنت أظهرت اعلى نسبة زيادة حيث كانت 2.5٪ للكثافة الطرية و 41٪ للهطول في 28 يومًا مقارنة بالخلطة المرجعية دون أي إضافة ، كذلك أظهرت الخواص المتصلبة للخرسانة (الانضغاط وقوة الشد والانثناء) في 28 يومًا زيادة عند استخدام الالجينات كنسبة مئوية من وزن الأسمنت ، حيث انه اعلى نسبة للزيادة كانت حوالي 40 ٪ عند 0.5 ٪ و 1.5 ٪ من إضافة الالجينات.


Article
Impact Strength for the 3D Textiles Fiber Reinforced Cementitious Composites Plates
تحمل الصدمة للصفائح السمنتية المركبة والمسلحة بنسيج زجاجي ثلاثي الابعاد

Loading...
Loading...
Abstract

The use of textile reinforcement made from non-corrosive materials, such as carbon and glass can reduce the required concrete material; this is known as Textile Reinforced Concrete (TRC). This study deals with plate specimens having dimension of 500×500×40mm tested under impact load at 28 and 90 days age under two conditions of ends, simply supported and fixed. Cement mortar with about 60 MPa, 7cm cube compressive strength at 28 days was designed for casting the plates. Plate specimens were divided into four groups, they consist of reference plates (no reinforcement) and plates reinforced with 3D glass fabric having three different thicknesses 6, 10 and 15mm.The results indicate that using 3D textile glass fabric cause an increase in number of blows, reduce in final stage deflection, an improvement in toughness and energy absorption under impact loads. Using 3D textile glass fiber with 10mm thickness gave higher number of blows for 28 and 90 days as compared with 6 and 15 mm. Plates with slice 6mm 3D textile glass fiber in two way reinforced has significantly enhancement in number of blows, the improvement was about (80 - 125%) and (128.5- 114. 3%) for 28 and 90 days respectively. The specimens showed increase in the energy absorption, besides the number and width of cracks was reduced and only few cracks are propagated up to the edge of the plates.

ان استخدام الالياف اوالنسيج بابعاد ثلاثية مصنوعة من مواد زجاجية اوكاربونية ذات طبيعة كيميائية خاملة يؤدي الى تقليل بكمية المواد السمنتية الداخلة بالخلطة الخرسانية. حيث تضمنت هذه الدراسة قياس تحمل الصدمة لصفائح بابعاد 500*500*40 ملم وبعمر 28 و90 يوم بواقع نوعين من الشروط الحدودية (بسيطة وثابتة). وتم صب الصفائح باستخدام مونة اسمنتية ذات مقاومة انضغاط 60 ميكاباسكال بعمر 28 يوم. قسمت الصفائح الى اربع مجاميع مؤلفة من صفائح بدون استخدام اي الياف لغرض المقارنة وصفائح مسلحة بثلاث اسماك مختلفة (6و10و15ملم) من الياف زجاجية ثلاثية الابعاد. فحصت الصفائح تحت تاثير حمل الصدمة واظهرت النتائج ان استخدام نسيج زجاجي ثلاثي الابعاد ادى الى تحسن في خواص الصفائح وذلك بزيادة عدد الضربات وتقليل الانحرافات وزيادة في مقدار الطاقة الممتصة. ان استخدام الياف زجاجية بسمك 10 ملم تطلب زيادة في عدد الضربات المطلوبة للفشل بعمر فحص 28 و90 يوم مقارنة مع سمك 6 و15 ملم. كما ان استخدام نسيج ثلاثي الابعاد على شكل شراح بطبقتين وبسمك 6 ملم ابدى قوى ربط اكبر وتحسن بعدد الضربات ، حيث كان التحسن بمقدار 80-128 % و128.5-114.3% لاعمار 28 و90 يوم اضافة الى ان جميع الصفائح اظهرت زيادة في امتصاص الطاقة ونقصان في سمك وعدد الشقوق خلال الفحص .