Article
Fabricating and characterizing of ZnO nanostructure solar cells
صناعة وقياس خصائص غشاء ZnO بتركيب نانوي للخلايا الشمسية

Author: Wisam J. Aziz,
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2013 Volume: 11 Issue: 4 Pages: 287-292
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Zinc oxide (ZnO) thin film on crystalline silicon (c-Si) substrate has been deposited by RF sputtering method to use it for fabricating a solar cell. Structural properties of ZnO films studied using high resolution X-ray diffraction (HRXRD) analysis of the films which show that the films have polycrystalline nature with orientation (002). Small crystallite size of prepared films was calculated using Scherrir formula that indicates our films are within Nano scale. In addition, optical properties have been done via scanning electron microscopy (SEM) which used to describe the surface morphology and Photoluminescence (PL) measurements which revealed that the energy bandgap of prepared films were in the UV emission at 380 nm. Finally, thickness of the films was measured with Filmetric (F-20). Our findings were the fabricated ZnO films are successful in simple and low cost method with high quality and unexpected nanostructure behavior. Good current-voltage behavior with high conversion efficiency of 14.5 % has been obtained.

في هذا البحث تم ترسيب أوكسيد الخارصينِ (ZnO) على السيليكونِ البلّوريِ ((c-Si بواسطة منظومة الترسيب (RF sputtering) لصناعة خلية شمسية. دَرستْ الخصائص التركيبية لغشاء ZnO بأستعمال اشعه سينية عالية الوضوحية (HRXRD) لتحليل الاغشية والذي بين بأن الاغشية لَها طبيعةُ polycrystalline)) بالتوجيهِ (002). الحجم البلوري الصغير للأفلامِ المُحَضّرةِ تم حسابه بأستعمال صيغةِ Scherrir والتي تُشيرُ إلىان الاغشية المرسبه هي ضمن مِقياسِ النانو. بالإضافة، الى الخصائص البصرية عُمِلتْ عن طريق استعمال جهاز مَسْح المجهر الألكترونِي (SEM) االذي يُستَعملُ لوَصْف السطح, وتم استخدام مقياس Photoluminescence (PL))) لمعرفة فجوة الطاقةَ للأفلامِ المُحَضّرةِ والتي كَانتْ في المنطقة UV في 380 nm. أخيراً، قِيسَ سُمك الأفلامِ بواسطة ((Filmetric (F-20). وفق هذه النتائج فان ترسيب اغشية ZnO تمت بنجاح وبكلفةِ بسيطةِ ومنخفضةِ بطريقة التركيب النانوي عالي النوعية. امكن الحصول على فولطيةِ وتيار عاليين وبكفاءةِ تحويلِ وصلت الى 14.5 %.


Article
Fabrication based porous silicon photo-detector and improving its spectral responsivity by depositing IZO thin films
صناعة كاشف ضوئي بالاعتماد على السليكون المسامي وتحسين استجابته الطيفية بترسيب اغشية اوكسيد الخارصين الرقيقه المشوبه بالانديوم

Author: Wisam J. Aziz and Abbas K. Jarhallah
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2014 Volume: 12 Issue: 4 Pages: 166-172
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work porous silicon was prepared by electrochemical etching, then IZO thin films were deposited on porous silicon. SEM pictures showed different morphology for all from porous silicon and IZO films deposited on porous silicon. The pores diameter ranges from (0.5-1 μ m). AFM pictures showed the smoothness increased with depositing IZO films. The average roughness is (34.12 nm), (23.4 nm) and the root mean square is approximately (41.88 nm), (28 nm) for porous silicon and IZO film deposited on porous silicon respectively. The results showed increasing of the spectral responsivity with depositing IZO film. Spectral responsivity for photo detractor is about (0.69 A / Watt) then it improved by depositing IZO films and becomes (0.84 A / Watt).

في هذا العمل تم تحضير السيليكون المسامي بالتنميش الكهروكيميائي، ثم تم ترسيب اغشية اوكسيد الخارصين المشوبة بالأنديوم على السيليكون المسامي. صور المجهر الالكتروني الماسح لكل من السيليكون المسامي و اغشية اوكسيد الخارصين المشوبة بالأنديوم المترسبة على السيليكون المسامي تظهر اختلاف في طبيعة السطح، تتراوح اقطار المسامات (0.5-1) مايكرو متر. بينت صور مجهر القوة الذرية زيادة النعومة مع ترسيب اغشية اوكسيد الخارصين المشوبة بلانديوم. متوسط الخشونة (34.12نانو متر),(23.4نانومتر) ومتوسط الجذر التربيعي تقريبا (41.88نانو متر)، (28نانو متر) للسيليكون المسامي و اغشية اوكسيد الخارصين المشوبة بلانديوم المترسبة على السيليكون المسامي على التوالي. بينت النتائج ازدياد الاستجابة الطيفية مع ترسيب اغشية اوكسيد الخارصين المشوبة بلانديوم. الاستجابة الطيفية للكاشف الضوئي (0.69 امبيرواط) ثم تحسنت بترسيب اغشية اوكسيد الخارصين المشوبة بلانديوم واصبحت (0.84امبير واط).


Article
Fabrication of ZnO-Ag Nanocomposite and Their Antibacterial Activities

Authors: Wisam J. Aziz --- Nisreen Z. Jassim
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 1 Pages: 204-207
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

ZnO nanopowder was synthesized by a simple hydrothermal technique using zinc acetate and Triethanolamine (TEA) as surfactant agents. The resultant powder was annealed at 140 ᵒC for 12 hours. The as – synthesized ZnO nanopowder was then mixed with AgNO3 to prepare ZnO-Ag nanocomposites. The structural, morphological, and optical properties were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and UV-Visible spectroscopy (UV-Vis). The results confirm that Ag nanoparticles (NPs) have been covered the ZnO hexagonal NPs, and show the redshift with the peak centered at 334 nm, because the interfacial electron coupling between ZnO and Ag NPs, the surface Plasmon peak centered at 403 nm was detected along with the excitonic peak of ZnO confirming the formation of ZnO-Ag nanocomposite. The antibacterial effect of ZnO - Ag nanocomposites was studied for Gram- negative (E.coli) and Gram– positive (Staphylococcus aureus), which showed that the diameter of the inhibition zone of pathogenic bacteria about 15 mm for E.coli and did not show any activity for Staphylococcus aureus.

في هذا العمل، تحضير جزيئات أوكسيد الخارصين بواسطة تقنية مائية حرارية بسيطة باستخدام خلات الخارصين و ثلاثي الايثيلامين كعامل مساعد للتفاعل. تم تلدين المسحوق الناتج عند 140 درجة مئوية لمدة 12 ساعة. ثم تم خلطها مع نترات الفضة لتحضير مركبات اوكسيد الخارصين- الفضة النانوية. وقد تم دراسة الخصائص الهيكلية وخصائص السطح والبصرية بحيود الأشعة السينية والمجهر الإلكتروني الماسح والأطياف المرئية للأشعة فوق البنفسجية حيث اكدت النتائج ان جسيمات الفضة المكعبة التركيب النانوية تغطي اوكسيد الخارصين ذو التركيب السداسي في حين تظهر نتائج الاشعة فوق البنفسجية انحياز نحو الاطوال الموجية الحمراء مقارنة مع اوكسيد الخارصين النقي وتم ملاحظة قمة البلازمون التي تؤكد تكوين المركبات النانوية. تم دراسة التاثير المضاد للبكتيريا لمركبات اوكسيد الخارصين - الفضة النانوية ضد بكتيريا جرام السالبة (الاشريكية القولونية ) وبكتريا جرام الموجبة ( المكورات العنقودية الذهبية), أظهرت النتائج أن قطر منطقة تثبيط البكتيريا المسببة للأمراض حوالي 15 ملم للإشريكية القولونية ولم تضهر اي نتيجة للمكورات العنقودية الذهبية.


Article
Preparation and characterization of SnO2 nanoparticles using pulsed laser ablation in liquid
تحضير ودراسة خصائص ثنائي اوكسيد القصدير النانوي باستخدام تقنية القشط بالليزر في السائل

Authors: .Wisam J. Aziz --- Raad S. Sabry --- Ahmed Sadek Ottman Ali
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2016 Issue: 1 Pages: 237-246
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this work, colloidal SnO2 nanoparticles were prepared by laser ablation of tin target immersed in solvent (deionize water) without the use of any chemical/surfactant. The effects of solvents, laser energy and number of pulses on the morphology, optical, chemical and electrical properties, of the synthesized nanoparticles were studied on glass substrate using defferent pulses at (1000 - 1500 - 2000) pulses.then Eg = ( 3.57- 3.8 - 3.85) and the average grain size found to be about (218 nm) while the RMS value about ( 0.859 nm).

في هذا البحث تم تحضير ثنائي اوكسيد القصدير النانوية باستخدم تقنية القشط بالليزر لقطعة معدنية نقية بنسبة (%99.99) من القصدير مغمورة في مذيب (ماء اللاايوني) من دون استخدام اضافات كيميائية عند التحضير. حيث ان هذه الطريقة تسمح لتحضير مواد نانوية مختلفة لأنها تقنية بسيطة ويمكن بسهولة السيطرة على معلمات الليزر. كما تمت دراسة تاثير المذيبات وطاقة الليزر وعدد نبضات الليزرعلى خصائص التركيبية والبصرية للجسيمات النانوية المحضرة


Article
Aggregation and Characterization of ZnO Nano Particles Using Laser Ablation Technique in Ethanol

Authors: Wisam J. Aziz --- M.A.Abid --- Hanan Kh. Mutlk
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2017 Volume: 20 Issue: 4 Pages: 32-39
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this work, ZnO nanoparticles were snthyesis using pulse laser ablation of zinc target (purity of 99.99%) immersed in ethanol with wave length of Nd:YAG laser (532 nm) operating at different laser energies (700, 800, 900 mJ) with 1Hz and (2000) pulse. A matching of the observed and standard (hkl) planes confirmed that the product is ZnO having a polycrystalline in nature with hexgonal structure perferention in (101) direction.FESEM images showed that NPs have different morphologies and not uniform consist of many small irregular nanoparticles. The surface structure, in the energy 700 mJ has been more uniform compared with others energy.


Article
Production of TiO2 Nanoparticles in Different Phases and Shapes by using PLA and Hydrothermal Method

Authors: Abbas K. Jarallah --- Raad S. Sabry --- Wisam J. Aziz
Journal: Al-Mustansiriyah Journal of Science مجلة علوم المستنصرية ISSN: 1814635X Year: 2018 Volume: 29 Issue: 2 Pages: 175-178
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Titanium dioxide was prepared using pulsed laser ablation (PLA) and hydrothermal method. Scanning electron microscopy images showed that the product from hydrothermal method had a nanotube shape, whereas those from PLA in liquid were nanoparticles. The optical properties in the absorption curve of product from the hydrothermal method were slightly greater than those from the PLA method, and the energy gaps were 3.39 and 3.26 eV for the hydrothermal method and PLA, respectively. XRD results showed that the TiO2 prepared through PLA showed one phase (rutile), whereas those prepared through hydrothermal method showed two phases (anatase and rutile). Moreover, the product from hydrothermal method had smaller particle size smaller than that from PLA. Furthermore, the product yield and the required reaction time of the hydrothermal method were higher than those of PLA.

في هذا البحث تم تحضير مادة اوكسيد التيتانيوم بطريقة القشط بالليزر النبظي وطريقة الهايدروثيرمال. اظهرت صور المجهر الالكتروني الماسح بان التشكيل المتكون على السطح بطريقة الهايدروثيرمال هي اشكال انابيب دقيقه ولكن الاشكال الظاهرة بطريقة القشط بالليزر هي اشكال كرويه.الخصائص البصريه اظهرت من خلال منحني الامتصاص بان الامتصاصيه بطريقة الهايدروثيرمال هي اكبر بقليل من الامتصاص الناتج بطريقة القشط بالليزر وان فجوة الطاقه كانت (3.26 eV -3.39 eV ) للنماذج المحضره بطريقة الهايدروثيرمال والليزر على التوالي. نتائج حيود الاشعه السينيه اظهرت بان ثنائي اوكسيد التيتانيوم الناتج بطريقة الليزر كان بطور واحد هو الروتايل بينما كان بطورين هما ( الروتايل والاناتاس ) بطريقة الهايدروثيرمال اضافة الى ذلك فان حجم الجسيمات الناتجه بواسطة الهايدروثيرمال كان اصغر من حجم الجسيمات الناتجه بطريقة الليزر وكذلك الزمن المطلوب لاتمام التفاعل بطريقة الهايدروثيرمال يكون اطول من الزمن اللازم بطريقة الليزر.


Article
Preparation of Tio2 nanoparticles by laser ablation in methanol solution

Authors: Wisam J. Aziz وسام عزيز جعفر --- Saja Q. Ali سجى قيس علي
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2016 Issue: 5 Pages: 331-338
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this work, Tio2 nanoparticles prepared by pulse laser ablation(PLA) of titanium target (purity of 99.99%) immersed in methanol solution by focused beam of 532 nm pulsed used Nd:YAG laser operating at different laser pulses in range (1000, 1500, 2000) pulses with 1Hz repetition rate, effective beam diameter 4.8 mm and 10 ns pulse width. Laser energy was kept constant at (900) mJ. The effects of methanol solution and number of laser pulses on the structural properties (XRD) and morphology (FESEM) was study. From XRD measurment have been revealed that 4peaks with 2θ values of 27.160, 36.2, 54.7 and 69.02 degree, corresponding to TiO2 crystal planes of (110), (101), (211) and (301) respectively at 2000 pulses in methanol solvent after heating at temperature 85 oC for 45 minute.

في هذا البحث تم تحضير الجسيمات النانوية من اوكسيد التيتانيوم Tio2 المحضر بواسطة الترسيب الفعال بالليزر النبضي بأستخدام ليزر ND:YAG الذي يعمل بطول موجي 532 نانو متر تم عملها بضربات ليزر مختلفة (2000,1500,1000) بأمد نبضة 10 نانو ثانيه وقطر حزمة 4.8mm كـوسيلة إقتلاع من سطح الهدف (التيتانيوم) ذو نقاوه 99.99% .تم دراسة تأثيرمحلول الميثانول وعدد ضربات الليزر على خصائص التركيبة و التشكيلية وبينت الدراسه من خلال قياسات الاشعة السينية وجود 4 قمم عند الزوايا 27.160=Ɵ 2 بالمستوى (110) , وقمة ايضآ عند الزاوية 36.2=Ɵ2 بالمستوى101) ) , وكذلك عند الزاويه =54.7Ɵ2 بالمستوى (211) وأخيرآ عند الزاوية 69.02=Ɵ2 بالمستوى (301) عند الشرط المثالي وهو 2000 ضربة بطاقة 900 بدرجة حرارة c˚ 85 لــ 45 ثانــيه.


Article
Structural and optical properties of different thicknesses nano-crystalline Pb0.2Cd0.8S prepared by chemical bath deposition

Authors: Raad S. Sabray --- Wisam J. Aziz --- L. A. Latif --- Huda J. Ali
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2015 Issue: 3 Pages: 159-170
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this study, nanostructure thick films of Pb0.2Cd0.8S were prepared by the chemical bath deposition technique on glass slides at 343 K with different thicknesses ( 2.65 , 3 and 3.58)μm.The surface morphology of films which characterized by AFM and SEM revealed the formation started in low thickness with small islands to reach the final structure formation in 3.58μm with nano sheets (Like- stars) and homogenous for whole area of top surface and the spherical crystallite size of the films is found to range from 50 nm to 100 nm. The optical absorption and transmission properties of films were determined by UV spectrophotometry.The energy band gap values were increased with thickness increased as 2.65 μm (2eV), 3 μm (2.2 eV) and 3.85 μm (2.23 eV) according to the principle of thickness relation with energy band gap.


Article
Studying the structural and morphological properties of ZnO nanoparticles using Pulse Laser Ablation techniquen ( PLA) in liquid
دراسة الخواص التركيبية لــ ZnO النانوية بـا استخدام PLA

Authors: Hanan Kh. Mutlk حنان خضير مطلك --- Wisam J. Aziz وسام جعفر عزيز --- Muslim A. Abid مسلم عز الدين عبد
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2016 Issue: 5 Pages: 281-288
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this work, Zno nanoparticles were fabricated by laser ablation of zinc target (purity of 99.99%) immersed in distilled water (DW) prepared on glass substrate by using the radiation of Nd:YAG laser (532 nm) operating at different laser pulses(1000, 1500, 2000) by 1Hz repetition rate, effective beam diameter of 4.8 mm and 10 ns pulse width. Laser energy was kept constant at (800) mJ. The Optimmaum condition of preparation was 2000 pulses with excellent structural (XRD) revealed that 4 with values of 36.32, 45.74, 56.76 and 68.08 degree, and morphology field emission scanning electron miceoscope (FESEM) properties

في هذا البحث تم تحضير جسيمات اوكسيد الخارصين النانوية بأستخدام تقنية الأستئصال بالليزر لهدف الخارصين ذو نقاوه 99.99% المغمور في الماء المقطر والذي أعد على شريحة الزجاج بواسطة تشعيع ليزر الأندياك الذي يعمل بطولا موجي (532) نانومتر لنبضات مختلفه (1000-1500-2000) ضربة ومعدل تكرار نبضه 1 هرتز وقطر حزمه 4.8 ملمتر وأمد نبضة 10 نانو ثانيه, و ان طاقة الليزر هنا ثابتة مقدارها 800 جول .و ان افضل شرط للعملية هو 2000 ضربة الذي يمتلك 4 قيم للزاويـــــــة Ɵ2 وهي 36.32 ,45.74 ,56.76 واخيرآ 68.08 درجة وخصائص التشكل المورفولوجية.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (9)


Year
From To Submit

2018 (2)

2017 (1)

2016 (3)

2015 (1)

2014 (1)

More...