Article
EFFECT OF COOLING RATE ON MECHANICAL PROPERTIES OF EUTECTIC AND HYPOEUTECTIC Al-Si ALLOYS

Author: Zeyad D. Kadhim
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 6 Pages: 1576-1583
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research the effect of cooling rate and mold type on mechanical properties of the eutectic and hypoeutectic (Al-Si) alloys has been studied. The alloys used in this research work were (Al- 12.6%Si alloy) and (Al- 7%Si alloy).The two alloys have been melted and poured in two types of molds with different cooling rates. One of them was a sand mold and the other was metal mold. Mechanical tests (hardness, tensile test and impact test) were carried out on the specimens. Also the metallographic examination was performed.It has been found that the values of hardness for the alloys(Al-12.6%Si and Al-7%Si) which poured in metal mold is greater than the values of hardness for the same alloy when it poured in a heated metal mold at different temperatures or in sand mold. The strength and impact resistance for the alloys (Al-12.6%Si and Al-7%Si) are greater when these were poured in a metal molds than that when it poured in a sand mold.Furthermore, the higher cooling rates enhance the strength, hardness and impact resistance for the two alloys, while the low cooling rates reduces these mechanical properties.The percentage of elongation and the amounts of formed porosity decreased when the cooling rates increased

درس في هذا البحث تأثير معدل التبريد ونوع القالب على الخواص الميكانيكية لسبائك (المنيوم – سليكون) اليوتكتيكية و تحت اليوتكتك. السبائك المستخدمة في هذا العمل البحثي كانت ( سبيكة المنيوم –٦, ١٢% سليكون ) و ( سبيكة المنيوم – ٧ % سليكون ). السبيكتين تم صهرها و صبها في نوعين من القوالب و بمعدلات تبريد مختلفة . أحدهما كان قالب رملي و الاخر كان قلب معدني . الاختبارات الميكانيكية (الصلادة ، أختبار الشد ، أختبار الصدمة) تم أجرأها على العينات. أنجز الفحص المجهري أيضا. لقد وجد بأن قيم الصلادة للسبائك (المنيوم –٦, ١٢% سليكون و المنيوم – ٧ % سليكون ) و التي صبت في القالب المعدني هي أكبر من قيم الصلادة لنفس السبائك عند صبها في قالب معدني مسخن عند درجات حرارية مختلفة أو في قالب رملي.المقاومة ومقاومة الصدمة للسبيكتين هي أكبر عند صبها في قوالب معدنية من تلك المصبوبة في قالب رملي. علاوة على ذلك ، معدلات التبريد العالية تحسن من المقاومة ، الصلادة و مقاومة الصدمة للسبيكتين بينما معدلات التبريد الواطئة تقلل من تلك الخواص الميكانيكية. أن النسبة المئوية للاستطالة و كمية المسامية المشكلة تقل عندما تزداد معدلات التبريد.


Article
Prediction of Enthalpy and Internal Energy of Saturated Steam

Authors: Sabah Jebour Al-Janabi --- Emad Talib Hashim --- Zeyad D. Kadhim
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2011 Issue: 5 Pages: 137-149
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The main aim of this work is to establish an empirical formula for calculation the enthalpy and internal energy of saturated steam. The use of this formula reflects a good result under saturated steam conditions. In order to obtain this reliable model for calculating these thermodynamic prosperities, a formula is established by nonlinear regression based on experimental data collection, after a thorough survey of literatures. Application of the proposed formula shows that, the average percentage error between the results obtained by this equation and the experimental data, is about (0.58%) for internal energy, and for enthalpy is about (0.64%), for 71 data points at each case.

هدف البحث هو ايجاد علاقة رياضية تجريبية لحساب المحتوى الحراري والطاقة الداخلية للبخار المشبع. استعمال هذه العلاقة عكست نتائج جيدة في ظروف البخار المشبع. ولاجل ان تكون العلاقة اكثر شمولية تم الاعتماد على الاساس اللاخطي الرياضي للنتائج العملية الماخوذة من المصادر.تم تطبيق العلاقة المذكورة واظهرت آلنتائج بان معدل نسبة الخطأ مقارنتا بالنتائج العملية هي (%0.58) للطاقة الداخلية و (%0.64) للمحتوى الحراري ول 71 نقطة عملية لكل حالة.


Article
Th∞retical I)ete耐nation of Physical Properties For Poly VinyI Pyrolidone

Authors: Raouf M.Raouf --- Khalid Mershed --- Zeyad D. Kadhim
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2010 Issue: 5 Pages: 221-253
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research A simple model has been presented for polyvinylpyrrolidone aqueous solutions to predict wave amplitude in C.R.O byusing Ulrasonic technician (ho,, "non-radiated", hri, "irradiated", andh*i, ils a function of h**). The use of this model reflects a good resultfor the samples of PVPD aqueous solutions, which was radiated withgaflrma rays of 150 Rad/min, dose for 22 min at room temperature,therefore this factor, will be constant in this work. These data wereused to develop a new method to predict the wave amplitude in C.R.O.The model can be used to calculate the ho,, & h"i, for a given primaryamplitude of wave in C.R.O ( h-o, h*), the distance between receiverand ultrasonic wave sender x, and PVPD concentration v. From thismodel we can calculate absorption coefficient (c) for non radiated andirradiated PVPD as a function of h,*, h'i,, and v. This predictionmethod give a good agreement with the measured values, where theabsolute average error for wave amplitude in C.R.O for non-radiatedh,- is (1.02), wave amplitude for iradiated in C.R.O h*i' is (0.14), andwave amplitude in C.R.O hxir as a function of h"* is (0.25). Theabsolute average error for non-radiated (a) is (0.45), and irradiated (c)is (1.04) for all data points of PVPD.

Keywords


Article
Effect of Shot Peening on Mechanical Properties for Steel AISI 1008

Authors: Mohammed Abdulraoof Abdulrazzaq محمد عبد الرؤوف عبد الرزاق --- Zeyad D. Kadhim --- Wassan S. Hussain
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2019 Volume: 12 Issue: 2 Pages: 54-64
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Residual stress has a significant effect for improving engineering properties for metals .Most of the surface treatments produce compressive residual stress at the metal surfaces, which reduce crack initiation and increasing the metal resistance to fatigue, which is shot peening process. Shot peening is usually used for this purpose for producing plastic deformations of surface of the metal which can lead to creation high residual compressive stresses at metal surface .This research include study the influence of shot peening process on fatigue resistance, surface hardness and surface roughness for low carbon steel (AISI 1008). This process accomplished with different times which were (10, 20 and 30(minutes. The result of the fatigue test showed that the fatigue limit increase when shot peening time increased and the best fatigue limit obtained when shot peening process was carried out at 30 minutes. Results of hardness test showed that surface hardness increased with increase of shot peening time. It can be seen that highest value of surface hardness is obtained from shot peening process at time (30 minutes) which is (235.1 HVN). Results of surface roughness test showed that the surface roughness of metal increased when time of shot peening increased


Article
An Investigation into the Railway Shoulder Manufacturing
تحريات من تصنيع اكتان سكك الحديد

Authors: Omar A. Abdulrazaq عمر عبد الرزاق --- Zeyad D. Kadhim زياد دوشان كاظم --- Akeel D. Subhi عقيل دحبجي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2009 Volume: 13 Issue: 2 Pages: 86-94
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Ductile cast iron is considered to be a recent member of the cast irons family.
Because of the high cost that spent in producing ferritic ductile iron using heat treatment
with long period of time. This work presents a brief picture to assess railway shoulder made
from ferritic ductile iron in the as-cast condition without any post heat treatment. The
manufacturing is achieved using RF induction furnace with the aid of instantaneous
chemical analysis using optical emission spectrometer (OES) to control the chemical
composition of the ferritic ductile iron. The results showed that the produced ferritic ductile
iron has properties satisfy the required application.

يعد حديد الزهر المطيلي المكون الاحدث ضمن عائلة حديد الزهر. نتيجة للكلفة العالية الناتجة من عملية الحصول على الحديد المطيلي الفرايتي بسبب الفترة الزمنية الطويلة اللازمة لاجراء التعامل الحراري. لهذا فان هذا البحث يهدف الى اعطاء صورة مختصرة عن تقييم كتف السكة الحديدية المصنوع من الحديد المطيلي الفرايتي المنتج بدون اجراء اي تعامل حراري. اذ تم انتاج الحديد المطيلي الفرايتي باستخدام فرن الحث المترافق مع التحليل الكيميائي الدوري اثناء عملية الصهر باستخدام مطياف الانبعاث الضوئي (OES) للسيطرة على التركيب الكيميائي. اوضحت النتائج ان الحديد المطيلي الفرايتي المنتج في هذا البحث يمتلك خواص تكافيء التطبيق المطلوب

Keywords


Article
Effect of the Diffusion Bonding Conditions on Joints Strength
تأثير شروط انتشار الربط على مقاومة المفاصل

Authors: Sabah J. Al-Janabi صباح الجنابي --- Ali I. Al- Azzawi علي العزاوي --- Zeyad D. Kadhim زياد دوشان كاظم
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2009 Volume: 13 Issue: 1 Pages: 179-188
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this research the effect of different parameters on the strength of joints which bonded by using diffusion bonding process has been studied. The specimens of copper and nickel were annealed in a vacuum furnace at (800 ºC). Specimens of Cu and Ni were plastically deformed to (0%, 10%, 20%, and 30%) in tension before diffusion bonding process. Diffusion bonding was carried out at different conditions (temperatures, pressures, periods of the time, and surface roughness of the mating surface).The parts were diffusion bonded using a creep machine with a jig in a vacuum chamber flushed with argon gas after evacuation to about 10-² torr to prevent oxidation. It has been found that the strength of bonded joints increased with increasing the parameters (temperature, pressure, and time of diffusion bonding). This increment of joint strength is just for a certain value and then decreased with increasing the pervious parameters.Besides that it has been found that the bonded joint strength decreases with increasing the roughness of the mating surface. Furthermore the bonded joint strength increased with increasing the percentage of plastic deformation of specimens before diffusion bonding process

درس في هذا البحث تأثير العوامل المختلفة على متانة الوصلات المربوطة بأستخدام عملية الربط الانتشاري حيث تم تلدين عينات من النحاس والنيكل عند درجة حرارة 800 مº في فرن مفرغ.تم أجراء عملية التشكيل اللدن على عينات من النحاس والنيكل بالسحب وبنسب أستطالة (0%، 10%، 20%، 30% ) ثم تم أجراء عملية الربط الانتشاري في ظروف مختلفة ( درجات الحرارة ، الضغط ، فترات من الزمن وخشونة سطحية متباينة للسطوح المتلامسة). العينات تم ربطها أنتشاريا بأستخدام ماكنة فحص الزحف والموجه وبأستخدام غرفة مفرغة وقد ضخ غاز الاركون بعد التفريغ (torr ² ­ 10 ( لغرض تفادي الأكسدة.وقد وجد بأن متانة الوصلات المربوطة تزداد مع زيادة أي من العوامل ( درجة الحرارة ، الضغط وزمن الربط الانتشاري) وأن هذه الزيادة تكون لقيمة معينة ثم تنخفض مع الاستمرار بزيادة هذه العوامل السابقة.بالإضافة إلى ذلك وجد بان متانة الوصلات المربوطة تقل مع زيادة الخشونة السطحية للسطوح المتلامسة. كما وجد بان متانة الوصلات المربوطة تزداد مع زيادة النسبة المئوية للتشكيل اللدن للعينات التي تمت قبل عملية الربط الانتشاري

Keywords


Article
Mechanical Properties of Burnished Steel AISI 1008
الخواص الميكانيكية للصلب المصقول نوع AISI 1008

Loading...
Loading...
Abstract

Burnishing improves fatigue strength, surface hardness and decrease surface roughness of metal because this process transforms tensile residual stresses into compressive residual stresses. Roller burnishing tool is used in the present work on low carbon steel (AISI 1008) specimens. In this work, different experiments were used to study the influence of feed parameter and speed parameter in burnishing process on fatigue strength, surface roughness and surface hardness of low carbon steel (AISI 1008) specimens. The first parameter used is feed values which were (0.6, 0.8, and 1) mm at constant speed (370) rpm, while the second parameter used is speed at values (540, 800 and 1200) rpm and at constant feed (1) mm. The results of the fatigue test showed that improvement in fatigue limit, where the highest fatigue limit was obtained at (1mm feed, 1200rpm speed) in burnishing process which was (169 Mpa). The hardness results, showed increasing feed and speed values lead to increasing the hardness. The burnishing process reduces surface roughness by producing accurate and better surface finish. The best surface fineness of metal at (1mm feed and 1200 rpm speed) was 0.11 μm.

الصقل يحسن مقاومة الكلال، الصلادة السطحية ويقلل الخشونة السطحية للمعدن لأنه هذه العملية تحول اجهادات الشد المتبقية الى الاجهادات الضغطية المتبقية. أداة الصقل الأسطواني أستخدمت في العمل الحالي على عينات الفولاذ منخفض الكاربون نوع .(AISI 1008) في هذا العمل، تجارب مختلفة أنجزت لدراسة تأثير عامل التغذية وعامل السرعة في عملية الصقل على مقاومة الكلال، الخشونة السطحية والصلادة السطحية لعينات الفولاذ منخفض الكاربون نوع .(AISI 1008) أول عامل مستخدم هو قيم التغذية التي كانت (0.6, 0.8, 1) مليميتر في سرعة ثابتة (370) دورة/ دقيقة، بينما ثاني عامل مستخدم هو قيم السرعة التي كانت (540, 800, 1200) دورة/دقيقة في تغذية ثابتة (1) مليميتر. نتائج اختبار الكلال توضح بأنه تم تحسين حد الكلال، حيث أعلى قيمة لحد الكلال تم الحصول عليها من العينات التي تمت معاملتها مع (1 مليميتر قيمة التغذية , 1200 دورة/ دقيقة قيمة السرعة) في عملية الصقل والتي كانت (169) ميكا باسكال. من نتائج اختبار الصلادة نلاحظ ان زيادة قيم التغذية والسرعة يؤدي الى زيادة الصلادة لسطح المعدن. نتائج اختبار الخشونة السطحية، في هذا البحث، توضح ان عملية الصقل تقلل الخشونة السطحية بأنتاج انهاء سطحي دقيق وجيد على سطح المعدن حيث أفضل نعومة للمعدن يمكن الحصول عليها من (1 مليميتر قيمة التغذية , 1200 دورة/ دقيقة قيمة السرعة) من عملية الصقل والتي هي (0.110) مايكرومتر.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (4)

Arabic and English (3)


Year
From To Submit

2019 (1)

2018 (1)

2011 (2)

2010 (1)

2009 (2)