Preparation and Properties of the Chitosan/PVA Blend for Heavy Metals Chelation

Author: Zuhair Jabbar Abdul Ameer
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 3 Pages: 531-538
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Current research based on the use of extracted chitosan mixed with Polyvinyl alcohol to manufacture blend that can been used in water purification from heavy metals such as copper, this due to chitosan properties and its ability to chelation these metals because of the presence of the functional groups in their structure. The blend has been treated with borax to increase the viscosity, and then high density polyethylene granulated coated with polymer solution to increase the surface area for chelation. The ultraviolet test showed the efficiency of blend to chelation of copper ions through lower the copper ions absorbance peak after each stage where the solution of copper ions pass on the polymer blend containing chitosan.

يستند البحث الحالي على مزج مستخلص الجتوسان مع البولي فينيل الكحول لتصنيع مزيج بوليمري يمكن استخدامه في عمليات تنقية المياه من المعادن الثقيلة مثل النحاس, وذلك لخواص الجتوسان وقابليته على اقتناص هذه المعادن بسبب وجود مجاميع فاعلة في تركيبه. المزيج البوليمري عولج بواسطة البوراكس لزيادة لزوجته, ولزيادة مساحة الاقتناص السطحية تم طلاء حبيبات من البولي اثلين العالي الكثافة بمحلول المزيج البوليمري. اختبار الاشعة الفوق البنفسجية اثبت كفاءة الجتوسان على اقتناص ايونات النحاس من خلال انخفاض بيك الامتصاصية لايونات النحاس بعد كل مرحلة يمرر فيها محلول ايونات النحاس على المزيج البوليمري المحتوي على الجتوسان.


Article
Study The Properties and Weight Loss Degradation of The Blend LDPE/Cellulose in Soil Environment

Authors: Zuhair Jabbar Abdul Ameer --- Ehood Hamizah Saber
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 2 Pages: 557-567
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Wider applications of polyethylene (PE) in packaging and agriculture have raised serious issue of waste disposal and pollution. Therefore, it is necessary to raise its biodegradability by additives.In this study, we will add cellulose to low density polyethylene to prepare polymer blend have ability to degradation in soil environment.The samples were prepared by using twin screw extruder.LDPE and CELL have been mixing with different weight proportions, and studied their properties in order to determine its compliance with the required specifications to be able to be used biodegradable polymers. To improve the viability of decomposition PEG has been added to the resulting blend. Several tests were applied to identify those properties such as tensile,hardness, density and creep test. FTIR, digital microscope and SEM test acheved in order to determine the miscibility and blend morphology befor and after degradation.The results show that,the blend weight loss increase with increasing CELL percent.

تطبيقات واسعة للبولي اثيلين جعلت قضية التخلص من النفايات والملوثات ترتفع. وبالتالي، فمن الضروري زيادة التحلل البيولوجي للبولي اثيلين من خلال الإضافات و في هذه الدراسة سوف نضيف السليلوز إلى البولي إثيلين المنخفض الكثافة لتحضير خليط بوليمر يمتلك القابلية على التحلل في التربة.العينات تحضر بواسطة باثق ثنائي اللولب حيث يتم خلط نسب مختلفة من البولي اثيلين والسليلوز وتدرس خواصهم لتحديد مدى تطابقها مع المواصفات المطلوبة لتكون قادرة على ان تسنخدم كبوليمرات قابلة للتحلل.لتحسين قابلية التحلل يتم اضافة بولي اثيلين كلايكول الى الخليط الناتج. عدة اختبارات تطبق لتحديد هذه الخصائص مثل اختبار الشد والصلادة والزحف.التحليل بالاشعة تحت الحمراء والمجهر الرقمي و الفحص المجهري الالكتروني تطبق لتحديد الامتزاجية والهيئة للخليط قبل وبعد التحلل. وتظهر النتائج أن فقدان الوزن للخليط تزداد مع زيادة نسبة السليلوز.


Article
Effect of Polyvinyl alcohol on Burning Rate for Flexible PVC with Addition of Magnesium hydroxide and Aluminum tri-hydroxide

Authors: Zuhair Jabbar Abdul Ameer --- Diyar Hussein Habbeb
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 2 Pages: 593-603
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this research study the effect each of Polyvinyl alcohol, magnesium hydroxide, Aluminum trihydroxide on Polyvinyl chloride combustion speed used in the manufacture of electrical cables. Several composite samples were manufactured using the twin screw extruder. Combustion speed measured by the specification (ASTM D 635-03) as been studying composite samples surfaces using scanning electron microscope technology. The results that the parent used three additives reduce the combustion speed and turning the surface of fine to coarse

في هذا البحث تم دراسة تأثير كل من البولي فينيل الكحول، هيدروكسيد المغنسيوم و ثلاثي هيدروكسيد الألمنيوم على سرعة احتراق البولي فنيل كلورايد المستخدم في تصنيع الكبيلات الكهربائية. عدة عينات تم تصنيعها باستخدام الباثق الحلزوني المزدوج وقيست سرعة الاحتراق حسب المواصفة العالمية (ASTM D 635-03)، كما تم دراسة سطوح العينات باستخدام تقنية مجهر المسح الإلكتروني .أضهرت النتائج أن المضافات الثلاث المستخدمة تقلل من سرعة الاحتراق وتحول السطح من ناعم الى خشن .


Article
Miscibility improvement of LDPE/PVA blends by using silane-coupling agent

Authors: Zuhair Jabbar Abdul Ameer --- Nabeel Hasan Hameed
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 3 Pages: 98-109
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Mixing two polymers usually results in an immiscible system, characterized by a coarse, easy to alter morphology, and poor adhesion between the phases. These blends have large size domains of dispersed phase and poor adhesion between them. Therefore, miscibility of polymer blend must be improved by using suitable additives such as compatibilizer. In this study 5% of silane 3-(trimethoxysilyl)propyl methacrylate is used as compatibilizer to improve the miscibility and compatibility of LDPE/PVA blends. The samples were prepared by using a twin screw extruder. LDPE and PVA have been mixed with different weight proportion. Several tests were carried out to identify the compatibility and miscibility of the blends such as tensile properties, hardness, density, Fourier transforms infrared FTIR, digital microscope, scanning electron microscopy SEM and differential scanning calorimetry DSC. Result show that tensile strength, young modulus, elongation at break, density and hardness is increased with silane addition to the blends. SEM and digital microscope shows an improvement in the miscibility due to the better interaction between the two polymers as silane is added.

خلط اثنين من البوليمرات عادة ما ينتج خليط بوليمري غير ممتزج، يتميز بالخشونة، سهولة تغير الشكل وضعف الترابط بين الطورين. إضافة الى كبر حجم الطور المشتت كبير وضعيف الارتباط بالطور الاخر. لذا فان الامتزاجية للبوليمرات يجب ان يتم تحسينها باستخدام مضافات مناسبة مثل محسن التوافقية. في هذه الدراسة تم استخدام السيلان كمحسن للتوافقية والامتزاجية بين البولي اثيلين واطئ الكثافة و بولي فنيل الكحول. تم تحضير العينات باستخدام الباثق ثنائي اللولب حيث تم خلط نسب مختلفة من البولي اثيلين و بولي فنيل الكحول وبإضافة %5 من مادة السيلان. عدة اختبارات أجريت لتحديد تأثير محسن التوافق على خصائص هذه الخلائط وامتزاجيتها مثل اختبار الشد والصلادة والكثافة والاشعة تحت الحمراء والتحليل الحراري التفاضلي و الفحص بالمجهر الالكتروني الماسح والمجهر الرقمي و أظهرت النتائج زيادة متانة الشد ومعامل يونك، الاستطالة عند القطع والصلادة والكثافة بإضافة السيلان اما نتائج المجهر الالكتروني الماسح والمجهر الرقمي فقد أظهرت حدوث تحسن في امتزاجية البوليمرين.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2018 (1)

2017 (2)

2016 (1)