Article
Synthesis Of Nano Ni-Mo/γ-Al2O3 Catalyst

Loading...
Loading...
Abstract

Nano γ-Al2O3 support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) oC. Then nano NiMo/γ-Al2O3 catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al2O3 support at calcination temperature 550 oC. Make the characterizations for prepared nano γ-Al2O3 support at different temperatures and for nano NiMo/γ-Al2O3 catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.The Ni and Mo percentages in the prepared nano NiMo/γ-Al2O3 catalyst determined by X-ray fluorescence were 2.924 wt % and 12.9 wt %, respectively. SEM of prepared nano γ-Al2O3 support at calcination temperature 550 oC. The average particles diameter of prepared γ-Al2O3 support determined by AFM at calcination temperatures 550, 600, and 750 oC and for prepared nano NiMo/γ-Al2O3 catalyst at calcination temperature 550 oC.


Article
EXPERIMENTAL INVESTIGATION OFTHERMAL CONDUCTIVITY ANDPRESSUREDROPFOR WATER– NANOFLUID MIXTURE
اختبار عملي للموصلية الحرارية وهبوط الضغط لخليط ماء وحبيبات متناهي الصغر

Author: Layth W. Ismael & Khalid F. Sultan
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2013 Volume: 13 Issue: 3 Pages: 570-585
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

يتضمن البحث الحالي اختبار عملي للموصلية الحرارية وهبوط الضغط لنوع جديد من المواد الهندسية التي تحتوي على حبيباتمتناهية الصغر مخلوطة مع المائع الأساسي تسمى الموائع متناهية الصغر. الدراسة تضمنت سوائل متناهية الصغر مكونة من أوكسيد النحاس CuOوأوكسيد الألمنيوم (الالومينا)γ-Al2O3 على شكل حبيبات متناهية الصغرمختلطة مع الماءالنقي كمائع أساسيبكسورحجمية وتراكيز مختلفة. النتائج العملية بينت تحسن ملحوظ في الموصلية الحرارية بسبب الحبيباتمتناهية الصغر المضافة الى المائع. كذلك بينت تأثير الحجم الحبيبي والتركيز على الموصلية الحرارية. تلك النتائج بينت تحسن ملحوظفي الموصلية الحرارية وخصوصاً للمائع متناهي الصغر الذي يحتوي على أوكسيد النحاس CuO مع الماء النقي حيث يصل الى (1.07%)، بينما يصل الى (1.05%) للمائع متناهي الصغر الذي يحتوي على أوكسيد الألمنيوم (الالومينا) γ-Al2O3مع الماء النقيبتركيز (6 % vol.) وبدرجة حرارة الغرفة. النتائج العملية لهبوط الضغط بينت ان الموائع متناهية الصغرفي حالة الجريان الطباقي لن تتسبب في عواقب إضافية في طاقة الضخ. وجد توافق جيد بين النتائج العملية المستحصلة من هذه الدراسة ونتائج أخرى من بحوث منشورة.

This research investigates experimentally the thermal conductivity and the pressure drop of a new kind of engineering materials consisting of nanometer sized particles dispersed in base fluid named nanofluid. The study investigatesnanofluids containing CuO and γ-Al2O3 oxide nanoparticles in distilled water as base fluid in different particle sizes and concentrations. The experimental results emphasize the enhancement of the thermal conductivity due to the nanoparticles presence in the fluid.Also the effect of the particle size and concentration on the thermal conductivity. These results show noticeable enhancement in the thermal conductivity especially for the CuO/distilled water nanofluid which reaches to (1.07%), while reaches to (1.05%) for theγ-Al2O3/distilled water nanofluidat the concentration of (6 % vol.) and at the room temperature.The experimental results of pressure drop show that the nanofluids in the laminar flow will not cause extra penalty in the pumping power. A good agreement was found between the experimental obtained data for this research and other results from published papers.


Article
Hydrodesulfurization and Hydrodearomatization of Kerosene over high metal loading Ni w/γ-Al2O3 Catalyst
ازالة الكبريت والمركبات العطرية بالهيدروجين من الكيروسين باستخدام عامل مساعد NiW/γ-Al2O3 ذو نسبة تحميل عالية

Loading...
Loading...
Abstract

The present research investigates hydrodesulfurization (HDS) and hydrodearomatization (HAD) of raw kerosene with 0.364 wt. % sulfur and 16.498 wt. % aromatics supplied from Al-Dura Refinery. Hydrotreating reactions were carried out in one stage reactor over high metal Ni W/γ-Al2O3 prepared catalyst at different temperatures 275-350oC, pressures 32-62 bar, LHSV 1-4 hr-1, and H2/HC ratios 200-500. The prepared catalyst was pre-sulfided remarkably at low temperature and high pressure to avoid risky of sintering associated with gaining the active sulfide phase at high temperatures. Results showed an obvious differences between HDS and HAD rates due to difficulty of polyaromatics saturation compared with desulfurization. Sulfur and aromatics removal were achieved from 74.9% to 95.6% and from 1% to 12.8% respectively at different operating conditions. Advanced saturation conditions were promoted the hydrogenation reaction bath and played a significant role for achieving acceptable levels of HDS and HDA. In general, HDS and HDA increased with decreasing LHSV and increasing temperature, pressure, and H2/HC ratio. Burning quality, fire hazard, and aromatics content of kerosene were characterized by measuring of smoke point, flash point, and aniline point respectively. These properties were enhanced at different hydrotreating conditions due to the skeletal conformation change of kerosene hydrocarbons during reactions.


Article
Preparation of bimetallic catalyst ( Ni –Co )for deep oxidative desulfurization
تـحـضيـر عـامـل مساعـد ثنائـي الـمـعـدن ( Ni –Co ) لاستخـدامـه فــي ازالـــة الـكـبـريــت بطريقة الأكسدة

Authors: Jalil R . Ugal --- Asmaa H. Hussein
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2014 Issue: المؤتمر العلمي الثاني لكلية العلوم Pages: 9-15
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

A bimetallic catalyst Ni-Co / γ-Al2O3was prepared by impregnationmethod . Characterizedby atomic absorption (AA) techniqueandXRDdiffraction. Thesurfacearea andpore volume was measuredaccordingthe BETmethod.Thiscatalyst was used in theoxidative desulfurization of gasoil in the presence of hydrogenperoxide H2O2 30% as an oxidizing agent. The results indicated that thecatalystwasefficient to remove sulfur from gas oil depending on temperature, hydrogen peroxide H2O2 30 % , solvent used for extraction. The maximum observed sulfur removal reached 70.44%.

تم خلال البحث تحضير عامل مساعد ثنائي المعدن من نوعNi-Co/γ-Al2O3بطريقة التشبيع وشخص بواسطة تقنيات الامتصاص الذري( AA ),وحيود الاشعة السينية وقياس المساحة السطحية والحجم الحبيبي .استخدم هـذا العامل المساعـد فـي عمليات الاكسدة لإزالة الكبريت من زيت الغاز بوجود بيروكسيد الهيدروجين كعامل مؤكسد.دلت النتائج على أن العامل المساعـد كان كفوءﴽ في ازالة الكبريت وتعتمد كفاءته على درجة الحرارة, وكمية بيروكسيد الهيدروجين وكمية المذيب المستخدم لأغراض الاستخلاص وانافضل ازالة للكبريت بلغت70.44%.


Article
Removal of Phenols from Refinery Wastewater using Trickle Bed Reactor
ازالة الفينول من مياة الصرف للمصافي النفطية باستخدام مفاعل الطبقة الوشلة

Authors: Muhammad Fadel Abd --- Farah Talib Jasim --- Luma Shihab Ahmed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 18 Part (A) Engineering Pages: 147-160
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The present work aims to study the performance of a trickle bed reactor for phenol degradation in refinery wastewater by investigating the applicability of a commercial 0.5% platinum/alumina catalyst, which is used currently for desulfurization process in the North Refinery Company-Iraq. Synthetic wastewater experimentally was prepared to simulate the specification of samples taken from North Company Refinary. Results showed that initial phenol concentration had adverse effect on phenol removal. The results exhibited that the highest phenol conversion of (98.47%) was obtained over 0.5% Pt/γ-Al2O3 at the studied conditions (i.e., operating pressur 0.8 Mpa, operating temperature 1200C, LHSV 2.5 h-1, and air superficial velocity 0.25 m/s), with initial phenol concentration of 200 mg/L. The present method characterized by low residence time, the end-products are environmantally harmless no sludge production which requires further treatment

تضمن البحث دراسة كفاءة اداء عمود الطبقة الوشلة لازالة الفينول من مياه الصرف للمصافي النفطية بأستخدام %Pt/Al2O30.5 كعامل مساعد والمستخدم حاليا في وحدة ازالة الكبريت " desulfurization process " في مصافي الشمال. النتائج أظهرت ان اعلى نسبه تحول للفينول ((98.47 تم الحصول عليه تحت الظروف التاليه (LHSV 2.5 سا-1, درجة حرارة=120 م°, الضغط التشغيلي =0.8 ميكاباسكال والتركيز الأبتدائي للفينول=200 مغم/لتر وسرعة الغاز 0.25 m/s). وان النواتج النهائية في هذه الطريقة المستخدمة في البحث لا تحتاج الى معالجات اضافية اخرى.


Article
Experimental Study of Pressure Drop and Wall Shear Stress Characteristics of γ /Al2O3-Water Nanofluid in a Circular pipe under Turbulent flow induced vibration.

Authors: Adil Abbas AL-Moosawy --- Hatem H. Obeid --- Hameed K. Hamzah
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 3 Pages: 643-657
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Experimental study of γ /Al2O3 with mean diameter of less than 50 nm was dispersed in the distilled water that flows through a pipe consist of five sections as work station ,four sections made of carbon steel metal and one sections made of Pyrex glass pipe, with five nanoparticles volume concentrations of 0%,0.1%,0.2%,0.3%,and 0.4% with seven different volume flow rates 100, 200 , 300, 400, 500, 600 ,and 700ℓ/min were investigated to calculated pressure distribution for the cases without rubber ,with 3mm rubber and with 6mm rubber used to support the pipe. Reynolds number was between 20000 and 130000. Frequency value through pipe was measured for all stations of pipe for all cases. The results show that the pressure drop and wall shear stress of the nanofluid increase by increasing the nanoparticles volume concentrations or Reynolds number, the values of frequency through the pipe increase continuously when wall shear stress increases and the ratio of increment increases as nanofluid concentrations increase. Increasing of vibration frequency lead to increasing the friction factor between the pipe and the wall and thus increasing in pressure drop. Several equations between the wall shear stress and frequency for all volume concentration and for three cases without rubber, with rubber has 3mm thickness ,and with rubber has 6mm thickness. Finally, the results led to that γ /Al2O3 could function as a good and alternative conventional working fluid in heat transfer applications. A good agreement is seen between the experimental and those available in the literature.

في هذا العمل أجريت دراسة عملية لمائع نانوي متكون من جزيئات اوكسيد الألمنيوم نوع كاما ذات معدل قطر اقل من (50 nm) ثم تعليقها في ماء مقطر بخمسة تراكيز حجميه مختلفة يتدفق المائع النانوي عبر أنبوب مصنوع من الصلب الكربوني بسبعة معدلات جريان حجميه مختلفة في منطقة الجريان الاضطرابي. تم حساب توزيع الضغط عبر الأنبوب في ستة مقاطع عمليا وكذلك التردد الاهتزازي للأنبوب ولثلاث حالات بوجود مادة مطاطية لإسناد الأنبوب سمك 6 ملم وسمك 3 ملم وحالة أخرى بدون استخدام مادة مطاطية . المادة المطاطية استخدمت لتقليل الاهتزاز الناتج من جريان المائع النانوي .أوجدت النتائج بان قيم انخفاض الضغط وإجهاد القص تزداد بزيادة التركيز ومعدلات الجريان اي بزيادة رقم رينولد.كذالك زيادة إجهاد الاهتزاز يودي إلى زيادة إجهاد القص وبالتالي زيادة انخفاض الضغط .تم إيجاد مجموعة معادلات تجريبية بين تردد الأنبوب وإجهاد القص الناتج من الجريان ولكافة الحالات التي تم دراستها.وكذالك تم الحصول على توافق بالنتائج مع البحوث السابقة لقيم الضغط والاهتزاز.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (6)


Year
From To Submit

2018 (1)

2016 (2)

2014 (1)

2013 (2)