Article
Comparing the Flexural Strength Values for Polymeric Material and other Fibrous Composite in 3 and 4 Point Bending Methods
مقارنة قيم متانة الانحناء لمادة بوليمرية واخرى متراكبة ليفية بطريقتي الانحناء ثلاثي ورباعي النقطة

Author: Awham M. Hameed اوهام محمد حميد
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2017 Issue: 1 Pages: 163-178
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This research aims to determine the flexural strength (F.S) values for epoxy material before the reinforcement and after it by carrying out 3and 4 bending tests then comparing the results that obtained from the two mentioned test methods. For this purpose, the casts of materials under study were prepared by using molds prepared previously for this objective. Epoxy resin reinforced with chopped glass fibers with volume fraction is (20%). After the solidification process, the samples were cut with length (10cm), width (1cm) and thickness (0.5cm), and then some tests were performed at room temperature. It was found from the results of tests that epoxy reinforced with glass fibers has higher (F.S) with less strain than that for un reinforced epoxy. It can be also noticed in 4-point bending test, the force needed for the sample failure of pure epoxy is higher than that required for failing the same sample subjected to 3- point bending test. Optical microscope was used for imaging the fracture surfaces and failure regions of samples.

يهدف بحثنا هذا الى تحديد قيم متانة الانحناء لمادة الايبوكسي قبل وبعد تسليحها بالالياف وذلك باجراء اختباري الانحناء ثلاثي النقطة (3-point bending test) واختبار الانحناء رباعي النقطة (4-point bending test) ومن ثم مقارنة النتائج المستحصلة من طريقتي الاختبارالمذكورة.ولهذا الغرض تم تحضير مصبوبات المواد قيد الدراسة باستخدام قوالب اعدت لهذا الغرض مسبقا علما بان الكسر الحجمي للالياف قدره (%20) وتم تسليح الايبوكسي بالياف الزجاج المقطعة (chopped glass fibers) وبعد عملية التصلب تم تقطيع العينات بطول (10cm) ، عرض cm) 10 (وسمك (0.5cm) وقد تم اجراء الاختبارات عند درجة حرارة الغرفة ، ولوحظ من نتائج الفحوصات ان الايبوكسي المسلح بالياف الزجاج يمتلك متانة انحناء اعلى من تلك للايبوكسي غير المسلح وكذلك اقل انفعال وقد لوحظ في اختبار الانحناء رباعي النقطة ان القوة اللازمة لفشل العينة من الايبوكسي النقي تكون اعلى من تلك اللازمة لفشل نفس العينة المعرضة لاختبار الانحناء ثلاثي النقطة ، تم تصوير سطوح الكسر ومنطقة الفشل الحاصل للعينات باستخدام المجهر الضوئي .


Article
Study of the Fracture Strength of Alumina (Al2O3) Ceramic Using 3-Point Bend and Uniaxial Compressive Test
دراسة مقاومة الكسر لسيراميك الالومينا (Al2O3) باستخدام اختباري الانحناء الثلاثي والانحناء العمودي

Author: Muzher T. Mohamed مزهر طه محمد
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2017 Volume: 13 Issue: 4 - part 2 Pages: 38-45
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The present work is studied the fracture strength of alfa- alumina using 3-point bend test and uniaxial compressive test. This work showed the fracture strength results of 3-point bend test better than uniaxial compressive test. Using low compressive stress at sintering of alumina leading to obtain low mechanical properties in spite of high sintering temperature.

يتناول هذا البحث دراسة مقاومة الكسر لسيراميك الالومينا من نوع الفا (α) باستخدام اختباري الانحناء الثلاثي والعمودي. من خلال الدراسة الحالية تم التوصل الى ان اختبار الانحناء الثلاثي اعطى افضل نتائج لمقاومة الكسر مقارنة مع اختبار الانحناء المحوري, وان استخدام ضغط قليل عند كبس الالومينا قد ادى الى الحصول على خصائص ميكانيكية واطئة بالرغم من درجة حرارة التلبيد العالية (Cͦ1500) .


Article
The Effects of Chemical Treatment of Wood Cinder on the Mechanical Properties of the Composite Materials(Polyester-Wood Excelsior)
تأثير المعالجة الكيمياوية لنفايات الخشب على الخواص الميكانيكية للمادة المركبة (بولي استر-نشارة خشب)

Loading...
Loading...
Abstract

The Mechanical properties of reinforced composite materials depend on bonding strength between reinforcements and matrix , improving the bonding strength can be achieved by surface treatment or sizing . In this investigation chemical treatment for wood excelsior carried out by using (H2O , NaCl , NaOH) solution to increase the surface roughness for excelsior surface . Group of tests was carried out to study the effect of this treatment on the mechanical (bending and compression) properties of a material composed of unsaturated polyester reinforced by (10 % wt) of treated wood excelsior . Also Calculation of the weight loss and executing of microscopic photo . The results show :- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (228 %) compared with samples reinforced with untreated excelsior . This maximum percentage was found when the excelsior are treated at room tempreature for (H2O) and (2 day) .- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (40 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaCl+90%H2O) and (8 day) .- Increase of the bending strength of treated wood excelsior reinforced composite materials with a maximum percentage of (177 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaOH+90%H2O) and (4 day) .- Increase of the compression strength of treated wood excelsior reinforced composite materials with a maximum percentage of (18 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (H2O) and (4 day) .- Increase of the compression strength of treated wood excelsior reinforced composite materials with a maximum percentage of (10 %) compared with samples reinforced with untreated excelsior , this maximum percentage was found when the excelsior are treated at room tempreature for (10 % NaCl+90%H2O) and (8 day) .- decrease of the compression strength of treated wood excelsior reinforced composite materials with a minimum percentage of (25 %) compared with samples reinforced with untreated excelsior , this minimum percentage was found when the excelsior are treated at room tempreature for (10 % NaOH+90%H2O) and (8 day) .- Increase of the weight loss to treated wood excelsior with (NaOH) more than weigth loss of.treated wood excelsior with (NaCl , H2O) .

تعتمد الخواص الميكانيكية للمواد المركبة المقواة على مقاومة الربط بين التقويات والارضية يتم تحسين مقاومة الربط بالمعاملة السطحية (Surface treatment) اوبالاكساء (Sizing) . حيث تم في البحث الحالي معالجة كيمياوية لنشارة الخشب باستخدام محاليل (H2O , NaOH , NaCl) لزيادة الخشونة السطحية لسطح النشارة وبالتالي زيادة التلاصق بين النشارة والارضية . اجريت مجموعة من الاختبارات لدراسة تأثير المعالجة الكيمياوية على الخواص الميكانيكية (انحناء وانضغاط) للمادة المركبة ذات اساس من البولي استر غير المشبع المقواة ب(10 %wt.) نشارة خشب معالجة . كذلك تم حساب الفقدان بالوزن واجراء تصوير مجهري . اظهرت نتائج الاختبارات ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (228 %) عند المعالجة ب(H2O) مقطر ولمدة (2 day) , ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (40 %) عند المعالجة ب (10% NaCl+90%H2O) ولمدة (8 day) , ارتفاع مقاومة الانحناء لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (177 %) عند المعالجة ب(10% NaOH+90%H2O) ولمدة (4 day). كما اظهرت نتائج الاختبارات ارتفاع مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (18 %) عند المعالجة ب(H2O) مقطر ولمدة (4 day) , ارتفاع مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (10 %) عند المعالجة ب(10% NaCl+90%H2O) ولمدة (8 day) , في حين انخفضت مقاومة الانضغاط لعينات المواد المركبة المقواة بنشارة خشب معالجة بنسبة اقصاها (25 %) عند المعالجة ب(10% NaOH+90%H2O) ولمدة (8 day) . كذلك اظهرت النتائج ارتفاع نسبة الفقدان بالوزن لنشارة الخشب المعالجة ب(NaOH) اكثر من النشارة المعالجة ب(H2O , NaCl) .


Article
The Effect of nano particles of TiO2-Al2O3 on the Mechanical properties of epoxy Hybrid nanocomposites
تأثير جسيمات ثنائي اوكسيد التيتانيوم النانوي والالومينا النانوية على الخصائص الميكانيكية للمتراكب النانوي الهجيني

Authors: Khalid R. Al-Rawi خالد رشاد الراوي --- Sarah Kh. Taha سارة خضير طه
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2015 Volume: 12 Issue: 3 Pages: 597-602
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Preparation of epoxy/ TiO2 and epoxy/ Al2O3 nanocomposites is studed and investigated in this paper. The nano composites are processed by different nano fillers concentrations (0, 0.01, 0.02 ,0.03, 0.04 ,0.05 ,0.07 and 0.1 wt%). The particles sized of TiO2,Al2O3 are about 20–50 nm.Epoxy resin and nano composites containing different shape nano fillers of (TiO2:Al2O3 composites),are shear mixing with ratio 1 to 1,with different nano hybrid fillers concentrations( 0.025 ,0.0 5 ,0.15 ,0.2, and 0.25 wt%) to Preparation of epoxy/ TiO2- Al2O3 hybrid composites. The mechanical properties of nanocomposites such as bending ,wearing, and fatigue are investigated as mechanical properties.

لقد تم في هذا البحث تحضير ودراسة متراكب ايبوكسي- ثنائي اوكسيد التيتانيوم والايبوكسي – الومينا فقد حضر المتراكب النانوي بتراكيز وزنية مختلفة وهي %(0.01،0.02،0.03،0.04،0.05،0.07،0.1) وكان الحجم الحبيبي لدقائق ثنائي اوكسيد التيتانيوم والالومينا يتراوح بين20-50 نانومتر ،وقد تم خلط ومزج دقائق ثنائي اوكسيد التيتانيوم والالومينا معا مع الايبوكسي بنسبة 1:1 وبتراكيز وزنية مختلفة %(0.025،0.05،0.1،0.15،0.2،0.25) لتحضير المتراكب الهجين ايبوكسي / ثنائي اوكسيد التيتانيوم والالومينا وقد اجريت الاختبارات الميكانيكية للمتراكب النانوي مثل اختبار الانحناء والبلى والكلال للتحقق من الخصائص الميكانيكية


Article
The Effects of Wet Etching of Glass Fibers and Polyamide Fibers on The Bending and Impact Properties of The Resulting Composite Materials
تأثير التحفير الرطب لالياف الزجاج والياف البولي اميد على خواص الانحناء والصدم للمواد المركبة الناتجة

Author: ذوالفقار كريم الابراهيمي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: 9 Issue: 2 Pages: 265-278
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Improving the bonding strength can be achieved by surface treatment of fibers . Etching is one of the methods of this treatment , in this investigation wet etching of E-glass fibers and polyamide fibers carried out by using (H2O + NaOH) solution to get pits on their surface to increase the surface roughness . Group of tests was carried out to study the effect of this treatment on the mechanical (bending and impact) properties of a material composed of unsaturated polyester reinforced by (10 % wt) of etched glass fibers and Etched polyamide fibers . Also Calculation of the weight loss and executing of microscopic photo .The results show :- Increase of the bending strength of etched glass fibers reinforced composite materials with a maximum percentage of (301 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the bending strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (155 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1.5 % NaOH) and (3 hr) .- Increase of the impact strength of etched glass fibers reinforced composite materials with a maximum percentage of (270 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the impact strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (232 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (0.5 % NaOH) and (5 hr) .- Increase of the weight loss of polyamide fibers than weigth loss of glass fibers .

يتم تحسين مقاومة الربط بالمعاملة السطحية للالياف . التحفير (Etching) احد اساليب هذه المعاملة حيث تم في البحث الحالي التحفير الرطب لالياف زجاج نوع (E-glass) والياف بولي اميد باستخدام محلول (H2O+NaOH) للحصول على حفر تزيد من الخشونة السطحية . اجريت مجموعة من الاختبارات لدراسة تأثير التحفير على الخواص الميكانيكية (انحناء وصدم) للمادة المركبة ذات اساس من البولي استر غير المشبع المقواة ب(10 % wt) الياف زجاج محفرة والياف بولي اميد محفرة . كذلك تم حساب الفقدان بالوزن واجراء تصوير مجهري . اظهرت نتائج الاختبارات ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (301 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (155 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1.5 % NaOH) ولمدة (3 hr) . كما اظهرت نتائج الاختبارات ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (270 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (232 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (0.5 % NaOH) ولمدة (5 hr) . كذلك اظهرت النتائج ارتفاع نسبة الفقدان بالوزن لالياف البولي اميد اكثر من نسبة الفقدان بالوزن لالياف الزجاج .


Article
Comparative Study of Mechanical Properties of MWCNTS/Epoxyand SWCNTS/Epoxy Composites

Authors: Khansaa D. Salman --- Sameir A. Aziez --- Aqeel H. Alwan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 5 Pages: 28-42
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The single – walled carbon nanotubes (SWCNTs) and multi – walled carbon nanotubes (MWCNTs) embedded into resin matrix with different weight concentrations ranging about (0.1, 0.3, 0.5 and 1 wt. %), the nanocomposites are synthesized by casting method. The main applications of this nanocomposites are in the sensors, actuators, radar. Mechanical tests were done for this study such as: tensile test, bending test and hardness test. Also many examinations were utilized to define the microstructure like scanning electron microscopy (SEM), X-ray diffraction and Raman spectroscopy.The results of this work showed that obviously an improvement in mechanical properties of the processed nanocomposites such as young’s modulus, ultimate tensile strength, bending strength and Shore hardness. Also the micrographs of SEM demonstrated that SWCNTs and MWCNTs homogeneously dispersed into epoxy. On the other hand Raman spectra and XRD revealed that same results for SEM.Finally all the results for mechanical properties and microstructure evaluation show that SWCNTs give extremely higher values and properties than MWCNTs.

تم دمج انابيب كاربونية نانوية احادية الطبقة وانابيب كاربونية نانوية متعددة الطبقات مع الايبوكسي وبتراكيز وزنية مختلفة تتراوح بحدود (0.1, 0.3, 0.5, 1 wt. %) وقد تم تصنيع هذه المادة النانوية بطريقة السباكة. من اهم التطبيقات لهذه المادة النانوية المركبة هي في المتحسسات, المشغلات والرادارولهذه الدراسة اجريت العديد من الاختبارات الميكانيكية مثل: اختبار الشد ، اختبار الانحناء والصلادة. كذلك تم استخدام العديد من الفحوصات لتحسين البنية المجهرية مثل الفحص بالمجهر الالكتروني الماسح ، الفحص بحيود الاشعة السينية والفحص بمطياف رامان. وقد اظهرت نتائج هذا العمل ان هناك تحسن واضح في الخواص الميكانيكية للمادة النانوية المركبة مثل معامل يونك ، مقاومة الشد القصوى ، مقاومة الانحناء وصلادة شور.وقد اظهرت الصور المجهرية المؤخوذة بالمجهر الالكتروني الماسح ان الانابيب الكاربونية احادية الطبقة والمتعددة الطبقات قد تم تشتيتها بشكل متجانس في الاليبوكسي. من ناحية اخرى اظهرت نتائج الفحص بمطياف رامان وحيود الاشعة السينية نفس النتائج المجهر الالكتروني الماسح. اخيرا قد اظهرت جميع نتائجالخواص الميكانيكية والبنية المجهرية بأن الانابيب الكاربونية احادية الطبقة تعطي نتائج افضل من نظيرتها ذات الانابيب الكاربونية المتعددة الطبقات.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

Arabic (3)

English (2)

Arabic and English (1)