Study the Optical Properties of Transparent Epoxy Resin (Epoprimer) Plates
دراسة الخصائص البصرية لالواح راتنج الايبوكسي(Epoprimer) الشفاف

Author: Suma.H.AL-Shaikh Hussin سُمّا حكمت عبد الوهاب آل شيخ حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2010 Volume: 7 Issue: عدد خاص بمؤتمر العلمي النسوي 1 Pages: 20-30
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Epoxy plates have been made in the laboratory by mixing epoxy resin (A) with, hardener (B) in ratio (A: B) = (2:1), so they made (6) plates of different thickness about (0.95-5.8)mm . The optical properties have been studied like (absorption, transmittance, reflectance, energy gap and fluorescent) also the optical constant were found including (absorption coefficient, extinction coefficient and refraction index) for all plates. The results have shown that by increasing the thickness of plates the absorption intensity increase; at plates thickness (0.95-5.8)mm the absorption intensity were ، (0.20,0.69) respectively , and since absorption peak for epoxy occur in ultraviolet region and exactly at wavelength (330 nm) and energy gap (Eg=3.59(eV)) ; so the plates have transmittance about (60-92)% in visible region . The refraction index for Epoprimer epoxy is (n=1.3) and its reflectance is (R=20 %) at wavelength (330 nm) . While the fluorescence spectrums that result form shifting absorption spectrum (stoke shift) for epoxy plates it differ according to the used plate’s thickness. Where the shift increases toward longer wavelengths the (red shift) with the increase in plates thickness as the results show; so at plate thickness of (0.95, 3 ,5.8)mm the fluorescence spectrum shift was (100,131,140)nm respectively .

حضرت الواح راتنج الايبوكسي في المختبر بخلط راتنج الايبوكسي (A) مع المصلب B)) بنسبة خلط(2:1)(A:B) وبذلك تم صناعة(6) الواح مختلفة السمك تتراوح بين . (0.95-5.8)mm درست الخصائص البصرية كالامتصاصية والنفاذية و الانعكاسية وفجوة الطاقة والفلورة لحساب الثوابت البصرية معامل الامتصاص و معامل الخمود و معامل الانكسار و للألواح جميعها . لقد أظهرت النتائج العملية انه بزيادة سمك الالواح تزداد شدة الامتصاص فعند سمك (0.95-5.8)mmكانت شدة الامتصاص تساوي (0.20, 0.69)(a.u.) على التوالي , وان قمة الامتصاص لمادة الايبوكسي تقع عند المنطقة فوق البنفسجية و بالتحديد عند الطول الموجي (330 nm) وفجوة الطاقة (Eg=3.59 (eV) ) وتمتلك الالواح نفاذية تتراوح بين (60-92)% في منطقة الضوء المرئي ومعامل الانكسار للايبوكسي (n=1.3) والانعكاسية (R=20%) عند الطول الموجي يساوي (330)(nm). من دراسة طيف الفلورة الناتج عن ازاحة طيف الامتصاص (ازاحة استوك) لالواح الايبوكسي النقي فيختلف بحسب سمك الالواح المستخدمة اذ تزداد الازاحة نحو الاطوال الموجية الاطول (ازاحة حمراء ) بزيادة سمك الالواح كما أوضحت النتائج ذلك فعند الالواح بسمك (0.95, 3 ,5.8)mm كان مقدار ازاحة طيف الفلورة (ازاحة استوك) (100 ,131 ,140)nm على التوالي.


Article
Evaluation of the Effect of Addition of Poly Vinyl Pyrrolidone on, Dimensional Changes of Heat Cured Acrylic Resin Denture Base Material
تقييم تاثير اضافة البوليمر فنيل بايروليدون على دقة ابعاد قاعدة الطقم الراتنجي الاكريلي

Author: Shaymaa Majed Abd-Alhameed شيماء ماجد عبدالحميد
Journal: Al-Rafidain University College For Sciences مجلة كلية الرافدين الجامعة للعلوم ISSN: 16816870 Year: 2014 Issue: 33 Pages: 255-269
Publisher: Rafidain University College كلية الرافدين الجامعة

Loading...
Loading...
Abstract

The most common materials used for fabrication of denture bases are poly methyl methacrylate (PMMA). Preparation of modified heat cured denture base acrylic resin was carried out by preparing of (PMMA)(80%) and poly vinyl pyrrolidon (PVP)(20%) and the liquid part composed of methyl methacrylate (MMA) monomer. A(10) specimens for each experimental group were tested . All specimens were cured by using short curing cycle (90 min.at 74C° followed by 30 min .at 100C°).Evaluation was made by measuring dimensional stability and accuracy of the prepared denture base material in comparison with the control denture base material . The dimensional accuracy of acrylic resin denture base is the main necessity ,where it effects the retention and stability of the denture .A silicon mold was used to prepare a(40) stone mandibular master casts (control and experimental). Acrylic dough was prepared and packed for processing ,the flask were closed with pressure technique and placed in clamps after final closure .Distances were measured between (3) points marked on denture bases before and after thermocycling for both control and experimental groups. For AB and BC distances the PVP had improved the dimensional stability and accuracy before and after thermocycling while for AC distance the control group material before and after thermocycling improved the dimensional stability and accuracy.

تعتبر مادة بولمير مثيل ميثااكريليت اكثر المواد شيوعا في عمل اطقم الاسنان المبلمرة حراريا .في هذه الدراسة تم خلط بوليمر مثيل ميثااكرليت (80%) وبوليمير فنيل بايروليدون (20%) وتم خلطها مع سائل مثيل ميثااكرليت. تم تحضير (40) عينة بمعدل (10) عينات لكل اختبار من كل مادة. لكل العينات تم غمر القوارير في حوض ماء بدرجة حرارة الغرفة وتم التعهد بدورة معالجة قصيرة (سخنت حتى درجة 74 مئوية لمدة 90 دقيقة ثم تركت لتغلي لمدة 30 دقيقة). التقييم تم بدراسة بعض الخواص الفيزيائية لعينات المادة التجريبية مثل دقة ابعاد قاعدة طقم الراتنج الاكريلي ومقارنتها مع عينات المادة القياسية .دقة ابعاد قاعدة طقم الراتنج الاكريلي تشكل ضرورة اساسية ، حيث ان لها تاثير مباشر في عملية ثبات واستقرار الطقم .استعمل قالب سيليكوني لتحضير (20) قالب علوي رئيسي من الحجر الصلب . قسمت هذه القولب الى مجموعتين حسب نوع المادة المستخدمة لتحضير قاعدة الطقم (قياسية وتجريبية) حيث ان كل مجموعة تحتوي على (10) عينات , تم قياس المسافات بين ثلاث نقاط محددة على قاعدة الطقم (A في الامام وB&C في الخلف) باستعمال الورنية الرقمية قبل وبعد التدوير الحراري لكلا المادتين اظهرت النتائج ان البوليمر فنيل بايروليدون يعطي احسن نتائج لابعاد قاعدة الطقم قبل وبعد التدوير الحراري وان المادة القياسية تعطي احسن النتائج بعد التدوير الحراري.


Article
Thermal Initiation of Metiyl Methacrylate Polymerization by lron(111) Chelate Complexes l-tris (diethyl dithiocarbamato) iron (111) . 2- Tris (diphenyl dithiocarbamato) Iron (111) .
بدء البلمرة الحرارية الميثاكريليت Metiyl بواسطة lron (111) كلاب المجمعات L-تريس (اثيل dithiocarbamato) الحديد (111). 2 - تريس (ثنائي dithiocarbamato) الحديد (111).

Author: Amir .F. Dawood -Al Niaimi امير ف. داوود
Journal: Journal of Research Diyala humanity مجلة ديالى للبحوث الانسانية ISSN: 1998104x Year: 2010 Issue: 42 Pages: 314-335
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The bulk polymerizations of methylmethacrylate initiated by l--tris (diethyl dithiocarbamato)iron(l 11) .2- Tris (diphenyl dithiocarbamatollront(l 1 1) .has been studied at 80oC in the dark, without inhibition or retardation is observed, and the rate of polymerization is directly proportional to the square root of initiator concentration, the order with respect to the initiator concentration is (0.5),while the order with respect to monomer concentration was found to be close to (1.8) for initiators and this means that the rate of initiation is dependent on monomer concentration.The total activation energy (Et),initiation energy (Ei) and the values of the kinetic parameter ratio Kp / Kt12(where Kp & kt the rate constants of propagation and termination respectively) were determined .Gravimetric technique is used for determination of the rate polymerization and viscosity is used for determination of average degree of polymerization .The UV-Vis spectrophotometer is used to determine the rate of initiator decomposition and the end group in the polymer and IR spectrophotometer is used to identify the initiators structure there thermal decomposition products and the tactility of the polymer structure chain.According to the experimental results obtained a mechanism of thermal initiation reaction is proposed .

وpolymerizations الجزء الأكبر من methylmethacrylate التي بدأها L - تريس (اثيل dithiocarbamato) الحديد ل (11). 2 - تريس (ثنائي dithiocarbamatollront ل (1 1). وقد درس في 80oC في الظلام، وبدون لوحظ تثبيط أو التخلف، ومعدل البلمرة يتناسب طرديا مع الجذر التربيعي للتركيز المبادر، الأمر فيما يتعلق تركيز المبادر هو (0.5)، في حين أن النظام مع الاحترام إلى تركيز مونومر وجدت لتكون على مقربة من (1.8) للمبادرين وهذا يعني أن معدل استهلال يعتمد على تركيز مونومر. طاقة التنشيط مجموع (ET)، استهلال الطاقة (EI) وقيم نسبة المعلمة الحركية كيمبرلي / Kt1 2 (حيث كيمبرلي وكيلوطن الثوابت معدل الانتشار وإنهاء التوالي) كانوا مصممين. وتستخدم تقنية الجاذبية لتحديد معدل البلمرة ويستخدم اللزوجة لتحديد متوسط ​​درجة البلمرة. يستخدم مقياس الطيف للأشعة فوق البنفسجية فيس لتحديد معدل التحلل المبادر والمجموعة في نهاية البوليمر ومعمل الأشعة تحت الحمراء وتستخدم لتحديد هيكل المبادرين هناك الحرارية منتجات التحلل، وحاسة اللمس في سلسلة هيكل البوليمر. وفقا للنتائج التجريبية التي تم الحصول عليها ويقترح آلية لبدء رد فعل الحراري.


Article
RESIDUAL ELASTO-PLASTIC STRESSES ANALYSIS OF POLYMERIC THICK –WALLED PRESSURIZED CYLINDER
تحليل الاجهادات المرنة – اللدنة المتبقية للاسطوانه البوليميرية السميكة الجد ا رن والمعرضة لضغوظ داخلية

Loading...
Loading...
Abstract

AbstractA theoretical solution is presented for polymeric thick pressurized cylinder,where material behaviour is described by the modified Von Mises criterion. Thesolution is carried out using different values of Yc/Yt ratio to demonstrate their effectson the plastic zone radius and on the radial and hoop stresses also on the residualstress components.The results is indicated that the influence of α ratio or (Yc/Yt) ratio on theplastic zone radius and stress distributions is significant, and it can be shown that ,when α ratio increases the plastic zone radius decreases , the value of α ratio has noeffect on the value and distribution of radial stress, and when α ratio increases thelevel of the hoop stress increases in the plastic zone and decreases in the elastic zoneand the value of α ratio is directly proportional to the value of residual radial andhoop stresses in the cylinder. A published finite element results give a reasonableagreement with the obtained results.

الخلاصةفي هذا البحث تم د ا رسة وتقديم حل نظري للاسطوانات البوليميرية السميكة الجد ا رن. لقد استخدمYc/Yt لوصف سلوك المادة معيارية فون ميسز المطورة. الحل تم باستعمال قيم مختلفة للتوضيح تأثيرها على نصف قطر مجال اللدونة وعلى توزيع الاجهادات القطرية والحلقية وكذلكواضحة على مجال α او نسبة Yc/Yt مركبات الاجهادات المتبقية. تشير النتائج ان تأثير نسبةفان نصف قطر α نصف قطر اللدونة وعلى توزيع الاجهادات ، حيث تبين انه عند زيادة نسبةلا تأثير لها على قيم وتوزيع الاجهاد القطري، حيث انه عند α مجال اللدونة سوف يقل وان قيمةفان الاجهاد الحلقي سوف يزداد في مجال اللدونة ويقل ضمن مجال المرونة، حيث ان α زيادةتتناسب طرديا مع قيمة الاجهاد المتبقي والاجهاد الحلقي في الاسطوانة. تم مقارنة نتائج α قيمةالحل النظري مع نتائج طريقة العناصر المحددة، والتي اظهرت تقاربا مقبولا.


Article
Synthesis, characterization and biohydrolysis drug release studies of polymer carrier with Naproxen
تحضير وتشخيص ودراسة حياتية لانطلاق الدواء من بوليمر محمل بالنابروكسين

Author: Hala M. G. Alzahawi هالة محمد غريب الزهاوي
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك للدراسات العلمية ISSN: 19920849 26166801 Year: 2018 Volume: 13 Issue: 1 Pages: 79-94
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

In the present work, the hydroxyl groups of "HPMC, HPC and HEC" polymers bonds with bioactive material "naproxen drug" by esterification process. (direct esterification and indirect esterification). The modified s polymers are characterized by some spectroscopic methods such as FTIR, UV, H1. NMR and C13. NMR. The degree of substitution (D.S) of the hydroxyl groups in suger molecule in polymer was determined in all cases.The hydrolysis of modified polymers is carried out in the heterogeneous phase in a buffer solution of pH (2.0, 7.4 and 9.0) at various temperatures (25, 37, and 45 Co). The amounts of released naproxen drugs were quantitatively determined by using calibration curve method. Biodegradation (in vitro degradation) of modification polymers is carried out by enzymatic cleavage (using lipase enzyme) at pH 7.4 (the human blood pH) and 37Co. The amounts of released naproxen were quantitatively determined by U.V visible spectrophotometry by using the usual calibration curve method. In general, it was found that the release in presence of enzyme was faster than in hydrolysis process

البحث الحالي يتضمن ارتباط بين البوليمرات (HPMC ,HPC ,HEC) مع المادة الدوائية ( نابروكسين) بواسطة مجموعة الهيدروكسيل العائدة للبوليمرات, وتتضمن عملية الاسترة (استرة مباشرة واسترة غير مباشرة) وشخصت البوليمرات المحورة بواسطة بعض الطرق الطيفية وهي تقنيات الاشعة تحت الحمراء (IR), واطياف الاشعة الفوق البنفسجية والمرئية (UV) وتقنية الرنين النووي المغناطيسي للبروتون والكاربون ( H1NMR ,C13NMR). كذلك تم حساب درجة التعويض (D.S) في جميع الحالات وقد تبين ان اعلى درجة التعويض تنتج عندما تكون الاسترة بواسطة كلورو اسيتايل كلورايد.وتم دراسة التحلل المائي في الطور غير المتجانس لمشتقات البوليمرات المحورة باستخدام محاليل منظمة بقيم الاس الهيروجيني(pH:2.0,7.4 and 9.0) وبدرجات حرارة مختلفةهي (25, 37 and 45) Coوحسبت كمية نابروكسين المتحرر من عملية التحلل المائي لمشتقات البوليمرات المحورة كميا بواسطة مطيافية الاشعة الفوق البنفسجية باستخدام طريقة المنحي القياسي للمادة الدوائية نابروكسين.وتم كذلك دراسة التحلل الحياتي للبوليمرات المحورة بواسطة التكسر الانزيمي بواسطة انزيم اللايبيز في محلول درجة الحموضةpH=7.4 (حموضة دم الانسان) ودرجة حرارة 37 Co وقد حسبت كمية النابروكسين المنطلق باستخدام المنحني القياسي وبشكل عام نلاحظ ان انطلاق جزيئات الدواء كان اسرع بوجود الانزيم.


Article
Influence of the Polymer Styrene Butadiene Rubber on Some of Clay Brick Properties
تأثير البوليمر (Styrene Butadiene Rubber) على بعض خواص الطابوق

Authors: هدى كريم حسين --- حيدر عادل عبد الحميد --- قيس جواد فريح
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 1 Pages: 55-65
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studied the improvement of clay brick durability by using twomethods of treatment, the first one by coating with Styrene Butadiene Rubber(Polymer) solution and the other by submerging bricks in polymer solution forvarious periods.The results showed that using coating method causes a slight increase in thecompressive strength with a maximum percentage of 3.8% for both yellow andgreen brick in comparison with untreated bricks, while the compressive strengthfor the two types of the brick reduced when they treated using submergingmethod, the percentage of reduction increases by about 26% and 7% for yellowand green brick respectively at submerged period of 24 hours.The results also indicated that no efflorescence appears for all treated bricks(treated by coating and submerging methods for all periods) and a decrease inabsorption with maximum percentages of 26.8% and 14.5% for yellow and greenbricks respectively when the specimens submerged in polymer solution for 24hours. All the results were compared with tested samples untreated with polymersolution.


Article
Optical properties of polymer composite PS-PC
الخصائص البصرية للأغشية الرقيقة لمركب البوليمر PS-PC

Author: Dana A. Tahir دانا عبدالله طاهر
Journal: kirkuk university journal for scientific studies مجلة جامعة كركوك للدراسات العلمية ISSN: 19920849 26166801 Year: 2010 Volume: 5 Issue: 1 Pages: 93-103
Publisher: Kirkuk University جامعة كركوك

Loading...
Loading...
Abstract

The optical properties of polymer composite polycarbonate-polystyrene (PC-PS) films prepared by casting technique were studied in the visible and ultraviolent wavelength regions. It was found that the optical absorption is due to direct allowed transitions for pure and composite polymer films, while the energy gaps and the width of the tail localized states of the composite was lied in the mid values of the pure samples. The optical constants refractive index , extinction coefficient , the real and the imaginary parts of the dielectric constant have been also calculated. The dielectric constant and refractive index become more stable for composite sample.

تمت دراسة الخصائص البصرية لأغشية مركب البوليمر بوليكاربونايت-بوليستايرين (PC-PS)المحضرة بالطريقة الصب في مناطق الاطول الموجية المرئية و فوق البنفسجية. و قد وجد أن الامتصاص البصري ناتج عن الانتقالات المسموحة المباشرة لكل من ألاغشية البوليمرات النقية و المركبة، تبين ان فجوة الطاقة و اتساع المناطق الممتدة لبوليمرات المركبة يقع بين متوسط قيم النماذج النقية. تم أيضا حساب الثوابت البصرية الاتية: معامل الانكسار، معامل اكتلاشى ، الجزء الحقيقي و الجزء الخيالى لثابت العزل. بينت هذه الدراسة ان ثابت العزل و معامل الانكسار يصبحان اكثر استقرارا للبوليمرات المركبة.


Article
Effect of water on impact strength for unsaturated polyester composites reinforced with E-glass fibers
تأثير الماء على مقاومة الصدمة لمتراكبات البولي استر غير المشبع المدعم بالألياف الزجاجية

Author: Mohammed Ghazi Hammed محمد غازي حمد
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2012 Volume: 5 Issue: 2 Pages: 279-294
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The present research aimed to study the effect of distilled water on impact strength for unsaturated polyester composites reinforced with E-glass fibers with volume fraction 35%, all samples were prepared by using hand lay up technique. Unsaturated polyester resin was used as matrix for the reinforced materials that consist of artificial glass fibers (woven roving) with directional (0,90) and chopped glass fibers with the random direction. The samples were cutting with measurement (60 x 6) mm and the sample thickness dependent on the number of layers of glass fibers. The impact tests are carried out on samples under the influence of normal conditions (laboratory temperature). The results and examinations for these samples shows acceptable improvement in impact strengths of the matrix was observed after addition of glass fibers, to explain the effect of water on impact properties, the samples immersion in water for (50) days. The results show that as the exposure time increased the impact strength of samples increase.

إن البحث الحالي يهدف إلى دراسة تأثير الماء المقطر على متانة الصدمة لمتراكبات البولي استر غير المشبع والمسلح بالألياف الزجاجية وبكسر حجمي مقداره (35%)، كل العينات حضرت بتقنية التشكيل اليدوي. استخدم راتنج البولي استر الغير مشبع كمادة رابطة لمواد التسليح والمتضمنة ألياف الزجاج الصناعية ذات الاتجاهية (0,90) والمحاكة بشكل حصيرة والألياف الزجاجية المقطعة عشوائية الاتجاه. إن العينات قطعت بالقياسات (60 x 6) ملم وذات سمك يعتمد على عدد طبقات ألياف الزجاجية وحسب مواصفات الجهاز المستخدم في الفحص. أجريت اختبارات الصدمة على العينات في الظروف القياسية (درجة حرارة المختبر). من خلال ملاحظة النتائج والفحوصات للعينات نلاحظ إن هناك تحسن في مقاومة الصدمة بالنسبة للمادة الرابطة بعد إضافة ألياف الزجاج لها، ولغرض توضيح تأثير الماء على مقاومة الصدمة غمرت العينات في الماء المقطر لمدة (50) يوما. من خلال ملاحظة النتائج أيضا نجد انه كلما ازداد زمن تعرض العينات للماء فأن متانة الصدمة تزداد أيضا.


Article
Studying Flexural Behavior of Reinforced Concrete Beams Strengthened with Different Lengths of FRP Strips by Using NSM Technique
دراسة سلوك الانثناء للعتبات الخرسانية المسلحة والمقواة بأطوال مختلفة من شرائط ألياف البوليمر الكاربونية باستخدام تقنية التقوية بالرصع القريب من الوجه((NSM

Author: د. بيار جعفر السليفاني، أستاذ رؤى سهيل محمد زيدان، مدرس مساعد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 2 Pages: 1-11
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This research includes practical results of study the behavior of the reinforced concrete beams strengthening by carbon fiber strips using near surface mounting (NSM) technique. The study is carried out on (8) concrete beams, the variables which considered are (the length of CFRP strips, no. of CFRP layers), this established by dividing the practical program into two groups, the first one includes (3) beams strengthened with variable carbon fiber strips length and one strip, Second group of this study includes (3) beams which strengthened with variable carbon fiber strips length and two strips, as well as two control beams . The results indicated that the carbon fibers had a noticeable effect in increasing the bearing capacity of the near surface mounting (NSM) strengthened technique reinforced beams, , the results indicated that strengthening the beams with carbon fibers and not along the length of the beam and in one layer did not contribute to increasing the beams strength, but when the number of layers was increased for the same length of fibers an increase in beam strength was noticed at a rate range (34%-55%).

يحتوي هذا البحث نتائج عملية لدراسة سلوك الانثناء للعتبات الخرسانية المسلحة والمقواة بألياف الكاربون وذلك باستخدام تقنية الرصع القريب من الوجه (NSM). أجريت الدراسة على (8)عتبات خرسانية مسلحة والمتغيرات التي أخذت بنظر الاعتبار هي: (أطوال ألياف الكاربون, عدد طبقات ألياف الكاربون). إذ قسمت الدراسة إلى محورين, الأول يضم ثلاث عتبات قويت بأطوال مختلفة من شرائط ألياف الكاربون وبطبقة واحدة والمحور الثاني يضم ثلاث عتبات قويت بطبقتين وبأطوال مختلفة من ألياف الكاربون. بالإضافة إلى عتبتي السيطرة, فحصت العتبات بواسطة حمل متمركز في نقطتين.أظهرت النتائج تأثير ألياف الكاربون في زيادة تحمل العتبات ضد قوى الانثناء, وقد أظهرت النتائج بأن تقوية العتبات الخرسانية بشرائط ألياف الكاربون على جزء من الطول الكلي للعتبة وبطبقة واحدة لايساهم في زيادة قابلية التحمل للعتبات, أما عند زيادة عدد الطبقات لنفس اطول شرائط الألياف, لوحظ زيادة في تحمل العتبات وبنسب تتراوح بين(34%-55%).


Article
Uses of Acidic Polymer Support Crosslink " Dowex SO3H.NO2 " in Preparation of " Benzoic Acid Azo acetophenone " dye as Acidic Catalyst
استعمال البوليمر الساند الحامضي المتشابك Dowex SO3H.NO2 في تحضير صبغة (Benzoic Acid Azo Acetophenone) بوصفه عاملاً مساعداً حامضياً

Author: Ammad .M.Osaj عماد محمد عوسج
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2015 Volume: 11 Issue: 4 Pages: 45-53
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Uses of acidic polymer support crosslink " Dowex SO3H.NO2 " in preparation of derivative azo dye from " p- amino acetophenone " by prepare Diazonium salt for second amine then happen of coupling processer with salicylic acid to give salicylic acid azo acetophenone . polymer support is worked as acidic catalyst to give H+ and from sod.nitrate give nitrose acid and this last acid was converted sec.amine group to diazonium salt N2+ as strong electrophil to coupling reaction happiness and formation of azo group was carried of correct dye .

تم استخدام البوليمر الساند الحامضي المتشابك Dowex SO3H.NO2 في تحضير صبغة الازو المشتقه من ( بارا امينو اسيتوفينون ) عن طريق تحضير ملح الديازونيوم Diazonium salt للامين الثانوي المذكور ثم حصول عملية الازدواج مع ( حامض السلسلك ) ليعطي بالنتيجة صبغة ( حامض السلسلك ازو اسيتوفينون ) . يعمل البوليمر الساند كعامل مساعد حامضي أذ يطلق بروتون H+ في المحلول ومن نتريد الصوديوم NaNO2 يتكون حامض النتروز HONO و الذي بدوره يحول مجموعة الامين الثانوي الى ملح ديازونيوم N2+ كالكتروفيل قوي لحصول عملية الازدواج و تكوين الصبغة الحاملة لمجموعة الازو المقابل .

Listing 1 - 10 of 27 << page
of 3
>>
Sort by
Narrow your search

Resource type

article (27)


Language

English (17)

Arabic (8)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (5)

2017 (6)

2016 (1)

2015 (3)

More...