Studying the Physical Properties of System (Al-BuC) Composite
دراسة الخواص الفيزيائية لمادة متراكبة من نظام (الالمنيوم _كاربيد البورون ((B4C )

Authors: فاضل عطية جياد --- احمد حسين علي --- رونق صلاح الدين مهدي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 10 Pages: 485-494
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this research is studying some physical properties (bulk density,apparent density, apparent porosity percentage, water absorption percentage) formetal matrix composite material. Aluminum matrix consists boron carbide particlesas a reinforced phase. Different percents (0%, 2%, 5%, 10%, and 15%) of (B4C)have been used. powder technology process is used for preparing the specimens,the results shows that the bulk and apparent density decrease, apparent porositypercentage and water absorption percentage were increasing as percentage of (B4C)particles increase.

يهدف هذا البحث الى دراسة بعض الخواص الفيزيائية (الكثافة الظاهرية, الكثافةالحجمية, والنسبة المئوية للمسامية الظاهرية, والنسبة المئوية لمتصاص الماء) لمادة متراكبة ذاتوبنسب (B4C) اساس معدني من الالمنيوم ومدعمة بدقائق من مسحوق رابع كاربيد البورون0) ومصنعة بطريقة تكنولوجيا المساحيق حيث اظهرت %, 2%, 5%, 10%, وزنية (% 15النتائج نقصان كل من الكثافة الظاهرية والكثافة الحجمية وزيادة النسبة المئوية للمسامية الظاهرية.(B4C) وامتصاص الماء مع زيادة نسبة دقائق


Article
EFFECT OF PARTICLES FROM MAGNESIUM OXIDE IN THERMAL INSULATION OF CONBEXTRA EPOXY (EP-10) RESIN
تأثير دقائق من أُوكسيد المغنيسيوم في العزل الح ا رري ل ا رتنج الإيبوكسي كونبكست ا ر (EP-10)

Author: Haqi I.Gattea حقي إسماعيل كاطع
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 4 Pages: 784-791
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Abstract:Magnesium oxide with (5 μm) particle size with different Weight percentages (5%,15%,25%)was added to conbextra epoxy (EP-10) resin and measured the changing in thermal insulation tothis resin . Fourier equation was used to calculate the changing in coefficient of thermalconductivity (k) for conbextra epoxy (EP-10) before and after addition of magnesium oxide ,wherethe results show improved thermal insulation of the resin by reduced in thermal conductivitycoefficient value after oxide addition , and the value of thermal insulation will increased withincreasing of additive percentage of magnesium oxide ,where it change from(0.24 W/m.ºC) beforeadded oxide to (0.16 W/m.ºC) after addition (25%) from oxide at temperature (40 ºC) which thebest value from oxide additive .

الخلاصة:(%25،%15،% 5) وبنسب وزنية مختلفة ( 5 •m) تم إضافة دقائق من أُوكسيد المغنيسيوم وبحجم حبيبيوقياس التغير في العزل الح ا رري لهذا ال ا رتنج . تم إستخدام معادلة (EP- إلى ا رتنج الإيبوكسي كونبكست ا ر ( 10ل ا رتنج الإيبوكسي كونبكست ا ر قبل وبعد إضافة (k) فورير لحساب التغير في قيمة معامل التوصيل الح ا رريأُوكسيد المغنيسيوم إليه، حيث أظهرت النتائج تحسن العزل الح ا رري لل ا رتنج عن طريق إنخفاض قيمة معاملالتوصيل الح ا رري بعد إضافة هذا الأُوكسيد ، وتزداد قيمة العزل الح ا رري مع زيادة نسبة أُوكسيد المغنيسيوم0.16 ) بعد إضافة W/m.ºC) 0.24 ) قبل إضافة الأُوكسيد إلى W/m.ºC) المضافة ،إذ تغيرت من40 ) وهي أفضل قيمة للأُوكسيد المضاف. ºC) %25 ) من الأُوكسيد عند درجة ح ا ررة )


Article
تأثير التقوية بدقائق MgO على الصفات الحرارية والميكانيكية لراتنج الإيبوكسي

Author: Ali Ibrahem علي إب ا رهيم الموسوي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 3 Pages: 560-570
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractThis research aims to, first : to increased thermal insulation to conbextra epoxy(EP-10) by additive magnesium oxide (MgO) with (5 μm) particle size as a filler withdifferent Weight percentages (10%,20%,30%) to resin and study the effect of thisadditive on thermal insulation of the resin . Fourier equation was used to calculate thechanging in thermal conductivity coefficient (k) for conbextra epoxy (EP-10) beforeand after addition of magnesium oxide ,where the results show improved thermalinsulation of the resin by reduced in thermal conductivity coefficient value after oxideaddition , and the value of thermal insulation will increased with increasing of additivepercentage of magnesium oxide ,where it change from(0.24 W/m.ºC) before addedoxide to (0.13 W/m.ºC) after addition (30%) from oxide at temperature (40 ºC) whichthe best value from oxide additive . The second : to study the mechanical behavior ofthe resin after reinforced it by the above weight percentage of magnesium oxide andstudied its effect on mechanical properties of the resin which included : impact strength, tensile strength , and compression strength . It has shown an improvement in thesemechanical properties after reinforcement by magnesium oxide where the value ofmechanical properties will increase with increasing percentage of reinforcement.Impact strength increased from(30Kj/m2) to (39Kj/m2) , and tensile strengthfrom(60Mpa)to (74Mpa), and compression strength from(132Mpa)to (146 Mpa), forreinforcing percentages 0% and 30% from magnesium oxide respectively .

الخلاصة .(EP- يهدف البحث الحالي إلى، أولاً: زيادة العزل الح ا رري ل ا رتنج الإيبوكسي كونبكست ا ر ( 105) كحشوة وبنسب وزنية مختلفة μm) وبحجم حبيبي (MgO) بإضافة أُوكسيد المغنيسيوم%30 ) إليه ود ا رسة مدى تأثير هذه الإضافات على العزل الح ا رري لهذه المادة ،%20،%10)ل ا رتنج (k) ال ا رتنجية . تم إستخدام معادلة فورير لحساب التغير في قيمة معامل التوصيل الح ا رريالإيبوكسي كونبكست ا ر قبل وبعد إضافة أُوكسيد المغنيسيوم إليه، حيث أظهرت النتائج تحسنالعزل الح ا رري لل ا رتنج عن طريق إنخفاض قيمة معامل التوصيل الح ا رري بعد إضافة هذاالأُوكسيد ، وتزداد قيمة العزل الح ا رري مع زيادة نسبة أُوكسيد المغنيسيوم المضافة ،إذ تغيرت من0.13 ) بعد إضافة ( 30 %) من W/m.ºC) 0.24 ) قبل إضافة الأُوكسيد إلى W/m.ºC)40 ) وهي أفضل قيمة للأُوكسيد المضاف. وثانياً : د ا رسة السلوك ºC) الأُوكسيد عند درجة ح ا ررةالميكانيكي لل ا رتنج بعد تقويته بالنسب الوزنية أعلاه من أُوكسيد المغنيسيوم ود ا رسة مدى تأثرالخواص الميكانيكية لل ا رتنج بهذا التغيير وقد شملت هذه الخواص كل من : مقاومة الصدمة ،مقاومة الشد ، ومقاومة الإنضغاط . أظهرت النتائج تحسن هذه الخواص بعد التقوية بأُوكسيدالمغنيسيوم وتزداد هذه الخواص بزيادة قيمة هذه الخواص مع زيادة نسبة التقوية . فبالنسبة60 ) إلى Mpa) 39 ) ومقاومة الشد من Kj/m 30 ) إلى ( 2 Kj/m لمقاومة الصدمة إرتفعت من( 2146 ) ولنسب التقوية 0% و Mpa) 132 ) إلى Mpa) 74 ) ومقاومة الإنضغاط من Mpa)%30 من أُوكسيد المغنيسيوم على التوالي .


Article
Silicon Carbide Particle Reinforced Aluminum Matrix Composite Prepared by Stir-Casting.

Authors: Ali Hubi Haleem --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 2 Pages: 442-449
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The developed aluminum matrix composite (AMCs) is considered to be a promising material for low and high temperature applications. Particles reinforced AMCs materials have high specific strength and modulus of elasticity, together with excellent heat resistance. Silicon carbide particles reinforced aluminum matrix composite (AMCs) for hardness, impact strength, and material toughness improvement were prepared. Stir-casting processing was optimized. The hardness, impact strength, and material toughness were evaluated. Under stir-casting, the silicon carbide particles were uniformly distributed in the aluminum and well bonded with aluminum matrix. The hardness and material toughness were increased 1.84 and 2.16 times respectively at particles weight fraction (10% ) that of the of the unreinforced aluminum based on the high hardness and deformation resistance of the silicon carbide particles.

تعتبر المواد المركبة المتقدمة ذات الأساس المكون من معدن الألمنيوم (AMCs) من المواد المهمة في التطبيقات ذات درجات الحرارة المرتفعة والمنخفضة. تمتاز هذه المواد (AMCs) بامتلاكها مقاومة نوعية ومعامل مرونة نوعي عالي مقترنة بمقاومة جيدة لدرجات الحرارة المرتفعة.تم تحضير مادة مركبة ذات أساس ألمنيوم مدعم بدقائق كاربيد السليكون بهدف تحسين الصلادة ومتانة المادة المركبة. اعتمدت طريقة السباكة بالخلط في اسلوب التحضير, حيث توزعت دقائق كاربيد السليكون بانتظام في مادة الأساس (الألمنيوم). إذ ارتبطت الدقائق بشكل جيد مع مادة الأساس. ازدادت الصلادة ومتانة المادة بمقدار( 1.84 , (2.16 مرة على التوالي وبنسبة تقوية وزنية ((10% بالمقارنة مع معدن الألمنيوم غير المقوى. وهذا يعود إلى الصلادة العالية ومقاومة التشوه الجيدة التي تمتاز بها دقائق كاربيد السليكون.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic (3)

English (1)


Year
From To Submit

2012 (1)

2011 (2)

2010 (1)