THE EFFECT OF SUBSTRATE TEMPERATURES ON THE STRUCTURAL AND OPTICAL PROPERTIES FOR (CDS) THIN FILMS
تأثير تغيير درجة حرارة الأساس على الخواص التركيبية والبصرية لأغشية (CdS) الرقيقة.

Loading...
Loading...
Abstract

In this research work optical and structural properties for (CdS) thin films werestudied .The (CdS) thin films were prepared by chemical spray pyrolysis with different substrate temperatures (250,300,350,400) C0 . Such a film was deposited on glass slides substrate of (350) nm thickness . The absorption coefficient was found to be greater than (104)cm-1 for all films and hence allowed for electrons transation . The value of the energy gap for (CdS) thin films prepared by the previous mentioned substrate temperatures became (2.3, 2.45, 2.55, 2.6) eV, respectively.The absorption coefficient ,transmittance ,refractive index and extinction coefficient) found to be dependent on the substrate temperatures . The structure of the (CdS) thin films have been diagnosed by the use of X-ray diffraction (XRD) . This technology was applied to the poly crystalline and Hexagonal structure . The results of the X-ray diffraction showed that grain-size increases with substrate temperature increasing.

تم في هذا البحث دراسة الخواص التركيبيةوالبصرية لأغشية المركب (CdS) الرقيقة المحضرة بطريقة الرش الكيميائي الحراري وبدرجات حرارة أساس مختلفة (250,300,350,400)C0 والمرسبة على قواعد زجاجية وبسمك (350)nm. وجد إن معامل الامتصاص البصري (α (أكبر من(104) cm-1 لجميع الأغشية ، وهذا يعني أن الانتقالات الالكترونية من النوع المباشر المسموح . إنﱠ قيم فجوة الطاقة البصرية للأغشية المحضرةأصبحت(2.3, 2.45, 2.55, 2.6)eV , وكذلك بينت الدراسات أن (معامل الامتصاص،النفاذية، معامل الانكسار ومعامل الخمود) تعتمد على درجة حرارة الأساس إذ تزداد بزيادتها، وقد تم تشخيص تركيب الأغشية بتقنية حيود الأشعة السينية (XRD) حيث كانت الأغشية متعددة التبلور وذات تركيب سداسي، كما أوضحت نتائج حيود الأشعة السينية إن الحجم الحبيبي يزداد بزيادة درجة حرارة الأساس.


Article
Study the Effect of Zn Doping in the Structural and Electrical Properties of CdTe Thin Films
دراسة تأثيرالتشويب بالخارصين في الخواص التركيبية والكهربائية لاغشية CdTe الرقيقة

Loading...
Loading...
Abstract

Some of structural,and electrical properties of pure and zinc (Zn) doped cadmium telluride thin films with impurity percentages (0.5, 1, 1.5)%, deposited on hot glass substrate (temperature equals to 423K) of thickness of 300nm and rate deposition of 0.5nm.s-1 by thermal co-evaporation technique under vacuum of (2×10-5)Torr have been investigates.The structural properties for the prepared films were studied before and after. doping process by analysis of the X-ray diffraction, and it appeared that pure and dopant CdTe thin films are polycrystalline and have the cubic structure with preferential orientation in the [111] direction, and the crystal structure of the films were improved due to doping process. From d.c.electrical conductivity in range of (291-495)K, we noticed that there are two activation energies Ea1 and Ea2, and their values decrease withthe..increase.of.Zn.percentages,so..(σd.c.)..of..those..thin.films.increase.From Hall.effect.measurements we showed that the..(σd.c.)..for CdTe thin film is of n-type and converted to p-type when they adopted with Zn, and charge carrier concentration increases with the increase of Zn percentages, so Hall mobility (μH) decreases.

لقد أجريت دراسة بعض الخواص التركيبية والكهربائية لأغشية تيليرايد الكادميوم( CdTe) النقية والمشوبة بالخارصين (Zn) وبالنسب %(0.5,1,1.5)، المرسبة على أرضيات زجاجية عند درجة حرارة أرضية (423K) وبسمك (300nm) وبمعدل ترسيب (0.5nm.s-1) باستعمال تقنية التبخير الحــراري المــزدوج في الفراغ تحت ضغط (2×10-5Torr).وتمت دراسة الخواص التركيبية للأغشية المحضرة قبل التشويب وبعده عن طريق فحوصات الأشعة السينية، وتبين أن أغشية CdTe النقية والمشوبة ذات تركيب متعدد التبلور ومن النوع المكعب بالاتجاه المفضل [111]، وان عملية التشويب أدت إلى تحسين في التركيب البلوري للأغشية الرقيقة.وخلال قياسات التوصيلية الكهربائية المستمرة ضمن المدى (291-495)K لاحظنا وجود طاقتين للتنشيط Ea1، Ea2، وان قيم طاقتي التنشيط تقل مع زيادة النسبة المئوية لشوائب Zn ومن ثم فان التوصيلية الكهربائية المستمرة (d.cσ) لتلك الأغشية تزداد.تبين من قياسات تأثير هول أن التوصيلية الكهربائية المستمرة لأغشية CdTe هي من النوع السالب (n-type) وتصبح من النوع الموجب (p-type) عندما تشوب الأغشية بـZn ، وان تركيز حاملات الشحنة يزداد مع زيادة نسب الشوائب ومن ثم فان تحركية هول (μH) تقل.


Article
The Effect of Cadmium Substitution on the Structural and Electrical Properties in Nickel Ferrite
دراسة تأثير الأيونات الاستبدالية للكادميوم على الخواص التركيبية والكهربائية لمركبات نيكل- فرايت

Loading...
Loading...
Abstract

Nickel – Cadmium ferrites having the chemical formula (Ni1-xCdxFe2O4), (0 ≤ X ≤ 0.5) were prepared by using powders technology method. The grain size of the ferrite samples were estimated from X-ray diffraction studies after the confirmation of the formation of single phase spinel structure of the ferrites. We found that the Lattice constant and density (ρx-ray), ( ρd) increased with Cd content while the porosity was noticed to decrease. The electrical resistivity and the dielectric constant was found to increases with the increase of cadmium concentration, while the loss factor and the dielectric loss tangent decreases with the increase of cadmium concentration. A maximum of loss factor and the dielectric loss tangent was observed when the hopping frequency is equal to the external electric field frequency. The dielectric constant and the loss factor and the dielectric loss tangent decreases with the rise in frequency. Also notice decrease in resistivity with temperature is normal behavior for semiconductors.

تم تحضير مركبات النيكل – كادميوم ذات الصيغة الكيميائية Ni1-xCdxFe2O4 حيث ان 5.0 ≥ X ≥ 0 وذلك باستخدام طريقة تكنلوجيا المساحيق . تم حساب الحجم الحبيبي لجميع مركبات الفرايت المحضرة من حيود الأشعة السينية بعد التأكد من تشكيل الطور الأحادي ذو التركيب البلوري مغزلي الشكل. كما تم حساب ثابت الشبيكة و الكثافة بنوعيها الكثافة الظاهرية المحسوبة من حيود الأشعة السينية (ρx-ray) والكثافة الفيزياوية ( ρd) ,حيث وجد أنها تزداد مع زيادة تركيز نسبة الكادميوم، بينما كانت المسامية تنقص مع زيادة تركيز الكادميوم . لقد وجد أن المقاومة الكهربائية وثابت العزل الكهربائي يزداد مع زيادة تركيز الكادميوم بينما قيم عامل الفقد و ظل زاوية الفقد تقل مع زيادة تركيز الكادميوم ,والقيم العظمى لعامل الفقد وظل زاوية الفقد وجدت عند تساوي تردد قفز حاملات الشحنة مع تردد المجال الكهربائي الخارجي المسلط .حيث وجد إن ثابت العزل الكهربائي وعامل الفقد و ظل زاوية الفقد تتناقص مع الزيادة في الترددات .كما لوحظ ان المقاومية تنخفض مع زيادة درجة الحرارة لذلك تظهر خصائص شبه موصل.


Article
Effect Gamma Radiation of CdTe Thin Films Deposited by Thermal Evaporation
تأثير اشعة كاما في اغشية كادميوم تالورايد المرسبة بطريقة التبخير الحراري

Author: Enase Y.Abid ايناس ياسين عبد
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2016 Volume: 29 Issue: 2 Pages: 31-40
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The effect of 0.66 μeV gamma radiation on the structural and optical properties of theCdTe thin films prepared by thermal evaporation at thickness 350nm, The samples wereirradiated with time (50 h and 79h) at room temperature. The absorption spectra for all thesamples were recorded using UV-VIS spectrometer in order to calculate the energy gap,refractive index and others parameter . The optical energy gap was found decrease from (1.9to 1.67) eV.

الخلاصةالمحضرة بطريقة التبخير الحراري CdTe 0.66 في الخواص البصرية لأغشية μeV تم دراسة تأثير اشعة كاما بطاقة79 ) ساعة بدرجة حرارة الغرفة. سجل طيف الامتصاصية لجميع ، 350 ,شععت العينات بزمنين ( 50 nm باستعماللحساب فجوة الطاقة البصرية ، معامل الانكسار وبعض العوامل الأخرى، ووجد أن UV-VIS النماذج باستعمال مطياف. eV ( فجوة الطاقة البصرية تقل من ( 1.9 إلى 1.6


Article
The Influence of Aluminum Doping on Structural and Optical Properties of (Bi2O3)Thin Films
تأثير التشويب بالألمنيوم على الخواص التركيبية والبصرية لأغشية (Bi2O) الرقيقة

Loading...
Loading...
Abstract

In this research, the structural and optical properties were studied for Bi2O3 and Bi2O3:Al thin films with different doping ratios ( 1, 2, 3 ) % , which were prepared bythermal evaporation technique under vacuum , with thickness ( 450 ± 20 ) nm depositedon glass substrates at room temperature ( 300 ) K , Structural measurements by ( XRD)techniques demonstrated that all samples prepared have polycrystalline structurewith tetragonal structure and a preferred orientation [ 201 ] the optical measurementshows that all films have a direct energy gap , and in general decrease with theincrease of doping ratio except ratio ( 3% Al ) .The optical constant such as absorption coefficient , extinction coefficient , refractive indexreal and imaginary parts of the dielectric constant and optical conductivity werecalculated before and after doping with the range of wave lengths ( 300 - 1100 ) nm .

الخلاصةالرقيقة غير (Bi2O يتناول هذا البحث دراسة الخواص التركيبية والبصرية لأغشية اوكسيد البزموث ( 3بنسب مختلفة %( 1,2,3 ) التي حضرت بطريقة التبخر الحراري في ( Al ) المشوبة والمشوبة بالألمنيوم300 ) . وقد اظهرت ) K 450 التي رسبت على قواعد زجاجية بدرجة حرارة الغرفة ± 20 ) nm الفراغ بسمكان تركيب الاغشية المحضرة هو من ( X – Ray ) نتائج الفحوصات التركيبية من خلال حيود الاشعة السينيةالنوع متعدد التبلور وبطور رباعي وبالاتجاه السائد [ 201 ] , ومن خلال القياسات البصرية تبين ان هذه الأغشية. ( تمتلك فجوة طاقة بصرية مباشرة تقل قيمتها بزيادة نسبة التشويب ما عدا النسبة ( % 3وقد حسبت الثوابت البصرية مثل معامل الامتصاص ومعامل الخمود ومعامل الانكسار وثابت العزل بجزئية. ( 300 – 1100 ) nm الحقيقي والخيالي قبل عملية التشويب وبعدها خلال مدى من الاطوال الموجية


Article
The effect of Cadmium Substitution on the structural and magnetic properties of Nickel Ferrite
دراسة تأثير الأيونات الاستبدالية للكادميوم على الخواص التركيبية والمغناطيسية للمركب نيكل- فرايت

Author: خلف إبراهيم خليل الجبوري
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 2 Pages: 155-161
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Nickel – Cadmium ferrites having the chemical formula (Ni1-xCdxFe2O4), (0 ≤ X ≤ 0.5) were prepared by using powders technology method. The particle size of the ferrite samples were estimated from X-ray diffraction studies after the confirmation of the formation of single phase spinel structure of the ferrites. We found that the Lattice constant and density (ρx-ray) increased with Cd content while the porosity was noticed to decrease. Also the magnetic testing showed decreases in values the Coercive Force from (0.408 KA/m) to (0.384 KA/m) and the Remnant Magnetization from (0.056 Tesla) to ( 0.048 Tesla) and the Magnetic Relative permeability is the within range (0.137 ~ 0.125) with increasing of the Cadmium concentration while the Magnetic Susceptibility was noticed to increase from (0.862) to (0.875).

تم تحضير مركبات النيكل – كادميوم ذات الصيغة الكيميائية Ni1-xCdxFe2O4 حيث ان 0 ≤ X ≤ 0.5 وذلك باستخدام طريقة تكنلوجيا المساحيق. تم حساب الحجم الحبيبي لجميع مركبات الفرايت المحضرة من حيود الأشعة السينية بعد التأكد من تشكيل الطور الأحادي ذو التركيب البلوري مغزلي الشكل. كما تم حساب ثابت الشبيكة و الكثافة الظاهرية المحسوبة من حيود الأشعة السينية (ρx-ray),حيث وجد أنها تزداد مع زيادة تركيز نسبة الكادميوم, بينما كانت المسامية تنقص مع زيادة تركيز الكادميوم. أما نتائج الفحوصات المغناطيسية فقد أظهرت نقصان قيم القوة القاهرة (0.408 ~ 0.384 KA/m) و المغناطيسية المتبقية (0.056 ~ 0.048 Tesla)والنفوذية المغناطيسية (0.137 ~ 0.125) مع زيادة تركيز الكادميوم بينما أدى إلى زيادة قيم التأثرية المغناطيسية(0.862 ~ 0.875) .


Article
A Study of structural and electrical properties ofCuIn (Sex Te1-x) 2 thin films
دراسـة الخواص التركيبية والكهربائية لاغشية الرقيقة CuIn (Sex Te1-x)2

Author: Sabah Noori mazher صباح نوري مزهر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2009 Volume: 6 Issue: 1 Pages: 73-85
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, resistivity of CuIn (Sex Tel-x)2 thin films prepared by thermal evaporation of thickness (250+25nm) , was measured in an electrical measurement system in the temperature ranges ( 293oK - 423oK). Resistivity of the samples was also measured after annealing for one hour in vacuum for two temperatures ( 373oK and 423oK) . Activation energies of these films were calculated before and after annealing, type of majority charge carrier was known by (Hall effect) and concentration of charge carrier and its mobility before and after annealing was also calculated.

تم في هذا البحث قياس المقاومية (Resistivity) لاغشية 2 CuIn (Sex Te1-x) الرقيقة . حضرت العينات باستخدام طريقة التبخير الحراري ((Vacuum thermal evaporation بسمك قدرة (250+25nm) للعينات في منظومة كهربائية ذات مدى حراري (293oK) الى(423oK) ، كما تم قياس المقاومية لنفس الاغشية المحضرة بعد تلدينها (Annealing) عند درجات الحرارة (373oK) و(423oK) لمدة ساعة بوجود الفراغ . تم حساب طاقات التنشيط لهذا الاغشية قبل التلدين وبعده .وتم معرفة نوع حاملات الشحنة الاغلبية من خلال اجراء تجربة هول ( Hall effect ) ومن ثم حساب تركيز حاملات الشحنة وتحركيتها قبل التلدين وبعده.


Article
The Structural and Surface Morphology Properties of Aluminum Doped CdO Thin Films Prepared by Vacuum Thermal Evaporation Technique.
الخواص التركيبيةومورفولوجية السطح لأغشية(Al) النقيةوالمشوبة ب(CdO)والمحضرة بتقنية التبخير الحراري في الفراغ

Loading...
Loading...
Abstract

Undoped and Al-doped CdO thin films have been prepared by vacuum thermal evaporation on glass substrate at room temperature for various Al doping ratios (0.5, 1 and 2)wt.% . The films are characterized by XRD and AFM surface morphology properties. XRD analysis showed that CdO:Al films are highly polycrystalline and exhibit cubic crystal structure of lattice constant averaged to 0.4696 nm with (111) preferred orientation. However, intensity of all peaks rapidly decreases which indicates that the crystallinity decreases with the increase of Al dopant. The grain size decreases with Al content (from 60.81 to 48.03 nm). SEM and AFM were applied to study the morphology and to estimate the surface roughness of the obtained films. All films were homogeneous and smooth, with a characteristic spherical grain size depending on Al content. The )RMS) roughness of the films increases with the increase of Al dopant.The improvement of the structural and surface morphology properties of Al-doped CdO has potential applications for different optoelectronic device applications

حضرت أغشية أوكسيد الكادميومCdO)) الرقيقة النقية والمشوبة ب(Al) بنسب تشويب (0.5, 1, 2)% وبإعتماد تقنية التبخير الحراري الفراغي على أرضيات زجاجية بدرجة حرارة الغرفة. دُرست الخواص التركيبية بأستخدام تقنية (XRD), وكذلك مواصفات مورفولوجية السطح للأغشية المحضرة بإستخدام تقنية (AFM) و(SEM) . أظهرت نتائج قياسات حيود الأشعة السينية XRD)) إن جميع الأغشية المحضرة النقية والمشوبة كانت ذا تركيب بلوري متعدد التبلور ومن النوع المكعب الذي يمتلك ثابت شبيكة طوله nm 0.4696مع هيمنة النمو بالإتجاه (111) للأغشية النقية والمشوبة كافة مع إزاحة في زاوية الحيود, وحدوث أنخفاض في شدة القمم المقاسة مما يدل على نقصان التبلور وتناقص واضح أيضاً يظهر في معدل الحجم الحبيبي nm (60.81-48.03) عند زيادة التشويب بالألمنيوم (Al). أستخدمت تقنية مجهر القوة الذرية (AFM) والمجهر الإلكتروني الماسح (SEM) لدراسة طوبوغرافية وخشونة سطوح الأغشية الرقيقة المحضرة. أظهرت نتائج فحوصات المجهر أن جميع الأغشية متجانسة وناعمة وأن شكل الحجم الحبيبي المتكون أشبه بالشكل الكروي بالأعتماد على نسبة التشويب, مع زيادة معدل خشونة السطح (RMS) بإزدياد نسبة التشويب. وأظهرت النتائج أن الخواص التركيبية ومورفولوجية السطح تتحسن لأغشيةCdO بعد تشويبها بنسب قليلة جداً من Al مما يجعل هذه الأغشية واسعة التطبيقات في مجال النبائط الالكتروضوئية.


Article
Studying the Structural and Optical Properties of ZnO Thin Films Doping by AL and Cu Prepared by Chemical Spray Pyrolysis
دراسة الخواص التركيبية والبصرية لأغشية اوكسيد الخارصين المشوبة بالألمنيوم والنحاس المحضرة بطريقة التحلل الكيميائي الحراري

Authors: Dawood S. Abd AL Khader داود سلمان عبد القادر --- Jobair A. Najem جبير عبد الله نجم --- Hamid S.Aljumaily حامد صالح الجميلي
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2016 Volume: 12 Issue: 3 - part 2 Pages: 61-74
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Undoped and AL,Cu-doped ZnO at (3-7 wt. %) thin films have been prepared by by chemical spray pyrolysis on glass substrates at 400ºC. The structural and optical properties of these films were studied. The results of the structural tests showed that these films are of a polycrystalline hexagonal structure with a preferred orientation in the (002) direction, the optical properties included.transmittance, energy gap. The energy gap values were found to decrease from (3.3ev) for ZnO pure to(3.29- 3.2 eV) for ZnO:AL films and(3.2-3.26) for ZnO:Cu films. the average transmittance was found about (90%) in the visible region.

في هذه الدراسة تم تحضير أغشية ZnO النقية والمطعمة بالألمنيوم والنحاس بنسبة (3%, 5% ,7%) بأستخدام طريقة التحلل الكيميائي الحراري وعلى قواعد من الزجاج بدرجة حرارة 400 °C .تمت دراسة الخواص التركيبية والبصرية لهذه الأغشية بينت نتائج التشخيص ان هذه الأغشية متعددة التبلور وذات تركيب سداسي والاتجاه المفضل عند (002) وتضمنت دراسة الخواص البصرية (طيف النفاذية وفجوة الطاقة) ووجد ان قيم فجوة الطاقة للأنتقالات المباشرة المسموحة تتناقص عند التشويب من (3.3ev) للأغشية النقية الى (ev (3.29-3.2 للأغشية المشوبة بالالمنيوم و (ev (3.2-3.26 للأغشية المشوبة بالنحاس وان معدل النفاذية 90 % ضمن منطقة الطيف المرئي.


Article
Study of Some Structural and Optical Properties of AgAlSe2 Thin Films
دراسة بعض الخواص التركيبية والبصرية للأغشية الرقيقة AgAlSe

Loading...
Loading...
Abstract

The structural properties of ternary chalcopyrite AgAlSe2 compound alloys and thinfilms that prepared by the thermal evaporation method at room temperature on glass substratewith a deposition rate (5±0.1) nm s-1 for different values of thickness (250,500 and 750±20)nm, have been studied, using X-ray diffraction technology. As well as, the optical propertiesof the prepared films have been investigated. The structural investigated shows that the alloyhas polycrystalline structure of tetragonal type with preferential orientation (112), while thefilms have amorphous structure. Optical measurement shows that AgAlSe2 films have highabsorption in the range of wavelength (350-700 nm). The optical energy gap for alloweddirect transition were evaluated, which decreases with film thickness increasing, i.e. itdecreases from 2.5 eV to 2.2 eV when thickness varies from 250±20 nm to 750±20 nm.

واغشيته التي حضرت بوساطة طريقة التبخير AgAlSe درست الخواص التركيبية لسبيكة المركب الثلاثي 25±0.1 ). وبسمك ) nm sec- الحراري في الفراغ عند درجة حرارة الغرفة على قواعد من الزجاج بمعدل ترسيب 120 ±)نانومتر بأستعمال تقنية حيود الأشعة السينية كما درست الخواص البصرية للأغشية مختلف ( 750,500,250المحضرة. بينت الفحوصات التركيبية أن السبيكة تملك تركيبا متعدد التبلور من النظام البلوري الرباعيمع هيمنة الاتجاه ( 112 ) ، بينما تمتلك الأغشية المحضرة تركيبا عشوائيا. أوضحت القياسات البصرية أن (Tetragonal)700 ) نانومتر. وتم حساب فجوة - ذات امتصاصية عالية للأطوال الموجية في المنطقة المرئية ( 350 AgAlSe أغشية 2(2.2eV) 2.5 ) إلى eV) الطاقة ذات الانتقال المباشر المسموح، وان قيمة هذه الفجوة تتناقص مع تزايد السمك،اذ قلت من750 )على التوالي. ± 250 ) نانومتر الى ( 20 ± بزيادة السمك من ( 20

Listing 1 - 10 of 23 << page
of 3
>>
Sort by
Narrow your search

Resource type

article (23)


Language

Arabic (10)

Arabic and English (8)

English (5)


Year
From To Submit

2019 (1)

2018 (3)

2017 (2)

2016 (8)

2015 (3)

More...