Studying the Effect of some Parameters on PS Microfibers by Electrospinning Technique

Authors: Balkees M. Al Dabbagh --- Hanaa J. Khadim --- Dayah N. Raouf
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 3 Pages: 577-586
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this search is prepared and study of PS/( CL.F0.5+DMF0.5) Microfibers by electrospinning technique under different working condition including solution parameters such as (solvent, viscosity, concentration, conductivity, surface tension) and set up parameters including (voltage, flow rate) . Results show the diameter of micro fibers decreased with increasing of voltage value, conductivity of media solution. While the Microfibers diameter increased with increasing of (viscosity, flaw rate, tip diameter, and concentration of solution) . AC- HV leads to higher diameter than DC-HV but with more alignment of Microfibers

الهدف من هذا البحث تحضير ودراسة الياف البولي ستايرين المذاب في مزيج من الكلوروفورم و داي مثيل فورما اميد بنسبة (0.5:0.5) المايكروية المحضرة بواسطة منظومة الغزل الكهربائي تحت ظروف عمل مختلفة تشمل ظروف خاصة بالمحلول مثل (المذيب، اللزوجة، التركيز، التوصيلية، والشد السطحي) ، وكذلك ظروف خاصة بتنصيب المنظومة وتشمل (الفولتية، نسبة الضخ )اثبتت النتائج ان قطر الليف يقل بزيادة الفولتية وتوصيلية المحلول ، كما ان قطر الليف يزداد بزيادة كل من (اللزوجة ونسبة الضخ وتركيز المحلول) .كما اثبتت النتائج ان الفولتية المتناوبة تؤدي الى قطر ليف اكبر من الفولتية المستمرة لكن مع اصطفاف اكبر للالياف المايكروية.


Article
Preparation and Study of some Physical Properties of (Polystyrene/Ethel vinyl acetate) Blend Nanofibers

Authors: Hanaa J. Khadhim --- Rana M. Salih
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 4 Pages: 1267-1274
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This search aims to fabricate immiscible nanofibers (Polystyrene/Ethyl phenyl acetate) blends with different average porous for different applications by electrospinning technique. PS and EVA were mixed by (50/50) to prepare 0.1 (w/v) con.%, each polymer dissolved in (Tetra hydro furan ). Resulting nanofibers morphology was studied by Atomic force microscopy (AFM) and high optical resolution microscope (HORM) , Contact angle between the water and the surface of nanofibers by contact angle analyzer also studied for (hydrophilic or hydrophopic behavior ). FTIR test for checking the emergence or not of new bonds in the nanofibers blend was performed. AFM Results show that the prepared blends of (PS+EVA) have homogenous needle structures (nanofibers) at three dimensions , while the results of (HORM) shows the nonwoven structures contain intermediates pours structure , Contact angle results show that decrease of the contact angle after adding the EVA polymer to PS, and this refers to the (EVA/PS) nanofibers blends have hydrophilic behavior.

يهدف هذا البحث الى تحضير انسجة نانوية من خلائط غير متجانسة من الياف (بولي ستايرين / اثيل فاينيل استيت) النانوية ومعدلات مختلفة المسامسية لتطبيقات مختلفة باستخدام تقنية الغزل الكهربائي . تم خلط اثيل فاينيل استيت مع البولي ستايرين بنسبة (50/50) لتحضير تركيز (0.1 w/v) ، حيث اذيب كل بوليمير في مذيب التتراهيدروفيوران . خواص المورفولوجية للنسيج المحضر درست باستخدام مجهر القوة الذرية AFM ومجهر ضوئي عالي الوضوح . كما استخدم محلل زاوية التماس لقياس زاوية التماس وتحديد سلوك النسيج المحضر من ناحية الماء . كما استخدم مطياف الاشعة تحت الحمراء لمعرفة ظهور او عدم ظهور اواصر جديدة في النسيج النانوي المحضر. اثبتت نتائج مجهر القوة الذرية ان النسيج المحضر يحتوي تراكيب ابرية متجانسة والتي هي عبارة عن الالياف النانوية بتوزيع منتظم في ثلاثة ابعاد . كما اثبتت نتائج المجهر الضوئي ان النسيج المحضر يحتوي ضمن تركيبه على بعض التراكيب المسامية . اما محلل زاوية التماس فقد اثبت ان سلوك النسيج المحضر يتحول من كاره للماء لالياف البولي ستايرين النانوية الى محب للماء بعد اضافة اثيل فاينيل استيت.


Article
Preparation and Study of some Physical Properties of (Polystyrene/Ethel vinyl acetate) Blend Nanofibers

Authors: Hanaa J. Khadhim --- Rana M. Salih
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 4 Pages: 1267-1274
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This search aims to fabricate immiscible nanofibers (Polystyrene/Ethyl phenyl acetate) blends with different average porous for different applications by electrospinning technique. PS and EVA were mixed by (50/50) to prepare 0.1 (w/v) con.%, each polymer dissolved in (Tetra hydro furan ). Resulting nanofibers morphology was studied by Atomic force microscopy (AFM) and high optical resolution microscope (HORM) , Contact angle between the water and the surface of nanofibers by contact angle analyzer also studied for (hydrophilic or hydrophopic behavior ). FTIR test for checking the emergence or not of new bonds in the nanofibers blend was performed. AFM Results show that the prepared blends of (PS+EVA) have homogenous needle structures (nanofibers) at three dimensions , while the results of (HORM) shows the nonwoven structures contain intermediates pours structure , Contact angle results show that decrease of the contact angle after adding the EVA polymer to PS, and this refers to the (EVA/PS) nanofibers blends have hydrophilic behavior.

يهدف هذا البحث الى تحضير انسجة نانوية من خلائط غير متجانسة من الياف (بولي ستايرين / اثيل فاينيل استيت) النانوية ومعدلات مختلفة المسامسية لتطبيقات مختلفة باستخدام تقنية الغزل الكهربائي . تم خلط اثيل فاينيل استيت مع البولي ستايرين بنسبة (50/50) لتحضير تركيز (0.1 w/v) ، حيث اذيب كل بوليمير في مذيب التتراهيدروفيوران . خواص المورفولوجية للنسيج المحضر درست باستخدام مجهر القوة الذرية AFM ومجهر ضوئي عالي الوضوح . كما استخدم محلل زاوية التماس لقياس زاوية التماس وتحديد سلوك النسيج المحضر من ناحية الماء . كما استخدم مطياف الاشعة تحت الحمراء لمعرفة ظهور او عدم ظهور اواصر جديدة في النسيج النانوي المحضر. اثبتت نتائج مجهر القوة الذرية ان النسيج المحضر يحتوي تراكيب ابرية متجانسة والتي هي عبارة عن الالياف النانوية بتوزيع منتظم في ثلاثة ابعاد . كما اثبتت نتائج المجهر الضوئي ان النسيج المحضر يحتوي ضمن تركيبه على بعض التراكيب المسامية . اما محلل زاوية التماس فقد اثبت ان سلوك النسيج المحضر يتحول من كاره للماء لالياف البولي ستايرين النانوية الى محب للماء بعد اضافة اثيل فاينيل استيت.


Article
Study The Effect of Conditions of The Electro Spinning Cabin (Humidity) on Electro-spun PolyVinyl Alcohol (PVA) Nano-fibers

Authors: Samara Alswid --- Manal Issa
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2017 Volume: 20 Issue: 3 Pages: 520-525
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Electrospinning is a simple and highly versatile method for generating ultrathin fibers (mainly polymers) with diameters ranging from a few micrometres to tens of nanometres. This technique has attracted tremendous recent interest in both academia and industry, owing to its unique ability to produce ultrafine fibers of different materials in various fibrous assemblies. Electrospinning is a process that uses an electric potential to overcome the surface tension of a solution to produce an ultra-fine jet, which elongates, thins and solidifies as it travels through the electric field to a collector.. In this research, we studied the effect of conditions of the cabin “specifically humidity” on the diameter of nanofibers manufactured by electrospinning. We used Polyvinyl alcohol (PVA) polymeric solution with weight concentration of 10%, voltage 20 kv, under different values of relative humidity. Fiber morphology and fiber diameter were determined using scanning electron microscope, and measuring the fiber diameter by using image j program. It was found that the diameter of the fibers increased with increasing the relative humidity within our studying area .

تعتبر عملية الغزل الكهربائي عملية سهلة و بسيطة لإنتاج ألياف نانوية بأقطار تتراوح بين بضعة ميكرومترات و عشرات النانو مترات. وقد لاقت هذه الطريقة اهتماماً كبيراً مؤخراً في المجالات الأكاديمية و الصناعية, وذلك بسبب قدرتها على إنتاج ألياف متناهية في الصغر من مواد مختلفة وبأشكال مختلفة. يتم في هذه التقنية استخدام تيار كهربائي عالي الجهد يتغلب على التوتر السطحي للمذيب فيتشكل تيار بثق عالي الدقة, ويستطيل ثم يتصلب أثناء انتقاله إلى مجمع مأرض أو مشحون عكسياً. تم في هذا البحث دراسة تأثير شروط الحجرة وتحديداً الرطوبة على قطر الألياف النانوية الناتجة عن عملية الغزل الكهربائي حيث تم استخدام محلول بوليميري من ال PVA بتركيز وزني 10 % , و فرق كمون 20 kV و تم تطبيق قيمة مختلفة للرطوبة النسبية. تم تحديد شكل و قطر الألياف الناتجة باستخدام المجهر الالكتروني و قياس أقطار الألياف الناتجة باستخدام برنامج Image j, و تم ملاحظة تزايد القطر مع زيادة نسبة الرطوبة وذلك ضمن المجال المدروس.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2017 (3)

2016 (1)