Article
THE INFLUENCE OF VARIOUS PARAMETERS ON CREVICE CORROSION OF TWO DIFFERENT TYPE GEOMETRY OF 304L STAINLESS STEEL
تاثير عوامل مختلفة علئ التاكل التصدعي لشكلين مختلفين من الفولاذ المقاوم للصدأ(304L)

Loading...
Loading...
Abstract

ABSTRACTAn investigation was carried out to study the effect of various parameters on crevice corrosion oftwo different type geometry of ( rod, square) 304L stainless steel in 3.4% NaCl solution under staticconditions at different temperatures (25, 50) C°, rotation cylinder electrode was used for 100, 200rpm at the same temperatures. It was found the maximum attack was in square 304L SS at 50 C°under static conditions in account of geometric of specimen whereas slightly effect as the velocityincreases due to the passive film is formed on the steel surface. In contrast, the results show theeffect of temperature changes and velocity on corrosion rate in rod 304LSS is more pronounced astemperatures and velocities rises enable the migration of chloride ions into the crevice

الخلاصةتم في هذا البحث د ا رسه تأثير عدة عوامل على التأكل التصدعي لشكلين مختلفين من الفولاذ المقاوم للصدأ(25 ) في حالة , 50) C° 304 ) في محلول كلوريد الصوديوم بتركيز 3.4 % بدرجات ح ا ررة مختلفة LSS100 ). وجد ان اعلى معدل تأكل كان للعينة , 200 rpm) السكون وكذلك استخدم قطب اسطوني دووار بسرع50 ) قد يعود السبب الى الشكل الهندسي للعينة في حين كان تأثير ) C° المربعة في حالة السكون بدرجةالسرع عليها طفيف بسبب تكون طبقة الاوكسيد على السطح(منطقة الخمود) وعلى العكس حيث اظهرتالنتائج ان تأثير درجات الح ا ررة والسرع واضح على العينة ذات الشكل الاسطواني ويعزى ذلك لتمكن ايوناتالكلور الى النفاذ الى داخل الصدع


Article
Effect of Spindle Speed on the Drilling Length and Surface Finish in Deep Drilling Operation
تأثير سرعة عمود الدوران على طول الثقب والإنهاء السطحي في عملية التثقيب العميق

Author: سعد حميد نجم الشافعي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: 9 Issue: 3 Pages: 427-441
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research deals with studying the effect of spindle speed on the drilling length and surface finish for producing deep holes. Where experiments are done by using twist drills having (9, 10, 11) mm diameters by using samples of stainless steel under dry cutting conditions. The results show that increases of the spindle speed limits from producing drilling length and it has negative effect upon magnitude of drill deflection and its vibration , it keeping in mind the drill deflection and its vibration these have small diameter will be more for the drill that has big diameter . The speed and drill diameter have clear effect on flank wear land, in another word, with the increasing of speed and drill diameter, the flank wear land will increase. Also, there is a direct proportional relationship between the speed and drill diameter in one hand and the surface quality on the other hand, therefore; the roughness increase when the speed and drill diameter increases.

يتضمن البحث الحالي دراسة تاثير سرعة عمود الدوران على طول الثقب والإنهاء السطحي للثقوب المنتجة ، حيث تم إجراء التجارب باستخدام برايم حلزوني Twist Drills باقطار (9،10،11) ملم وباستخدام عينات من الفولاذ المقاوم للصدأ تحت ظروف من القطع الجاف . من النتائج لوحظ ان زيادة سرعة عمود الدوران تحد من طول الثقب المنتج ولها تأثير سلبي على مقدار انحراف البريمة واهتزازها، وان انحراف واهتزاز البريمة الأقل قطرا يكون اكثر مما للبريمة الأكبر قطرا . ولهذه السرعة وقطر البريمة اثرهما الواضح على عرض البلى الخلوصي فبزيادتهما يزداد عرض البلى . كذلك لوحظ ان هنالك علاقة طردية بين هذه السرعة وقطر البريمة من جهه وجودة السطح من جهة اخرى ، حيث ان قيم الخشونة تزداد كلما زادت السرعة وقطر البريمة .


Article
Investigation on Mechanical Properties of Austenitic Stainless-Steel Pipes Welded by TIG Method

Author: Mushtaq Albdiry
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 315-323
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper investigates the mechanical properties of austenitic stainless steel (type 204) pipes welded by Tungsten Inert Gas (TIG) welding process. Testing of hardness (HRC), tensile strength and bending strength was performed for the steel pipes welded at two different welding temperatures (700 °C and 900 °C) with and without using the weld filler wire. The microstructure of the welding regions was examined by using an optical microscopy. The properties showed that the steel pipes welded by 900 °C with using the weld filler obtained the highest tensile strength and bending strength versus these welded by 700 °C without the use of the weld filler. This is attributed to the weld filler heated and melt at sufficient temperature (900 °C) and compensate losing in the Ni metal occurred in the base steel metal during the welding process.

هذا البحث يدرس الخواص الميكانيكية للأنابيب الفولاذية الاوستنايتي (نوع 204) الملحومة بطريقة اللحام بغاز التنغستن الخامل. اجريت فحوصات اختبار الصلادة روكويل C، قوة الشد وقوة الانحناء لأنابيب الصلب الملحومة بدرجتين مختلفتين من درجة حرارة اللحام 700 درجة مئوية و900 درجة مئوية مع وبدون استخدام حشوة اللحام. كذلك تم إجراء فحص البنية المجهرية لمناطق اللحام. أظهرت الخصائص أن اللحامات الفولاذية المكتملة عند 900 درجة مئوية مع استخدام حشوة اللحام أعلى مقاومة شد ومقاومة انحناء مقارنة بتلك الملحومة بدرجة 700 بدون حشوة اللحام ويعزى ذلك الى ان حشوة اللحام انصهرت بدرجة حرارة كافية وقد ملئت النقص الحاصل لمعدن النيكل في المادة الاساس اثناء فترة اللحام.


Article
Controlling Angular Distortion in Manual Metal Arc Welding of Austenitic Stainless Steels Using Back-step Technique

Author: Abdul Sameea Jasim Abdul Zehra Jilabi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 2 Pages: 311-319
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Nowadays, austenitic stainless steels (A.S.S.) have many industrial applications in the fields of chemical and petrochemical processing, marine, medicine, water treatment, petroleum refining, food and drinks processing, nuclear power generation etc. The secret behind this wide range of applications is the fact that A.S.S. have great corrosion resistance, high strength and scale resistance at elevated temperatures, good ductility at low temperatures approached to absolute zero in addition to notable weldability. On the other hand, manual metal arc (MMA) is probably the most common process used for the welding of A.S.S. Unfortunately, MMA welding of A.S.S. could be associated with considerable distortion. Uncontrolled or excessive distortion usually increases the cost of the production process due to the high expense of rectification or replacing the weldment by a non-distorted one. MMA welding of A.S.S. was carried out using the back-step technique with various bead lengths, and without using this technique for comparison. Results have showed that the angular distortion was a function of the bead length in the back-step welding of A.S.S. The angular distortion decreased by (14.32%) when the back-step technique was used with a (60 mm) length for each bead, and by (41.08%) when the bead length was (40 mm). On the other hand, it increased by (25%) when the back-step technique was done with a (30 mm) length for each bead.

يمتلك الفولاذ المقاوم للصدأ الأوستنايتي حاليا العديد من التطبيقات الصناعية في مجالات المعالجة الكيميائية والبتروكيماوية، والبحرية، والطب، ومعالجة المياه، وتكرير النفط، وتجهيز الأغذية والمشروبات، وتوليد الطاقة النووية وغيرها. ويعود السر في هذا المدى الواسع من التطبيقات الى ان الفولاذ المقاوم للصدأ الأوستنايتي يمتلك مقاومة عالية للتاكل، ومقاومة ميكانيكية ومقاومة للتقشر عاليتين في درجات الحرارة المرتفعة، ومطيلية جيدة في درجات الحرارة المنخفضة والتي تقترب من الصفر المطلق بالإضافة إلى قابلية ملحوظة للحام. وتكون طريقة القوس الكهربائي اليدوي على الأرجح هي الطريقة الأكثر شيوعاً واستخداماُ في لحام الفولاذ المقاوم للصدأ الأوستنايتي. إلا إن لحام هذا الفولاذ بطريقة القوس الكهربائي اليدوي ترافقه تشوهات كثيرة، والتشوه المفرط أو غير المسيطر عليه عادة ما يزيد من كلفة العملية الإنتاجية بسبب التكلفة العالية للمعالجة، أو ربما استبدال الملحومة بأخرى غير مشوهة عندما يصعب معالجتها.وقد تم لحام الفولاذ المقاوم للصدأ الأوستنايتي بطريقة القوس الكهربائي اليدوي باستخدام تقنية اللحام التراجعي، وبأطوال مختلفة لدرزات اللحام، إضافة إلى لحامه بدون استخدام هذه التقنية للمقارنة.وقد أظهرت النتائج ان التشوه الزاوي كان دالة لطول الدرزة في اللحام التراجعي للفولاذ المقاوم للصدأ الأوستنايتي، حيث انخفض التشوه الزاوي بنسبة (14.32%) عند استخدام تقنية اللحام التراجعي بطول (60 ملم) للدرزة الواحدة، و بنسبة (41.08%) عندما كان طول الدرزة (40 ملم)، في حين ارتفع بنسبة (25%) عندما نفذت تقنية اللحام التراجعي بطول (30 ملم) للدرزة الواحدة.


Article
STUDY TO DETERMINE THE LONGEST VALIDITY PERIOD FOR ORTHODONTIC WIRES IN A DIFFERENT ENVIRONMENTS
دراسة تحديد أطول فترة صلاحية لأسلاك تقويم الأسنان في أجواء مختلفة

Author: Mohammed Abdulateef Ahmed محمد عبد اللطيف أحمد
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2014 Volume: 7 Issue: 1 Pages: 25-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The research summary to knowing longest period of validity for orthodontic wires in four corrosive media ,the first medium approximately similar to human mouth such as corrosive medium (Artificial Saliva), human body temperature, hydrogen power (pH), and aeration ,and compared with orthodontic wires these serve in same corrosive medium but at room temperature and the identical aeration as a second corrosive medium, and compared to orthodontic wires present or attending in sodium chloride solution instead of artificial saliva at room temperature and the like aeration as a third corrosive medium. The final comparison test with orthodontic wires present in sodium chloride solution at human body temperature and the like aeration too. The study done by using device or system was native designed and manufactured according to modified American standard specification (ASTM G31), the orthodontic wires were from type austenitic stainless steel (301). After four mentioned corrosion experiments for serial six months period ,and usage Corrosion Penetration Rate law (CPR) and by traditional mathematical methods addition to the microstructures of samples before and after corrosion experiments ,conclude that ;the longest validity period for orthodontic wires at environment approximately similar to human mouth ,then wires worked in artificial saliva at room temperature, followed by the wires served in sodium chloride solution at room temperature, finally; orthodontic wires were worked in sodium chloride solution at human body temperature had shortest validity period.

يتلخص البحث بتحديد أطول فترة صلاحية لأسلاك تقويم الأسنان في أربع أجواء أكالة ، الأول جو مماثل لفم الأنسان تقريبا" من حيث الوسط الأكال (اللعاب الصناعي) (Artificial Saliva) و درجة الحرارة والحامضية والتهوية، ومقارنتها بالأسلاك العاملة في نفس الوسط الأكال والتهوية ولكن بدرجة حرارة الغرفة كجو أكال ثاني، ثم الأسلاك المتواجدة في محلول كلوريد الصوديوم (3.5%wt NaCl) بدلا" عن اللعاب الصناعي وبدرجة حرارة الغرفة وبنفس التهوية كجو أكال ثالث وأخيرا" المقارنة مع الأسلاك المتواجدة في محلول كلوريد االصوديوم وبدرجة حرارة جسم الأنسان ومعرضة لنفس التهوية أيضا". وتمت الدراسة بأستخدام منظومة مصممة و مصنعة محليا" حسب المواصفة القياسية الأميركية المعدلة (ASTM G31)، وأسلاك تقويم الأسنان المستخدمة من نوع الفولاذ المقاوم للصدأ الأوستنايتي (301)، وبعد إجراء أختبارات التآكل الأربعة أعلاه و لفترة زمنية مقدارها ستة أشهر متتالية وبأستخدام قانون معدل تغلغل أومعدل نفاذ تنقر التآكل (Corrosion Penetration Rate ) وبالطرق الرياضية التقليدية ومن الصور المجهرية للعينات قبل وبعد حالات التآكل نستنتج بأن الأسلاك تكون بفترة صلاحية أطول عند جو مماثل لفم الأنسان وتليها الأسلاك العاملة في اللعاب الصناعي وعند درجة حرارة الغرفة ثم تليها الأسلاك العاملة في كلوريد الصوديوم عند درجة حرارة الغرفة و أقصر فترة صلاحية تكون للأسلاك العاملة في محلول كلوريد الصوديوم عند درجة حرارة جسم الأنسان.


Article
Improvement of Hot Corrosion Resistance of Austenitic Stainless Steel by Chromizing-Siliconizing

Authors: Ali Hobi Halem --- Haydar Hassan Jaber --- Roaa Hatim Hatif
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 4 Pages: 788-796
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Simultaneous deposition of chromium and silicon by pack cementation is very effective in protecting substrates from hot corrosion and oxidation environments at high temperature. In this study, chromium and silicon were simultaneously deposited by diffusion into austenitic stainless steel 316L alloy by the pack cementation process using a pack mixtures containing (67 wt. % Cr, 8wt. %Si, 2wt. %NH4Cl and 23wt. %Al2O3) when required. It was found that diffusion coating time of six hours at 950oC produces coating thickness of 80-100μm and consist mainly of CrSi2 and Cr3Si phases.

ترسيب الكروم والسليكون بواسطة عملية السمنتة له تأثير فعال في تكوين طبقه واقية حاميه من التآكل الحار والأكسدة في أوساط تآكليه مختلفة عند درجات حرارة عالية. في هذه الدراسة تم ترسيب الكروم والسليكون آنيا عند سطح الفولاذ الاوستنايتي باستخدام تقنية السمنتة باعتماد ألية الطلاء الانتشاري، وباستخدام خليط مكون من: (67% Cr, 8% Si, 2% NH4Cl, 23% Al2O3) جرت عملية الطلاء ألانتشاري عند درجة حرارة 950 مْ ولمدة 6 ساعة في جو من الآركون . لقد وجد إن سمك طبقة الطلاء (80-100) مايكرومتر وتتكون من الأطوار CrSi2 و Cr3Si.


Article
Adenine as Environmentally- Friendly Corrosion Inhibitor for Stainless Steel in Sodium Chloride Acid Solution
الإدينين كمثبط صديق بيئياً لتآكل الفولاذ المقاوم للصدأ في محلول حامضي لكلوريد الصوديوم

Authors: Wisal A. Isa وصال عبد العزيز عيسى --- Marwa S. Hussain مروة صباح حسين
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042/ 25213407 Year: 2015 Volume: 28 Issue: 1 Pages: 113-131
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The corrosion behavior and the influence of the concentration of adenine (AD) on the corrosion of 316L stainless steel in 0.6 mol.dm-3 sodium chloride acid solutions were studied. The research was performed in two pH values (pH=2 and pH=4) over the temperature range (293- 308)K. The investigation involved electrochemical polarization method using potentiostatic technique. Tafel polarization study revealed that (AD) acted as a mixed inhibitor. The inhibition efficiency increased with an increase in the concentration of adenine, but decreased with increase in temperature. (efficiency= 87% at 0.01 M AD & at T= 293K). The adsorption of (AD) has been found to occur on the surface of 316L stainless steel according to the Langmuir isotherm. The kinetic and thermodynamic parameters for stainless corrosion and adenine adsorption respectively were determined and discussed.

يتناول موضوع في دراسة كهروكيميائية لسلوك تآكل الفولاذ المقاوم للصدأ نوع (316L) وتأثير تركيز مثبط الإدينين [Adenine (AD)] على اعاقة التآكل في محلول حامضي لكلوريد الصوديوم بتركيز (0.6 mol.dm-3). تم اجراء البحث عند قيمتين للأس الهيدروجيني (pH = 2 وpH = 4) على مدى من درجات الحرارة (293-308 K) كما اشتملت الدراسة على طريقة الاستقطاب الكهروكيميائي (استقطاب تافل) باستعمال جهاز المجهاد الساكن ، إذ تم التوصل عن طريقه الى معرفة سلوك مثبط (AD) بانه يعمل على تقليل كل من التفاعلين الانوديوالكاثودي (mixed inhibitor)، أي إنه يقوم بعملية تثبيط تآكل سبيكة الفولاذ المقاوم للصدأ بكفاءة مقدارها 87%. كما وجد بان الكفاءة تزداد بزيادة تركيز المثبط وتقل بزيادة درجة الحرارة؛ اذ ان قيمة الكفاءة 87% تقع عند تركيز المثبط (AD) المساوي (0.01 M) عند درجة حرارة 293K. كما اوضحت الدراسة ان عملية امتزاز مثبط الإدينين (AD) على سطح الفولاذ المقاوم للصدأ تتبع متساوي درجة الحرارة للامتزاز للانكمير (Langmuir Isotherm for Adsorption).تم حساب ومناقشة المعلمات الحركية والثرموديناميكية لعمليتي تآكل الفولاذ المقاوم للصدأ وامتزاز مثبط AD على التوالي.


Article
Nugget mechanical properties of combination (rectangular and round) welded and soldered stainless steel wires

Authors: Zainab M. Hasan --- Fakhri A. Ali فخري عبد علي
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2014 Volume: 26 Issue: 3 Pages: 169-173
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: This study aimed to compare the mechanical properties between four groups of newly fabricatedcombination wires according to their method of union, according to the gauges of wires and a comparison weremade between them and their originals.Materials and method: A total of 60 stainless steel combination wires were fabricated , divided into four groupsaccording to gauge of wires and their method of union, each of them with 15 samples, the groups were welded(0.016x0.022-0.016 and 0.016x0.022-0.018) and soldered (0.016x0.022-0.016 and 0.016x0.022-0.018), samples weremade according to certain parameters which were : for the welded samples: length,weight, duration of pulsationand size of copper electrode tips used; for the soldered samples: length, weight, distaince from the heat source andduration of heat applicationResults: The descriptive statistics showed that the maximum value for ultimate force and ultimate tensile strength wasfor the soldered 0.016x0.022+0.018 inches combination wires, while the minimum was for the welded0.016x0.022+0.016inches wires. Elastic modulus showed higher values for the soldered 0.016x0.022+0.016 and resiliencyvalues for the welded 0.016x0.022+0.016 were the highest. Comparison between combination wires and theiroriginals showed a decrease in the mechanical properties after soldering and welding.Conclusion: Higher gauge wires and soldering method of union showed better mechanical properties than the othergroups and both soldering and welding method showed changes in the mechanical properties of the newlyfabricated wires when comparing them with their originals

المقدمة: تھدف ھذه الدراسة إلى المقارنة بین الخواص المیكانیكیة بین أربع مجموعات من الأسلاك المركبھ وفقا لطریقتھم في الاتحاد،وفقا لقیاسات الأسلاك وتم إجراء مقارنة بینھاوبین الاسلاك الاصلیھ.المواد والطریقھ: مجموعھ من 60 سلك مصنوع من مادة الفولاذ المقاوم للصدأ ، قسمت الى أربع مجموعات وفقا لقیاسات الأسلاك وطریقةاللحام، كل واحد منھم یتكون من 15 عینة،0.022 ) وفقا لبعض الضوابط والتي كانت: الطول، الوزن،ومدة النبض وحجم نحاس االاقطاب x0.016+ 0.022 و 0.018 x0.016+ تم لحم الاسلاك ذات القیاسات التالیھ ( 0.016المستخدمة (بلنسبھ للعینات الملحومھ عن طریق التیار الكھربائي) ومدة عملیة اللحام والبعد من مصدر الحراره (للعینات الملحومھ عن طریق الحراره).0.018-0.022 ) قیم عالیة بالمقارنة مع العینات الاخرى الاقل × النتائج:أظھرت النتائج للقوه القصوى المحتملھ ولقوة الشد القصوى للعینات الملحومھ عن طریق الحراره ( 0.0160.016-0.022 ) قیم عالیھ بلمقارنھ مع العینات الاخرى × حجما والملحومة عن طریق التیار الكھربائي, و اظھرت نتائج معامل المرونھ للعینات الملحومھ عن طریق الحراره( 0.016(0.016 -0.022 × الاكبر حجما الملحومھ عن طریق التیار الكھربائي , اما نتائج معامل الطاقھ المخزونھ فقد اظھرت قیم عالیھ للعینات الملحومھ عن طریق التیار الكھربائي ( 0.016وقد لوحظ انخفاضا في الخواصالمیكانیكیھ عند مقارنة الاسلاك المركبھ مع الاسلاك الاصلیة قبل اللحیم.الخلاصةأظھرت الأسلاك ذات القیاس الأعلى وأسلوب لحام عن طریق الحراره خواصامیكانیكیة أفضل من المجموعات الأخرى وعلى حد سواء عند مقارنة الاسلاك الجدیده مع النسخ الأصلیةالخاصة بھم اظھرت النتائج انخفاضا في الخواصالمیكانیكیھ بلنسبھ للاسلاك المركبھ الجدیده.


Article
Similar and Dissimilar Nd:YAGlaser Welding of NiTi Shape Memory Alloy to AISI 420Stainless Steel

Author: Jassim Mohammed Salman Al-Murshdy
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 1 Pages: 60-69
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Similar NiTi shape memory alloy(SMA) plates, 420 Martensitic stainless steelplates and dissimilar NiTi shape memory alloy with Martensiticstainless steel were welded by a pulsed Nd:YAGlaser welding method.The nature microstructure of the base metal (BM), weld zone (WZ), interface and the heat affected zones(HAZ) were showedby in a scanning electron microscope (SEM) and optical microscope.Vickers hardness tests wasconducted to specifythe properties of the weld. The outcomes showed that the hardness of dissimilar NiTi-Stainless steel (St.St.) weld is higher than that in similar NiTi-NiTi and St.St.-St.St. weld.TheMicrostructural examination in both NiTi-St.St. and NiTi-NiTi welds illustrates that the solidification process in the fusion zone changed the kind of plan to the cell type as well as the changes that occur in the cell to dentritic kind of intra- region of the weld through the weld center in the welded sample sides but in the St.St.-St.St. weld showed dendrite microstructure. In this study it is found that the increase of the welding speed leads to a decrease in hardness in all jointsNiTi-NiTi, NiTi-St.St. and St.St.-St.St.

صفائح متشابهة للسبيكة الذاكرة الشكل (نيكل تيتانيوم)، صفائح الفولاذ المقاوم للصدأ المارتنسايتي(420) والصفائح المختلفة من السبيكة الذاكرة الشكل (نيكل تيتانيوم) والفولاذ المقاوم للصدأ المارتنسايتي قد تم لحامها بطريقة اللحام الليزر النبضي. تم استخدام المجهر الالكتروني الماسح والمجهر الضوئي لاظهار البنية المجهرية لمعدنالاساس ومنطقة اللحام والمنطقة المتاثره بالحرارة والمنطقة البينيه. جرىاختبار صلادة فيكرز لتحديد خواص اللحام.اشارتالنتائج الى ان صلادة اللحام للنيكل تيتانيوم-الفولاذ المقاوم للصدأ هو اعلى من صلاده اللحام المتشابة نيكل تيتانيوم- نيكل تيتانيوم او الفولاذ المقاوم للصدأ- الفولاذ المقاوم للصدأ. البنية المجهرية لكلا النوعين من اللحام نيكل تيتانيوم – الفولاذ المقاوم للصدأ، نيكل تيتانيوم- نيكل تيتانيومظهرت نوع التجمد على طول منطقة الانصهارو تتغير من مستوي الخلوي الى شجيري ظمن الحد الفاصل لمنطقة اللحام الى الخط الوسطي للمنطقة نفسها وفي كلا الجانبين من نيكل تيتانيوم وكذلك الفولاذ المقاوم للصدأ، لكن البنية المجهرية تظهر على شكل شجيري في اللحام الفولاذ المقاوم للصدأ-الفولاذ المقاوم للصدأ.في هذه الدراسة وجد أيضا ان زيادة سرعة اللحام تؤدي الى تقليل الصلاده في الأنواع الثلاثة من الربط.


Article
THE EFFECT OF PULSED ND:YAG LASER WELDING ON SHEAR FORCE AND MICROSTRUCTURE FOR NITI SHAPE MEMORY ALLOY WITH 304L AUSTENITE STAINLESS STEEL WELDMENTS
تأثيرلحام الليزر النبضي على قوة القص والبنية المجهرية للحام السبيكة النيكل- تيتانيوم الذاكرة الشكل مع الفولاذ المقاوم للصدأ الاوستنايتي

Loading...
Loading...
Abstract

Dissimilar welding of austenitic stainless steel AISI 304L to shape memory alloy SMA NiTi was conducted by utilized Nd: YAG laser beam welding technique. Both AISI 304ASS and SMA have the same dimension (80*20*0.5) mm. The experimental investigation included tensile shear test and microstructure. The results demonstrate that the maximum shear force found in the sample (No/10) reach (2552 N) which has the better laser parameters in this research (peak power of (2.25 KW), pulse duration of (2.4 ms), pulse repetition rate of (40 Hz), and welding speed of (8 mm/Sec). SEM with optical microscope demonstrate the solidification method along the fusion area various in different joints, where they become the planer shape to cellular and transformed the last to dendritic from intra-fusion welding area toward the center because towards weld area interface to weld centerline cooling rate will be rise in all SMA (NiTi) and Austenite stainless steel (ASS) sides.

اجريت عملية لحام المعادن غير المتشابهة وهي الفولاذ المقاوم للصدء الاوستنايتي (304L) وسبيكة ذاكرة الشكل نيكل- تيتانيوم بواسطة استخدام تقنية اللحام باليزر النبضي (Nd:YAG). الفولاذ المقاوم الاوستنايتي وكذلك سبيكة ذاكرة الشكل كلاهما نفس الابعاد (80*20*0.5) mm. الاختبارات العملية شملت اختبار الشد, والبنية المجهرية. النتائج تظهر ان العينة العاشرة تعطي اعلى قوة قص تصل الى (2552N) التي نفذت خلال هذا البحث بمتغيرات هي (الطاقة العظمى (2.25KW), مدة النبضة (2.4ms), معدل تكرار النبضة (40Hz), سرعة اللحام (8mm/s). المجهر الالكتروني الماسح والضوئي يضهر ان التجمد عبر منطقة الانصهار يتغير من مستوي الى خلوي وشجيري بسبب الزيادة بمعدل التبريد من الحد الفاصل باتجاة مركز اللحام على جانبي الفولاذ المقاوم للصدء الاوستنايتي(304L) وسبيكة ذاكره الشكل نيكل – تيتانيوم .

Listing 1 - 10 of 13 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (13)


Language

English (10)

Arabic (2)

Arabic and English (1)


Year
From To Submit

2018 (5)

2017 (2)

2015 (1)

2014 (3)

2011 (1)

More...