Mechanical and Physical Properties of PZT/xAl2O3 Ceramics Systems
الخصائص الميكانيكية والفيزيائية لنظم (PZT/xAl2O3) السيراميكية

Author: Abdulkarim Ziedan Khalf عبد الكريم زيدان خلف
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2014 Volume: 10 Issue: 1 Pages: 84-90
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The compound of Ferroelectric nanopowrer Lead Zirconate Titanate (PZT) Pb(ZrxTi1-x)O3 was prepared using Oxalate method. Al2O3 was doped using solid state sintering method as general system PZT/xAl2O3 at (x= 0.5, 1, 1.5 vol. %). The effects of Al2O3 addition on the mechanical and physical properties of PZT ceramics were investigated. Increased Vickers Hardness with addition Al2O3 to PZT which its maximum hardness value was found for the samples containing 1vol. %Al2O3. Also, the maximum value of dielectric strength of containing 1vol.%Al2O3. This is indicating that the addition Al2O3 into PZT leads to improve dielectric properties of PZT ceramics. It is observed that the mechanical properties of the ceramics systems PZT/xAl2O3 are larger than of PZT ceramics

تم إعداد مركبات فيروكهربائية ذي الصيغة (Pb(ZrxTi1-x)O3) بأستخدام طريقة الاوكزالات. ثم إضافة (Al2O3) الى (PZT) بطريقة تفاعل الحالة الصلبة وحسب الصيغة (PZT/xAl2O3) وعند النسب (x= 0.5, 1, 1.5 vol. %). وقد تم التحقق من تأثير أضافة (Al2O3) الى (PZT)على الخصائص الميكانيكية والفيزيائية. زيادة الصلادة مع إضافة (Al2O3) الى (PZT) والذي عثر على أعلى قيمة للصلادة للعينات التي تحتوي (1vol.%) من (Al2O3). أيضا أعلى قيمة لمتانة العزل الكهريائي عند النسبة (1vol.% ) من (Al2O3 ), وهذا يدل على أن إضافة (Al2O3) الى (PZT) يؤدي الى تحسين خواص العزل الكهربائي لل (PZT). لوحظ أن الخواص الميكانيكية للنظام (PZT/xAl2O3) أكبر من (PZT).


Article
Study structural, dielectric and ferroelectric properties of Pb (Zr1-x Tix)O3 ceramics near the morphotropic phase boundary
"دراسة الخواص التركيبية والعزلية والفيروكهربائية لسيراميكPb(Zr(1-x)Tix)O3 بالقرب من الاطوار الحدودية"

Author: Abdulsamee Fawzi Abdul Aziz AL-Bayati عبدالسميع فوزي عبدالعزيز البياتي
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 3 Pages: 125-134
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In the present work, Pb(Zr(1-x)Tix) ceramics (x = 0.50, 0.48, 0.45 and 0.42) were prepared using the solid state reaction method, at the sintaring temperature (1100 oC ) for (6hr).X-ray diffraction results demonstrate that all the samples lie within the morphtropic phase boundary (MPB) region in the pure perovskite tetragonal structure with Miller transactions (100), (110), (111), (200), (210), (211), (220), (103) and (311) that the prevailing trend is (110) and the results of plasticity microwave very close sense of distance intra-convergent also relatively few crystalline defects. Increasing the bulk density of the true density of altered concentration of zirconium and titanium. Results of the examination microscope also showed that the particle size (Dnm) be tight between the samples and the homogeneity of the granules, as well as increasing the homogeneity of compositional structure, causing an improvement in the structural and electrical properties. Shown technique results EDAX compound of the interacting elements of the composition and there is little difference between the real weight and the weight is noticeable. The temperature and concentration of titanium dependences of the dielectric constant of the ceramics has been investigated in detail. Excellent dielectric properties have been obtained for the selected compositions. Polarization-Elctric field hysteresis studies were carried out for all compositions at room temperature. It was found that with the increase of concentration of titanium content in the composition the remnant polarization decreases and ferroelectric loops get constricted.

تم تحضيرسيراميك تيتانات زركونات الرصاص ذات الصيغة الكيميائية O3(Zr1-x Tix)Pb حيث أنّ (x = 0.5,0.48,0.45,0.42) وذلك بإستخدام طريقة تفاعلات الحالة الصلبة حيث تم تلبيد النماذج المحضرة عند درجة حرارة (1100˚C) ولمدة (12hr). حيث أظهرت نتائج حيود الاشعة السينية ان جميع النماذج الواقعة ضمن منطقة الاطوار الحدودية كانت ذات تراكيب بروفسكايت رباعية نقية ومعاملات ميلر (001), (100) , (110) , (111) ,(002) , (200) , (210) , (211) ,(220),(221), (103) وأن الإتجاه السائد هو(110) ونتائج المطاوعة الميكروية متقاربة جداً بمعنى المسافة البينية متقاربة أيضاً والتشوهات البلورية قليلة نسبياً. زيادة الكثافة الظاهرية عن الكثافة الحقيقية بإختلاف تركيز الزركونيوم والتيتانيوم. كما أظهرت نتائج فحص المجهر الألكتروني أنّ الحجم الحبيبي (Dnm) يكون متقارب بين النماذج وتجانس الحبيبات, بالاضافة الى ان زيادة تجانس البنية التركيبية قد سبب تحسننا في الخواص التركيبية والكهربائية. ان نتائج تقنية EDAX قد اظهرت تكوين المركب من العناصر المتفاعلة ، مع وجود اختلاف قليل بين الوزن الحقيقي والوزن الملاحظ . كما تم دراسة تاثير كل من درجة الحرارة وتركيز التتانيوم على ثابت العزل الكهربائي للمركبات السيراميكية بشكل مفصل. كما تم دراسة حلقات الهسترة الكهربائية ( P-E loop ) لجميع المركبات عند درجة حرارة الغرفة . أذ تبين ان زيادة تركيز نسبة التيتانيوم في المركبات الى تناقص مقدار الاستقطابية المتبقية والحصول حلقات محدودة.


Article
Manufacturing and study the structural and electrical properties of the compounds Pb (Zr, Ti)O3 prepared in a manner Powders
تصنيع ودراسة الخواص التركيبية والكهربائية لمركبات Pb(Zr,Ti)O3 المحضرة بطريقة المساحيق

Loading...
Loading...
Abstract

Was prepared lead Zrconat titanate compounds with the chemical formula Pb (Zr1-x Tix) O3 as (x = 0.5,0.48) and using technology the way powders were prepared Plasticizer models at a temperature (1000˚C) and for (6hr). physical tests of the models were conducted, where it was the study of the structural properties, in terms of X-ray diffraction measurements as results showed that all models were four-wheel installation (Tetragonal) with Miller transactions (001), (100), (110), (111), (002), (200), (210), (211), (220), (221), (103) and that the prevailing trend is (110) and the results of plasticity microwave very close sense of distance intra-convergent also relatively few crystalline defects. Increasing the bulk density of the true density of altered concentration of zirconium and titanium. Results of the examination microscope-mail also showed that the particle size (Dnm) be tight between the models and the homogeneity of the granules, as well as increasing the homogeneity of compositional structure, causing an improvement in the physical properties and A mechanical. shown technique results EDAX compound of the interacting elements of the composition and there is little difference between the real weight and the weight is noticeable. To study the electrical properties as included electrical properties study both the dielectric constant true of both types ('ε) and fantasy ("ε) as well as the loss of the separation (tanδ) and connectivity alternating (σac)

تم تحضير مركبات تيتانات زركونات الرصاص ذات الصيغة الكيميائية O3(Zr1-x Tix)Pb حيث أنّ (x=0.5,0.48) وذلك بإستخدام طريقة تكنلوجيا المساحيق حيث تم تلدين النماذج المحضرة عند درجة حرارة (1000˚C) ولمدة (6hr). أجريت الفحوصات الفيزياوية للنماذج, حيث تم دراسة الخواص التركيبية, بدلالة قياسات حيود الأشعة السينية إذ أظهرت نتائجها أنّ جميع النماذج كانت ذات تركيب رباعي(Tetragonal) ذات معاملات ميلر (001) , (100) , (110) , (111) , (002) , (200) , (210) , (211) , (220) , (221) , (103) وأن الإتجاه السائد هو (110) ونتائج المطاوعة الميكروية متقاربة جداً بمعنى المسافة البينية متقاربة أيضاً والتشوهات البلورية قليلة نسبياً . زيادة الكثافة الظاهرية عن الكثافة الحقيقية بإختلاف تركيز الزركونيوم والتيتانيوم . كما أظهرت نتائج فحص المجهر الألكتروني أنّ الحجم الحبيبي (Dnm) يكون متقارب بين النماذج وتجانس الحبيبات , وكذلك زيادة تجانس البنية التركيبية مسبباً تحسن في الخواص الفيزيائية والميكانيكية. أظهرت نتائج تقنية EDAX تكوين المركب من العناصر المتفاعلة وهناك فرق قليل بين الوزن الحقيقي والوزن الملاحظ . كما تمت دراسة الخواص الكهربائية إذ تضمنت الخواص الكهربائية دراسة كل من ثابت العزل بنوعيه الحقيقي ('ε) والخيالي("ε) وكذلك خسارة العازل (tanδ) والتوصيلية المتناوبة (acσ) .


Article
Studying the effect of Strontium Titanate on the Dielectric Constant of the Barium Titanate
دراسة تأثير اضافة تيتانات السترونتيوم على ثابت العزل الكهربائي لتيتانات الباريوم

Author: كنعان محمد موسى
Journal: journal of al-qadisiyah for pure science(quarterly) مجلة القادسية للعلوم الصرفة (فصلية). ISSN: 19972490 Year: 2016 Volume: 2 Issue: 21 Pages: 169-176
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

In this study, the effect of adding strontium titanate (SrTiO3) on the dielectric constant of the barium titanate (BaTiO3) was investigated. For this purpose, the BaTiO3 powder was first prepared by mixing barium carbonate (BaCO3) with titanium dioxide (TiO2) and sintering by vacuum furnace at 1200 ºC under Argon. Then, the SrTiO3 powder was prepared by mixing strontium carbonate (SrCO3) with titanium dioxide (TiO2) and sintering at 1150 ºC. Different weight percentages (5-50 %) of SrTiO3 were added into the BaTiO3 and mixed for 72 hour to prepare different mixtures of (BaSr)TiO3 for electrical insulators. All samples of (BaSr)TiO3 insulators were compacted and sintered at 5 tons and 1350 ºC, respectively. The crystalline structural characterizations of the prepared powders as well as the (BaSr)TiO3 mixtures were analyzed by the X-ray diffraction (XRD). Values of the dielectric contacts and the bulk density for all prepared mixtures were measured. The results showed that the electrical insulators made from the mixture of 30 % SrTiO3 and 70 % BaTiO3 revealed the highest electric constant with a reasonable density.

في هذا البحث, تمت دراسة تأثير إضافة تيتانات السترونتيوم (SrTiO3) على ثابت العزل الكهربائي للتيتانات الباريوم (BaTiO3). لهذا الغرض، تم تحضير مسحوق تيتانات الباريوم أولاً من خلط كاربونات الباريوم (BaCO3) مع ثاني أوكسيد التيتانيوم (TiO2) وتلبيدها بواسطة فرن مفرغ تحت الأركون عند 1200 درجة مئوية . ومن ثم تحضير تيتانات السترونتيوم عن طريق خلط كاربونات السترونتيوم (SrCO3) مع ثاني أكسيد التيتانيوم (TiO2) وتلبيدها بدرجة 1150 مئوية. تمت إضافة نسب وزنية مختلفة (5-50٪) من تيتانات السترونتيوم الى تيتانات الباريوم وخلطها لفترة 72 ساعة من اجل اعداد خلطات مختلفة من (BaSr)TiO3 لتصنيع العوازل الكهربائية. جميع العينات حضرت بضغط كبس مقداره 5 طن ولبدت بدرجة حرارة مقدارها 1350 مئوية. تم اجراء تحليل حيود الأشعة السينية (XRD) للمساحيق المحضرة ولمسحوق (BaSr)TiO3 المعتمد لتحضير العوازل, كذلك قياس قيم ثابت العزل الكهربائي والكثافة الظاهرية لجميع الخلطات المحضرة. أظهرت النتائج أن العوازل الكهربائية المصنوعة من خليط 30٪ SrTiO3 و 70٪ BaTiO3 بانها تمتلك أعلى ثابت عزل كهربائي بكثافة معقولة.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

Arabic (2)

English (2)


Year
From To Submit

2016 (3)

2014 (1)