STATE SOME MECHANICAL PROPERTIES FOR Al- ALLOY WELDED BY SEAM WELDING TECHNIQUE
حالة بعض الخواص الميكانيكية لسبائك الألمنيوم الملحومة بطريقة اللحام الخطي

Author: Latfe Y .Zedan لطفي يوسف زيدان
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2010 Volume: 3 Issue: 1 Pages: 80-90
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The aim of this paper was perpetrated lap joint welding samples welded by seam welding method ,2014 heat treatable aluminum alloy ,the paper studied some groups at different variable welding ,welding time was studied at electrode pressure 1,1.5 KN with thickness 1.5 mm and another group at 2 mm .after welding process shear strength ,Vickers hardness were tested at different variables.The paper stated the best shearing strength at 1.5mm thickness with 45 KA welding current at 1.5 KN electrode pressure. Increase 0.5 mm in thickness lead to decrease 20% of shearing strength.

تهدف الدراسة الحالية إلى تحضير وصلات لحام تراكبية ملحومة بطريقة اللحام الخطي ,حيث تم استخدام سبيكة الألمنيوم (2014) القابلة للتعامل الحراري ,تم دراسة متغيرات عملية اللحام وفق مجاميع مختلفة . تم دراسة زمن اللحام عند ضغط اليكترود ،KN(1,1.5) بسمكmm 1.5 والمجموعة الأخرى بنفس الظروف ولكن بسمك (2MM) وبعد إجراء عملية اللحام تم حساب مقاومة القص بالظروف المختلفة وكذلك حساب الصلادة المجهرية عند خط اللحام وبجانبه .ومن الدراسة لوحظ أن أفضل مقاومة قص لوصلة اللحام كانت عند سمك mm 1.5 وتيار لحام KA45 عند 1.5 KN ضغط اليكترود. كما لوحظ أن زيادة السمك بmm 0.5 تنخفض قيمة مقاومة القص إلى 20%.


Article
EFFECT OF ADDING COPPER FOILS ON SEAM WELDING JOINTS OF 304 AUSTENITIC STAINLESS STEEL
تأثيـــر أضافــة رقائـق النحـــاس على وصـــلات اللـحام الخـطــي للصــلب المقــاوم للصـــدأ الأوســتنايتي نوع 304

Loading...
Loading...
Abstract

The aim of this work is to study the effect of adding copper (C10200 AISI) foils on the welding joint of the austenitic stainless steel type (AISI 304).The austenitic stainless steel has low weldability by resistance welding where the concentrated current causing a high thermal expansion. Due to heat stored, non-complete fusion, burn throw, warp edge and distortion of weldments even when change machine settings. So to solve this problems a copper strips used as a filler metals between the stainless steel sheets, these problem disappears, because of that strip will be act as a heat sink and no burn through; but complete fusion, uniform weld.

يهــدف البحـث الى دراســة تأثير إضافة رقائق من النحاس الى وصلة اللحام الخطي للصـلب المقـاوم للصـدأ الأوستنايتي نوع304) ). أن الصـلب المقــاوم للصدأ الأوستنايتي يمتلك قابليــة لحام واطئة عند استخــدام طرق اللحـام بالمقاومـة الكهربائيـة لان التيار المتركز في منطقة اللحام يؤدي الى تمدد حراري عالي. وبسبب الحرارة المتولــدة من ذلك فأن رقائق الصـلب المقــاوم للصدأ تعاني من اللحام غير المنتظم الذي يؤدي الى عـدم اكتمال الانصهار في بعض المواضع أوالأحتراق في مواضع أخرى وتشوه الشكل الخارجي للملحومة. وهذه المشاكل لا تختفي حتى أذا تم تقليل تيار اللحام الى أقل قيمة له. ولحــل هذه المشكلة تــم أستخدام شـرائط رقيقــة من النحـاس بين رقائق الصـلب المقــاوم للصـدأ الأوستنايتي لتسهيــل عمليــة تسريب الحرارة خلال المعـدن وحصول انصهار كامل ولحام منتظم لوصلــة اللحـــام التي تحسنت بواسطة هذه الإضافة.