In the present work, the study of some rheologyical and Mechanical properties for(unsaturated Polyester-Wood Excelsior) composite materials .the chemical treatment to wood excelsior by using solution of (NaCl)by percent (0.5) at (85C ) for(4hr) to different percentages (2–10) % g/ml. the rate grain- size for Wood Excelsior was remained constant at (50mm)for all groups.The rheologyical properties for composite materials Polyester-Wood Excelsior which include, the density and shear viscosity were measured by using Ostwald Viscometer.The mechanical properties, the Ultrasonic velocity had been measured by Ultrasonic waves system with frequency (26KHz), we calculate theoretically , absorption coefficient , relaxation time, relaxation amplitude , compressibility, bulk modulus, and specific acoustic impedance. At room temperature (20C). The results showed that all properties composite materials(Polyester-Wood Excelsior increase exponentially or linearly by increasing of concentration while velocity, specific acoustic impedance and bulk modules decrease by increasing concentration. This study show association between polyester-Wood Excelsior and solvent molecules, and also between polyester molecules it self .

في البحث الحالي تم دراسة بعض الخواص الريولوجية والميكانيكية لمتراكب البولي أستر غير المشبع - نشارة الخشب حيث تم معالجة كيماوية لنشارة الخشب باستخدام محلــول (NaCl) بنسبة 0.5 عند درجة الحرارة 85oC)) لمدة أربعة ساعات ولمختلف التراكيز ml/g (2-10)% مع بقاء معدل الحجم الحبيبي لنشارة خشب ثابت في جميع المجموعات مقداره μm. 50 أن الخواص الريولوجية اشتملت الكثافة واللزوجة القصية التي قيست بواسطة استخدام مقياس اللزوجة أستولد.أما الخواص الميكانيكية لمتراكب البولي أستر – نشارة الخشب فقد تم قياس سرعة الموجات فوق السمعية باستخدام تقنية الموجات فوق السمعية ذو التردد (26khz) وتم نظريا حساب معامل الامتصاص وزمن الاسترخاء وسعة الاسترخاء الانضغاطية ومعامل المرونة والممانعة الصوتية النوعية للموجات فوق السمعية عند درجة حــرارةالغرفة (20 oC). أظهرت النتائج أن جميع الخواص المذكورة آنفاً لمتراكب البولي أستر غير المشبع - نشارة الخشب تزداد مع زيادة التركيزأسيا اوخطيا أما السرعة والممانعة الصوتية النوعية ومعامل المرونة لمتراكب البولي أستر غير المشبع - نشارة الخشب حيث وجد أنها تتناقص مع زيادة التركيز.وهذه النتيجة تبين وجود اندماج داخلي بين الجزيئات البولي أستر وجزيئات النشارة وكذلك بين جزيئات البولي أستر وحده.

: البولي أستر --- المعالجة السطحية --- نشارة الخشب --- والمواد المركبة . --- Polyester --- surface treatment --- wood excelsior --- composite materials

Improving the bonding strength can be achieved by surface treatment of fibers . Etching is one of the methods of this treatment , in this investigation wet etching of E-glass fibers and polyamide fibers carried out by using (H2O + NaOH) solution to get pits on their surface to increase the surface roughness . Group of tests was carried out to study the effect of this treatment on the mechanical (bending and impact) properties of a material composed of unsaturated polyester reinforced by (10 % wt) of etched glass fibers and Etched polyamide fibers . Also Calculation of the weight loss and executing of microscopic photo .The results show :- Increase of the bending strength of etched glass fibers reinforced composite materials with a maximum percentage of (301 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the bending strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (155 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1.5 % NaOH) and (3 hr) .- Increase of the impact strength of etched glass fibers reinforced composite materials with a maximum percentage of (270 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the impact strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (232 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (0.5 % NaOH) and (5 hr) .- Increase of the weight loss of polyamide fibers than weigth loss of glass fibers .

يتم تحسين مقاومة الربط بالمعاملة السطحية للالياف . التحفير (Etching) احد اساليب هذه المعاملة حيث تم في البحث الحالي التحفير الرطب لالياف زجاج نوع (E-glass) والياف بولي اميد باستخدام محلول (H2O+NaOH) للحصول على حفر تزيد من الخشونة السطحية . اجريت مجموعة من الاختبارات لدراسة تأثير التحفير على الخواص الميكانيكية (انحناء وصدم) للمادة المركبة ذات اساس من البولي استر غير المشبع المقواة ب(10 % wt) الياف زجاج محفرة والياف بولي اميد محفرة . كذلك تم حساب الفقدان بالوزن واجراء تصوير مجهري . اظهرت نتائج الاختبارات ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (301 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (155 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1.5 % NaOH) ولمدة (3 hr) . كما اظهرت نتائج الاختبارات ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (270 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (232 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (0.5 % NaOH) ولمدة (5 hr) . كذلك اظهرت النتائج ارتفاع نسبة الفقدان بالوزن لالياف البولي اميد اكثر من نسبة الفقدان بالوزن لالياف الزجاج .

wet etching --- surface roughness --- surface treatment --- glass fibers --- polyamide fibers --- bending test --- impact test and composite materials. --- التحفير الرطب --- الخشونة السطحية --- المعالجة السطحية --- الياف الزجاج --- الياف بولي اميد --- اختبار الانحناء --- اختبار الصدم والمواد المركبة .