Article
Fracture Toughness and Hardness studying for Polymer-Ceramic Composite
دراسة متانة الكسر والصلادة لمتراكب بوليمر- سيراميك

Authors: Khalid R. Al-Rawi خالد رشاد الراوي --- Ali A. bander علي عباس بندر --- Samara J. Aljoboury سمارة جاسم الجبوري
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2014 Volume: 11 Issue: 2 عدد خاص بالمؤتمر النسوي الثاني Pages: 547-553
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

A particulate composite material was prepared by adding the Titanium dioxide (TiO2) with a particle size of (75-150) µm to Epoxy resin at weight percentage of (10%,20%,30%,40%,50%).The following some mechanical properties were studied,fracture toughness, hardness.casting preparation methods were used in this study includes preparing plate of matrix and composites. specimens were prepared according to ASTM for the Mechanical properties tests. After that Another samples were heat treated for three and six hour at 65Cο.Fracture toughness (Kic) represent for stress intensity factor results were showed that the curve of three hours aging increases in fracture toughness (Kic) for composites but for six hours aging increases fracture toughness (Kic) for polymer matrix. Hardness tests was showed that hardness results increased with the increase in weight fraction while a samples that not treated thermally have higher hardness than the samples for treated thermally. Finally, fracture surfaces were showed morphology failure surfaces by using an optical Microscope.

تم تحضير مادة متراكبة بوليمرية دقائقية عن طريق اضافة مسحوق مادة TiO2بحجم حبيبي (75-150) µm إلـى راتنـج الايبوكسي وبنسب وزنية تبلغ (%50 ,%40, %30 ,%20 , %10) ولقد تمت دراسة بعض الاختبارات الميكانيكية المتمثلة باختبار متانة الكسر والصلادة .أستخدمت طريقة الصب خلال هذه الدراسة لاعداد الواح ذات اشكال مربعة من المادة الاساس والمتراكبات ثم تم تقطيعها الى عينات قياسية وفقاً للموصفات العالمية لغرض استخدامها في الفحوصات. وبعد ذلك تمت معاملة العينات حرارياً لفترة ثلاث ساعات وست ساعات بدرجة حرارة Cο 65.عند أجراء اختبارات متانة الكسر (Kic) المتمثلة بايجاد معامل حساسية شدة الاجهاد عند مقدمة الشق فكانت النتائج على شكل منحنى قيم(Kic) وسجلت المتراكبات المعاملة لمدة ثلاث ساعات اعلى قيم عن مثيلاتها بينما سجلت المادة الاساس والمعاملة لمدة ست ساعات اعلى متانة كسر. بينما كانت نتائج فحوصات الصلادة هي الزيادة بزيادة النسب الوزنية وسجلت العينات غير المعاملة حرارياً صلادة اعلى من غيرها. وتم أخذ صور مجهريه لسطوح الكسر ودراسة تركيبها باستعمال المجهرالضوئي.


Article
Effect of Quenching on the forming limit diagram of Aluminum alloy sheets(2024 T3)
تأثير عملية الإخماد على مخطط حد التشكيل لصفائح من سبيكة الألمنيوم (T3 2024)

Authors: T. F. Sultan ثائر فائز احمد --- W. J. Ali وليد جلال علي
Journal: AL Rafdain Engineering Journal مجلة هندسة الرافدين ISSN: 18130526 Year: 2009 Volume: 17 Issue: 1 Pages: 22-33
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Quenching is known as the most critical step in the sequence of heat-treating operations. The objective of quenching is to preserve the solid solution formed at the solution heat-treating temperature, by rapidly cooling to some lower temperature, usually near room temperature. The scope of this study is to construct the forming limit diagram experimentally for aluminum alloy (2024-T3) sheet, as received and after Quenching from solid solution temperature. The results which have been obtained experimentally showed that at (6 hours) after Quenching, there is a considerable effect on the FLC, Quenching increases the FLC at the as received condition in the range of (19-31 %) . الكلمات الدالة: مخطط حد التشكيل ، الإخماد، المعاملة الحرارية المحلولية .

الخلاصة يعرف الإخماد (Quenching) من درجة الحرارة المحلولية بأنه الخطوة الأحرج في تتابع عمليات المعاملة الحرارية المحلولية والهدف من الإخماد هو لحفظ تشكيل المحلول الجامد المكوّن عند درجة حرارة المعاملة المحلولية الحرارية ، ويتم ذلك بالتبريد السريع إلى درجة حرارة الغرفة. الهدف من هذا البحث هو تعيين منحني حد التشكيل عمليا لصفيحة من سبيكة الألمنيوم (2024-T3) كما مستلمة وكذلك إنشاؤه بعد إجراء عملية الإخماد من درجة الحرارة المحلول الجامد ودراسة تأثير عملية الإخماد على منحني حد التشكيل. واختيرت هذه السبيكة لكثرة استخدامها وخاصة في هياكل الطائرات. أشارت النتائج التي تم الحصول عليها في الجانب العملي خلال هذه الدراسة إلى أن عملية الإخماد وبعد مرور 6 ساعات على إجراءها لها تأثير ملموس على منحني حد التشكيل، اذ أدت إلى زيادة في منحني حد التشكيل للسبيكة كما مستلمة (أي بدون المعاملة الحرارية) وكانت هذه الزيادة تتراوح بين (19 and 31 %).


Article
The Effect of Increasing Carbon Concentration Increasing on the Mechanical Properties of TiCx Thin Films
تأثير زيادة نسبة الكاربون على الخواص الميكانيكية لكاربيد التيتانيوم المنجز بالافلام الرقيقة

Author: احمد محمد حسن الغبان
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2013 Volume: 9 Issue: 1 Pages: 94-100
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Carbides or nitrides thin films present materials with good mechanical properties for industrial applications as they can be coatings at low temperatures serve temperature sensitive surfaces. In this work the effect of the C percentage on the mechanical properties represented by the Young modulus (E) of combinatorial magnetron sputtered TiCx (34%x˂65%) has been studied. The structure of the produced films is TiC independent on the C concentration. The mechanical properties are increased with increasing the C concentration up to 50%, and then decreasing with further C % increasing. These results can be explained by considering the resultant residual stresses.

تمثل الافلام الرقيقة المكونة من مواد كاربيدية او نايتريدية ذات اهمية فائقة في مجال الصناعة لما لها من خواص ميكانيكية ممتازة مثل الصلادة اضافة الى امكانية الطلاء بدرجات حرارية واطئة تخدم السطوح الحساسة لدرجات عالية. في هذا البحث تمت دراسة تاثير نسبة الكاربون على الخواص الميكانيكية ممثلة بمعامل المرونة لافلام رقيقة من كاربيد التيتانيوم المنتج بواسطة التذرية المغنترونية لمدى معين من التراكيب الكيمياوية. وقد لوحظ ان هنالك استقرارية للخواص البنيوية للطور الناتج مع نسبة الكاربون المضافه حيث ان الطورالناتج هو في الغالب لكاربيد التيتانيوم بغض النظرعن نسبة الكاربون من حدود 34% الى غاية اقل من 65%. لوحظ ارتباط الخواص الميكانيكية للطورالكاربيدي بنسبة الكاربون. حيث تزداد الخواص الميكانيكية ( تزداد الصلادة) للطورالمنتج لغاية نسبة كاربون بمقدار 50% وثم تبدا بالتناقص بنسب كاربون اعلى. قد تشير هذه النتائج الى علاقة وثيقة بين الخواص البنيوية (Microstructure) والميكانيكية من جهة وبين الاجهادات المتبقية في الفلم الناتج من جهة ثانية.


Article
The Effect of Heat Treatments on the Corrosion Rate of Hypo-eutectoid Steel in the Water and Salt Environments
تأثير المعاملات الحرارية على مقاومة التأكل للصلب تحت اليوتكتويدي في أوساط ملحية ومائية

Loading...
Loading...
Abstract

The aim of this work is to study the effect of three types of heat treatments (Annealing-Quenching-Tempering) on the Hypo-eutectoid steel corrosion rate in water and salt solutions. The results showed that the maximum corrosion rate was registered for the steel samples treated by quenching in both solutions, and minimum corrosion rate for tempered samples, while the corrosion rate of annealed steel samples was between them. It was found also the corrosion rate of all samples were exposed to salt solution was greater than that in water solution. The results showed also that the corrosion rate of all samples decrease with increasing the time of exposing to the corrosion media. This is because the corrosion product which form the isolation film protect the metal from further corrosion.

في هذا البحث تم دراسة تأثير ثلاثة انواع من المعاملات الحرارية أجريت على عينات من الصلب تحت اليوتكتويدي وهي التقسية والتلدين والمراجعة على معدل تأكلها في الاوساط المائية والملحية وقد أظهرت النتائج التي تم الحصول عليها بأن اكبر معدل للتأكل سجلت هي للصلب الكربوني الواطئ عند اخمادها في الماء0،وأقل معدل للتأكل كان للصلب المعامل بالمراجعة بينما كان معدل تأكل الصلب المعامل بالتلدين متوسطاً بينهما وقد تم قياس التأكل بطريقة فقدان الوزن، كما أظهرت النتائج بان معدل التأكل لجميع العينات كان أكبر عند تعريضها الى وسط التأكل (الماء المالح) بينما سجلت معدلات تأكل أقل في حالة وسط التأكل (ماء الشرب) كما بينت النتائج بأن معدل التأكل في جميع العينات يقل مع زيادة فترة التعريض الى وسط التأكل الى (4 – 5) أشهر وذلك بسبب ظهور ترسبات كلسية على سطح المعدن تعمل كطبقة عازلة تحمي المعدة من التعرض الى الوسط وتقلل من معدلات التأكل.


Article
Effect of Thermal Treatment on Some Physical and Mechanical Properties of Cermet Coating by Flame Spraying Technology

Authors: aSameen F. Mohammed --- bSalih Y. Darweesh
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 7 Pages: 269-268
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this research, thermal flame spraying technology was used for the purpose of producing a ceramic composite material produced from a mixture of ceramic material Al2O3, 25% and 50% with Ni-Al bonding material by 75% and 50% respectively, Coating through tests. The paint was made of graphite after it was tarnished by teething method. The spraying distance was 12 cm. The thermal treatment of the coated samples was at 1000 ولفت and for a period of two hours only. Through the tests of porosity, hardness and x-ray resistance, it was found that the best ratio of ceramic coating was in the ratio (50% alumina) with (50% of the bonding material).Where the best porosity was about 50% of the alumina and of the bond material as it reached 10.52%, the best hardness was also at 50% of the alumina and 50% of the bonding material as it reached 47.48Hv, the thermal treatment helped reduce the porosity to 7.44% and increased the hardness to 56.22Hv at the rate of 50% of the alumina and 50% of the bonding material, Finally the thermal treatment at (1000 ℃ ) and for two hours helped improve the crystalline uniformity at the angles of diffraction of defects.

تم في هذا البحث استخدام تقنية الرش الحراري باللهب لغرض انتاج مادة مركبة سيرميتية ناتجة من خليط مادة سيراميكية هي الألومينا Al2O3 بنسبة 25%، 50% مع مادة رابطة معدنية من(Ni-Al) بنسبة 75%،50% على التوالي والتعرف على افضل نسبة طلاء من خلال الفحوصات. قواعد الطلاء كانت من الكرافيت بعد ان تم تخشينها بطريقة التسنين، اما مسافة الرش كانت 12 سم، والمعاملة الحرارية للعينات المطلية كانت عند (1000) ولفترة زمنية مقدارها ساعتين فقط. من خلال اختبارات المسامية والصلادة وحيود الاشعة السينية وجد ان افضل نسبة طلاء سيرميتية كانت عند النسبة (50% الومينا) مع (50% من المادة الرابطة), حيث ان افضل مسامية كانت عن النسبة 50% من الألومينا و من المادة الرابطة اذ وصلت الى 10.52%, افضل صلادة ايضا كانت عند النسبة 50% من الألومينا و50% من الماده الرابطة اذ وصلت الى 47.48Hv, المعاملة الحرارية ساعدت الى تخفيض نسبة المسامية الى 7.44% وعملت على رفع قيمة الصلادة الى 56.22Hv عند النسبة 50% من الألومينا و50% من المادة الرابطة، واخيرا فأن المعاملة الحرارية عند ((1000 ◦C ولزمن ساعتين ساعد على تحسن في الانتظام البلوري عند مواقع زوايا الحيود دلالة على تجانس طبقات الطلاء وخلوها من العيوب.


Article
Tensile Strength Determination of heat Treated Austenitic Stainless Steel AISI 316L Using (ABI) Method
ايجاد مقاومة الشد القصوي للصلب المقاوم للصدأ اللاوستنايتي AISI 316L المعامل حراريا وذلك باستخدام تقنية (ABI)

Author: Ramadhan H. Gardi رمضان حسين الجردي
Journal: AL Rafdain Engineering Journal مجلة هندسة الرافدين ISSN: 18130526 Year: 2012 Volume: 20 Issue: 2 Pages: 98-105
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

AbstractIn this study, austenitic stainless steel AISI 316L has been selected to investigate the effect of aging time and temperature on tensile strength using (ABI) technique. Heat treatment consisted of aging at temperature of 400 oC, 600 oC and 800 oC and socking time for 0.5, 1.5, 10, 24 and 72 hrs.For microstructure examination, an optical microscope were used. The results showed that with increasing the aging time at 400 oC and 600 oC the tensile strength will increase but this approach inverted at 800 oC. These results could be attributed to some metallurgical transformation that occurs during heat treatment like changing in grain size, carbide and nitride precipitation along the grain boundaries, and secondary austenite.KEY WORDS: Tensile strength, 316L, austenitic stainless steel, ABI, heat treatment

الخلاصةفي هذه الدراسة استخدمت سبيكة الصلب المقاوم للصدا الآستنايتى AISI 316L لتحديد تاثير التغيرات الميتالورجية التى تحصل نتيجة المعاملات الحرارية علي مقاومة الشد القصوي وذلك باستخدام تقنية (ABI) (Automated Ball Indentation). المعاملة الحرارية تتكون من التعتيق في ثلاث درجات الحرارية المختلفة (400 oC,600 oC,800 oC )و لخمسة فترات زمنية مختلفة (0.5,1.5,10,24,72)ساعة لكل درجة.اضهرت النتائج بان زيادة زمن التعتيق من oC 400 و 600 oC ان مقاومة القصوي تزداد و لكن المادة تتصرف عكس ذلك في درجة الحرارة 800 oCوان اسباب هدة النتائج تعود بشكل اساسي الي التغيرات الميتالورجية في الصلب اللاوستنايتي ومن بين هدة التغيرات التحولات الطورية,تغير حجم البلورات ،ترسيب كاربيدات ونتريدات علي حدود البلورات،.......الخالكلمات الدالة:مقاومة الشد،الصلب الاوستنايتيكى،ABI،المعاملة الحرارية


Article
The Influence of Annealing and Doping by Copper on Electrical Conductivity of CdTe Thin Films
تأثير التلدين والتشويب بالنحاس فى التوصيلية الكهربائية لأغشية CdTeالرقيقة

Author: Bushra. K.H.Al-Maiyaly بشرى كاظم حسون الميالي
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2015 Volume: 28 Issue: 1 Pages: 33-42
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research CdTe and CdTe: Cu thin films with different doping ratios (1, 2, 3, 4 and5) %, were deposited by thermal evaporation technique under vacuum on glass substrates atroom temperature in thickness 450 nm.The measurements of electrical conductivity (σ), and activation energies (Ea1, Ea2), havebeen investigated on (CdTe) thin films as a function of doping ratios, as well as the effect ofthe heat treatment at (373, 423, and 473) K° for one hour on these measurements werecalculated and all results are discussed.The electrical conductivity measurements show all films prepared contain two types oftransport mechanisms, and the electrical conductivity (σ) increases whereas the activationenergy (Ea) would decrease as the increasing (Cu) percentage in the sample except 5%. It isalso noticed that the electrical conductivity (σ) showed a decreasing trend with increasingannealing temperature, while the activation energies (Ea1, Ea2) showed opposite trend, wherethe activation energies increased with annealing temperature. Also the electrical conductivityvalues was found increased about 3- 4 orders when pure CdTe films are doped with (3, 4) %Cu and annealing at 473 K°.

في هذا البحث حضرت اغشية CdTe الرقيقة غير المشوبة والمشوبة بالنحاس بنسب تشويب مختلفة (1,2,3,4, 5) %بتقنية التبخير الحراري بالفراغ على ارضيات من الزجاج وبسمك 450nm عند درجة حرارة الغرفة . وحسبتقياسات التوصيلية الكهربائية (σ),وطاقات التنشيط(Ea1, Ea2) لاغشية (CdTe)دالة لتغيرنسب التشويب.وكذلك حسب تاثير المعاملة الحرارية بدرجات (373, 423, and 473) K° ومدة ساعة واحدة على هذه القياسات ونوقشت جميع هذه النتائج.وقد أظهرت قياسات التوصيلية الكهربائية ان لكل الاغشية المحضرة آليتين للانتقال الالكتروني ولوحظ زيادة التوصيلية الكهربائية مع نقصان طاقات التنشيط بزيادة نسبة (Cu) بالانموذج ماعدا النسبة 5%. كما لوحظ نقصان التوصيلية الكهربائية مع زيادة درجات حرارة التلدين ، بينما أظهرت طاقات التنشيط سلوكاُ معاكساُ,إذ أزدادت طاقات التنشيط مع زيادة درجة حرارة التلدين. كذلك وجد ان قيم التوصيلية الكهربائية تزداد بمقدار 3- 4 مراتب عند تطعيم اغشية CdTe النقية بنسبة (3, 4) % Cu وتلدينها عند درجة حرارة 473 K°.


Article
تأثير المعاملة الحرارية الايزوثيرمية السريعة والمحلولية (T6) على خواص السبيكة (A319) المنتجة بطريقة السباكة بالضغط

Authors: محمد مهنا متعب --- نجيب سلمان عبطان --- رائد نجيب رزوقي
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2015 Volume: 22 Issue: 2 Pages: 74-80
Publisher: Tikrit University جامعة تكريت


Article
EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE
تأثير النسب الوزنية لمادة الزجاج والمعاملة الحرارية على الخواص الميكانيكية ومعدل البلى لمتراكبات الألمنيوم - 2% كرافيت

Author: Hashim Shukur Hammood هاشم شكر حمود الكرغولي
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2017 Volume: 10 Issue: 4 Pages: 33-41
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research studied the effect of the Heat Treatment on the Mechanical Properties and the Wear Rate of the pure Aluminum with a particle size of (≤53μm). The Aluminum is reinforced by graphite with a particle size of (≤63μm) with an addition of glass particles with different weight ratios of (3, 6, 9, and 12) Wt. % and a particle size was (≤ 53μm).Powder metallurgy technique has been used to manufactured the samples, where the samples are pressed uniaxial at room temperature with (500 Map), then sintering at (550 C0) for (2 hr.). After that, heat treatment is applied on the samples at (500 OC) for one hour and Quenched in water.There was a great improvement of the mechanical properties such as the hardens and the compressive strength. This improvement was proportional with the Weight ratio of the glass particles before and after the Heat Treatment.On the other hand, there was a decrease of the wear rate versus the increase of the Weight ratio of the glass particles and heat treatment.

يهدف هذا البحث الى دراسة تأثير اضافة دقائق الزجاج بنسب وزنية مختلفة Wt%(3,6,9,12) بحجم (≤53 μm) مع اضافة نسبة وزنية ثابتة % 2 من كرافيت بحجم جسيمي(≤ 63 μm) وتأثير المعاملة الحرارية على الخواص الميكانيكية ومعدل البلى للالمنيوم النقي وبحجم جسيمي (≤53 μm) .استُخدمت تقانة ميتالورجيا المساحيق لتصنيع النماذج اذ كبست النماذج على البارد بضغط كبس ( Mpa500) تم تلبيدها بدرجة حرارة (550 Co) ولمدة ساعتين ثم سُخنتْ النماذج الى درجة حرارة (500 Co) لمدة ساعة واحدة ثم بردت بالماء.بعدَ اجراء فحص الصلاده ومقاومة الانضغاط اظهرت النتائج حدوث تحسن كبير في الصلاده ومقاومة الانضغاط مع زيادة نسب اضافة دقائق الزجاج الى المتراكب قبل وبعد المعاملة الحرارية.تبين من خلال اختبار البلى حدوث انخفاض واضح مع زيادة نسب الاضافة قبل وبعد المعاملة الحرارية.


Article
Effect of partial heat treatment on the mechanical properties of high carbon tool steel used in manufacturing active parts in cold work tool steel dies
تأثير المعاملة الحرارية الجزئية على الخواص الميكانيكية لصلب العدة عالي الكربون المستخدم في صناعة الأجزاء الفعالة لقوالب القطع على البارد

Author: نيفين جمال الونداوي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 5 Pages: 181-189
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Effect of partial heat treatment on the mechanical properties of high carbon tool steel used in manufacturing active parts in cold work tool steel dies was investigated in this work. High carbon alloy steel (X210Cr12) classified as(QN1.2080) according to (DIN) was used for machining specimens withdimensions (5×44×20mm).(18) specimens were insulated from the middle to the end by graphite with (5mm)thickness and (18) specimens were insulated by ceramic (Al2O3 + Kaolin) with(5mm) thickness. The distance between the middle to the sharp edge was notinsulated. All these specimen were subjected to heat treatment, They show that canobtain hardness (65HRC) for the sharp edge at (980oC) after the specimens werequenched in oil. Stress relive was subjected to all specimens , it has been shownduring heating between (100-200oC) There is no big effect on the hardness and thestrength was increased, also when heating temperature increase up to (600 C ) thehardness decrease at (30 HRC) .Rockwell hardness test was employed to all specimens, at four locationsfor each specimen. The first location is at distance (10mm) from the sharp edge andthe second at (20mm) from the sharp edge within un insulated part. The thirdlocation is at (30mm) and the forth at (40mm) from the sharp edge withininsulated part.The best values of hardness for the insulated specimen with graphite are(65,64HRC) within the un insulated part and (47,48 HRC) within the insulatedpart. For the specimen with ceramic insulation the hardness values are (65,64HRC) within the un insulated part and (51,52 HRC) within the insulated part.The results of this work was applied on the active parts of some pressworking sheet metal dies, produced in central tool room plant/Nasser statecompany, it has been shown that the life and fracture strength of these parts (punch,die and stripper) were increased and improved.

تم اجراء الم عاملة الحرارية الجزئية ودراسة تاثيرها على الخواص الميكانيكية لصلب(X210Cr العدة عالي الكربون في هذا البحث . استخدمت سبيكة الفولاذ عالي الكربون نوع ( 12الالماني في تشغيل عينات بابعاد (DIN) والمصنفة بالرقم ( 1.2080 ) حسب نظام ال5) ملم تم عزل العينات من المنتصف بواسطة نوعين من غلاف عازل، اذ تم عزل ×44×20)18 ) عينة بواسطة غلاف من الكرافيت بسمك ( 5ملم)، وعزلت ( 18 ) عينة اخرى بواسطة )غلاف من مادة سيراميكية (الومينا+كاؤولين) بسمك ( 5 ملم )، واجريت المعاملة الحرارية للسطحبالتسخين التدريجي، اذ تبين عند ((Sharp edge) الغيرمعزول (من المنتصف الى الحد القاطع65 ) بعد HRC) 980 ) يتم الحصول على اعلى قيمة للصلادة oC) التسخين الى درجة حرارةوتمت دراسة عملية ازالة الاجهادات (Quenching in oil) اجراء عملية الاخماد بالزيت100-200 ) لم يطرأ تغيير oC) اذ تبين عند التسخين الى درجة حرارة مابين (Stress relives)كبير على قيمة الصلادة وادت العملية الى زيادة المتانة بشكل ملحوظ . وانخفضت الصلادة الى.(600oC) 30 ) عند التسخين الى درجة حرارة HRC) ادنى معدل لها وهيلعينات البحث حيث تم تحديد اربع نقاط على (HRC) اجري اختبار صلادة روكويلسطح كل عينة، تبعد ال نقطة الاولى بمسافة ( 10 ملم ) عن الحد القاطع والنقطة الثانية ( 20 ملم )عن الحد القاطع ضمن السطح الغير معزول والنقطة الثالثة ( 30 ملم) والنقطة الرابعة ( 40 ملم )عن الحد القاطع ضمن السطح المعزول.65,64 )، من الحد القاطع الى المنتصف ضمن السطح الغير HRC) وسجلت قيم الصلادة48,47 ) ضمن السطح المعزول بالنسبة للعينات المعزو لة بغلاف كرافيتي . اما HRC) معزول، و65,64 ) من الحد القاطع الى HRC) العينات المعزولة بغلاف سيراميكي فقد سجلت قيم الصلادة51,52 ) من المنتصف الى نهاية العينة ضمن السطح HRC) المنتصف للسطح الغير معزول والمعزول. تم ملاحظة تقارب قيم الصلادة للعينات المعزولة بغلاف كرافيتي والعينات المعزولةبغلاف سيراميكي.تم اجراء المعاملة الحرارية الجزئية الذي تم التوصل اليها من خلال البحث للأجزاء الفعالة (ذكرلقوالب القطع والقوالب المرحلية التي ينتجها معمل القوالب والعدد (Punch &Die وانثى القالبالمركزي/شركة نصر العامة للصناعات الميكانيكية، حيث تم ملاحظة زيادة عمر الاجزاءالمذكورة وزيادة مقاومتها للكسر تحت ظروف العمل المختلفة.

Listing 1 - 10 of 10
Sort by
Narrow your search

Resource type

article (10)


Language

Arabic (7)

Arabic and English (2)

English (1)


Year
From To Submit

2018 (2)

2017 (1)

2015 (2)

2014 (1)

2013 (1)

More...