Measure of Thermoelectric Power of CdSe Thin Films that Prepared with Different Depositions Rate.
قياس القدرة الكهروحرارية لأغشية CdSe المحضرة بمعدلات ترسيب مختلفة.

Author: Raad Saedon Sabri رعد سعدون صبري
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2009 Volume: 3 Issue: 1 Pages: 103-107
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In this paper CdSe thin films have been prepared deposited on galas substrate by thermalevaporation technique at thickness 250 nm with different depositions rate ( 0.2,0.4,0.6,0.8,1,1.2) nm/sand substrate temperatures ( Ts) (300,373,423,473)K . Thermoelectric power were measured to thisfilms ,Seebak coefficient and activation energy were evaluated, the results shows that all films wereof n-type conductivity and activation energy increases with dispositions rate and substrate temperaturefilms prepared at 0.8 nm/s with 425 K and 1.2 nm/s with Ts (425 ,475 ) K , except that they wereof p-type conductivity .

:في هذا البحث تم تحضير أغشية CdSe على قواعد زجاجية بطريقة التبخير الحراري في الفراغ وبسمك nm 2.50 وبمعدلات ترسيب s / nm ( 0.2,0.4,0.6,0.8,1,1.2) ودرجات حرارة أساس مختلفة K ( 300,373,433,473 ) وحساب معامل سيباك وطاقة التنشيط وقد تبين أن جميع الأغشية وبكافة معدلات الترسيب هي من نوع ( n-type ) وان طاقة التنشيط تزداد مع زيادة كل من معدل الترسيب وزيادة درجات الحرارة الأساس عدا الأغشية المحضرة بمعدل ترسيب s / nm 0.8 ودرجة حرارة أساس K 452 والأغشية المحضرة بمعدل ترسيب s /nm 1.2 ودرجات حرارة أساس K 425,475 فقد كان من نوع p-type .