Inhibiting of C --steelL80 Corrosion by Using of Polyacrylamide and Thiophene -2- Carboxaldehyde
تثبيط تآكل C - SteelL80 باستخدام البولي اكريل امايد مع الثايوفين -2- كاربوكسي الديهايد -

Loading...
Loading...
Abstract

In this research Five steady weights (0.5) g. of polyacrylamide were mixed with five different volumes of thiophene-2-carboxildehyde (0.5, 1, 1.5, 2 and 2.5) ml to obtain five concentrations of inhibitor in (50)ml of 15% HCl. (C-Steel L80) bars were immersed in the prepared solution and the lost weights were calculated in different temperatures (40,60, 80 and 90) ℃ at different times (3, 4, 5 and 6)hrs. the covered surface area (θ)and the efficiency were calculated from the lose weights; then the thermodynamic constants were calculated. It was observed that the less corrosion was obtained by increasing the inhibitor concentration.

في هذا البحث استخدمت خمسة اوزان ثابتة (0.5)غم من البولي اكريل امايد ومزجها مع خمسة احجام مختلفة من ثايوفين-2-كاربوكسيل ديهايد (0.5,1,1.5, 2, 2.5)مل للحصول على خمسة تراكيز من المثبط في 50 مل من15% HCl وبعدها تم غمر سبائك (C-SteelL80)بالمحلول المحضر وتم حساب الاوزان المفقودة لدرجات حرارية مختلفة (40, “60, “80, “90)مل وازمنة مختلفة (3, 4,5, 6) ساعة ، ومن الاوزان المفقودة تم حساب الكفاءة ومساحة السطح المغطى (θ) وبعدها حسبت الثوابت الثرموديناميكية ولوحظ ان بزيادة تركيز المثبط يقل التآكل.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic (1)


Year
From To Submit

2018 (1)