Article
Manufacturing of Refractory Bricks from Iraqi Flint
تصنيع طابوق حراري من خام الفلنت العراقي

Author: E.M. Hadi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2017 Volume: 35 Issue: Special Issue 1 Pages: 161-171
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

It was done in this study the preparation of bricks refractory from Iraqi Flint and adding Iraqi white kaolin as a binding material in ratio (25, 30, 35, 40, 45)%. The samples were formed by dry pressing, dried at room temperature for 24hr then at (110)̊C for 6hr then fired at (1200)˚C with soking time for 2hr. Linear shrinkage, Apparent density, Porosity, water absorption and microstructure by (SEM) as physical properties, diametrical strength and surface roughness as mechanical testing, and thermal conductivity, linear thermal expansion and thermal shock resistance as thermal properties were studied in this study. According to (SEM) and (XRD) results, the refractories consist of mullite phase and glass phase. The results show the increase of linear shrinkage and decrease of apparent porosity and water absorption with the increasing of kaolin adding because of the increasing of ceramic raw material, which mean increasing of glass phase. For the same reason linear thermal expansion increase with the kaolin adding increasing.

في هذا العمل تم تحضير حراريات من خام الفلنت العراقي وبإضافة الكاؤلين العراقي الأبيض كمادة رابطة بالنسب الوزنيةالتالية %) 25,30,35,40,45 (، شكلت النماذج بطريقة الكبس الجاف و جففت عند درجة حرارة الغرفة ولمدة ) 24hr ( ومن ثمعند (110)̊C ولمدة ) 6hr ( ثم حرقت عند (1200)˚C ولزمن انضاج لمدة ) 2hr (. تم دراسة التقلص الطولي والكثافة الظاهريةوالمسامية ونسبة امتصاص الماء والبنية المجهرية بالمجهر الالكتروني الماسح كخصائص فيزيائية، ومتانة الكسر المحوريوخشونة السطح كخصائص ميكانيكية والتوصيلية الحرارية والتمدد الحراري الطولي ومقاومة الصدمة الحرارية كخصائصحرارية. أثبتت نتائج دراسة البنية المجهرية وحيود الاشعة السينية تكون الحراريات المحضرة من طور المولايت والطورالزجاجي. اظهرت النتائج ازدياد نسبة التقلص الطولي وانخفاض المسامية الظاهرية ونسبة امتصاص الماء مع زيادة نسبةالكاؤلين المضافة وذلك نتيجة لزيادة نسبة المادة الخام بمعنى زيادة الطور الزجاجي في المنتج الحراري. ولنفس السبب يزدادالتمدد الحراري الطولي بزيادة نسبة الكاؤلين المضافة.


Article
Effect of Zirconia (ZrO2) Addition on Some Characteristics of Iraqi Bauxite Refractories
تأثير إضافة الزركونيا (ZrO2 ) في بعض خصائص حراريات البوكسايت العراقي

Authors: شهاب أحمد زيدان الجبوري --- انتصار محمد خضير البدراني
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 14 Pages: 467-483
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Use Iraqi Bauxite (64.2%) Alumina was calculated at (1400 oC ) and Graingradient limited after add kaolin and Sodium Silicate to increase compaction bauxite grain and then addition different weight percentage from zirconia to mixture (0, 5, 10, 15, 20 %wt). The specimens were formed by using bi- axial pressing. These specimens were fired in two temperatures (1200 oC , 1400 oC) . Studies the physical properties (density and porosity), mechanical properties (Diametrical strength) and thermal shock,. Increasing of zirconia percentage leads todecreasing of porosity, and increasing of (density and Diametrical strength). also, thermal shock effective passively on diametrical strength, where diametrical strength decreasing with increasing shock temperature. Add zirconia effected on properties from two sides; first from side general characteristics and another from side made zirconium silicate phase

1400 ) وبتدرج oC) استعمل البوكسايت العراقي (% 64.2 الومينا) المحروق بدرجة حرارة حبيبي محدد بعد إضافة الكاؤولين وسليكات الصوديوم لزيادة ترابط حبيبات البوكسايت. أضيفت نسب وشكلت العينات بإتباع طريقة الكبس (wt% 20 ,15 ,10 ,5 , مختلفة من الزركونيا إلى الخليط ( 0 1400 ) . درست أهم oC , 1200 oC) المحوري ثم حرقت العينات بدرجتين حراريتين مختلفتين الخصائص الفيزياوية ( الكثافة ، المسامية ) ومتانة الكسر المحوري والصدمة الحرارية.لوحظ من خلال القياسات أن المسامية الظاهرية تناقصت بشكل بسيط مع زيادة نسبة الزركونيا 1400 ) فقد oC) 1200 ) أما عند حرق النماذج بدرجة حرارة oC) عند حرق النماذج بدرجة حرارة ظهر التناقص بشكل واضح . أما الكثافة ومتانة الكسر المحوري فقد ازدادتا مع زيادة نسبة الزركونيا المضافة .كذلك درس تأثير الصدمة الحرارية على متانة الكسر المحوري حيث لوحظ تناقص فيمتانة الكسر المحوري مع زيادة درجة حرارة الصدمة الحرارية. إن إضافة الزركونيا أثرت في صفات البوكسايت من ناحيتين الأولى من ناحية خصائصها العامة والأخرى من ناحية تكوين طور سليكات الزركونيوم نتيجة اتحادها مع الكرستوبلايت (الناشئ من حرق الكاؤولين) ومن سليكات الصوديوم المضافة.