This research deals with the study of the structural and optical energy gap of NiO nano films in thickness 100nm were deposited on a glass substrate using sol-gel spin coating technique . XRD results indicated that the films are polycrystalline and have cubic structure with a preferred orientation along (111) . The average grain sizes of the crystallites estimated form XRD data was found to lie in the range of 19.11-23.05 nm. Data of AFM indicate that the surface of films is smooth . The optical transmittance value of nano NiO film reaches to 94% in the VIS and NIR regions, while it is value of films deposited with 0.1mol%Cu reaches to (92)% which is important for its applications as window layers in solar cells .The values of optical energy gap of NiO and Cu doping by 0.01,0.05, 0.1mol% were equal to 3.73 and (3.61,3.49,3.42eV) respectively.

في هذا البحث دُرست الخصائص التركيبية وفجوة الطاقة البصرية لأغشية NiO النقية والمشوبة بالنحاس بتراكيز مختلفة 0,0.01,0.05,0.1mol%)) نانوية بالسمك 100nmرسبت على قواعد زجاجية بتقنية الطلاء الدوار Spin Coating)) . بينت نتائج فحوصات XRD أن جميع الأغشية متعددة البلورات من النوع ألمكعبي مع قمة حادة سائدة باتجاهية 111)) .وقد تم حساب الحجم الحبيبي من بيانات XRD ووجد انه يَزداد حجم الحبيبات بزيادة نسبة التشويب في المدى 19.11 nm-23.05. بيانات AFM أشارت إلى نعومة سطوح الأغشية النفاذية البصرية لغشاء NiO النانوي ذات مقدار كبير تصل إلى94%) ) ضمن المنطقة المرئية وتستمر إلى المنطقة تحت الحمراء القريبة, تناقصت لتصل إلى 92%)) مع التشويب عند نسبة Cu 0.1mol% وهذا يؤكد أمكانية استخدامها كطبقات نافذة في الخلايا الشمسية . قيم فجوة الطاقة البصرية لغشاء NiO والأغشية المشوبة بالنحاس بالنسب 0.01,0.05,0.1 mol% 0,هيeV (3.73,3.61, 3.49, 3.42) على التوالي .

NiO:Cu --- nano films --- Sol-Gel method --- : Cu: NiO --- أغشية نانوية --- طريقة المحلول الغروي.