Improvement Of Properties Of Iraqi Bentonite For Foundry Moulding Sands
تحسين خواص البنتونايت العراقي لاغراض صناعة القوالب الرملية

Author: Ahid Younis Al-Mallah عاهد يونس الملاح
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2009 Volume: 14 Issue: 3 Pages: 176-184
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The deposit of bentonite (Upper Cretaceous and Danian ) is exposed at 35 km south of H3, western desert of Iraq. The bentonite consist of (55% -85%) highly crystalline (Ca , Na ) montmorillonite mineral, also palygorskite mineral and variable constituents include sepiolite, dolomite, calcite, francolite, quartz and lesser amount of barite and secondary gypsum.The bentonite is characterized by high content of calcite (5% - 15% ) and low cation exchange capacity ( 50 – 86 meq /100 gm ) . The slaking are common and the clay show low swelling power. The described properties lead to clay weak bonding properties for foundry moulding sands .Effort were made to enhance the green compression strength ,dry compression strength, plasticity and ability of dispersion, therefore the clay is subjected to purification and sodium carbonate activation according to production line (crushing-purification-activation-drying-milling-screening-end product) precede the application in foundry work. The results of quality control tests for treated clay are: humidity (2.35%), pH (9), colloidal content (100%), fineness (173%), L.O.I (13.6%) and swelling ratio (2 gm/ 31ml). After mixing with standard sand, the green compression amounts to (45-50 gm/cm²) and dry resistance to (1810-1930 gm/cm²). The end product comply with the standard specification of foundry moulding sands at Naser company/ Iraq .

تنكشف رواسب البنتونايت (الكريتاسي العلوي والدانيان ) على بعد (35 كم) جنوب محطة الضخ ( H3 ) / الصحراء الغربية – العراق. وتتالف من معدن المونتموريلونايت ( Ca ، Na ) عالي التبلور وبنسبة تتراوح (55% - 58%) فضلا عن معدن الباليغورسكايت وكميات متباينة من معادن السبيولايت، الدولومايت، الكالسايت، الفرانكولايت والكوارتز مع كميات قليلة من البارايت والجبس الثانوي.وتمتاز هذه الاطيان بارتفاع نسبة معدن الكالسايت (5 % - 15 % ) وسعة تبادل كتايوني منخفضة تراوحت مابين (meq/100gm 50 – 86) وقابلية انتفاخ واطئة من خلال شيوع ظاهرة الاطفاء (Slaking ) فيها. وادت هذه الصفات الى امتلاك اطيان المونتموريلونايت خواص ربط (Bonding Properties) ضعيفة وغير كافية في مجال استخدامها في صناعة القوالب الرملية ( Moulding sands ) . ولغرض تحسين قوى الربط لهذه الاطيان والمتمثلة بزيادة انضغاطيتها الرطبة (Green Compression Strength ) ومقاومتها الجافة ( Dry Compression Strength) فضلا عن زيادة البلاستيكية وقابلية قوة الانتشار وبالتالي زيادة الانتفاخ ، فقد خضعت اطيان المونتموريلونايت مختبريا وميدانيا الى عمليات تنقية لفصل الاحجام الفعالة وزيادة نسبة تبادل ايون الصوديوم بين طبقات معدن المونتموريلونايت من خلال عمليات التنشيط بالقاعدة ( (Na2CO3 وفق خط الانتاج ( تكسير الخام – معالجة وتركيز – تنشيط – تجفيف – طحن - نخل- منتوج نهائي ) .خضع المنتوج النهائي الى اعمال السيطرة النوعية الخاصة بصناعة القوالب الرملية.واظهرت النتائج ان نسبة الرطوبة تبلغ (2.35 %) والدالة الحامضية (pH= 9) والمحتوى الغروي ( 100 % ) والنعومة (173 %) والفقدان في الحرق (13.6%) بنسبة انتفاخ (2 gm/31 ml).كما اظهرت نتائج الخلط مع الرمل القياسي ان قيمة الانضغاطية الرطبة تراوحت مابين (gm/cm2 48 – 50 ) اما المقاومة الجافة فقد تراوحت مابين (gm/cm2 1810 - 1930) والتي تقع ضمن المديات المنصوص عليها في المواصفات الخاصة بصناعة القوالب الرملية في مسبك شركة نصر العامة.


Article
أستخدام كاربونات الكالسيوم الصوديوم في انتاج مخاريط عالية الحرارة

Authors: سلام احمد حمزة --- محمد حمزة المعموري --- عبد الحميد فاضل البياتي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 5 Pages: 1165-1178
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study included the possibility of using Kaolin Duekhla and sand Ardma as materials in the production of local thermal cones with the addition of other materials such as sodium carbonate and calcium carbonate, red lead oxide, potassium feldspar, borax and fled in different proportions as material help smelting.Chemical analysis was to sand Erdma and Kaolin Duekhla to prove disqualified for work. Models have been formed through the stone cast and after mixing materials in a dry water was added to it to facilitate manual stamping CBS models were then drying models degree oven 120c. Program was burning in the oven at a rate of 300c per hour. Was prepared nine models change ratios of sodium carbonate and calcium carbonate for the difference in the degree of bending.The results of the fusion behavior of calcium carbonate are extrusive nonlinear Unlike Sodium Carbonate, which is in reverse, with the higher percentage of carbonate, sodium told temperature, and vice versa, either (density) rises with increasing temperature extrusive nonlinear unlike (porosity) drops with increasing temperature incineration Lama (hardness) and (compressibility) with a gradual increase in the temperature rise

تضمنت هذه الدراسة امكانية استخدام كاؤلين دويخلة ورمل ارضمة بوصفها مواد اولية محلية في انتاج مخاريط حرارية مع إضافة مواد أخرى مثل كاربونات الصوديوم وكاربونات الكالسيوم, اوكسيد الرصاص الاحمر,فلسبار بوتاسيوم, والبوراكس فرت بنسب مختلفة كمواد مساعدة على الصهر . تم التحليل الكيميائي لرمل أرضمة و كاؤلين دويخلة لاثبات صلاحيتهما للعمل. تم تشكيل النماذج من خلال قالب جبسي وبعد خلط المواد بشكل جاف تمت إضافة الماء اليها لتسهيل كبس النماذج بالكبس اليدوي ثم تم تجفيف النماذج بالفرن بدرجة 120c . برنامج الحرق في الفرن كان بمعدل 300c لكل ساعة .تم نحضير تسعة نماذج بتغير نسب كاربونات الصوديوم وكاربونات الكالسيوم للحصول على فارق في درجات الانحناء.وبينت نتائج الانصهارية سلوك كاربونات الكالسيوم بشكل طردي لاخطي بعكس كاربونات الصوديوم التي هي بشكل عكسي اذ كلما ارتفعت نسبة كاربونات الصوديوم قلت درجة الحرارة والعكس صحيح,اما (الكثافة) فترتفع مع زيادة درجة الحرارة بشكل طردي لاخطي بعكس (المسامية) فتنخفض مع زيادة درجة حرارة الحرق اما (الصلادة) و(الانضغاطية) فزيادة تدريجية مع ارتفاع درجة الحرارة .


Article
أستخدام كاربونات الصوديوم وفلسبار بوتاسيوم في انتاج مخاريط واطئة الحرارة

Authors: سلام احمد حمزة --- محمد حمزة المعموري --- عبد الحميد فاضل البياتي
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2014 Volume: 22 Issue: 6 Pages: 1404-1415
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study included the possibility of using Kaolin Duekhla and sand Ardma as materials in the production of local thermal cones with the addition of other materials such as sodium carbonate and calcium carbonate, red lead oxide, potassium feldspar, borax and fled in different proportions as material help smelting.Chemical analysis was to sand and Erdma Kaolin Duekhla to prove disqualified for work. Models have been formed through the template created by the researcher and Gypsum After mixing the materials are dry water was added to it to facilitate manual stamping CBS models were then drying models degree oven 120c. Program was burning in the oven at a rate of 300c per hour.Was prepared seven models change ratios of sodium carbonate and potassium feldspar for the difference in the degree of bending. The results showed high temperature with increasing feldspar potassium and is extrusive nonlinear The results (density) an increase with increasing temperature is nonlinear and also results (compressibility) increase with rising temperature Lama (hardness) Increasing the few with a high temperature, unlike (porosity) decrease with increasing temperature.

تضمنت هذه الدراسة امكانية استخدام كاؤلين دويخلة ورمل ارضمة بوصفها مواد محلية في انتاج مخاريط حرارية مع إضافة مواد أخرى مثل كاربونات الصوديوم وكاربونات الكالسيوم,واوكسيد الرصاص الاحمر,وفلسبار بوتاسيوم, والبوراكس فرت بنسب مختلفة كمواد مساعدة على الصهر. تم التحليل الكيميائي لرمل أرضمة و كاؤلين دويخلة لاثبات صلاحيتهما للعمل. تم تشكيل النماذج من خلال قالب جبسي صنعه الباحث وبعد خلط المواد بشكل جاف تمت إضافت الماء اليها لتسهيل كبس النماذج بالكبس اليدوي ثم تم تجفيف النماذج بالفرن بدرجة 120c.برنامج الحرق في الفرن كان بمعدل300c لكل ساعة .تم تحضير سبعة نماذج بتغير نسب كاربونات الصوديوم وفلسبار بوتاسيوم للحصول على فارق في درجات الانحناء.وبينت النتائج ارتفاع درجة الحرارة مع زيادة فلسبار بوتاسيوم وبشكل طردي لاخطي وجاءت نتائج (الكثافة) بارتفاع مع زيادة درجة الحرارة بشكل لاخطي وايضا نتائج (الانضغاطية) زيادة مع ارتفاع درجة الحرارة اما (الصلادة) فزيادة قليلة مع ارتفاع درجة الحرارة بعكس (المسامية) انخفاض مع زيادة درجة الحرارة