Evaluations of Some Physical Properties of Cement with PVA/Polyol as Binder Material to produce insulating board
دراسة الخواص الفيزيائية لمزيج البوليمر البولي فاينيل اسيتيت/البولي اول المخلوط مع الاسمنت

Loading...
Loading...
Abstract

The composition of polymer blend (PVA/Polyol) by percentage 3:1, which is mixed with different a percentage (10%-90%) with different percentages of cement (10%-90%), where investigated. The optimal percentage of polymer blend and cement is 10% and 90% respectively. Physical properties of the mixture such as density, water absorption and compressive strength were determined; mixture of 10% cement was used as a binder to study the physical properties with different percentages of polymer blend and sand. This will prove a resistance to water absorption and can be used in ready construction panels.

تكوين مزيج من خلط البولي فينيل اسيتيت/البولي اول بنسبة 3:1الذي تم دراسته بنسب مختلفة (10-90)% مع نسب مختلفة من الاسمنت (10-90)%. كانت النسبة المثلى من خلط مزيج البوليمر و الاسمنت 10% و90% على التوالي. تم تعيين الخواص الفيزيائية للخليط، مثل الكثافة, امتصاص الماء و مقاومية الانضغاطية. كذلك دراسة الخواص الفيزيائية بأستخدام خليط بنسبة 10% اسمنت كرابط مع نسب مختلفة من مزيج البوليمر والرمل. هذا الخليط سوف يبرهن على مقاوميته لأمتصاص الماء وأمكانية أستخدامه في ألواح البناء الجاهز.


Article
Thermal Properties of Polyvinyl acetate (PVA) and Toluene Diisocyanate (TDI) With Prepared Solfonated Phenol Formaldehyde Resin (SPF) as Composites.
الخصائص الحرارية لمكون البولي فينايل اسيتيت/تلوين داي ايسوسيانيت مع راتنج الفينول-فورمالديهايد المسلفن المحضر

Author: Thamir Salman Bachari ثامر سلمان بجاري
Journal: basrah journal of science البصرة للعلوم ISSN: 18140343 Year: 2015 Volume: 33 Issue: 1A Pages: 47-69
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Two similar specimens of polyvinyl acetate (PVA) and toluene diisocyanate (TDI) blend and prepared solfonated phenol formaldehyde resin (SPF) as a mixture composite. SPF was diagnosed by infrared Fourier transformation (FTIR) spectrophotometer. The specimens were subjected to thermal heating by using copper electric heater; this was connected to d.c power supply. Three copper-constantan thermocouples were connected from junctions in two copper plates with dimension 4.2x 3.5x 0.2 cm3. in length, width and thickness respectively, to voltmeters for measuring the temperature across two similar specimens, with respect to the ambient and ice point temperatures. Negative electric potential (voltage) -2.7 mv and -3.1 mv dependence for thermal conductivity of the composite has indicated at 0.3%wtSPF. The calculated thermal conductivity were 0.0043 W.m-1.k-1 and 0.00239 W.m-1.k-1 at temperature 303 k and 203 k. for 0.2%wtSPF and 0.3%SPF respectively to 0.007 W.m-1.k-1 and 0.001 W.m-1.k-1 at 602.985 k and 582.999 k for 0.4%wtSPF and 2%wtSPF respectively. Maximum extrapolation is 0.07 W.m-1.k-1 for 1%wtSPF.

تم عمل نموجين متشابهين من مزج البولي فينايل اسيتيت و تلوين داي ايسوسيانيت مع نسب وزن مختلفة من راتنج الفينول-فورمالديهايد المسلفن المحضر لعمل خليط المكون. تم سكب الخلائط في قالبين متشابهين تم عملهما في صفيحتين من البولي اثلين, لتحضير نموذجين متشابهين لكل خليط. تم تشخيص البولي فينايل أسيتيت/تلوين داي أيسوسيانيت مع راتنج الفينول-فورماليهايد المسلفن بأستخدام جهاز مطياف تحويلات فورير للاشعة تحت الحمراء. تم تعريض النماذج للتسخين الحراري بأستخدام مسخن من النحاس والذي تم أيصاله الى مجهز قدرة. ثلاث مزدوجات حرارية تم أيصالها عبر نقاط في صفيحتين متشابهتين من النحاس بابعاد 0.2x 3.5x 4.2 سم3 في الطول, العرض والسمك على التوالي, الى فولتمترين لقياس درجة الحرارة النموذجين المتشابهين والمتماثلين لابعاد المسخن بالنسبة الى درجة حرارة المسخن والمحيط داخل المستودع ونقطة أنجماد الجليد. تم تعيين جهد سالب -2.7 ملي فولت -3.7 ملي فولت عند النسبة .0.3%wtSPFتم حساب التوصيلية الحرارية, 0.0043 واط.م-1. كلفن-1, , 0.00239 واط.م-.كلفن-1, عند درجة حرارة 313 كلفن و203 كلفن, للنسبة للنسبة 0.2%wtSPF و0.3%wtSPF. على التوالي و 0.007 واط.م-1.كلفن-1 و 0.001 واط.م-1.كلفن-1. عند درجة حرارة 602.985 كلفن و 582.999 كلفن للنسبة 0.4%wtSPF و 2%wtSPF على التوالي. أعلى قيمة استقرائية للمكون 0.07 واط.م-1زكلفن-1 للنسبة 1%wtSPF.