The Effect of Using a Paraffin Wax-Aluminum Chip Compound As Thermal Storage Materials in a Solar Air Heater
تأثير استخدام مجموعة الشمع البرافيني- برادة الالمنيوم كمواد خازنة للحرارة في مسخن هواء شمسي

Author: Khalil Ibrahim Abaas خليل ابراهيم عباس
Journal: Al-Rafidain University College For Sciences مجلة كلية الرافدين الجامعة للعلوم ISSN: 16816870 Year: 2014 Issue: 34 Pages: 259-284
Publisher: Rafidain University College كلية الرافدين الجامعة

Loading...
Loading...
Abstract

This paper presents an experimental investigation of a designed and fabricated air heater consisting of three cases. The first case used concrete as the main part of the air heater. The second case used paraffin wax as phase change material (PCM) accompanied with concrete as the main part of the air heater. In the third case aluminum chip was added to PCM and concrete. It was used as a thermal storage compound in a solar air heater. Results show that the exit air temperature was increased highly for the third case compared with the other cases and the efficiency of system was improved and the maximum storage efficiency achieved was 100% higher than the concrete case. The air heating gained was in its maximum value with the third case and the maximum increment achieved was 147.52% at Feb. also.

تم في هذه الدراسة تصميم وصناعة مسخن هواء يتضمن ثلاث حالات، في الحالة الأولى استخدم الكونكريت كجزء اساسي من مسخن الهواء، وفي الحالة الثانية اضيف الشمع البرافيني كمادة متغيرة الطور الى الكونكريت، وفي الحالة الثالثة اضيف برادة الألمنيوم الى مجموعة الكونكريت والمادة متغيرة الطور. واستخدمت التركيبة كخازن حراري لمسخن الهواء الشمسي.بينت النتائج ازدياد درجة حرارة الهواء الخارج بشكل كبير في الحالة الثالثة مقارنة بالحالتين الأخريين، كما تحسنت كفاءة النظام ووصلت قيمة كفاءة الخزن القصوى الى 100% أكثر من حالة استخدام الكونكريت بمفرده، كما كان الكسب الحراري للهواء المسخن في اعلى قيمه عند عمل المنظومة في الحالة الثالثة، وكانت اقصى زيادة تم الوصول لها 147.52% في شهر شباط.


Article
INVESTIGATION OF COMBINATION BETWEEN LATENT AND SENSIBLE HEAT STORAGE MATERIALS ON THE PERFORMANCE OF FLAT PLATE SOLAR AIR HEATER
دراسة التاثير المشترك لمادة الخزن الحراري الكامن والمحسوس كمادة خزن حراري جديدة على اداء سخان الهواء الشمسي المستوي

Loading...
Loading...
Abstract

In this work, a combination between latent heat storage materials (LHSm) and sensible heat storage materials (SHSm) as new storage heat material in flat plate solar air heater was tested experimentally. PCM (paraffin wax) at a certain ratios (10%) and (20%) were used as LHSm with a pure cement (base material) as SHSm. The experimental tests was done indoor at irradiance of (1000W/m2) with forced convection, the mass flow rate of air are (0.5kg/min) and (1.13kg/min). The results indicated that the enhancing thermo-physical properties of adding pure cement by a certain ratios of paraffin wax led to enhancement in thermal energy stored. The percentage increasing in storage heat duration time was (29%) for compound cement with (10%PCM), (38.4%) for compound cement with (20%PCM), compared with pure cement at (0.5kg/min) air mass flow rate. And at (1.13kg/min) air mass flow rate, it was (33.3%) for compound cement with (10%PCM) and (52.6%) for compound cement with (20%PCM) compared with pure cement.

في هذا العمل, الجمع بين مادة الخزن الحراري الكامن و مادة الخزن الحراري المحسوس كمادة خزن حراري جديدة في سخان الهواء الشمسي مستوي الصفيحة حضرت وفحصت عملياً. استخدمت مادة متغيرة الطور(شمع البارافين) بنسب محددة (10%) و (20%) استخدمت كمادة خزن حراري كامن مع السمنت النقي (مادة اساسية) كمادة خزن حراري محسوس. الفحوصات العملية تمت مختبرياً تحت تعرض اشعاع ( 1000واطمتر مربع) مع حمل قسري (0.5 كغدقيقة) و ( 1.131كغدقيقة). بينت النتائج ان التحسين بالخصائص الفيزيائية-الحرارية للسمنت النقي بإضافة نسب محددة من شمع البارافين ادى الى تحسين بالطاقة الحرارية المخزونة. كانت النسبة المئوية للزيادة بزمن التخزين الحراري (29%) لمركب السمنت مع (10% مادة متغيرة الطور), ( 38.4 %) لمركب السمنت مع (20% مادة متغيرة الطور) مقارنة مع السمن النقي عند معدل تدفق هواء كتلي (0.5كغدقيقة). و عند معدل تدفق هواء كتلي (1.13 كغدقيقة), كانت (33.3%) لمركب السمنت مع (10% مادة متغيرة الطور) و (52.6%) لمركب السمنت مع (20% مادة متغيرة الطور) مقارنة مع السمن النقي.