PREPARATION OF BaCoxTix Fe12-2x o19 Ferrite as RAM material at x- Band
تحضير ماصات رادارية لفيرايت نوع BaCoXTiXFe12-2xO19ضمن نطاق- X

Author: Ahmed .Rafeeq أحمد رفيق عبد المجيد
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2013 Volume: 9 Issue: 4 Pages: 30-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Composite RAM Material Single on Multilayer at x- Band Frequency (8-12.5 GHZ) Such as BaCoxTix Fe12-2x O19Prepared in Our Work For Different Values of x (0.25 , 0.5 , 0.7 , 0.9 ,).Reflection Loss (-dB)AND TANGENT Loss TAN Ɛ , TAN µ were Measured using Wave Guide System. Powder Technology used to Prepare the Above Ferrite at 1350 co for 12 hr as Sintering Temperature to be as Filler for Composite Absorber using Epoxy Resin as Amatrix. We Found in our Work that Barium Ferrite at Microwave Frequencies and That We Can Prepare Thin Layer Absorber Less Than 1mm Think RAMMaterials. We Found Also That at x=0.5 , 0.7 , 0.9 We Can Cover The Most Frequencie of the x – Band With Reflection Loss Larger Than (-20db) . So We Can Prepare Four Larger With Less Than 4mm Thickness With Band Width (3.5 GHZ ).

أن قلة انعدام المواد المناسبة التي تمتلك قيم نفاذية نسبية ( rµ) أكبر من واحد عند الترددات المايكروية اكبر من( (1GHz أدى الى أستخدام المواد الفرايتية سداسية التركيب نوع – M حيث تمتلك قيم ᴦμ(5~) على مديات ترددية ضيقة حيث تم تحضير فرايت نوع باريوم فرايت Ba Cox Tix Fe12-2x O19 ) ) وبقيم x:0.25 ,0.5 ,0.75 ,0.9) ) بطريقة تكنلوجيا المساحيق ودراسة خصائصها المغناطيسية والكهربائية وزاويةالفقد ومعامل الفقد ضمن ترددات النطاق – X(8-12.5 GHz) كماص أحادي الطبقة ومتعددة الطبقات وكمتراكب راتنجي مكون من ايبوكسي وحشوة فرايتية وبأسماك رقيقة تصل الى 1mm للطبقة الواحدة وبأربع طبقات تصل الى 2.5 mm .وأظهرت النتائج قيم الذروة لمعامل التوهين تصل الى (-32.2dB) ضمن النطاق الترددي 10.2 GHZلقيم x=0.25(-32.25dB) ضمن النطاق الترددي (8.2GHZ) لقيم x=0.5 وان لقيم x=0.7 هناك (-32.25dB) ضمن النطاق (8.8 GHZ) و(-26.4dB) ضمن النطاق (11.2GHZ) و (-21.66dB) ضمن النطاق (11.6GHZ) .ولقيم x=0.9 هناك تغطية كبيرة ضمن الترددات 8.2 GHZ و 9GHZ و 11.2 GHZ و 11.6GHZ وهكذا تصميم ماص متعدد الطبقات يمكن ان تغطي مدى واسع من ترددات النطاق ونعرض نطاق واسع كبير مما يؤكد ان هذا النوع من الفرايت اكثر أهمية من النوع ذو التركيب الرباعي .


Article
PREPARATION OF Single and multilayer RAMs of (Ni 0.4 Zn 0.6) 1-x (Fe2O3) 1+x Ferrite And studying Its Electrical And Magnetic Properties
تحضير ماصات رادارية متعددة الطبقات لفيرايت نوع(Ni0.4 Zn 0.6 )1-x(Fe2O3)1+x ودراسة خواصها المغناطيسية والكهربائية

Author: Dr AHMED RAFEEQ د. احمد رفيق عبدالمجيد
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2013 Volume: 9 Issue: 3 Pages: 1-10
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Composite RAM materials single and multi layer at x-Band frequencies (8-12.5GHz) were prepared by using ferrite of spindle type( Ni0.4 Zn 0.6) 1-x (Fe2o3)1+x as a filler and resins as matrix. The attenuation properties of the used ferrite (Ni0.4 Zn 0.6) 1-x (Fe2o3)1+x in our work such as reflection loss (-dB) and tangent loss tan δμ ,tan δE and the angle of loss δμ δE were studied carefully. Power technology Method used in our work to prepare the ferrite at sintering temperature 1300 as Filler for composite absorber. Attenuation character istic test was done by using slotted waveguide system show that ferrite mentioned above . having maximum attenuation (-29.4dB) at frequency 11.8GHz and (-20.8 dB ) at frequency 11.4 GHz (-34.1 dB) at frequency (10.2 GHz) and (-46.06) at frequency (10GHz) for different values of (x) .To increase the bandwidth frequencies we prepared multi layer absorber by using epoxy or PU resins as a matrix and add carbon- black powders to build multi-layer ferrite composites .We found that we have built excellent multi- layer RAMs with attenuation Greater than (-10dB) consisted of four layers less than 4mm thickness to cover the X-band frequencies with broadband width equal 3,5 GHz.

لبناء ماصات رادارية متراكبة ( احادية ومتعددة الطبقات )في النظام الترددي (8-12.5 GHz) يجب علينا اولا دراسة خصائصها المغناطيسيه والكهربائية وكذلك خصائص التوهين مثل قيم فقد الانعكاس وعرض النطاق الترددي الماص وسمك الماص الراداري وفي هذا البحث تم تحضير فيرايت النيكل زنك نوع 1+X(Fe2O3) 1-X(Zn0.6 Ni0.4) بطريقه السيراميك التقليدية عند درجة تلبيد (1300 ) لمده عشرة ساعات لاستخدامها كمادة حشو في عدة بوليمرات كمواد متراكبه لبناء ماصات رادارية احادية ومتعددة الطبقات وباستخدام الدليل الموجي تم قياس خصائص التوهين لهذه الطبقات وتبين ان هذه المواد الفيرايتية تمتلك دورة توهين مقداره dB(29.4-) عند التردد ((11.8GHz و (-20.8) عند التردد 11.4GHz)) و dB(-34.1) عند التردد GHz(10.2) و(-46.06) dB عند التردد 10 GHz وذلك حسب اختلاف القيم (x) وكذلك نوع المضيف ( matrix) مثل الايبوكسي او البولي يورثين ولاجل زيادة عرض النطاق تم اضافة مسحوق اسود الكاربون له وبنسب وزنية مختلفة وكذلك بناء ماصات متكونة من اربع طبقات وبسمك كلي لايتجاوز (4mm) لتغطية مديات النطاق الترددي باكمله وبعرض نطاق (3.5GHz)