Article
Preparation of Silver Nanoparticles by Sol - Gel Method and Study their Characteristics
تحضير الفضة النانوية بطريقة السول - جل ودراسة خصائصها

Loading...
Loading...
Abstract

Powder of silver nanoparticles was prepared by Sol - Gel method successfully using silver nitrate , (AgNO3) gesture is added to sodium citrate (C6H5O7Na3) as a reducing agent and by using Magnetic Stirrer to mix the solutions and heated then using centrifuge machine to separate the silver nanoparticles from solution .It is then dried in an oven at a temperature 40oC for 24 hours.Structure characteristics was studied , the synthetic silver powder was prepared through the use of an (XRD). Results showed the composition of silver nanoparticles is a (fcc) and a constant lattice (4.086 ± 0.006 Å) by comparing it with standard tables (JCPDS) which is found perfectly matched to file with a number 04-0783, which is due to the space group Fm3 ̅m No. 225.Particle size of nanoparticles was calculated for samples prepared using the Scherrer equation where the average grain size of (18.84 nm - 50.23 nm) was also found using the equation Williamson - Hall and ranged from (10.11 nm - 39.60 nm). As well as the mass density, density of dislocations, texture factor and the surface area of nano-particles were calculated. In addition samples prepared with an atomic force microscope (AFM) were examined and had the average diameter of the grains between (84.32 nm - 97.35 nm), and the average height ranged between (1.54 nm - 5.02 nm).

حُضر مسحوق الفضة النانوية بطريقة السول - جل بنجاح باستخدام نترات الفضة (AgNO3) بصفته بادرة يضاف لها سترات الصوديوم (C6H5O7Na3) عاملاً مختزلاً وبإسخدام المحرك المغناطيسي (Magnetic Stirrers) لخلط المحاليل وتسخينها ثم إستخدمت آلة الطرد المركزي ( (centrifuge machine لفصل الفضة النانوية عن المحلول ومن ثم تجفيفها في فرن بدرجة حرارة 40oC مدة 24 ساعة . دُرست الخصائص التركيبية لمسحوق الفضة المحضرة من خلال استخدام جهاز حيود الاشعة السينية (XRD). اظهرت نتائج (XRD) إن تركيب الفضة النانوية هو مكعب متمركز الاوجه (fcc) وبثابت شبيكة (4.086 ± 0.006 Å)وبمطابقتها مع الجداول القياسية (JCPDS) وجدت مطابقة تماماً للملف ذي الرقم 04-0783الذي يعود للمجموعة الفضائية (space group)Fm3 ̅m رقم 225)). حُسب حجم الحبيبات النانوية للعينات المحضرة باستعمال معادلة شيرر , إذ كان متوسط حجم الحبيبات من (18.84 nm – 50.23 nm) كما تم ايجادها باستعمال معادلة وليمسون - هول وكانت تتراوح من (10.11 nm –39.60 nm) . كذلك حُسبت الكثافة الكتلية وكثافة الإنخلاعات وعامل التشكيل والمساحة السطحية للحبيبات النانوية . فضلاً عن ذلك فحصت العينات المحضرة بمجهر القوة الذرية (AFM) وقد كان متوسط قطر الحبيبات يتراوح بين (84.32 nm – 97.35 nm) , ومتوسط ارتفاعها تراوح بين (1.54 nm – 5.02 nm) .


Article
XRD and AFM Analysis of Iron Oxide (Fe2O3) Thin Films Prepared by Chemical Spray Pyrolysis Method :The Effect of Substrate Temperature
تحليل صور الاشعة السينية ومجهز القوة الذرية لأغشية أوكسيد الحديديك (Fe2O3) المحضرة بطريقة التحلل الكيميائي الحراري: تأثير درجة حرارة القاعدة

Authors: Ahmed N. Jasim أحمد نصيف جاسم --- Asaad A. Kamil أسعد احمد كامل --- Khudheir A. Mishjil خضير عباس مشجل
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2015 Volume: 11 Issue: 3 Pages: 1-13
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Iron Oxide (Fe2O3) thin films were prepared by Chemical Spray Pyrolysis technique, on glass substrates at (400,450,500)°C , XRD analysis reveals that all the prepared films were polycrystalline and Hexagonal with a preferred orientation a long (104) plane, The increase in temperature cause an increase in the crystallization of film and homogeneity in addition to increase the grain size, It has been found that an increase in temperature leads to an increase in the crystalline grain size and working to improve the crystal structure. Moreover, the results showed an atomic force microscope (AFM) an increase in the values of the square root of the mean square roughness (RMS), an increase of temperature.

حضرت أغشية أوكسيد الحديديك (Fe2O3) بدرجات حرارة مختلفة باستخدام طريقة التحلل الكيميائي الحراري على قواعد زجاجية عند (400,450,500 °C)، وأظهرت نتائج فحوصات الاشعة السينية (XRD) ان كافة الاغشية المحضرة ذات تركيب متعدد التبلور من النوع السداسي وبالاتجاه السائد للمستوي (104). وقد أدت الزيادة بدرجات الحرارة الى زيادة في تبلور الغشاء وتجانسه فضلا عن زيادة الحجم الحبيبي، وقد وجد أن زيادة درجة الحرارة تؤدي إلى زيادة في حجم الحبيبات البلورية وتعمل على تحسين التركيب البلوري. فضلا عن ذلك فقد أوضحت نتائج مجهر القوة الذرّية (AFM) زيادة في قيم الجذر التربيعي لمربع متوسط الخشونة (RMS) بزيادة درجة الحرارة.


Article
Effect of Substrate Temperature on Structural and Optical Properties of CdO Thin Films
تأثير درجة حرارة القاعدة في الصفات التركيبية والبصرية لأغشيةCdO الرقيقة

Author: Hanan R. A. Ali حنان رضا عبد علي
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2016 Volume: 21 Issue: 3 Pages: 121-124
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Thin films of CdO have been prepared by spray pyrolysis technique. XRD analysis reveals that all the prepared samples were polycrystalline and have preferred orientation along [111] orientation. The surface topography was determined by AFM which indicate that surface roughness and rms roughness were increased by the increasing of substrate temperature. The optical energy gap was determined and its value lies between (2.4-2.5) eV.

تم تحضير اغشية CdO الرقيقة بتقنية التحلل الكيميائي الحراري. اظهر تحليل حيود الاشعة السينية XRD ان جميع النماذج المحضرة هي من نوع متعدد التبلور وأن اعلى المستويات البلورية كانت (111) للأغشية المرسبة كافة . وبينت نتائج مجهر القوة الذرية AFM ان جميع الأغشية المحضرة تمتلك سطحا ناعما وان قيمة متوسط الجذر التربيعي rms)) تزداد بزيادة درجة حرارة القاعدة وتراوحت قيمة فجوة الطاقة بين2.4- 2.5 الكترون فولت.


Article
Synthesis of Pure Nano semiconductor Oxide ZnO with Different AgNO3 Concentrations
تحضير اكاسيد اشباه الموصلات النانويه اوكسيد الخارصين النقي واضافه تراكيز مختلفه من نترات الفضه

Authors: Ali S. Al-Taie علي سلمان الطائي --- Hiba S. Abd Alwahab هبه سامي عبدالوهاب
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2017 Volume: 14 Issue: 2 Pages: 379-389
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Zinc oxide nanoparticles sample is prepared by the precipitation method. This method involves using zinc nitrate and urea in aqueous solution, then (AgNO3) Solution with different concentrations is added. The obtained precipitated compound is structurally characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Atomic force microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR). The average particle size of nanoparticles is around 28nm in pure, the average particle size reaches 26nm with adding AgNO3 (0.05g in100ml =0.002 M) (0.1g in100ml=0.0058M), AgNO3 (0.2g in 100ml=0.01M) was 25nm. The FTIR result shows the existence of -CO, -CO2, -OH, and -NO2- groups in sample and oxides (ZnO, Ag2O).and used an atomic force microscope and microscope scanning electron to model the record.

تم تحضير النموذج بطريقة الترسيب المباشرة لتخليق اوكسيد الخارصين باستخدام نترات الخارصين واليوريا في المحلول المائي واضافة نترات الفضة بتراكيز مختلفة. وقد تم دراسة خواص النموذج بواسطة حيود الاشعة السينية ومجهر الماسح الضوئي ومجهر القوة الذرية وطيف الاشعه تحت الحمراء .اظهرت النتائج بان متوسط حجم الجسيمات النانوية لاوكسيد الخارصين النقي 28 نانومتر وبعد اضافة المنشط ( نترات الفضة) بتراكيز مختلفة ( 0,05غم مذابة في 100مل=0,002مولاري)و(0.1غم مذابة في 100مل= 0,0058 مولاري) وصل الى 26نانومتر وباضافة ( 0,2غم مذابة في 100مل=0,01 مولاري) وصل الى 25 نانومتر.اظهر طيف الاشعة تحت الحمراء المجاميع الفعالة (CO- ,NO2-,COO- ,OH-) وموقع اوكسيد الفضة واوكسيد الخارصين.تم استخدام مجهر القوة الذرية ومجهر الماسح الالكتروني لتحاليل النموذج المحضر.


Article
Fabricated of Cu Doped ZnO Nanoparticles for Solar Cell Application
تشكيل جسيمات أكسيد الزنك النانويه المطعمه بالنحاس لتطبيقات الخلايا الشمسية

Authors: Nada K.Abass ندى خضير عباس --- Zainab J. Shanan زينب جاسم شنان --- Teeba H. Mohammed طيبة حسين --- Lamia K. Abbas لمياء خضير عباس
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2018 Volume: 15 Issue: 2 Pages: 198-204
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Copper with different concentrations doped with zinc oxide nanoparticles were prepared from a mixture of zinc acetate and copper acetate with sodium hydroxide in aqueous solution. The structure of the prepared samples was done by X-ray diffraction, atomic force microscopy (AFM) and UV-VIS absorption spectrophotometer. Debye-Scherer formula was used to calculate the size of the prepared samples. The band gap of the nanoparticle ZnO was determined by using UV-VIS optical spectroscopy.

تم تصنيع أوكسيد الزنك النانوي المطعم بتراكيز مختلفة من النحاس بطريقة الترسيب الكيميائي عند درجة حرارة الغرفة بواسطة التفاعل البسيط بين خلات الزنك وخلات النحاس مع هيدروكسيد الصوديوم في محلول مائي. ومن ثم دُرستَ الخصائص البصرية للمادة المصنعة بواسطة طيف الأمتصاص الاشعه فوق البنفسجيه والمرئية والخصائص التركيبة بواسطة حيود الاشعة السينية (XRD) ومجهر القوة الذرية (AFM). تم حساب حجم الحبيبة للمادة المحضرة بواسطة علاقة ديباي-شيرر من طيف الاشعة السينية ومن طيف الامتصاص. وأجريت دراسة التحليل الطيفي الضوئي . UV-VIS لتحديد فجوة الطاقة من أوكسيد الزنك جسيمات متناهية الصغر.


Article
Structural Analysis of Chemical and Green Synthesis of CuO Nanoparticles and their Effect on Biofilm Formation
تحليل التركيب لأوكسيد النحاس النانوي المصنع بالطريقة الكيميائية والنباتية وتأثيره على تكوين البايوفلم

Authors: Zainab J. Shanan زينب جاسم شنان --- Sabah M. Hadi صباح مهدي هادي --- Sabeeha K. Shanshool صبيحة خليل شنشول
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2018 Volume: 15 Issue: 2 Pages: 211-216
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Copper oxide nanoparticles (CuO NPs) were synthesized by two methods. The first was chemical method by using copper nitrate Cu (NO3)2 and NaOH, while the second was green method by using Eucalyptus camaldulensis leaves extract and Cu (NO3)2. These methods easily give a large scale production of CuO nanoparticles. X-ray diffraction pattern (XRD) reveals single phase monoclinic structure. The average crystalline size of CuO NPs was measured and used by Scherrer equation which found 44.06nm from chemical method, while the average crystalline size was found from green method was 27.2nm. The morphology analysis using atomic force microscopy showed that the grain size for CuO NPs was synthesized by chemical and green methods were 77.70 and 89.24 nm, respectively. The effectiveness of copper oxide nanoparticles on bacteria was measured for both gram positive, negative and fungi, copper oxide minutes showed excellent efficacy on biofilm formation.

صنع أوكسيد النحاس النانوي(CuO) بطريقتين, الأولى طريقة كيميائية بأستخدام نترات النحاس[Cu(NO3)2] وهيدروكسيد الصوديوم NaCl, اما الطريقة الثانية فكانت بطريقة نباتية بأستخدام مستخلص اوراق اليوكالبتوس (Eucalyptus camaldulensis) و[Cu(NO3)2]. تعد هذه الطرق من اكثر الطرق أنتاجية لمادة أوكسيد النحاس النانوي. أظهرت حيود الأشعة السينية XRD)) ظهور تركيب أحادي. ومعدل الحجم الحبيبي لمادة أوكسيد النحاس المصنع بالطريقة الكيميائية والمحسوب من معادلة شيرر (Scherer equation) حيث وجدت 44.06 نانومتر. في حين أن معدل الحجم البلوري لنفس المادة والمصنع بالطريقة النباتية تراوح 21.1نانومتر. كما أظهر التحليل التشكيلي بأستخدام المجهر القوة الذرية AFM)) بأن الحجم الحبيبي لمادة والمصنع بالطريقتين الكيميائية والنباتية بأنها تتراوح 77.70 و 89.24 نانومتر بالتتابع. وقد تم قياس تأثير أوكسيد النحاس النانوي على البكتيريا. وقد أظهرت دقائق أوكسيد النحاس النانوي فعالية جيدة على البكتيريا موجبة الغرام وسالبة الغرام والفطريات في تكوين البايوفلمbiofilm)).

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (5)

Arabic and English (1)


Year
From To Submit

2018 (2)

2017 (1)

2016 (1)

2015 (2)