Article
EFFECT OF GRAPHITE ON WEAR RESISTANCE OF ALUMINUM-SILICON ALLOY
تأثير الكرافيت على مقاومة البلى لسبيكة ألمنيوم - سيليكون

Loading...
Loading...
Abstract

This research deals with studying the effect of graphite on the wear resistance of aluminum – silicon alloy. Firstly this alloy (master alloy) is prepared using casting method then graphite particles added in weight ratio (5.5 %) by using vortex technique after that the master alloy and composite material casted in dies and prepared for sliding wear test , wear test was made under different conditions of applied load , sliding distance and surface roughness at the room temperature. The results show that wear rate increases with increasing any of the above conditions, also the composite material show higher resistance wear than of master alloy.

يتضمن البحث دراسة تأثير الكرافيت على مقاومة البلى لسبيكة ألمنيوم – سيليكون , إذ تم تحضير هذه السبيكة (السبيكة الأساس ) باستخدام طريقة السباكة بالمزج ثم إضافة دقائق الكرافيت بنسبة وزنية مقدارها (5.5%) باستخدام تقنية التحريك بتكوين دوامة (Vortex Technique) . بعدها تم صب السبيكة الأساس والمادة المتراكبة في قوالب معدنية وتحضيرها لاختبار البلى الانزلاقي حيث تم إجراء الاختبار تحت ظروف مختلفة من الحمل المسلط ومسافة الانزلاق وخشونة السطح وعند درجة حرارة الغرفة. من النتائج لوحظ إن معدل البلى يزداد في حالة زيادة أي من الظروف أعلاه وكذلك فان المادة المتراكبة تبدي مقاومة بلى أعلى منها في حالة السبيكة الأساس.


Article
Effect of Tempering Temperature on Wear Rate of Steel 100Cr6
تاثير درجة حرارة المراجعة على معدل البلى لفولاذ 100Cr6

Loading...
Loading...
Abstract

AbstractThis research aims to study the effect of quenching by oil with tempering at180°C and 400°C on wear rate of 100Cr6 steel. A pin-on-disc technique was used tomeasure wear rate at different loads and different sliding times with constant slidingspeed(2.199msec)and the hardness of steel dise was 45HRC.The results show that the wear resistance of the specimen quenched by oil andtempered at 400°C was more than the specimen quenched by oil and tempered at180°C.

الملخصيهدف البحث إلى د ا رسة تأثير التقسية بالزيت ثم إج ا رء الم ا رجعة عند درجات.100 Cr 400° على معدل البلى لفولاذ 6 C 180° و C ح ا رريةوقد استخدمت تقنيه المسمار على القرص لقياس معدل البلى عند تسليط أحمال مختلفة وفت ا رت.45HRC 2.199 ) وصلادة القرص الفولاذي msec) انزلاق مختلفة مع تثبيت سرعه الانزلاقوقد أظهرت النتائج ان معدل البلى يزداد مع زيادة الحمل المسلط والفترة الزمنية للانزلاق.وكذلك400° ذات مقاومه بلى C اظهرت النتائج ان العينه المقساة بالزيت والم ا رجعة عند درجه ح ا ررة.180°C أعلى بالمقارنة مع العينة المقساة بالزيت والم ا رجعة عند درجة ح ا ررة


Article
Wear Rate and Hardness of Boride Low Carbon Steel
معدل البلى والصلادة للفولاذ الواطئ الكاربون المبورن

Author: Jabbar Hussein Mohmmed جبار حسين محمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 10 Pages: 90-99
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

There are no single materials which can withstand all the extreme operating conditions in modern technology. Protection of the metals from hostile environments has therefore become a technical and economic necessity. In this work, for enhancing their wear-resistance, boride layers were deposited on the surface of low carbon steel by a pack cementation method at 850 °C for (2, 4, and 6) h using vacuum furnace. The boronizing process was achieved using different concentration of boron source (20, 25, and 30) % wt. into coating mixture to optimize the best conditions which ensure the higher properties with lower time. The coating was characteristic by X ray diffraction (XRD), and it is confirmed the presence of (Fe2B) and (FeB) in the coating. The wear rate, hardness and thickness of the boride layers were measured, and it was observed that they effected by concentration of boron and time holding of boronizing process. Experimental results show that the higher properties of coating layer were obtained with 30% wt. of boron concentration and 4 h time holding.

لا توجد مادة مفردة ممكن ان تتحمل ظروف التشغيل القاسية في التكنلوجيا الحديثة. لذلك, حماية المعدن من المحيط القاسي اصبح ضرورة تقنية واقتصادية. في هذا العمل، ولتحسين مقاومتها للبلى، تم ترسيب طبقات من البوريد على سطح الفولاذ المنخفض الكاربون باستخدام طريقة السمنتة الصلبة عند درجة حرارة 850 ْم ولازمان (2، 4، و6) ساعات باستخدام فرن مفرغ. تم اجراء عملية البورنة باستخدام تراكيز مختلفة لمصدر البورون (20، 25، و30) % من الوزن داخل خليط الطلاء للحصول على أفضل القيم لأفضل ظروف للحصول على أعلى خواص بأقل زمن. تم توصيف الطلاء باستخدام حيود الاشعة السينية وقد اثبتت وجود طوري (Fe2B) و(FeB) في الطلاء. تم قياس معدل البلى، الصلادة، وسمك طبقة البوريد، وقد لوحظ تأثرها بتركيز البورون وزمن الابقاء لعملية البورنة. اثبتت النتائج العملية ان افضل خواص ممكن الحصول عليها عند الطلاء ب 30 % من الوزن تركيز البورون مع زمن ابقاء 4 ساعات.


Article
WEAR RATE BEHAVIOR OF CARBON/EPOXY COMPOSITE MATERIALS AT DIFFERENT WORKING CONDITIONS
سلوك معدل البلى لمادة متراكبة ايبوكسي/الياف كاربون عند ضروف عمل مختلفة

Loading...
Loading...
Abstract

ABSTRACTA Pin -on- Disc wear testing rig of variable sliding speed with varying loadand sliding time has been used in this research to measure the wear rate of thecarbon/epoxy composite specimens at dry and wet working conditions.In this research the composite specimens made from the epoxy used as amatrix and the carbon fiber with length ≤ 3mm and volume fraction (3, 6 & 9 vol. %)as reinforcement.The results show that the wear rate of composite specimens increase innonlinear relationship with increase the applied load, sliding speed and sliding timeand decrease in nonlinear relationship with increase the volume fraction of carbonfiber.The results also show that the wear rate for the epoxy reinforced by carbonfibers for dry working conditions was higher than the wear rate for wet workingconditions. The maximum percentage reduction in wear rate was 30% for wetworking conditions and 18.5 % for dry working conditions at 9 % Vol. of carbonfibers when compared with the neat epoxy.

الخلاصةلقد استخدم جهاز قياس البلى ( المسمار - على - قرص ) ذو السرع المختلفة مع تغير الحمل وزمن الانزلاق لقياس معدلالبلى لعينات متراكبة مصنوعة من الايبوكسي المقوى بالياف الكاربون عند ضروف عمل جافة ورطبة.3mm ≥ في هذا البحث العينات المركبة مصنوعة من راتنج الايبوكسي كمادة اساس مقواة والياف الكاربون المتقطعة بطول3) كمادة تقوية. بينت النتائج بان معدل البلى للعينات المركبة يزداد بعلاقات لاخطية مع زيادة , 6 & 9 vol. %) وبكسر حجميالحمل المسلط والسرعة الانزلاقية والزمن الانزلاقي ويقل بعلاقات لاخطية مع زيادة الكسر الحجمي لالياف الكاربون. وكذلك بينت النتائجبان معدل البلى للايبوكسي المقوى بالياف الكاربون عندالضروف الجافة اعلى من معدل البلى عند الضروف الرطبة لنفس الكسر الحجمي.9) كانت (% 30 ) عند Vol.%) وان اقصى نسبة انخفاض في معدل البلى للايبوكسي المقوى بالياف الكاربون بكسر حجميالعمل في الضروف الرطبة و (% 18.5 ) عند العمل في الضروف الجافة مقارنة مع الايبوكسي الغير مقوى بالياف الكاربون


Article
Effect of Different Quenching Media on Microstructure, Hardness, and Wear Behavior of Steel Used in Petroleum Industries
تأثير أوساط التقسية المختلفة على التركيب المجهري، الصلادة، وسلوك البلى للفولاذ المستخدم في الصناعات النفطية

Authors: Jabbar Hussein Mohmmed --- Zahid I. Al-Hashimy
Journal: Journal of Petroleum Research & Studies مجلة البحوث والدراسات النفطية ISSN: 22205381 Year: 2018 Issue: 19 Pages: E198-E207
Publisher: Ministry of Oil وزارة النفط

Loading...
Loading...
Abstract

Medium carbon steel always used in most parts of the oil and gas industry, due to their cheap, simple manufacturing and easy deformation. However, as-rolled medium carbon steel usually does not meet the demands for many petroleum applications where high hardness and strength are needed; mainly because of their limitations in some mechanical features. Hence, many methods of thermal treatment techniques were adopted with a view to manipulate its structure and thus extend its scope of applications.This study focus on using a proper heat treatment to enhance medium carbon steel properties.Quenching and tempering treatments are usually the end of any manufacturing process to production of a machine component. However, the internal and residual stresses which generate during the heat treatments due to the non-uniform the quenched layer depth lead to distortion or cracked the machine component result in deteriorate the properties. Thus, the selection of optimum parameters of the quenching process is very important to ensure the achievement of the desired properties of the machine component. The main aim of this study is to get the optimal conditions for heat treatment which brought the best combination of mechanical properties of medium carbon steel without tempering treatment. Thus, in current study, an investigation of effects of polymer solution media on the quenching process was carried out with samples made of medium carbon steel. The samples were quenched in four different concentrations (0, 10, 15, 20) % of polymer (polyalkylene glycol) solution and set of quenched samples were tempered at 400 oC for 1h. The resulting as-quenched and tempered microstructures were compared and evaluated. Mechanical properties (hardness and wear rate) of the samples were determined using suitable standards. The results show that the quenched samples in polymer solution with 10% polyalkylene glycol were brought the best combination of mechanical properties as compared with other quenched and tempered samples.

الفولاذ المتوسط الكاربون عادة مستخدم في اغلب الاجزاء في صناعة النفط والغاز نتيجة لرخص ثمنه، بساطة تصنيعه، وسهولة تشكليه. لكن، عادة الفولاذ المتوسط الكاربون بحالته المدرفلة لا يلبي احتياجات العديد من التطبيقات النفطية والتي تحتاج الى مقاومة وصلادة عالية وذلك بسبب محدداته ببعض الصفات الميكانيكية. لهذا فقد اعتمدت العديد من تقنيات التعامل الحراري بغية تعديل تركيب الفولاذ وبالتالي توسيع نطاق تطبيقاته. هذه الدراسة تركز على استخدام معاملة حرارية مناسبة لتعزيز خواص الفولاذ المتوسط الكاربون. معاملات التقسية والمراجعة تكون عادة هي الانهاء لأي عملية تصنيع لإنتاج أجزاء الماكنة. لكن الاجهادات الداخلية والمتبقية والتي تتكون خلال المعاملات الحرارية بسبب عدم انتظام عمق طبقة التصليد تؤدي الى تشوه وتشقق أجزاء المكائن وبالنتيجة انخفاض الخواص. لهذا، اختيار العناصر المثلى لعملية التقسية يكون جدا مهم لضمان الحصول على الخواص المرغوب بها لجزء الماكنة. الهدف الرئيس لهذه الدراسة هو الحصول على الظروف المثلى للمعاملة الحرارية التي من خلالها نحصل على أفضل مجموعة من الخواص الميكانيكية للفولاذ المتوسط الكاربون بدون عملية المراجعة. لهذا، في الدراسة الحالية، تم اجراء دراسة لتأثيرات أوساط المحاليل البوليميرية على عملية التقسية لعينات مصنوعة من الفولاذ المتوسط الكاربون. تم تقسية العينات في أربع تراكيز مختلفة (0، 10، 15، 20) % لمحلول (polyalkylene glycol) البوليميري وتم اجراء عملية مراجعة عند 400م0 لمدة ساعة واحدة لمجموعة من العينات المقساة. التراكيب المجهرية للعينات المقساة والمراجعة تم مقارنتها وتقييمها. الخواص الميكانيكية (الصلادة ومعدل البلى) للعينات تم تحديدها باستخدام مقاييس ملائمة. بينت النتائج ان العينات المقساة بالمحلول البوليميري 10 % (polyalkylene glycol) قد اعطت أفضل مجموعة للخواص الميكانيكية عند مقارنتها بالعينات الأخرى التي تم تقسيتها ومراجعتها.


Article
Mechanical and Tribological Behavior of Glass- Polyester Composite System under Graphite Filler Content
تاثير كمية دقائق الكرافيت على السلوك الميكانيكي والترايبولوجي لراتنجات البولي استر المقوى بالياف الزجاج

Authors: Farag M. Mohammed --- Drai A. Smait
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 4 Pages: 672-683
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Experimental investigations had been done in this work to demonstrate the effect ofgraphite filler contents on the mechanical and tribological behavior of (30% volumefraction) glass-polyester composite system. The stress-strain relations, modulus ofelasticity, yield stress, ultimate tensile strength and ultimate compression strength werestudied according to ASTM-D 638-87and ASTM-D 695 to present the compositemechanical behavior. The wear rate and wear resistance were investigated according toASTM-D 5963 using pin on disc machine to present the composite tribological behavior.The results showed that the mechanical and tribological properties behavior wasimproved when the graphite filler content was increased up to 7.5% and then decreasedafter that. At 7.5% filler content the modulus of elasticity, yield stress, ultimate tensilestrength, ultimate compression strength and wear resistance increased by (41%, 64%,24%, 60% and 38%) greater than unfilled composite, while the wear rate was decreasedby 27% less than the unfilled one.

في هذا البحث تمت دراسة تأثير كمية الكرافيت على السلوك الميكانيكي والترايبولوجي لراتنجاتالبولي استر المقوى بالياف الزجاج عمليا وعند كسر حجمي 30 %. تم اختبار علاقة الاجهاد- الانفعالASTM-D ) و معامل المرونة و اجهاد الخضوع ومقاومة الشد والانضعاط الاعظم للمادة المتراكبة وفقالبيان تاثير كمية الكرافيت على السلوك الميكانيكي . ولمعرفة السلوك (ASTM-D 638-87 و 695بينت نتائج .ASTM-D الترايبولوجي تم اجراء اختبارات معدل البلى ومقاومة البلى وفقا 5963الاختبارات ان الخواص الميكانيكية والترايبولوجية تزداد بزيادة كمية الكرافيت الى اعلى قيمها عند%7.5 ومن ثم تنخفض بزيادة الكرافيت. عند كمية كرافيت 7.5 % فان معامل المرونة واجهاد الخضوع41% ) اكثر منها بدون الكرافيت في حين معدل البلى يقل عنها بمقدار % 27


Article
EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE
تأثير النسب الوزنية لمادة الزجاج والمعاملة الحرارية على الخواص الميكانيكية ومعدل البلى لمتراكبات الألمنيوم - 2% كرافيت

Author: Hashim Shukur Hammood هاشم شكر حمود الكرغولي
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2017 Volume: 10 Issue: 4 Pages: 33-41
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

This research studied the effect of the Heat Treatment on the Mechanical Properties and the Wear Rate of the pure Aluminum with a particle size of (≤53μm). The Aluminum is reinforced by graphite with a particle size of (≤63μm) with an addition of glass particles with different weight ratios of (3, 6, 9, and 12) Wt. % and a particle size was (≤ 53μm).Powder metallurgy technique has been used to manufactured the samples, where the samples are pressed uniaxial at room temperature with (500 Map), then sintering at (550 C0) for (2 hr.). After that, heat treatment is applied on the samples at (500 OC) for one hour and Quenched in water.There was a great improvement of the mechanical properties such as the hardens and the compressive strength. This improvement was proportional with the Weight ratio of the glass particles before and after the Heat Treatment.On the other hand, there was a decrease of the wear rate versus the increase of the Weight ratio of the glass particles and heat treatment.

يهدف هذا البحث الى دراسة تأثير اضافة دقائق الزجاج بنسب وزنية مختلفة Wt%(3,6,9,12) بحجم (≤53 μm) مع اضافة نسبة وزنية ثابتة % 2 من كرافيت بحجم جسيمي(≤ 63 μm) وتأثير المعاملة الحرارية على الخواص الميكانيكية ومعدل البلى للالمنيوم النقي وبحجم جسيمي (≤53 μm) .استُخدمت تقانة ميتالورجيا المساحيق لتصنيع النماذج اذ كبست النماذج على البارد بضغط كبس ( Mpa500) تم تلبيدها بدرجة حرارة (550 Co) ولمدة ساعتين ثم سُخنتْ النماذج الى درجة حرارة (500 Co) لمدة ساعة واحدة ثم بردت بالماء.بعدَ اجراء فحص الصلاده ومقاومة الانضغاط اظهرت النتائج حدوث تحسن كبير في الصلاده ومقاومة الانضغاط مع زيادة نسب اضافة دقائق الزجاج الى المتراكب قبل وبعد المعاملة الحرارية.تبين من خلال اختبار البلى حدوث انخفاض واضح مع زيادة نسب الاضافة قبل وبعد المعاملة الحرارية.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (4)

Arabic (3)


Year
From To Submit

2018 (1)

2017 (1)

2015 (1)

2012 (1)

2011 (2)

More...