Polymer Modified Polystyrene Concrete
خرسانة البوليستايرين المطورة بالبوليمر

Author: Yousif Khalaf Yousif يوسف خلف يوسف
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2011 Volume: 4 Issue: 2 Pages: 80-93
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This research work includes production of polymer modified polystyrene concrete and studies the mechanical properties. Several proportions of raw materials were used to produce this type of concrete. This study is intended to improve the mechanical properties of light weight polystyrene concrete using styrene butadiene rubber(SBR) with rate of (5,10,15and20)% of cement weight. Compressive strength, flexural strength, impact strength and dry density tests were made on more than 150 specimen at age of 28 days. The results show that the addition of (SBR) with range of (5-20)%of cement weight is improve the flexural strength with range (3.74-18)%, and improve the impact strength with range (39-163)%. Also the results show that it is possible to produce polystyrene concrete with density (1680,1433 and 1147) kg/m3 replacing light weight Polystyrene aggregate with volume fraction (30,50 and70)%of sand.

تضمن هذا البحث إنتاج ودراسة الخواص الميكانيكية لخرسانة البوليستايرين المطورة بالبوليمر،حيث تم استخدام نسب مختلفة من المواد الأولية الداخلة في إنتاج هذا النوع من الخرسانة . يهدف البحث إلى تحسين بعض الخصائص الميكانيكية لخرسانة البوليستايرين خفيفة الوزن باضافة البوليمر (مطاط الستايرين – بيوتادين SBR- ) بنسبة ( 5، 10، 15، 20 )%من وزن السمنت. تم اجراء فحص مقاومة الانضغاط ، مقاومة الانثناء ، مقاومة الصدم ، وفحص الكثافة الجافة على اكثر من 150 نموذج بعمر 28 يوم، وقد اثبتت النتائج ان اضافة (مطاط الستايرين – بيوتادين SBR- ) ضمن المدى ( 5 - 20 )% من وزن السمنت يؤدي الى تحسين مقاومة الانثناء بنسبة (3.74 – 18 )% وتحسين مقاومة الصدم بنسبة (39 -163 )%. كما اثبتت النتائج امكانية انتاج خرسانة البوليستايرين ذات كثافة (1680 ، 1433 ، 1147 )كغم/م3 وذلك بتعويض ركام البوليستايرين بنسبة (30، 50 ، 70 )% من حجم الركام الناعم.


Article
Studying of Some Mechanical Properties of Reactive Powder Concrete Using Local Materials
دراسة بعض الخواص الميكانيكية لخرسانة المساحيق الفعالة باستخدم مواد محلية

Author: Mohammed Mansour Kadhum محمد منصور كاظم
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 7 Pages: 113-135
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59% have been achieved for reinforced RPC contains 910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values were 1.5 times higher for the normal strength concrete in comparison with the reactive powder concrete.

يهدف هذا البحث لتحري وتقييم خرسانة المساحيق الفعالة المصنوعة من استخدام مواد اقتصادية. تم دراسة وتقييم خواصها الميكانيكية باستخدام انواع مختلفة من السمنت وغبار السيلكا والياف الحديد المحلية الصنع. من النتائج العملية المستحصلة لوحظ بان مقاومة الانضغط للخرسانة كانت 155,2 ميكاباسكال، 16,0 ميكاباسكال مقاومة الشد الغير مباشرة، 48,7 ميكاباسكال معامل المرونة الاستاتيكي، 43,5 ميكاباسكال لمقاومة الانثناء، 3294,4 كن.م و 0.59% فقدان الاحتكاك وهذه القيم تحققت لخرسانة المساحيق الفعالة المسلحة بالالياف بنسة حجمية 2% والحاوية على سمنت 910 كغم/م3 ومحتوى السيلكا 185 كغم/م3 من وزن السمنت. اما مقدار الامتصاص فقد سجل من الشغل العملي 1.5 مرة اكثر للخرسانة الاعتيادية مقارنة بخرسانة المساحيق الفعالة.


Article
Studying of Some Mechanical Properties of Reactive Powder Concrete Using Local Materials
دراسة بعض الخواص الميكانيكية لخرسانة المساحيق الفعالة باستخدم مواد محلية

Author: Mohammed Mansour Kadhum محمد منصور كاظم
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 7 Pages: 113-135
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59% have been achieved for reinforced RPC contains 910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values were 1.5 times higher for the normal strength concrete in comparison with the reactive powder concrete.

يهدف هذا البحث لتحري وتقييم خرسانة المساحيق الفعالة المصنوعة من استخدام مواد اقتصادية. تم دراسة وتقييم خواصها الميكانيكية باستخدام انواع مختلفة من السمنت وغبار السيلكا والياف الحديد المحلية الصنع. من النتائج العملية المستحصلة لوحظ بان مقاومة الانضغط للخرسانة كانت 155,2 ميكاباسكال، 16,0 ميكاباسكال مقاومة الشد الغير مباشرة، 48,7 ميكاباسكال معامل المرونة الاستاتيكي، 43,5 ميكاباسكال لمقاومة الانثناء، 3294,4 كن.م و 0.59% فقدان الاحتكاك وهذه القيم تحققت لخرسانة المساحيق الفعالة المسلحة بالالياف بنسة حجمية 2% والحاوية على سمنت 910 كغم/م3 ومحتوى السيلكا 185 كغم/م3 من وزن السمنت. اما مقدار الامتصاص فقد سجل من الشغل العملي 1.5 مرة اكثر للخرسانة الاعتيادية مقارنة بخرسانة المساحيق الفعالة.


Article
Behaviour of Reinforced Polymer Modified High Strength Concrete Slabs under Low Velocity Impact
تصرف الألواح الخرسانية ذات المقاومة العالية والمطورة البوليمر تحت الصدم واطئ السرعة

Author: Abdulkader Ismail Al-Hadithi عبد القادر إسماعيل الحديثي
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2012 Volume: المؤتمر الهندسي الأول لكلية الهندسة Issue: العدد الخاص - الجزء الثاني Pages: 171-189
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This research investigates the impact resistace of reinforced high strength concrete slabs with steel meshes (BRC) modified by styrene butadiene rubber (SBR) with different weight ratios of polymer to cement as follows: 3%, 5% and 7%. Reference mix was produced for comparison of results.For all selected mixes, cubes (100×100×100mm) were made for compressive strength test at (365) days. In conducting low-velocity impact test, method of repeated falling mass was used: 1400gm steel ball falling freely from height of 2400mm on reinforced panels of (50×50×800 mm) reinforced with one layer of (BRC).The number of blows causing first crack and final perforation (failure) were calculated, according to the former results, the energy of each case was found.Results showed an improvement in compressive strength of polymer modified high strength concrete (PMHSC) over reference mix; the maximum increase being of it were (3.93%-11.96%) at age of (365) days.There is significant improvement in low-velocity impact resistance of all polymer modified mixes over reference mix. Results illustrated that polymer modified mix of (3%) give the its higher impact resistance than others, the increase of its impact resistance at failure over reference mix was (154.76%) while, for polymer modified mix (5%) it was (30.95%) and it was (14.28%) for polymer modified mix of (7%).

يتضمن هذا البحث دراسة مقاومة الصدم لألواح خرسانية عالية المقاومة مسلحة بشبكات حديدية (BRC) ومحورة ببوليمر الـ Styrene Butadiene Rubber (SBR) . لقد تمت إضافة مادة البوليمر كنسبة مئوية من وزن السمنت حيث تم استخدام ثلاث نسب من (البوليمر:سمنت) وهي 3% ، 5% و 7% ، كما وتم انتاج خلطة مرجعية لغرض المقارنة.تم عمل مكعبات خرسانية بأبعاد (100×100×100ملم) لغرض فحص مقاومة الانضغاط لجميع الخلطات المختارة بعمر(365) يوم وأستخدم اسلوب الإسقاط الحر المتكرر لكرة فولاذية تزن 1400 غم من ارتفاع 2400ملم على الألواح الخرسانية بابعاد (50×50×800 ملم) والمسلحة بطبقة واحدة من الشبكات الحديدية (BRC) لغرض فحص مقاومة الصدم بالسرعة المنخفضة. لقد تم حساب عدد الضربات المسببة للتشقق الابتدائي والاختراق النهائي للكرة الفولاذية (الفشل) وإعتماداً على هذه النتائج تم حساب طاقة الصدم الكلية لكل حالة.اظهرت النماذج المصنعة من الخرسانة العالية المقاومة والمحورة بالبوليمر تحسناً في مقاومة الانضغاط ولقد كان مقدار الزيادة في مقاومة الانضغاط عن الخرسانة المرجعية يتراوح ما بين (3.93% - 11.96%) بعمر (365) يوم. لوحظ تحسناً في فحص مقاومة الصدم بالسرعة الواطئة لجميع الخلطات المحورة بالبوليمر عن الخلطة المرجعية, حيث أعطت نماذج الخلطات الثلاث المحورة بالبوليمر نتائج لمقاومة الصدم أعلى من الخلطة المرجعية وأظهرت النتائج المستحصلة من العمل المختبري بان الخلطة المحورة بالبوليمر بنسبة (3%) قد أعطت أعلى مقاومة للصدم حيث كان مقدار الزيادة في هذه المقاومة عند الفشل عنها للخلطة المرجعية هو (154.76%) بينما كان هذا المقدار للخلطة بنسبة بوليمر (5%) هو (30.95%) وكان (14.28%) للخلطة بنسبة بوليمر (7%).


Article
Influence of Mix Proportions on The Impact Resistance of High Strength Concrete
تأثير نسب المزج على مقاومة الصدم للخرسانة عالية المقاومة

Authors: Ali Hussain Ali علي حسين علي --- Mohammed Hazim Yasin محمد حازم ياسين
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2014 Volume: 18 Issue: 3 Pages: 84-103
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This research aim to study the Influence of mix proportions on the impact resistance of high strength concrete, Trial laboratory batches were used including as follows: -Normal concrete mixture (C1) as a reference mix ((w/c) = 0.45, without admixtures);-Four concrete mixtures (C2, C3, C4, C5) prepared by fixing (w/c) =0.45, and using different amount of super plasticizers (0.25, 0.50, 0.75, 1.00)% as a percentage of cement content, respectively; -Four concrete mixtures (C6, C7, C8, C9) prepared by reducing and fixing (w/c) = 0.30, and using silica fume = (15)% as replacement of cement content and different amount of superplasticizers (1.25, 1.50, 1.75, 2.00)% as a percentage of cement content; and -Three concrete mixtures (C10, C11, C12) prepared by fixing the amount of superplasticizers (1.50)% and using different (w/c) = (0.40, 0.29, 0.27).Results show that Mixture C11 prepared with (1.50%) addition of superplasticizers and (15%) addition of silica fume leads to (90.29%) increasing in the compressive strength and records an improvement in the impact resistance by (725.56%) as compared with the reference mix. On the other hand, all of the mix proportions lead to an increase in both compressive strength and impact resistance for all the mixes.

يهدف هذا البحث الى دراسة تاثير نسب المزج على مقاومة الصدم للخرسانة عالية المقاومة, حيث تم القيام بعمل خلطات تجريبية تتضمن كالاتي:-خلطة مرجعية C1 (نسبة (ماء/ سمنت) = 0,45 , بدون مضافات); -اربعة خلطات خرسانية (C2,C3,C4,C5) بتثبيت نسبة الماء الى السمنت = 0,45 واضافة كميات مختلفة من الملدنات الفائقة (0,25, 0,50, 0,75, 1,00)%, كنسب مئوية من وزن السمنت; -اربعة خلطات خرسانية (C6,C7,C8,C9 ) بتقليل وتثبيت نسبة الماء الى السمنت = 0,30 مع استعمال السليكا فيوم 15% كنسبة استبدال من وزن السمنت واضافة كميات مختلفة من الملدنات الفائقة (1,25, 1,50, 1,75, 2,00)%, كنسب مئوية من وزن السمنت; -وثلاث خلطات خرسانية(C10,C11,C12) بتثبيت نسبة الملدنات الفائقة = 1,50% واستعمال نسبة ماء الى السمنت (0,40, 0,29, 0,27).بينت النتائج ان الخلطة الخرسانية (C11) والتي تحتوي (1,5)%من الملدنات الفائقة و (15)% سليكافيوم ادت الى (90,29)زيادة بمقاومة الانضغاط وتحسين مقاومة التاكل والبري بنسبة(725,56)% مقارنة مع الخلطة المرجعية ,مع ملاحظة ان جميع نسب المزج ادت الى زيادة بمقاومة الانضغاط ومقاومة الصدم لجميع الخلطات الخرسانية.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

Arabic and English (3)

English (2)


Year
From To Submit

2015 (2)

2014 (1)

2012 (1)

2011 (1)