Some Durability Test of No-Fine Concrete
بعض فحوصات ديمومة الخرسانه الخاليه من الركام الناعم

Authors: Shakir Ahmed Salih شاكر أحمد صالح --- Tuqa Alaa Fidel تقى علاء فاضل
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 1 Pages: 15-30
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, two types of mixes were adopted by using two grading of coarse aggregate. The practical side of this study was to produce no-fine aggregate concrete by using crushed clay brick aggregates. The durability of the produced concrete and internal sulfate attack was studied. For durability assessment, it is found that the no-fine concrete made with crushed brick aggregate lost about (15-25) % of its compressive strength after being subjected to 60 cycles of wetting and drying with age 120 days. The curing condition showed that the water curing improved the compressive strength with a rate higher than that when sealed or air dry curing were used. The crushed brick no-fine concrete deteriorated in compressive strength after exposure to internal sulfate attack for 60 cycles; the percentage decrease was about (23.33-25) and (25-27.5) % for 0.57 and 0.83sulfate content respectively.

تم خلال هذه الدراسه استخدام نوعين من الخلطات الخرسانيه الخفيفه الوزن حاويه على تدرجين من الركام الخشن. تضمن الجانب العملي من البحث انتاج خرسانه خاليه من الركام الناعم باستخدام الركام الاعتيادي ومكسر الطابوق. وتم دراسة ديمومة الخرسانه الخفيفه في البحث. لتقيم الديمومه وجد ان مقاومه الانضغاط للخرسانه الخاليه من الركام الناعم تنخفض من (15-25) % بعد تعرضها الى 60 دورة ترطيب وتجفيف بعمر يعادل 120 يوم. كما وجد ان مقاومه لانضغاط عند انضاج النماذج في الماء افضل مقارنا مع انضاجها في الهواء الجاف او المغلفه باستخدام النايلون. كما دلت النتائج على تدهور الخرسانه الخاليه من الركام الناعم بعد تعرضها الى 60 دوره ترطيب وتجفيف كما وجد ان معدل النقصان في مقاومه الانضغاط يصل الى (25-27.5) % عندما يكون محتوى الاملاح 0.57 و 0.83 على التوالي.


Article
Effect of Addition of A Marble Dust on Drying Shrinkage Cracks of Cement Mortar Reinforced with Various Fibers

Author: Basim Thabit Al-Khafaji
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 2 Pages: 652-669
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This investigation is conducted to study the effect of addition of marble powder (marble dust) and different fibers on drying shrinkage cracks and some properties of fibers reinforcment cement mortar. Steel molds having a trapezoidal section, and the end restrained at square shape with( 2.7 meter) at length are used to study restrained drying shrinkage of cement mortar. Specimens of ( compressive .flextural. splitting strength) were cast. The admixture (marble dust) was used to replacie weight of cement with three levels of (4%, 8% and 16%) and the fiber hemp and sisal fiber were added for all mixes with proportion by volum of cement . All specimens were cured for (14 days). Average of three results was taken for any test of compressive, tensil and flextural strength. The experimental results showed that the adding of this admixture(marble dust) cause adelay in a formation of cracks predicted from a drying shrinkage ,decreases of its width , and hence increases of (compressive, splitting tensil and flextural strength) at levels of (4%, and 8%). Thus there is a the positive effect when fiberes added for all mixes of cement mortar with addition of (marble dust). All The admixtures (marble dust and fibers) have the obvious visible effect in the delay of the information of shrinkage cracks and the decrease of its width as Compared to the cement mortar mixes when marble dust added a alone.

هذه الدراسة تهدف الى دراسة تأثير اضافة (غبار المرمر) مع الياف مختلفة على انكماش الجفاف وبعض الخواص لمونة السمنت المسلحة بالالياف، في هذه الدراسة تم استخدام قوالب حديدية بمقطع على شكل شبه منحرف بطول (2.7 متر) ومن نهايتيه قالب بشكل مربع لغرض تقييد النموذج لضمان حدوث (تشققات انكماش الجفاف) لمونه السمنت وأيضاً تم صب نماذج لغرض تعيين مقاومة الانضغاط ومقاومة الانشطارو الانثناء. استخدمت ثلاث نسب مئوية من) مسحوق المرمر( وهي (4% مر و 8% و 16%) كاستبدال من وزن السمنت , واستخدمت الياف ( السيسال واالقنب ). بنسب حجمية من السمنت .تم انضاج النماذج جميعاً بفترة إنضاج) 14 يوم(. تم اخذ معدل ثلاثة نتائج لكل فحص من مقاومة الانضغاط والشد و الانثناء. أوضحت النتائج العملية أن إضافة ا المضاف(MD ( يؤخر حدوث التشققات الناتجة من (انكماش الجفاف ( لمونة السمنت ويقلل من عرضها ويزيد من مقاومة الانضغاط والشد و الانثناء عند النسب (4% و 8%) ونفس التاثير عند اضافة الالياف لمونة السمنت جميعا و كل على حدة مع (غبار المرمر) ولكل نسب الاضافة لها . وعند اضافةالالياف مع غبار المرمر سوية نلاحظ تأثير ملموس في تأخير حدوث (تشققات الانكماش(في مونة السمنت و تقليل في عرض تلك التشققات مقارنة مع خلطات مونة السمنت المضاف لها غبار المرمر لوحده .